CN103805013B - The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component and production method - Google Patents
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component and production method Download PDFInfo
- Publication number
- CN103805013B CN103805013B CN201410060439.3A CN201410060439A CN103805013B CN 103805013 B CN103805013 B CN 103805013B CN 201410060439 A CN201410060439 A CN 201410060439A CN 103805013 B CN103805013 B CN 103805013B
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- revs
- minutes
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component and production method, including parts by weight be 80-90 aqueous acrylic modified resin, parts by weight be 1-5 LS411C organotin drier, parts by weight be 2-5 GLIDE410 levelling agent, parts by weight be 5-10 nanometer cash, parts by weight be 1-5 12 coalescing agent of alcohol ester, parts by weight be 1-5 BYK-028 defoaming agent, parts by weight be 5-10 water, parts by weight be 1-5 DSX3256 polyurethane associative thickener.It is very good that its purpose is to provide a kind of wearability, water resistance, anti-flammabilitys, it normal construction can be used under subzero ten octaves environment Celsius, coating fast drying, short construction period, construction cost is low, it is nontoxic, tasteless, discharged without organic volatile, can the effectively acrylic acid aqueous low temperature resistant paint of wooden floor of conservation construction site not contaminated one-component and production method.
Description
Technical field
The present invention relates to a kind of acrylic acid aqueous low temperature resistant paint of wooden floor of one-component and ox to produce method.
Background technique
Existing paint of wooden floor, due to wearability, water resistance, in terms of performance it is ideal not to the utmost, it is difficult to
Meet the design requirement under many occasions.In addition, existing paint of wooden floor drying time is longer, construction period is caused accordingly to prolong
Long, this not only lowers working efficiencies, and than increasing construction cost, and existing aqueous paint of wooden floor is at 0 DEG C Celsius
Could construct above, lower temperature resistance it is poor.
Summary of the invention
It can be used for container, timber floor, house decoration, furniture, ship the purpose of the present invention is to provide one kind, vehicle,
The product surfaces such as bamboo weaving, wicker plaiting article Teng volume, wearability, water resistance, anti-flammability are very good, can be under subzero ten octaves environment Celsius just
Normal construction usage applies honest and clean fast drying, and short construction period, construction cost is low, it is nontoxic, tasteless, without organic volatile discharge, can be effective
The acrylic acid aqueous low temperature resistant paint of wooden floor of the not contaminated one-component in conservation construction site and production method.
The aqueous low temperature resistant paint of wooden floor of olefin(e) acid in one-component of the invention, the aqueous acrylamide for being 80-90 including parts by weight
GLIDE410 levelling agent that LS4110 organotin drier that acid modified resin, parts by weight are 1-5, parts by weight are 2-5, parts by weight
For the nano-silicon of 5-10, parts by weight be 1-5 12 coalescing agent of alcohol ester, parts by weight be 1-5 BYK-028 defoaming agent, weight
The DSX3256 polyurethane associative thickener that the water for part being 5-10, parts by weight are 1-5；
The aqueous acrylic modified resin is made of following methods：
It is 20 that parts by weight, which are added, in the water-based acrylic resin that parts by weight are 980 under 400-600 revs/min of stirring condition
CoatOSi12287 aqueous latex paint auxiliary agent stir 30 minutes as modifying agent, then store 48 hours, obtain described aqueous third
Olefin(e) acid modified resin；
By parts by weight be 80-90 aqueous acrylic modified resin under 400-600 revs/min of stirring condition, be first added
Parts by weight are the LS4110 organotin drier of 1-5 and stir 20-40 minutes that then adding parts by weight is 2-5's
GLIDE410 levelling agent stirs 5-20 minutes, and adding parts by weight is the nano-silicon of 5-10 with 800-1200 revs/min of stirring 20-
40 minutes, sequentially add 12 coalescing agent of alcohol ester that parts by weight are 1-5, the BYK-028 defoaming agent that weight snail part is 1-5 and again
The water that amount part is 5-10 stirs 5-20 minutes respectively under 400-600 revs/min of stirring condition, and adding parts by weight is 1-5's
DSX3256 polyurethane associative thickener stirs 10-30 minutes under 400-600 revs/min of stirring condition to get one-component third
The aqueous low temperature resistant paint of wooden floor of olefin(e) acid.
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention, wherein the aqueous acrylic modified resin
Parts by weight are 82-88, and the parts by weight of the LS4110 organotin drier are 2-4, the parts by weight of the GLIDE410 levelling agent
For 3-4, the parts by weight of the nano-silicon are 6-8, the parts by weight of 12 coalescing agent of the alcohol ester are 2-4, the BYK-028 disappears
Infusion parts by weight are 2-4, the parts by weight of the water are 6-8, the parts by weight of the DSX3256 polyurethane associative thickener are
2-4；
By parts by weight be 82-88 aqueous acrylic modified resin under 450-550 revs/min of stirring condition, be first added
Parts by weight are the LS4110 organotin drier of 2-4 and stir 25-35 minutes that then adding parts by weight is 3-4's
GLIDE410 levelling agent stirs 8-15 minutes, and adding parts by weight is the nano-silicon of 6-8 with 900-1100 revs/min of stirring 25-
35 minutes, sequentially add BYK-028 defoaming agent that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 2-4 are 2-4 and again
The water that amount part is 6-8 stirs 8-15 minutes respectively under 450-550 revs/min of stirring condition, and adding parts by weight is 2-4's
DSX3256 polyurethane associative thickener stirs 15-25 minutes under 450-550 revs/min of stirring condition to get one-component third
The aqueous low temperature resistant paint of wooden floor of olefin(e) acid.
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention, wherein the aqueous acrylic modified resin
Parts by weight are 84-86, and the parts by weight of the LS4110 organotin drier are 3, and the parts by weight of the GLIDE410 levelling agent are
3.5, the parts by weight of the nano-silicon are 7, the parts by weight of 12 coalescing agent of the alcohol ester are 3, the BYK-028 defoaming agent weight
Amount part is 3, the parts by weight of the water are 7, the parts by weight of the DSX3256 polyurethane associative thickener are 3；
By parts by weight be 84-86 aqueous acrylic modified resin under 500 revs/min of stirring conditions, weight is first added
Part for 3 LS4110 organotin drier and stir 30 minutes, then add parts by weight be 3.5 GLIDE410 levelling benefit stir
It mixes 10 minutes, adds the nano-silicon that parts by weight are 7 and stirred 30 minutes with 1000 revs/min, sequentially adding parts by weight is 3
The water that the BYK-028 defoaming agent and parts by weight that 12 coalescing agent of alcohol ester, parts by weight are 3 are 7 is in 500 revs/min of stirring conditions
It is lower to stir 10 minutes respectively, the DSX3256 polyurethane associative thickener that parts by weight are 3 is added in 500 revs/min of stirring bars
20 minutes are stirred under part to get the aqueous low temperature resistant paint of wooden floor of olefin(e) acid in one-component.
The production method of the aqueous low temperature resistant paint of wooden floor of olefin(e) acid in one-component of the invention, the water for being 980 by parts by weight
Property acrylic resin be added under 400-600 revs/min of stirring condition parts by weight be 20 CoatOSi12287 aqueous latex paint
Auxiliary agent stirs 30 minutes as modifying agent, then stores 48 hours, obtains aqueous olefin(e) acid modified resin again：
By parts by weight be 80-90 aqueous acrylic modified resin under 400-600 revs/min of stirring condition, be first added
Parts by weight are the LS4110 organotin drier of 1-5 and stir 20-40 minutes that then adding parts by weight is 2-5's
GLIDB410 levelling agent stirs 5-20 minutes, and adding parts by weight is the nano-silicon of 5-10 with 800-1200 revs/min of stirring 20-
40 minutes, sequentially add BYK-028 defoaming agent that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 1-5 are 1-5 and again
Most part is that the water of 5-10 stirs 5-20 minutes respectively under 400-600 revs/min of stirring condition, and adding parts by weight is 1-5's
DSX3256 polyurethane associative thickener stirs 1030 minutes under 400-600 revs/min of stirring condition to get one-component third
The aqueous low temperature resistant paint of wooden floor of olefin(e) acid.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention, wherein it is preferred that being by parts by weight
The LS4110 that parts by weight are 2-4 is first added under 450-550 revs/min of stirring condition in the aqueous acrylic modified resin of 82-88
Organotin drier simultaneously stirs 25-35 minutes, then adds the GLIDE410 levelling agent that parts by weight are 3-4 and stirs 8-15 points
Clock, add parts by weight be 6-8 nano-silicon with 900-1100 revs/min stirring 25-35 minutes, sequentially adding parts by weight is
The water that the BYK-028 defoaming agent and parts by weight that 12 coalescing agent of alcohol ester, the parts by weight of 2-4 are 2-4 are 6-8 450-550 turn/
It is stirred respectively 8-15 minutes under minute stirring condition, adds the DSX3256 polyurethane associative thickener that parts by weight are 2-4 and exist
15-25 minutes are stirred under 450-550 revs/min of stirring condition to get the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component.
The production method of the acrylic acid aqueous resistance to low rapid paint of wooden floor of one-component of the invention, wherein will further preferably weigh
Snail part is the aqueous acrylic modified resin of 84-86 under 500 revs/min of stirring conditions, and the LS4110 that parts by weight are 3 is first added
Organotin drier simultaneously stirs 30 minutes, then adds the GLIDE410 levelling agent that parts by weight are 3.5 and stirs 10 minutes, then plus
Enter the nano-silicon that parts by weight are 7 to stir 30 minutes with 1000 revs/min, sequentially adds the alcohol ester 12 that parts by weight are 3 and form a film
The water that the BYK-028 defoaming agent and parts by weight that auxiliary agent, parts by weight are 3 are 7 stirs 10 under 500 revs/min of stirring conditions respectively
Minute, it adds the DSX3256 polyurethane associative thickener that parts by weight are 3 and stirs 20 points under the conditions of whisking for 500 revs/min
Clock is to get the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component.
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention and production method are matched by the present invention is distinctive
The aqueous acrylic modified resin that parts by weight are 80-90 is stirred at 400-600 revs/min using unique processing step side
Under the conditions of, the LS4110 organotin drier that parts by weight are 1-5 is first added and stirs skewer 20-40 minutes, then adds parts by weight
It is stirred 5-20 minutes for the GLIDE410 levelling agent of 2-5, adding parts by weight is the nano-silicon of 5-10 with 800-1200 revs/min
Stirring 20-40 minutes sequentially adds the BYK-028 that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 1-5 are 1-5 and disappears
The water that infusion and parts by weight are 5-10 stirs 5-20 minutes respectively under 400-600 revs/min of stirring condition, adds parts by weight
For 1-5 DSX3256 polyurethane associative thickener stirred under 400-600 revs/min of stirring condition 10-30 minutes to get
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component.The aqueous low temperature resistant paint of wooden floor of olefin(e) acid, can use in manufactured one-component
In container, timber floor, house decoration, furniture, ship, the product surfaces such as vehicle, bamboo weaving, wicker plaiting article Teng compile, single group of the invention
The acrylic acid aqueous low temperature resistant paint of wooden floor of part, wearability, water resistance, the anti-flammability of coating are very good, can be Celsius subzero
Normal construction uses under ten octave environment, changes 0 DEG C of water paint or more the requirement that could be constructed；And coating fast drying,
Can 15 minutes tables in, short construction period, construction cost is low.
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention is a kind of water quality product, have it is nontoxic, tasteless,
Reactive organometal compound volatile emission, without kindling, without explosion, one-component is easy for construction, fast drying the features such as, and it is easy for construction,
It can effectively protect and applies that fourth scene is not contaminated, be the green product in a kind of really view meaning.
Make furtherly below with reference to the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the present invention and production method
It is bright.
Specific embodiment
Embodiment 1
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention, the aqueous acrylamide for being 80-90 including parts by weight
GLIDE410 levelling agent that LS4110 organotin drier that acid modified resin, parts by weight are 1-5, parts by weight are 2-5, parts by weight
For the nano-silicon of 5-10, parts by weight be 1-5 12 coalescing agent of alcohol ester, parts by weight be 1-5 BYK-028 drop down infusion, weight
The DSX3256 polyurethane associative thickener that the water for part being 5-10, parts by weight are 1-5；
The aqueous acrylic modified resin is made of following methods：
It is 20 that parts by weight, which are added, in the water-based acrylic resin that parts by weight are 980 under 400-600 revs/min of stirring condition
CoatOSi12287 aqueous latex paint auxiliary agent stir 30 minutes as modifying agent, then store 48 hours, obtain described aqueous third
Olefin(e) acid modified resin；
By parts by weight be 80-90 aqueous acrylic modified resin under 400-600 revs/min of stirring condition, be first added
Weight most part is the LS4110 organotin drier of 1-5 and stirs 20-40 minutes that then adding parts by weight is 2-5's
GLIDE410 levelling agent stirs 5-20 minutes, and adding parts by weight is the nano-silicon of 5-10 with 800-1200 revs/min of stirring 20-
40 minutes, sequentially add BYK-028 defoaming agent that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 1-5 are 1-5 and again
The water that amount part is 5-10 stirs 5-20 minutes respectively under 400-600 revs/min of stirring condition, and adding parts by weight is 1-5's
DSX3256 polyurethane associative thickener stirs 10-30 minutes under 400-600 revs/min of stirring condition to get one-component third
The aqueous low temperature resistant paint of wooden floor of olefin(e) acid.
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention, the preferably described aqueous acrylic modified resin
Parts by weight are 82-R8, and the parts by weight of the LS4110 organotin drier are 2-4, the parts by weight of the GLIDE410 levelling agent
For 3-4, the parts by weight of the nano-silicon are 6-8, the parts by weight of 12 coalescing agent of the alcohol ester are 2-4, the BYK-028 disappears
Infusion parts by weight are 2-4, the parts by weight of the water are 6-8, the parts by weight of the DSX3256 polyurethane associative thickener are
2-4；
By parts by weight be 82-88 aqueous acrylic modified resin under 450-550 revs/min of stirring condition, be first added
Weight most part is the LS4110 organotin drier of 2-4 and stirs 25-35 minutes that then adding parts by weight is 3-4's
GLIDE410 levelling agent stirs 8-15 minutes, and adding parts by weight is the nano-silicon of 6-8 with 900-1100 revs/min of stirring 25-
35 minutes, sequentially add BYK-028 defoaming agent that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 2-4 are 2-4 and again
The water that amount part is 6-8 stirs 8-15 minutes respectively under 450-550 revs/min of stirring condition, and adding parts by weight is 2-4's
DSX3256 polyurethane associative thickener stirs 1525 minutes under 450-550 revs/min of stirring condition to get one-component third
The aqueous low temperature resistant paint of wooden floor of olefin(e) acid.
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention, the more preferable aqueous acrylic modified resin
Parts by weight be 84-86, the parts by weight of the LS4110 organotin drier are 3, dizzy amount part of the GLIDE410 levelling agent
It is 3.5, the parts by weight of the nano brick are 7, the parts by weight of 12 coalescing agent of the alcohol ester are 3, the BYK-028 defoaming agent
Parts by weight are 3, the parts by weight of the water are 7, dizzy amount part of the DSX3256 polyurethane associative thickener is 3；
By parts by weight be 84-86 aqueous acrylic modified resin under 500 revs/min of stirring conditions, weight is first added
Part for 3 LS4110 organotin drier and stir 30 minutes, then add parts by weight be 3.5 GLIDE410 levelling agent stir
It mixes 10 minutes, adds the nano-silicon that parts by weight are 7 and stirred 30 minutes with 1000 revs/min, sequentially adding parts by weight is 3
The water that the BYK-028 defoaming agent and parts by weight that 12 coalescing agent of alcohol ester, parts by weight are 3 are 7 is in 500 revs/min of stirring conditions
It is lower to stir 10 minutes respectively, the DSX3256 polyurethane associative thickener that parts by weight are 3 is added in 500 revs/min of stirring bars
20 minutes are stirred under part to get the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention is：It is 980 by parts by weight
The CoatOSi12287 water based emulsion that parts by weight are 20 is added in water-based acrylic resin under 400-600 revs/min of stirring condition
It paints auxiliary agent to stir 30 minutes as modifying agent, then stores 48 hours, obtain aqueous acrylic modified resin；
By parts by weight be 80-90 aqueous acrylic modified resin under 400-600 revs/min of stirring condition, be first added
Parts by weight are the LS4110 organotin drier of 1-5 and stir 20-40 minutes that then adding parts by weight is 2-5's
6LIDE410 levelling agent stirs 5-20 minutes, and adding parts by weight is the nano-silicon of 5-10 with 800-1200 revs/min of stirring 20-
40 minute hands sequentially add BYK-028 defoaming agent that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 1-5 are 1-5 and again
The water that amount part is 5-10 stirs 5-20 minutes respectively under 400-600 revs/min of stirring condition, and adding parts by weight is 1-5's
DSX3256 polyurethane associative thickener stirs 1030 minutes under 400-600 revs/min of stirring condition to get one-component third
The aqueous low temperature resistant paint of wooden floor of olefin(e) acid.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention：Preferably it is by parts by weight
The LS4110 that parts by weight are 2-4 is first added under 450-550 revs/min of stirring condition in the aqueous acrylic modified resin of 82-88
Organotin drier simultaneously stirs 25-35 minutes, then adds the GLIDE410 levelling agent that parts by weight are 3-4 and stirs 8-15 points
Clock, add parts by weight be 6-8 nano-silicon with 900-1100 revs/min stirring 25-35 minutes, sequentially adding parts by weight is
The water that the BYK-028 defoaming agent and parts by weight that 12 coalescing agent of alcohol ester, the parts by weight of 2-4 are 2-4 are 6-8 450-550 turn/
It is stirred respectively 8-15 minutes under minute stirring condition, adds the DSX3256 polyurethane associative thickener that parts by weight are 2-4 and exist
15-25 minutes are stirred under 450-550 revs/min of stirring condition to get single to the acrylic acid aqueous low temperature resistant paint of wooden floor of part.
The production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component of the invention：More preferably it is by parts by weight
The LS4110 organotin that parts by weight are 3 is first added under 500 revs/min of stirring conditions in the aqueous acrylic modified resin of 84-86
Drier simultaneously stirs 30 minutes, then adds the GLIDE410 levelling agent that parts by weight are 3.5 and stirs 10 minutes, adds weight
It part is stirred 30 minutes for 7 nano-silicon with 1000 revs/min, sequentially adds 12 coalescing agent of alcohol ester, again that parts by weight are 3
The water that the BYK-028 defoaming agent and parts by weight that amount part is 3 are 7 stirs 10 minutes respectively under 500 revs/min of stirring conditions, then
Be added parts by weight be 3 DSX3256 polyurethane associative thickener stirred under 500 revs/min of stirring conditions 20 minutes to get
The acrylic acid aqueous low temperature resistant paint of wooden floor of one-component.
The above-described embodiments are merely illustrative of preferred embodiments of the present invention, not to model of the invention
It encloses and is defined, without departing from the spirit of the design of the present invention, this field ordinary engineering and technical personnel is to the technology of the present invention side
The various changes and improvements that case is made should all be fallen within the scope of the conservation that claims of the present invention determines.
Claims (6)
1. the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component, it is characterised in that the aqueous acrylamide for being 80-90 including parts by weight
GLIDE410 levelling agent that LS4110 organotin drier that acid modified resin, parts by weight are 1-5, parts by weight are 2-5, parts by weight
For the nano-silicon of 5-10, parts by weight be 1-5 12 coalescing agent of alcohol ester, parts by weight be 1-5 BYK-028 defoaming agent, weight
The DSX3256 polyurethane associative thickener that the water for part being 5-10, parts by weight are 1-5；
The aqueous acrylic modified resin is made of following methods：
It is 20 that parts by weight, which are added, in the water-based acrylic resin that parts by weight are 980 under 400-600 revs/min of stirring condition
CoatOSi12287 aqueous latex paint auxiliary agent stirs 30 minutes as modifying agent, then stores 48 hours, obtains the aqueous acrylamide
Acid modified resin；
By parts by weight be 80-90 aqueous acrylic modified resin under 400-600 revs/min of stirring condition, weight is first added
Part is the LS4110 organotin drier of 1-5 and stirs 20-40 minutes, then adds the GLIDE410 that parts by weight are 2-5 and flows
Flat agent is stirred 5-20 minute, add parts by weight for 5-10 nano-silicon with 800-1200 revs/min stirring 20-40 minutes, then
Sequentially adding BYK-028 defoaming agent that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 1-5 are 1-5 and parts by weight is 5-
10 water stirs 5-20 minutes respectively under 400-600 revs/min of stirring condition, and it is poly- to add the DSX3256 that parts by weight are 1-5
Urethane association thickener stirred under 400-600 revs/min of stirring condition 10-30 minutes it is acrylic acid aqueous to get one-component
Low temperature resistant paint of wooden floor.
2. the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component according to claim 1, it is characterised in that：It is described aqueous
The parts by weight of acrylic acid modified resin are 82-88, and the parts by weight of the LS4110 organotin drier are 2-4, described
The parts by weight of GLIDE410 levelling agent are 3-4, and the parts by weight of the nano-silicon are the weight of 6-8,12 coalescing agent of the alcohol ester
Amount part is 2-4, the parts by weight of the BYK-028 defoaming agent are 2-4, the parts by weight of the water are 6-8, the poly- ammonia of the DSX3256
The parts by weight of ester association thickener are 2-4；
By parts by weight be 82-88 aqueous acrylic modified resin under 450-550 revs/min of stirring condition, weight is first added
Part is the LS4110 organotin drier of 2-4 and stirs 25-35 minutes, then adds the GLIDE410 that parts by weight are 3-4 and flows
Flat agent is stirred 8-15 minute, add parts by weight for 6-8 nano-silicon with 900-1100 revs/min stirring 25-35 minutes, then according to
It is secondary be added parts by weight be 2-4 12 coalescing agent of alcohol ester, parts by weight be 2-4 BYK-028 defoaming agent and parts by weight be 6-8's
Water stirs 8-15 minutes respectively under 450-550 revs/min of stirring condition, adds the DSX3256 polyurethane that parts by weight are 2-4
Association thickener stirred under 450-550 revs/min of stirring condition 15-25 minutes it is acrylic acid aqueous resistance to low to get one-component
Warm paint of wooden floor.
3. the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component according to claim 2, it is characterised in that：It is described aqueous
The parts by weight of acrylic acid modified resin are 84-86, and the parts by weight of the LS4110 organotin drier are 3, the GLIDE410
The parts by weight of levelling agent are 3.5, and the parts by weight of the nano-silicon are 7, the parts by weight of 12 coalescing agent of the alcohol ester are 3, institute
The parts by weight for stating BYK-028 defoaming agent are 3, the parts by weight of the water are 7, the DSX3256 polyurethane associative thickener
Parts by weight are 3；
By parts by weight be 84-86 aqueous acrylic modified resin under 500 revs/min of stirring conditions, first be added parts by weight be 3
LS4110 organotin drier and stir 30 minutes, then add parts by weight be 3.5 GLIDE410 levelling agent stirring 10
Minute, it adds the nano-silicon that parts by weight are 7 and is stirred 30 minutes with 1000 revs/min, sequentially add the alcohol ester that parts by weight are 3
The water that the BYK-028 defoaming agent and parts by weight that 12 coalescing agents, parts by weight are 3 are 7 divides under 500 revs/min of stirring conditions
Jiao Ban not be 10 minutes, the DSX3256 polyurethane associative thickener that parts by weight are 3 is added under 500 revs/min of stirring conditions
Stirring 20 minutes to get the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component.
4. the production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component, it is characterised in that：The water for being 980 by parts by weight
Property acrylic resin be added under 400-600 revs/min of stirring condition parts by weight be 20 CoatOSi12287 aqueous latex paint
Auxiliary agent stirs 30 minutes as modifying agent, then stores 48 hours, obtains aqueous acrylic modified resin；
By parts by weight be 80-90 aqueous acrylic modified resin under 400-600 revs/min of stirring condition, weight is first added
Part is the LS4110 organotin drier of 1-5 and stirs 20-40 minutes, then adds the GLIDE410 that parts by weight are 2-5 and flows
Flat agent is stirred 5-20 minute, add parts by weight for 5-10 nano-silicon with 800-1200 revs/min stirring 20-40 minutes, then
Sequentially adding BYK-028 defoaming agent that 12 coalescing agent of alcohol ester, parts by weight that parts by weight are 1-5 are 1-5 and parts by weight is 5-
10 water stirs 5-20 minutes respectively under 400-600 revs/min of stirring condition, and it is poly- to add the DSX3256 that parts by weight are 1-5
Urethane association thickener stirred under 400-600 revs/min of stirring condition 10-30 minutes it is acrylic acid aqueous to get one-component
Low temperature resistant paint of wooden floor.
5. the production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component according to claim 4, feature exist
In：By parts by weight be 82-88 aqueous acrylic modified resin under 450-550 revs/min of stirring condition, parts by weight are first added
For 2-4 LS4110 organotin drier and stir 25-35 minutes, then add parts by weight be 3-4 GLIDE410 levelling
Agent is stirred 8-15 minute, add parts by weight for 6-8 nano-silicon with 900-1100 revs/min stirring 25-35 minutes, then successively
Be added parts by weight be 2-4 12 coalescing agent of alcohol ester, parts by weight be 2-4 BYK-028 defoaming agent and parts by weight be 6-8 water
It is stirred respectively under 450-550 revs/min of stirring condition 8-15 minutes, adds the DSX3256 polyurethane that parts by weight are 2-4 and form
Thickener stirred under 450-550 revs/min of stirring condition 15-25 minutes it is acrylic acid aqueous low temperature resistant to get one-component
Paint of wooden floor.
6. the production method of the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component according to claim 5, feature exist
In：By parts by weight be 84-86 aqueous acrylic modified resin under 500 revs/min of stirring conditions, first be added parts by weight be 3
LS4110 organotin drier and stir 30 minutes, then add parts by weight be 3.5 GLIDE410 levelling agent stirring 10
Minute, it adds the nano-silicon that parts by weight are 7 and is stirred 30 minutes with 1000 revs/min, sequentially add the alcohol ester that parts by weight are 3
The water that the BYK-028 defoaming agent and parts by weight that 12 coalescing agents, parts by weight are 3 are 7 divides under 500 revs/min of stirring conditions
Jiao Ban not be 10 minutes, the DSX3256 polyurethane associative thickener that parts by weight are 3 is added under 500 revs/min of stirring conditions
Stirring 20 minutes to get the acrylic acid aqueous low temperature resistant paint of wooden floor of one-component.