CN103817764B - The manufacture method of mahogany furniture - Google Patents
The manufacture method of mahogany furniture Download PDFInfo
- Publication number
- CN103817764B CN103817764B CN201410067682.8A CN201410067682A CN103817764B CN 103817764 B CN103817764 B CN 103817764B CN 201410067682 A CN201410067682 A CN 201410067682A CN 103817764 B CN103817764 B CN 103817764B
- Authority
- CN
- China
- Prior art keywords
- furniture
- parts
- casting
- tenon
- timber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the manufacture method of a kind of mahogany furniture, decrease to greatest extent wood change and taking out of causing is swollen, cracking;Reduce the loss of the original waxiness of timber, increase the mechanical property of timber, reduce the reduction of the original toughness of timber;Joinery and its construction degree of accuracy is high, efficiency is high, degree of tightness is suitable;The natural texture of furniture material, color and luster, breath can be remain, and color and luster gentleness is natural;It is easily recognized out the real material of furniture;It is easily recognized the fineness of the processing technology such as carver, polishing;Wax natural environmental-protective on furniture surface, meets healthy living location;During use, waxing furniture top layer gloss can be increasingly brighter.
Description
Technical field
The present invention relates to the manufacture method of mahogany furniture.
Background technology
The manufacture method of existing mahogany furniture, has the drawback that
1, timber waxiness runs off big, and mechanical property is deteriorated, and toughness reduces;
2, joinery and its construction is not ideal enough;
3, it is not easy to recognize the real material of furniture;
4, it is not easy to recognize the fineness of the processing technology such as carver, polishing;
5, furniture material is natural texture, color and luster, breath can not effectively preserve;
6, can not effectively reduce wood to change and swollen, the cracking of taking out of causing etc..
Summary of the invention
It is an object of the invention to overcome defect present in prior art, it is provided that a kind of redwood man
The manufacture method of tool, decreases wood change to greatest extent and taking out of causing is swollen, cracking;Subtract
The loss of few original waxiness of timber, increases the mechanical property of timber, reduces the original toughness of timber
Reduce;Joinery and its construction degree of accuracy is high, efficiency is high, degree of tightness is suitable;Furniture material sky can be remain
Right texture, color and luster, breath, and color and luster gentleness are natural;It is easily recognized out the real of furniture
Material;It is easily recognized the fineness of the processing technology such as carver, polishing;Wax on furniture surface
Natural environmental-protective, meets healthy living location;During use, waxing furniture top layer gloss can be got over
Come the brightest.
For achieving the above object, the technical scheme is that and design the manufacture of a kind of mahogany furniture
Method, comprises the steps:
1) select materials: select log according to the profile of each furniture parts, color, texture, will
Sapwood removed by log, leaves core;
2) sawing sheet: core is sawn into all parts woollen for forming furniture;
3) it is dried: all parts woollen is classified, is respectively implanted drying baker and is dried, temperature
Degree controls at 25-65 DEG C, and arid cycle is 25-35 days, by the drying of wood to moisture
8%-12%;
4) casting: dried all parts woollen is carried out casting by electrical heating wax injector,
The composition of institute's casting is 100% macromolecule synthesising wax, and temperature controls at 100-200 DEG C, according to plate
Material thickness and density are adjusted, and the casting cycle is 10-15 days, make waxiness 100% penetrated wood,
It is not intended to be limited to timber top layer;
5) thicknesser: all parts woollen after casting is made parts concentrate respectively through thicknesser,
The size making all parts of composition furniture is more accurate;
6) mortise chisel eye: by the connection of furniture all parts, make joinery and its construction, institute
Stating tenon structure is double tenon structure, length of tenon 30-40mm, width 25-35mm, thickness
5-10mm, the gap between tenon and tenon is 5-10mm;
7) engraving and tentatively polishing: to needing the parts carved to carry out Carving Machining, then
Tentatively is polished in surface;
8) fine buff: all parts is carried out respectively more than 3 times polishings, by each portion
Part ground smooth;
9) priming: to all parts last time priming paint after a fine buff, then pass through
It is polished for a plurality of times, each parts surface paint matter is all polished totally, leave behind the part penetrating into pore;
Described priming paint is environmental protection seal coat;
10) assemble: all upper parts crossing priming paint are assembled;
11) secondary fine smooth poliss: the furniture assembled is carried out 7-8 polishing, makes furniture table
It is reflective that face presents minute surface.
12) wax: at furniture surface last layer Cera Flava.
Preferably, described polishing uses No. 600-5000 husky skin.
Through the furniture that above step is produced, under 30 DEG C of dry weathers of constant temperature, will not ftracture,
Will not deform;Will not expand out in the environment of region following the line of the sea weather is relatively more moistening.Maximum limit
Decrease wood to change and swollen, the cracking of taking out of causing etc. degree.
After furniture made by timber after dry casting, completely solve and do not stay asking of expansion joint
Topic;
Being dried the timber after casting, its original waxiness runs off seldom;
Being dried the timber after casting and add mechanical property, original toughness reduces small.
Double tenon in joinery and its construction connects, and degree of accuracy is high, efficiency is high, degree of tightness is suitable.
Furniture after waxing remains the texture of the natural uniqueness of furniture material, color and luster, breath, and
And color and luster gentleness is natural;
It is easily recognized out the real material of furniture;
It is easily recognized the fineness of the processing technology such as carver, polishing;
Through the Cera Flava natural environmental-protective of processed, meet healthy living location;
During use, waxing furniture top layer gloss can be increasingly brighter;
In use, natural " bag slurry " can be gradually formed, be the natural of a kind of uniqueness
Protective layer.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Below
Embodiment is only used for clearly illustrating technical scheme, and can not limit with this
Protection scope of the present invention.
The technical scheme that the present invention is embodied as is:
The manufacture method of a kind of mahogany furniture, comprises the steps:
1) select materials: select log according to the profile of each furniture parts, color, texture, will
Sapwood removed by log, leaves core;
2) sawing sheet: core is sawn into all parts woollen for forming furniture;
3) it is dried: all parts woollen is classified, is respectively implanted drying baker and is dried, temperature
Degree controls at 25-65 DEG C (preferably 25 DEG C, 45 DEG C, 65 DEG C), and arid cycle is 25-35 days
(preferably 25 days, 30 days, 35 days), by the drying of wood to moisture 8%-12% (preferably
It is 8%, 10%, 12%);
4) casting: dried all parts woollen is carried out casting by electrical heating wax injector,
The composition of institute's casting is 100% macromolecule synthesising wax, and temperature controls at 100-200 DEG C (preferably
100 DEG C, 150 DEG C, 200 DEG C), adjusted according to sheet metal thickness and density, the casting cycle is
10-15 days (preferably 1-10 days, 13 days, 15 days), make waxiness 100% penetrated wood, not
It is limited only to timber top layer;
5) thicknesser: all parts woollen after casting is made parts concentrate respectively through thicknesser,
The size making all parts of composition furniture is more accurate;
6) mortise chisel eye: by the connection of furniture all parts, make joinery and its construction, institute
Stating tenon structure is double tenon structure, length of tenon 30-40mm, width 25-35mm, thickness
5-10mm, the gap between tenon and tenon is 5-10mm;
7) engraving and tentatively polishing: to needing the parts carved to carry out Carving Machining, then
Tentatively is polished in surface;
8) fine buff: all parts is carried out respectively more than 3 times polishings, by each portion
Part ground smooth;
9) priming: to all parts last time priming paint after a fine buff, then pass through
It is polished for a plurality of times, each parts surface paint matter is all polished totally, leave behind the part penetrating into pore;
Described priming paint is environmental protection seal coat;
10) assemble: all upper parts crossing priming paint are assembled;
11) secondary fine smooth poliss: the furniture assembled is carried out 7-8 polishing, makes furniture table
It is reflective that face presents minute surface.
12) wax: at furniture surface last layer Cera Flava.
Described polishing use No. 600-5000 husky skin (preferably No. 600 husky skins, No. 2000 husky skins,
No. 5000 husky skins).
The above is only the preferred embodiment of the present invention, it is noted that lead for this technology
For the those of ordinary skill in territory, on the premise of without departing from the technology of the present invention principle, it is also possible to
Making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (1)
1. the manufacture method of mahogany furniture, it is characterised in that comprise the steps:
1) select materials: select log according to the profile of each furniture parts, color, texture, will
Sapwood removed by log, leaves core;
2) sawing sheet: core is sawn into all parts woollen for forming furniture;
3) it is dried: all parts woollen is classified, is respectively implanted drying baker and is dried, temperature
Degree controls at 25-65 DEG C, and arid cycle is 25-35 days, by the drying of wood to moisture
8%-12%;
4) casting: dried all parts woollen is carried out casting by electrical heating wax injector,
The composition of institute's casting is 100% macromolecule synthesising wax, and temperature controls at 100-200 DEG C, casting week
Phase is 10-15 days, makes waxiness 100% penetrated wood, is not intended to be limited to timber top layer;
5) thicknesser: all parts woollen after casting is made parts concentrate respectively through thicknesser,
The size making all parts of composition furniture is more accurate;
6) mortise chisel eye: by the connection of furniture all parts, make joinery and its construction, institute
Stating joinery and its construction is double tenon structure, length of tenon 30-40mm, width 25-35mm, thickness
5-10mm, the gap between tenon and tenon is 5-10mm;
7) engraving and tentatively polishing: to needing the parts carved to carry out Carving Machining, then
Tentatively is polished in surface;
8) fine buff: all parts is carried out respectively more than 3 times polishings, by each portion
Part ground smooth;
9) priming: to all parts last time priming paint after a fine buff, then pass through
It is polished for a plurality of times, each parts surface paint matter is all polished totally, leave behind the part penetrating into pore;
Described priming paint is environmental protection seal coat;
10) assemble: all upper parts crossing priming paint are assembled;
11) secondary fine smooth poliss: the furniture assembled is carried out 7-8 polishing, makes furniture table
It is reflective that face presents minute surface;
12) wax: at furniture surface last layer Cera Flava;
Wherein, described polishing uses No. 600-5000 husky skin.