CN103819097A - 一种加花折弯玻璃的制造方法 - Google Patents

一种加花折弯玻璃的制造方法 Download PDF

Info

Publication number
CN103819097A
CN103819097A CN201410082326.3A CN201410082326A CN103819097A CN 103819097 A CN103819097 A CN 103819097A CN 201410082326 A CN201410082326 A CN 201410082326A CN 103819097 A CN103819097 A CN 103819097A
Authority
CN
China
Prior art keywords
glass
parts
bending
paint
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410082326.3A
Other languages
English (en)
Inventor
冯继燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410082326.3A priority Critical patent/CN103819097A/zh
Publication of CN103819097A publication Critical patent/CN103819097A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种加花折弯玻璃的制造方法，包括有以下步骤：（1）加花：使用高温的玻璃油漆在玻璃上加花，玻璃油漆是由以下各组分的原料组成：羟乙基纤维素11-12份、滑石粉4-6份、碱式氯化铋3-5份、水溶树脂5-6份、丁醇3-4份、硬脂酸丁酯5-6份、光油2-4份、水30-40份；玻璃油漆的温度为500-600℃；（2）折弯：采用热弯玻璃机，在热弯温度为600-700℃的环境下对加花后的玻璃进行折弯成型。采用上述玻璃油漆和温度，可以使得玻璃油漆很好地附着于玻璃上，具有很好的耐酸耐碱耐水性，玻璃油漆在接受二次高温加热时不会掉漆，可快速地先在未折弯的玻璃上进行喷涂着色加花，然后再进行折弯，提高了作业效率，有效提升了产品质量，为玻璃的加工制造带来方便。

Description

一种加花折弯玻璃的制造方法
技术领域
本发明涉及玻璃加工制造领域技术，尤其是指一种加花折弯玻璃的制造方法。
 
背景技术
现有的玻璃钢化加工是对 5mm-20mm 厚度的平板玻璃在成套的加工设备中经过炉体的低温区进入高温区根据不同的玻璃厚度确定不同的加热时间，然后送出炉体在风栅区进风栅钢化处理，玻璃的折弯变形加工是在炉膛内高温区后进入折弯变形区，开启两侧的加热管放下上压杠，炉体两侧配重铁按到要求位置，变形后的玻璃再送至风栅钢化区进行钢化，上述玻璃的加工钢化工艺比较成熟，为了使折弯后的玻璃更加美观，通常使用玻璃油漆在玻璃上进行热喷涂着色加花。即现有技术中是采用先折弯后加花的方式对玻璃进行加工，采用此种方式的主要原因是目前的玻璃油漆附着力不够好，不能进行二次高温加热，否则会出现掉漆现象，现有技术中，采用上述方式虽然可避开玻璃油漆进行二次高温加热，然而上述方式难以对玻璃的弯位进行喷镀着色加花，效率较低，并且产品质量不好。
 
发明内容
有鉴于此，本发明针对现有技术存在之缺失，其主要目的是提供一种加花折弯玻璃的制造方法，其能有效解决现有之折弯玻璃采用先折弯后喷涂着色加花的方式存在难以对玻璃的弯位进行喷镀着色加花导致效率较低、产品质量不好的问题。
为实现上述目的，本发明采用如下之技术方案：
一种加花折弯玻璃的制造方法，包括有以下步骤：
（1）加花：使用高温的玻璃油漆配合利用玻璃印花机在玻璃需要折弯的位置上以及平面上加花，玻璃油漆是由以下各组分的原料组成 ：羟乙基纤维素 11-12 份、滑石粉 4-6 份、碱式氯化铋 3-5 份、水溶树脂 5-6 份、丁醇 3-4 份、硬脂酸丁酯5-6 份、光油2-4份、水 30-40 份；玻璃油漆的温度为500-600℃；
（2）折弯：采用热弯玻璃机，在热弯温度为600-700℃的环境下对加花后的玻璃进行折弯成型。
优选的，羟乙基纤维素为11份，滑石粉为5份、碱式氯化铋为5份、水溶树脂为6份、丁醇为3.5份、硬脂酸丁酯为5份、光油为3份、水为37份；玻璃油漆的温度为575℃；热弯温度为650℃。
本发明与现有技术相比具有明显的优点和有益效果，具体而言，由上述技术方案可知：
通过采用上述配方的玻璃油漆，并配合采用上述温度，可以使得玻璃油漆很好地附着于玻璃上，并具有很好的耐酸耐碱耐水性，同时，玻璃油漆在接受二次高温加热时不会掉漆，如此可快速地先在未折弯的玻璃上进行喷涂着色加花，然后再进行折弯，完全取代了传统之先折弯后喷涂着色加花的方式，大大提高了作业效率，同时也有效提升了产品质量，为玻璃的加工制造带来方便。
 
具体实施方式
一种加花折弯玻璃的制造方法，包括有以下步骤：
（1）加花：使用高温的玻璃油漆配合利用玻璃印花机在玻璃需要折弯的位置上以及平面上加花，玻璃油漆是由以下各组分的原料组成 ：羟乙基纤维素 11-12 份、滑石粉 4-6 份、碱式氯化铋 3-5 份、水溶树脂 5-6 份、丁醇 3-4 份、硬脂酸丁酯5-6 份、光油2-4份、水 30-40 份，以上为质量分数；玻璃油漆的温度为500-600℃，通过采用上述配方的玻璃油漆，并配合采用上述温度，可以使得玻璃油漆很好地附着于玻璃上，并具有很好的耐酸耐碱耐水性，同时，玻璃油漆在接受二次高温加热时不会掉漆。
在本实施例中，以下面配方为最佳：羟乙基纤维素为11份，滑石粉为5份、碱式氯化铋为5份、水溶树脂为6份、丁醇为3.5份、硬脂酸丁酯为5份、光油为3份、水为37份；同时，以玻璃油漆的温度575℃最佳，附着力最强，耐酸耐碱耐水性最好，更好地防止在二次高温加热时发生掉漆现象。
（2）折弯：采用热弯玻璃机，在热弯温度为600-700℃的环境下对加花后的玻璃进行折弯成型，在本实施例中，以热弯温度665℃为最佳。
本发明的设计重点是：通过采用上述配方的玻璃油漆，并配合采用上述温度，可以使得玻璃油漆很好地附着于玻璃上，并具有很好的耐酸耐碱耐水性，同时，玻璃油漆在接受二次高温加热时不会掉漆，如此可快速地先在未折弯的玻璃上进行喷涂着色加花，然后再进行折弯，完全取代了传统之先折弯后喷涂着色加花的方式，大大提高了作业效率，同时也有效提升了产品质量，为玻璃的加工制造带来方便。
以上结合具体实施例描述了本发明的技术原理。这些描述只是为了解释本发明的原理，而不能以任何方式解释为对本发明保护范围的限制。基于此处的解释，本领域的技术人员不需要付出创造性的劳动即可联想到本发明的其它具体实施方式，这些方式都将落入本发明的保护范围之内。

Claims (2)

1.一种加花折弯玻璃的制造方法，其特征在于：包括有以下步骤：
（1）加花：使用高温的玻璃油漆配合利用玻璃印花机在玻璃需要折弯的位置上以及平面上加花，玻璃油漆是由以下各组分的原料组成 ：羟乙基纤维素 11-12 份、滑石粉 4-6 份、碱式氯化铋 3-5 份、水溶树脂 5-6 份、丁醇 3-4 份、硬脂酸丁酯5-6 份、光油2-4份、水 30-40 份；玻璃油漆的温度为500-600℃；
（2）折弯：采用热弯玻璃机，在热弯温度为600-700℃的环境下对加花后的玻璃进行折弯成型。
2.如权利要求1所述的一种加花折弯玻璃的制造方法，其特征在于：所述羟乙基纤维素为11份，滑石粉为5份、碱式氯化铋为5份、水溶树脂为6份、丁醇为3.5份、硬脂酸丁酯为5份、光油为3份、水为37份；玻璃油漆的温度为575℃；热弯温度为665℃。
CN201410082326.3A 2014-03-07 2014-03-07 一种加花折弯玻璃的制造方法 Pending CN103819097A (zh)