CN103805013A - Single-component acrylic water-based low temperature resistant wood floor paint and production method thereof - Google Patents
Single-component acrylic water-based low temperature resistant wood floor paint and production method thereof Download PDFInfo
- Publication number
- CN103805013A CN103805013A CN201410060439.3A CN201410060439A CN103805013A CN 103805013 A CN103805013 A CN 103805013A CN 201410060439 A CN201410060439 A CN 201410060439A CN 103805013 A CN103805013 A CN 103805013A
- Authority
- CN
- China
- Prior art keywords
- weight part
- stir
- rev
- minute
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses single-component acrylic water-based low temperature resistant wood floor paint and a production method thereof. The paint consists of 80-90 parts by weight of water-based acrylic modified resin, 1-5 parts by weight of LS411C organic tin drier, 2-5 parts by weight of GLIDE410 flatting agent, 5-10 parts by weight of nano rock, 1-5 parts by weight of coalescing agent, i.e., 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 1-5 parts by weight of BYK-028 defoaming agent, 5-10 parts by weight of water and 1-5 parts by weight of DSX3256 polyurethane associative thickener. The single-component acrylic water-based low temperature resistant wood floor paint disclosed by the invention is quite excellent in abrasive resistance, water resistance and fire resistance, capable of supporting normal construction and use at minus 18 DEG C, rapid to dry coating, short in construction cycle, low in construction cost, free from toxicity, smell and discharge of organic volatile compounds, and capable of effectively protecting a construction field from pollution, and a production method thereof is provided.
Description
Technical field
The present invention relates to the acrylic acid aqueous low temperature resistant paint of wooden floor of a kind of single-component and ox product method.
Background technology
Existing paint of wooden floor, because the performance at aspects such as wear resistance, water tolerance, flame retardant resistances is desirable not to the utmost, is difficult to meet the design requirements under many occasions.In addition, existing paint of wooden floor is longer time of drying, causes the corresponding prolongation of construction period, and this has not only reduced working efficiency, than having increased construction cost, and the paint of wooden floor of existing water-based Celsiusly more than 0 ℃ could constructing, lower temperature resistance is poor.
Summary of the invention
The object of the present invention is to provide one to can be used for freight container, timber floor, house decoration, furniture, boats and ships, the product surfaces such as vehicle, bamboo weaving, wicker plaiting article Teng's volume, wear resistance, water tolerance, flame retardant resistance are very good, can under subzero ten octave environment Celsius, use by normal construction, be coated with honest and clean fast drying, short construction period, construction cost is low, nontoxic, tasteless, without organic volatile discharge, can effectively protect and expand the acrylic acid aqueous low temperature resistant paint of wooden floor of the not contaminated single-component in working-yard and production method.
The low temperature resistant paint of wooden floor of olefin(e) acid water-based in single-component of the present invention, comprises that weight part is the aqueous acrylic modified resin of 80-90, the LS4110 organotin siccative that weight part is 1-5, the GLIDE410 flow agent that weight part is 2-5, the nano-silicon that weight part is 5-10, alcohol ester 12 film coalescence aid that weight part is 1-5, the BYK-028 defoamer that weight part is 1-5, the water that weight part is 5-10, the DSX3256 polyurethane associative thickener that weight part is 1-5;
Described aqueous acrylic modified resin adopts following methods to make:
It is that 20 CoatOSi12287 aqueous latex paint auxiliary agent is as properties-correcting agent that the water-borne acrylic resin that is 980 using weight part adds weight part under 400-600 rev/min of agitation condition, stir 30 minutes, deposit again 48 hours, obtain described aqueous acrylic modified resin;
The aqueous acrylic modified resin that is 80-90 by weight part is under 400-600 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 1-5 and stir 20-40 minute, and then add weight part be 2-5 GLIDE410 flow agent stir 5-20 minute, add again weight part be 5-10 nano-silicon with 800-1200 rev/min stir 20-40 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 1-5 again, the water that the BYK-028 defoamer that heavy snail part is 1-5 and weight part are 5-10 stirs respectively 5-20 minute under 400-600 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 1-5 stirs 10-30 minute under 400-600 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention, the weight part of wherein said aqueous acrylic modified resin is 82-88, the weight part of described LS4110 organotin siccative is 2-4, the weight part of described GLIDE410 flow agent is 3-4, and the weight part of described nano-silicon is that the weight part of 6-8, described alcohol ester 12 film coalescence aid is that the weight part for 2-4, described water of 2-4, described BYK-028 defoamer weight part is that the weight part of 6-8, described DSX3256 polyurethane associative thickener is 2-4;
The aqueous acrylic modified resin that is 82-88 by weight part is under 450-550 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 2-4 and stir 25-35 minute, and then add weight part be 3-4 GLIDE410 flow agent stir 8-15 minute, add again weight part be 6-8 nano-silicon with 900-1100 rev/min stir 25-35 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 2-4 again, weight part is that the BYK-028 defoamer of 2-4 and water that weight part is 6-8 stir respectively 8-15 minute under 450-550 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 2-4 stirs 15-25 minute under 450-550 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention, the weight part of wherein said aqueous acrylic modified resin is 84-86, the weight part of described LS4110 organotin siccative is 3, the weight part of described GLIDE410 flow agent is 3.5, the weight part of described nano-silicon is 7, the weight part of described alcohol ester 12 film coalescence aid is 3, described BYK-028 defoamer weight part be 3, the weight part of described water is 7, the weight part of described DSX3256 polyurethane associative thickener is 3;
The aqueous acrylic modified resin that is 84-86 by weight part is under 500 revs/min of agitation conditions, first to add weight part be 3 LS4110 organotin siccative and stir 30 minutes, and then to add weight part be that 3.5 GLIDE410 levelling profit stirs 10 minutes, adding weight part is that 7 nano-silicon stirs 30 minutes with 1000 revs/min again, adding successively weight part is 3 alcohol ester 12 film coalescence aid again, weight part is that the water that 3 BYK-028 defoamer and weight part are 7 stirs respectively 10 minutes under 500 revs/min of agitation conditions, adding weight part is that 3 DSX3256 polyurethane associative thickener stirs 20 minutes under 500 revs/min of agitation conditions again, obtain the low temperature resistant paint of wooden floor of olefin(e) acid water-based in single-component.
The production method of the low temperature resistant paint of wooden floor of olefin(e) acid water-based in single-component of the present invention, it is that 20 CoatOSi12287 aqueous latex paint auxiliary agent is as properties-correcting agent that the water-borne acrylic resin that is 980 using weight part adds weight part under 400-600 rev/min of agitation condition, stir 30 minutes, deposit again 48 hours, obtain water-based olefin(e) acid modified resin again:
The aqueous acrylic modified resin that is 80-90 by weight part is under 400-600 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 1-5 and stir 20-40 minute, and then add weight part be 2-5 GLIDB410 flow agent stir 5-20 minute, add again weight part be 5-10 nano-silicon with 800-1200 rev/min stir 20-40 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 1-5 again, weight part is that the BYK-028 defoamer of 1-5 stirs respectively 5-20 minute with the water that part is 5-10 heavily under 400-600 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 1-5 stirs 1030 minutes under 400-600 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention, the aqueous acrylic modified resin that is preferably wherein 82-88 by weight part is under 450-550 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 2-4 and stir 25-35 minute, and then add weight part be 3-4 GLIDE410 flow agent stir 8-15 minute, add again weight part be 6-8 nano-silicon with 900-1100 rev/min stir 25-35 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 2-4 again, weight part is that the BYK-028 defoamer of 2-4 and water that weight part is 6-8 stir respectively 8-15 minute under 450-550 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 2-4 stirs 15-25 minute under 450-550 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The production method of the acrylic acid aqueous resistance to low rapid paint of wooden floor of single-component of the present invention, the aqueous acrylic modified resin that is preferably further wherein 84-86 by heavy snail part is under 500 revs/min of agitation conditions, first to add weight part be 3 LS4110 organotin siccative and stir 30 minutes, and then to add weight part be that 3.5 GLIDE410 flow agent stirs 10 minutes, adding weight part is that 7 nano-silicon stirs 30 minutes with 1000 revs/min again, adding successively weight part is 3 alcohol ester 12 film coalescence aid again, weight part is that the water that 3 BYK-028 defoamer and weight part are 7 stirs respectively 10 minutes under 500 revs/min of agitation conditions, adding weight part is that 3 DSX3256 polyurethane associative thickener whisks under condition and stirs 20 minutes at 500 revs/min again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention and production method, by the distinctive formula of the present invention, adopt unique processing step, the aqueous acrylic modified resin that is 80-90 by weight part is under 400-600 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 1-5 and stir skewer 20-40 minute, and then add weight part be 2-5 GLIDE410 flow agent stir 5-20 minute, add again weight part be 5-10 nano-silicon with 800-1200 rev/min stir 20-40 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 1-5 again, weight part is that the BYK-028 defoamer of 1-5 and water that weight part is 5-10 stir respectively 5-20 minute under 400-600 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 1-5 stirs 10-30 minute under 400-600 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.The low temperature resistant paint of wooden floor of olefin(e) acid water-based in the single-component of making, can be used for freight container, timber floor, house decoration, furniture, boats and ships, the product surfaces such as vehicle, bamboo weaving, wicker plaiting article Teng's volume, the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention, the wear resistance of its coating, water tolerance, flame retardant resistance are very good, can under subzero ten octave environment Celsius, use by normal construction, change the requirement that water-borne coatings more than 0 ℃ could be constructed; And coating fast drying, can 15 points clock and watch in, short construction period, construction cost is low.
The acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention is a kind of water quality product; there is nontoxic, tasteless, reactive organometal compound volatile emission, without catching fire, without features such as blast, single-component easy construction, fast dryings; and easy construction; can effectively protect that to execute fourth scene not contaminated, be the Green Product in a kind of real view meaning.
Below in conjunction with the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention and production method are described further.
Embodiment
Embodiment 1
The acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention, comprises that weight part is the aqueous acrylic modified resin of 80-90, LS4110 organotin siccative that weight part is 1-5, weight part is 2-5 GLIDE410 flow agent, nano-silicon that weight part is 5-10, alcohol ester 12 film coalescence aid that weight part is 1-5, the BYK-028 that weight part is 1-5 drop down the water that infusion, weight part are 5-10, the DSX3256 polyurethane associative thickener that weight part is 1-5;
Described aqueous acrylic modified resin adopts following methods to make:
It is that 20 CoatOSi12287 aqueous latex paint auxiliary agent is as properties-correcting agent that the water-borne acrylic resin that is 980 using weight part adds weight part under 400-600 rev/min of agitation condition, stir 30 minutes, deposit again 48 hours, obtain described aqueous acrylic modified resin;
The aqueous acrylic modified resin that is 80-90 by weight part is under 400-600 rev/min of agitation condition, first add the LS4110 organotin siccative that part is 1-5 heavily and stir 20-40 minute, and then add weight part be 2-5 GLIDE410 flow agent stir 5-20 minute, add again weight part be 5-10 nano-silicon with 800-1200 rev/min stir 20-40 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 1-5 again, weight part is that the BYK-028 defoamer of 1-5 and water that weight part is 5-10 stir respectively 5-20 minute under 400-600 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 1-5 stirs 10-30 minute under 400-600 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention, preferably the weight part of described aqueous acrylic modified resin is 82-R8, the weight part of described LS4110 organotin siccative is 2-4, the weight part of described GLIDE410 flow agent is 3-4, and the weight part of described nano-silicon is that the weight part of 6-8, described alcohol ester 12 film coalescence aid is that the weight part for 2-4, described water of 2-4, described BYK-028 defoamer weight part is that the weight part of 6-8, described DSX3256 polyurethane associative thickener is 2-4;
The aqueous acrylic modified resin that is 82-88 by weight part is under 450-550 rev/min of agitation condition, first add the LS4110 organotin siccative that part is 2-4 heavily and stir 25-35 minute, and then add weight part be 3-4 GLIDE410 flow agent stir 8-15 minute, add again weight part be 6-8 nano-silicon with 900-1100 rev/min stir 25-35 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 2-4 again, weight part is that the BYK-028 defoamer of 2-4 and water that weight part is 6-8 stir respectively 8-15 minute under 450-550 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 2-4 stirs 1525 minutes under 450-550 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention, more preferably the weight part of described aqueous acrylic modified resin is 84-86, the weight part of described LS4110 organotin siccative is 3, dizzy amount part of described GLIDE410 flow agent is 3.5, the weight part of described nanometer brick is 7, the weight part of described alcohol ester 12 film coalescence aid is 3, described BYK-028 defoamer weight part be 3, the weight part of described water is 7, dizzy amount part of described DSX3256 polyurethane associative thickener is 3;
The aqueous acrylic modified resin that is 84-86 by weight part is under 500 revs/min of agitation conditions, first to add weight part be 3 LS4110 organotin siccative and stir 30 minutes, and then to add weight part be that 3.5 GLIDE410 flow agent stirs 10 minutes, adding weight part is that 7 nano-silicon stirs 30 minutes with 1000 revs/min again, adding successively weight part is 3 alcohol ester 12 film coalescence aid again, weight part is that the water that 3 BYK-028 defoamer and weight part are 7 stirs respectively 10 minutes under 500 revs/min of agitation conditions, adding weight part is that 3 DSX3256 polyurethane associative thickener stirs 20 minutes under 500 revs/min of agitation conditions again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention is: it is that 20 CoatOSi12287 aqueous latex paint auxiliary agent is as properties-correcting agent that the water-borne acrylic resin that is 980 using weight part adds weight part under 400-600 rev/min of agitation condition, stir 30 minutes, deposit again 48 hours, obtain aqueous acrylic modified resin;
The aqueous acrylic modified resin that is 80-90 by weight part is under 400-600 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 1-5 and stir 20-40 minute, and then add weight part be 2-5 6LIDE410 flow agent stir 5-20 minute, adding weight part is that the nano-silicon of 5-10 stirs 20-40 minute hand with 800-1200 rev/min again, adding successively weight part is alcohol ester 12 film coalescence aid of 1-5 again, weight part is that the BYK-028 defoamer of 1-5 and water that weight part is 5-10 stir respectively 5-20 minute under 400-600 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 1-5 stirs 1030 minutes under 400-600 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention: the aqueous acrylic modified resin that to be preferably weight part be 82-88 is under 450-550 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 2-4 and stir 25-35 minute, and then add weight part be 3-4 GLIDE410 flow agent stir 8-15 minute, add again weight part be 6-8 nano-silicon with 900-1100 rev/min stir 25-35 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 2-4 again, weight part is that the BYK-028 defoamer of 2-4 and water that weight part is 6-8 stir respectively 8-15 minute under 450-550 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 2-4 stirs 15-25 minute under 450-550 rev/min of agitation condition again, obtain single to a part acrylic acid aqueous low temperature resistant paint of wooden floor.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component of the present invention: the aqueous acrylic modified resin that is more preferably 84-86 by weight part is under 500 revs/min of agitation conditions, first to add weight part be 3 LS4110 organotin siccative and stir 30 minutes, and then to add weight part be that 3.5 GLIDE410 flow agent stirs 10 minutes, adding weight part is that 7 nano-silicon stirs 30 minutes with 1000 revs/min again, adding successively weight part is 3 alcohol ester 12 film coalescence aid again, weight part is that the water that 3 BYK-028 defoamer and weight part are 7 stirs respectively 10 minutes under 500 revs/min of agitation conditions, adding weight part is that 3 DSX3256 polyurethane associative thickener stirs 20 minutes under 500 revs/min of agitation conditions again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
Embodiment recited above is described the preferred embodiment of the present invention, not scope of the present invention is limited, design under spiritual prerequisite not departing from the present invention, various distortion and improvement that the common engineering technical personnel in this area make technical solution of the present invention, all should fall into the definite guarantor of claims of the present invention and expand in scope.
Claims (6)
1. the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component, is characterized in that comprising that weight part is the aqueous acrylic modified resin of 80-90, the LS4110 organotin siccative that weight part is 1-5, the GLIDE410 flow agent that weight part is 2-5, the nano-silicon that weight part is 5-10, alcohol ester 12 film coalescence aid that weight part is 1-5, the BYK-028 defoamer that weight part is 1-5, the water that weight part is 5-10, the DSX3256 polyurethane associative thickener that weight part is 1-5;
Described aqueous acrylic modified resin adopts following methods to make:
Using heavy part be that under 400-600 rev/min of agitation condition, to add weight part be that 20 CoatOSi12287 aqueous latex paint auxiliary agent is as properties-correcting agent for 980 water-borne acrylic resin, stir 30 minutes, deposit again 48 hours, obtain described aqueous acrylic modified resin;
The aqueous acrylic modified resin that is 80-90 by weight part is under 400-600 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 1-5 and stir 20-40 minute, and then add weight part be 2-5 GLIDE410 flow agent stir 5-20 minute, add again weight part be 5-10 nano-silicon with 800-1200 rev/min stir 20-40 minute, adding successively weight part is alcohol ester 12 film coalescence aid of 1-5 again, weight part is that the BYK-028 defoamer of 1-5 and water that weight part is 5-10 stir respectively 5-20 minute under 400-600 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 1-5 stirs 10-30 minute under 400-600 rev/min of agitation condition again, obtain the low temperature resistant paint of wooden floor of olefin(e) acid water-based in single-component.
2. the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component according to claim 1, it is characterized in that: the weight part of described aqueous acrylic modified resin is 82-88, the weight part of described LS4110 organotin siccative is 2-4, the weight part of described GLIDE410 flow agent is 3-4, and the weight part of described nano-silicon is that heavy snail part of 6-8, described alcohol ester 12 film coalescence aid is that the weight part for 2-4, described water of 2-4, described BYK-028 defoamer weight part is that the weight part of 6-8, described DSX3256 polyurethane associative thickener is 2-4;
The aqueous acrylic modified resin that is 82-88 by weight part is under 450-550 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 2-4 and stir 25-35 minute, and then add weight part be 3-4 GLIDE410 flow agent stir 8-15 minute, add again part nano-silicon for 6-8 heavily to stir 25-35 minute with 900-1100 rev/min, adding successively weight part is alcohol ester 12 film coalescence aid of 2-4 again, weight part is that the BYK-028 defoamer of 2-4 and water that weight part is 6-8 stir respectively 8-15 minute under 450-550 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 2-4 stirs 15-25 minute under 450-550 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
3. the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component according to claim 2, it is characterized in that: the weight part of described aqueous acrylic modified resin is 84-86, the weight part of described LS4110 organotin siccative is 3, the weight part of described GLIDE410 flow agent is 3.5, the weight part of described nano-silicon is 7, described alcohol ester 12 film coalescence aid heavyly part be 3, described BYK-028 defoamer weight part be 3, the weight part of described water is 7, the weight part of described DSX3256 polyurethane associative thickener is 3;
By heavy part be that the aqueous acrylic modified resin of 84-86 is under 500 revs/min of agitation conditions, first to add weight part be 3 LS4110 organotin siccative and stir 30 minutes, and then to add weight part be that 3.5 GLIDE410 flow agent stirs 10 minutes, adding weight part is that 7 nano-silicon stirs 30 minutes with 1000 revs/min again, adding successively weight part is 3 alcohol ester 12 film coalescence aid again, weight part is that the water that 3 BYK-028 defoamer and weight part are 7 stirs respectively 10 minutes under 500 revs/min of agitation conditions, adding weight part is that 3 DSX3256 polyurethane associative thickener stirs 20 minutes under 500 revs/min of agitation conditions again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
4. the production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component, tool is characterised in that: it is that 20 CoatOSi12287 aqueous latex paint auxiliary agent is as properties-correcting agent that the water-borne acrylic resin that is 980 using weight part adds weight part under 400-600 rev/min of agitation condition, stir 30 minutes, deposit again 48 hours, obtain aqueous acrylic modified resin;
The aqueous acrylic modified resin that is 80-90 by weight part is under 400-600 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 1-5 and stir 20-40 minute, and then add part GLIDE410 flow agent for 2-5 heavily to stir 5-20 minute, add again weight part be 5-10 nano-silicon with 800-1200 rev/min stir 20-40 minute, add successively more dizzy amount part alcohol ester 12 film coalescence aid for 1-5, the water that the BYK-028 defoamer that heavy snail part is 1-5 and weight part are 5-10 stirs respectively 5-20 minute under 400-600 rev/min of agitation condition, add again the DSX3256 polyurethane associative thickener that heavy snail part is 1-5 to stir 10-30 minute under 400-600 rev/min of agitation condition, obtain olefin(e) acid water-based brush low temperature paint of wooden floor in single-component.
5. the production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component according to claim 4, it is characterized in that: the aqueous acrylic modified resin that is 82-88 by weight part is under 450-550 rev/min of agitation condition, first to add weight part be the LS4110 organotin siccative of 2-4 and stir 25-35 minute, and then add weight part be 3-4 GLIDE410 flow agent stir 8-15 minute, add again weight part be 6-8 nano-silicon with 900-1100 rev/min stir 25-35 minute, add successively heavier part alcohol ester 12 film coalescence aid for 2-4, weight part is that the BYK-028 defoamer of 2-4 and water that weight part is 6-8 stir respectively 8-15 minute under 450-550 rev/min of agitation condition, adding weight part is that the DSX3256 polyurethane associative thickener of 2-4 stirs 15-25 minute under 450-550 rev/min of agitation condition again, obtain the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component.
6. the production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of single-component according to claim 5, it is characterized in that: the aqueous acrylic modified resin that is 84-86 by weight part is under 500 revs/min of agitation conditions, first to add weight part be 3 LS4110 organotin siccative and stir 30 minutes, and then to add weight part be that 3.5 GLIDE410 flow agent stirs 10 minutes, adding weight part is that 7 nano-silicon stirs 30 minutes with 1000 revs/min again, adding successively weight part is 3 alcohol ester 12 film coalescence aid again, weight part is that the water that 3 BYK-028 defoamer and weight part are 7 stirs respectively 10 minutes under 500 revs/min of agitation conditions, adding weight part is that 3 DSX3256 polyurethane associative thickener stirs 20 minutes under 500 revs/min of agitation conditions again, obtain the low temperature resistant paint of wooden floor of olefin(e) acid water-based in single-component.