CN103820055A - 一种海洋工程用导电胶 - Google Patents
一种海洋工程用导电胶 Download PDFInfo
- Publication number
- CN103820055A CN103820055A CN201310668973.8A CN201310668973A CN103820055A CN 103820055 A CN103820055 A CN 103820055A CN 201310668973 A CN201310668973 A CN 201310668973A CN 103820055 A CN103820055 A CN 103820055A
- Authority
- CN
- China
- Prior art keywords
- parts
- conductive adhesive
- conductive resin
- nano
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种海洋工程用导电胶，所述导电胶的组成以重量份数计为：液体端羧基丁腈橡胶环氧树脂15～20份，分散剂0.05～0.5份，固化剂1～1.5份，微米银粉65～75份，纳米银颗粒0.08～4份，纳米碳管5～10份。该导电胶在5℃下贮存期为9个月。分别于100℃、120℃和140℃热固化1－2小时。液体端羧基丁腈橡胶环氧树脂，兼用适量的分散剂代替市场上普遍采用的环氧树脂，极大的提高了胶的耐高温性能，加入微米银粉、纳米银颗粒及纳米碳管极大提高了其导电性能，而加入导电和导热纳米碳管同时更提高了其导电和导热性能，同时具有良好的耐腐蚀性、耐侯性，使其适合船舶、海洋工程使用。
Description
技术领域
本发明涉及一种海洋工程用导电胶。
背景技术
导电胶是一种固化或干燥后具有一定导电性能的胶黏剂，它通常以基体树脂和导电填料即导电粒子为主要组成成分， 通过基体树脂的粘接作用把导电粒子结合在一起， 形成导电通路， 实现被粘材料的导电连接。由于导电胶的基体树脂是一种胶黏剂， 可以选择适宜的固化温度进行粘接， 同时，由于电子元件的小型化、微型化及印刷电路板的高密度化和高度集成化的迅速发展，而导电胶可以制成浆料， 实现很高的线分辨率。而且导电胶工艺简单，易于操作，可提高生产效率，所以导电胶是替代铅锡焊接， 实现导电连接的理想选择。
在导电胶领域中，环氧树脂由于其优良的性能在导电胶领域的应用十分广泛。但是，环氧树脂粘合剂体系也存在一些问题，例如粘度较大、耐热性较低、脆性强、保存时间短等。因此研制一种粘度适中、韧性强、耐高温、耐海洋环境腐蚀，并且保存时间长的环氧导电胶成为目前亟待解决的技术问题。
发明内容
为解决上述问题，本发明提供了一种海洋工程用导电胶。
所述导电胶的组成以重量份数计为：液体端羧基丁腈橡胶环氧树脂15～20份，分散剂0.05～0.5份，固化剂1～1.5份，微米银粉65～75份，纳米银颗粒0.08～4份，纳米碳管5～10份。
进一步的，所述分散剂为3－缩水甘油醚氧基丙基三甲氧基硅烷。
进一步的，所述固化剂为双腈胺、三乙烯四胺或其混合物。
进一步的，所述固化剂为双腈胺和三乙烯四胺的混合物，双腈胺和三乙烯四胺的质量比为1：2。
进一步的，所述导电胶的制备过程为：按重量份称取原料，在液体端羧基丁腈橡胶环氧树脂，加入微米银粉、纳米银颗粒及纳米碳管以转速400-500r/min搅拌15min，然后加入分散剂、固化剂继续搅拌15min，混合均匀后，移至三辊机上连续滚混三次制得导电胶。
本发明的积极效果在于：该导电胶在5℃下贮存期为9个月。分别于100℃、120℃和140℃热固化1－2小时。
液体端羧基丁腈橡胶环氧树脂，兼用适量的分散剂代替市场上普遍采用的环氧树脂，极大的提高了胶的耐高温性能，加入微米银粉、纳米银颗粒及纳米碳管极大提高了其导电性能，而加入导电和导热纳米碳管同时更提高了其导电和导热性能，同时具有良好的耐腐蚀性、耐侯性，使其适合船舶、海洋工程使用。
具体实施方式
下面结合实施例详细说明本发明的技术方案，但保护范围并不受此限制。
实施例1
液体端羧基丁腈橡胶环氧树脂15份，3－缩水甘油醚氧基丙基三甲氧基硅烷0.05份，双腈胺1.5份，微米银粉65份，纳米银颗粒4份，纳米碳管5份。
制备过程为：按重量份称取原料，在液体端羧基丁腈橡胶环氧树脂，加入微米银粉、纳米银颗粒及纳米碳管以转速400-500r/min搅拌15min，然后加入分散剂、固化剂继续搅拌15min，混合均匀后，移至三辊机上连续滚混三次制得导电胶。
实施例2
液体端羧基丁腈橡胶环氧树脂20份，3－缩水甘油醚氧基丙基三甲氧基硅烷0.2份，三乙烯四胺1.5份，微米银粉70份，纳米银颗粒1份，纳米碳管5份。
导电胶的制备过程为：按重量份称取原料，在液体端羧基丁腈橡胶环氧树脂，加入微米银粉、纳米银颗粒及纳米碳管以转速400-500r/min搅拌15min，然后加入分散剂、固化剂继续搅拌15min，混合均匀后，移至三辊机上连续滚混三次制得导电胶。
实施例3
液体端羧基丁腈橡胶环氧树脂18份， 3－缩水甘油醚氧基丙基三甲氧基硅烷0.08份，双腈胺0.4，三乙烯四胺0.8份，微米银粉70份，纳米银颗粒2份，纳米碳管8份。
按上述重量份称取原料，在液体端羧基丁腈橡胶环氧树脂，加入微米银粉、纳米银颗粒及纳米碳管以转速400-500r/min搅拌15min，然后加入分散剂、固化剂继续搅拌15min，混合均匀后，移至三辊机上连续滚混三次制得导电胶。
Claims (5)
1.一种海洋工程用导电胶，其特征在于：所述导电胶的组成以重量份数计为：液体端羧基丁腈橡胶环氧树脂15～20份，分散剂0.05～0.5份，固化剂1～1.5份，微米银粉65～75份，纳米银颗粒0.08～4份，纳米碳管5～10份。
2.根据权利要求1所述的一种海洋工程用导电胶，其特征在于：所述分散剂为3－缩水甘油醚氧基丙基三甲氧基硅烷。
3.根据权利要求1所述的一种海洋工程用导电胶，其特征在于：所述固化剂为双腈胺、三乙烯四胺或其混合物。
4.根据权利要求1所述的一种海洋工程用导电胶，其特征在于：所述固化剂为双腈胺和三乙烯四胺的混合物，双腈胺和三乙烯四胺的质量比为1：2。
5.根据权利要求1所述的一种海洋工程用导电胶，其特征在于：所述导电胶的制备过程为：按重量份称取原料，在液体端羧基丁腈橡胶环氧树脂，加入微米银粉、纳米银颗粒及纳米碳管以转速400-500r/min搅拌15min，然后加入分散剂、固化剂继续搅拌15min，混合均匀后，移至三辊机上连续滚混三次制得导电胶。