CN108556435A - A kind of biological nano waterproof wood floor and its manufacturing method - Google Patents
A kind of biological nano waterproof wood floor and its manufacturing method Download PDFInfo
- Publication number
- CN108556435A CN108556435A CN201810364661.0A CN201810364661A CN108556435A CN 108556435 A CN108556435 A CN 108556435A CN 201810364661 A CN201810364661 A CN 201810364661A CN 108556435 A CN108556435 A CN 108556435A
- Authority
- CN
- China
- Prior art keywords
- layer
- biological nano
- base material
- timber
- nano waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of biological nano waterproof wood floor and its manufacturing methods, including base material timber layer, it is pasted with upper timber layer, wood grain layer, biological nano waterproof layer and wearing layer successively in the upper surface of base material timber layer, undergrowth, balance timber layer and biological nano waterproof layer are pasted with successively in the lower surface of base material timber layer;The matched clamping groove of size and clamping tenon is respectively set in the relative side of base material timber layer, the two sides that clamping groove and clamping tenon are located in base material timber layer are provided with side waterproof layer.The overall structure advantages of simple of the biological nano waterproof wood floor, waterproof effect is excellent, and not easy to crack;By being coated with biological nano waterproof layer on surface and bottom edge, and side waterproof layer is coated in side, can comprehensive raising timber floor water resistance, and it is safe and reliable;In addition, the manufacturing process of the biological nano waterproof wood floor is simple, easily produce in batches.
Description
Technical field
The present invention relates to timber floor technical field, more specifically, it relates to a kind of biological nano waterproof wood floor and its
Manufacturing method.
Background technology
Timber floor refers to the floor made of timber, and the timber floor of domestic product is broadly divided into solid wooden floor board, strengthens wood ground
Plate, solid wooden compound floor, multi-layer composite floor, bamboo floor and six major class of cork flooring and emerging Wood-plastic floor.With
People's living standards continue to improve, timber floor have obtained widely applying in ground surface finishing indoors.With the hair of construction industry
Exhibition, the development that interior decoration industry will have bigger, and one of the important materials of timber floor as interior decoration will also develop therewith.According to
Prediction, the annual growth of Chinese Solid Wood Flooring Markets is about 15~30%.
Currently, timber floor is usually to mat formation on keel or directly mat formation in mixed mud layer surface, by water flooding air infiltration
Saturating influence, timber floor are easy to make moist, and cause timber floor to deform, waterproof and dampproof anti-deformation at present of even rotting is wooden
The breakthrough problem in floor, makes troubles to people’s lives, while shortening the service life of wood floors.
It meets water and easily swells deformation intolerant to impregnating, meet water, surface is not wear-resisting, easy flower and easily stays cut etc., is all now woodenlyly
Universal pain spot existing for board industry.In addition, Solid Wood Flooring Markets demand is huge, have broad prospects, thus develops a kind of novel
Biological nano waterproof wood floor and its manufacturing method, have greater significance.
Invention content
In view of the deficiencies of the prior art, the present invention intends to provide a kind of biological nano waterproof wood floor and its
Manufacturing method.
To achieve the above object, the present invention provides following technical solutions:
A kind of biological nano waterproof wood floor, including base material timber layer are pasted with overwood successively in the upper surface of base material timber layer
Layer, wood grain layer and biological nano waterproof layer,
The upper surface of biological nano waterproof layer is provided with wearing layer, lower wood is pasted with successively in the lower surface of base material timber layer
Layer, balance timber layer and biological nano waterproof layer;
The matched clamping groove of size and clamping tenon is respectively set in the relative side of base material timber layer, in base material timber layer position
The two sides of clamping groove and clamping tenon are provided with side waterproof layer.
As being further improved for this programme, the base material timber layer uses formaldehydeless wood-fiber board.
Using above-mentioned technical proposal, using formaldehydeless wood-fiber board, securely and reliably, the material for improving timber floor base is equal
Even property reduces intensity difference in length and breadth, and not easy to crack.
As being further improved for this programme, the upper timber layer uses hard solid wood board.
As being further improved for this programme, the wearing layer uses aluminum oxide wear layer.
As being further improved for this programme, the balance timber layer uses thermosetting resin sheet.
As being further improved for this programme, the side waterproof layer uses sealing wax waterproof layer.
It is further complete by coating wax waterproof layer in the two sides for connecing groove and clamping tenon using above-mentioned technical proposal
Orientation improves the water resistance of timber floor, and sealing wax waterproof layer, without catalyst, rapid fixed line, sagging, not environmentally friendly.
As being further improved for this programme, the composition of the wood-fiber board includes 95% wood-fibred and 5% adhesive, institute
Adhesive is stated to be made of polyurethane, polyacrylamide resin, epoxy resin and rubber made from soybean cake.
As being further improved for this programme, the biological nano waterproof layer is calculated by percentage to the quality, including below at
Point:
As being further improved for this programme, the dispersant is cellulose derivative.
A kind of manufacturing method of biological nano waterproof wood floor, which is characterized in that include the following steps:
S1, the molding of base material timber layer:The wood fibre of 95% mass is dispersed in water and manufactures slurry, then adds 5%
The adhesive of quality being made of polyurethane, polyacrylamide resin, epoxy resin and rubber made from soybean cake, then technique is dried, it controls
Its moisture content is made 6%~14%, it is last hot-forming;
S2, the matched clamping groove of size and clamping tenon are respectively formed on the both sides of molding base material timber layer;
S3, timber layer, wood grain layer, biological nano waterproof layer and wearing layer are pasted successively in the upper surface of base material timber layer,
Undergrowth, balance timber layer and biological nano waterproof layer are pasted successively in the lower surface of base material timber layer;
S4, the two sides for being located at clamping groove and clamping tenon in base material timber layer are provided with side waterproof layer.
Compared with prior art, it is an advantage of the invention that:
The overall structure advantages of simple of the biological nano waterproof wood floor, waterproof effect are excellent;By using the material of multilayer
The uniform plate layer of matter, greatly improves the intensity difference of timber floor, and not easy to crack;By being coated with biological nano on surface and bottom edge
Waterproof layer, and side waterproof layer is coated in side, can comprehensive raising timber floor water resistance, and it is safe and reliable;
In addition, the manufacturing process of the biological nano waterproof wood floor is simple, easily produce in batches.
Description of the drawings
Fig. 1 is three dimensional structure diagram in inventive embodiments;
Fig. 2 is structure front view in inventive embodiments;
Fig. 3 is structure division explosive view in inventive embodiments.
Reference sign:1, base material timber layer;2, upper timber layer;3, wood grain layer;4, biological nano waterproof layer;5, wearing layer;
6, undergrowth;7, timber layer is balanced;8, side waterproof layer;101, clamping groove;102, clamping tenon.
Specific implementation mode
Embodiment one:
Referring to figs. 1 to Fig. 3, a kind of biological nano waterproof wood floor, including base material timber layer 1, in the upper surface of base material timber layer 1
It is pasted with timber layer 2, wood grain layer 3 and biological nano waterproof layer 4 successively,
The upper surface of biological nano waterproof layer 4 is provided with wearing layer 5, is pasted with successively in the lower surface of base material timber layer 1
Undergrowth 6, balance timber layer 7 and biological nano waterproof layer 4;
The matched clamping groove 101 of size and clamping tenon 102 is respectively set in the relative side of base material timber layer 1, in base
Timber layer 1 is located at clamping groove 101 and the two sides of clamping tenon 102 are provided with side waterproof layer 8.
Embodiment two:
Structure of the present embodiment on the basis of embodiment one is improved.
Referring to figs. 1 to Fig. 3, a kind of biological nano waterproof wood floor, including base material timber layer 1, in the upper surface of base material timber layer 1
It is pasted with timber layer 2, wood grain layer 3 and biological nano waterproof layer 4 successively,
The upper surface of biological nano waterproof layer 4 is provided with wearing layer 5, is pasted with successively in the lower surface of base material timber layer 1
Undergrowth 6, balance timber layer 7 and biological nano waterproof layer 4;
The matched clamping groove 101 of size and clamping tenon 102 is respectively set in the relative side of base material timber layer 1, in base
Timber layer 1 is located at clamping groove 101 and the two sides of clamping tenon 102 are provided with side waterproof layer 8.
In the preferred embodiment, the base material timber layer 1 uses formaldehydeless wood-fiber board.Using formaldehydeless wood-fibred
Plate securely and reliably improves the property uniform in material of timber floor base, reduces intensity difference in length and breadth, and not easy to crack.The upper timber layer 2
Using hard solid wood board.The wearing layer 5 uses aluminum oxide wear layer 5.The balance timber layer 7 uses thermosetting resin
Plate.The side waterproof layer 8 uses sealing wax waterproof layer.By coating wax waterproof in the two sides for connecing groove and clamping tenon 102
Layer, the water resistance of further comprehensive raising timber floor, and sealing wax waterproof layer are without catalyst, rapid fixed line, not sagging, ring
It protects.
In the preferred embodiment, the composition of the wood-fiber board includes 95% wood-fibred and 5% adhesive, the gluing
Agent is made of polyurethane, polyacrylamide resin, epoxy resin and rubber made from soybean cake.
The biological nano waterproof layer 4 is calculated by percentage to the quality, including following component:
Embodiment three:
Structure of the present embodiment on the basis of embodiment two is improved.In the preferred embodiment, described point
Powder is cellulose derivative.
Example IV:
Structure of the present embodiment on the basis of embodiment one is improved.
Referring to figs. 1 to Fig. 3, a kind of biological nano waterproof wood floor, including base material timber layer 1, in the upper surface of base material timber layer 1
It is pasted with timber layer 2, wood grain layer 3 and biological nano waterproof layer 4 successively,
The upper surface of biological nano waterproof layer 4 is provided with wearing layer 5, is pasted with successively in the lower surface of base material timber layer 1
Undergrowth 6, balance timber layer 7 and biological nano waterproof layer 4;
The matched clamping groove 101 of size and clamping tenon 102 is respectively set in the relative side of base material timber layer 1, in base
Timber layer 1 is located at clamping groove 101 and the two sides of clamping tenon 102 are provided with side waterproof layer 8.
In the preferred embodiment, the base material timber layer 1 uses formaldehydeless wood-fiber board.Using formaldehydeless wood-fibred
Plate securely and reliably improves the property uniform in material of timber floor base, reduces intensity difference in length and breadth, and not easy to crack.The upper timber layer 2
Using hard solid wood board.The wearing layer 5 uses aluminum oxide wear layer 5.The balance timber layer 7 uses thermosetting resin
Plate.The side waterproof layer 8 uses sealing wax waterproof layer.By coating wax waterproof in the two sides for connecing groove and clamping tenon 102
Layer, the water resistance of further comprehensive raising timber floor, and sealing wax waterproof layer are without catalyst, rapid fixed line, not sagging, ring
It protects.
In the preferred embodiment, the composition of the wood-fiber board includes 95% wood-fibred and 5% adhesive, the gluing
Agent is made of polyurethane, polyacrylamide resin, epoxy resin and rubber made from soybean cake.
The biological nano waterproof layer 4 is calculated by percentage to the quality, including following component:
In the preferred embodiment, the dispersant is cellulose derivative.
In the preferred embodiment, a kind of manufacturing method of biological nano waterproof wood floor, which is characterized in that including following
Step:
S1, base material timber layer 1 are molded:The wood fibre of 95% mass is dispersed in water and manufactures slurry, then adds 5%
The adhesive of quality being made of polyurethane, polyacrylamide resin, epoxy resin and rubber made from soybean cake, then technique is dried, it controls
Its moisture content is made 6%~14%, it is last hot-forming;
S2, the matched clamping groove 101 of size and clamping tenon 102 are respectively formed on the both sides of molding base material timber layer 1;
S3, timber layer 2, wood grain layer 3, biological nano waterproof layer 4 and wearing layer are pasted successively in the upper surface of base material timber layer 1
5, undergrowth 6, balance timber layer 7 and biological nano waterproof layer 4 are pasted successively in the lower surface of base material timber layer 1;
S4, the two sides for being located at clamping groove 101 and clamping tenon 102 in base material timber layer 1 are provided with side waterproof layer 8.
The overall structure advantages of simple of the biological nano waterproof wood floor, waterproof effect are excellent;By using the material of multilayer
The uniform plate layer of matter, greatly improves the intensity difference of timber floor, and not easy to crack;By being coated with biological nano on surface and bottom edge
Waterproof layer 4, and side waterproof layer 8 is coated in side, can comprehensive raising timber floor water resistance, and it is safe and reliable;
In addition, the manufacturing process of the biological nano waterproof wood floor is simple, easily produce in batches.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (10)
1. a kind of biological nano waterproof wood floor, including base material timber layer, the upper surface of base material timber layer be pasted with successively upper timber layer,
Wood grain layer and biological nano waterproof layer, it is characterized in that:
The upper surface of biological nano waterproof layer is provided with wearing layer, the lower surface of base material timber layer be pasted with successively undergrowth,
Balance timber layer and biological nano waterproof layer;
The matched clamping groove of size and clamping tenon is respectively set in the relative side of base material timber layer, is located at card in base material timber layer
The two sides for connecing groove and clamping tenon are provided with side waterproof layer.
2. biological nano waterproof wood floor according to claim 1, it is characterized in that:The base material timber layer is using formaldehydeless
Wood-fiber board.
3. biological nano waterproof wood floor according to claim 1, it is characterized in that:The upper timber layer uses hard solid wood
Plate.
4. biological nano waterproof wood floor according to claim 1, it is characterized in that:The wearing layer uses alundum (Al2O3)
Wearing layer.
5. biological nano waterproof wood floor according to claim 1, it is characterized in that:The balance timber layer uses thermosetting property tree
Fat plate.
6. biological nano waterproof wood floor according to claim 1, it is characterized in that:The side waterproof layer is anti-using sealing wax
Water layer.
7. biological nano waterproof wood floor according to claim 2, it is characterized in that:The composition of the wood-fiber board includes
95% wood-fibred and 5% adhesive, the adhesive are made of polyurethane, polyacrylamide resin, epoxy resin and rubber made from soybean cake.
8. biological nano waterproof wood floor according to claim 1, it is characterized in that:The biological nano waterproof layer is with quality
Percentage calculation, including following component:
9. biological nano waterproof wood floor according to claim 8, it is characterized in that:The dispersant derives for cellulose
Object.
10. a kind of manufacturing method of biological nano waterproof wood floor, which is characterized in that include the following steps:
S1, the molding of base material timber layer:The wood fibre of 95% mass is dispersed in water and manufactures slurry, then adds 5% mass
The adhesive being made of polyurethane, polyacrylamide resin, epoxy resin and rubber made from soybean cake, then technique is dried, controls it
Moisture content is last hot-forming 6%~14%;
S2, the matched clamping groove of size and clamping tenon are respectively formed on the both sides of molding base material timber layer;
S3, timber layer, wood grain layer, biological nano waterproof layer and wearing layer are pasted successively in the upper surface of base material timber layer, in base material
Undergrowth, balance timber layer and biological nano waterproof layer are pasted successively in the lower surface of timber layer;
S4, the two sides for being located at clamping groove and clamping tenon in base material timber layer are provided with side waterproof layer.