CN103803887B - 一种可感知压强的混凝土块 - Google Patents
一种可感知压强的混凝土块 Download PDFInfo
- Publication number
- CN103803887B CN103803887B CN201410080317.0A CN201410080317A CN103803887B CN 103803887 B CN103803887 B CN 103803887B CN 201410080317 A CN201410080317 A CN 201410080317A CN 103803887 B CN103803887 B CN 103803887B
- Authority
- CN
- China
- Prior art keywords
- concrete blocks
- pressure
- percent
- particle diameter
- concrete block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种混凝土块及生产工艺，特别涉及一种可感知压强的混凝土块。本发明一种可感知压强的混凝土块是由以下重量百分比的原料制成：①水泥，30%-40%；②水，20%-25%；③细砂，25%-35%；④小粒径的可发性聚苯乙烯颗粒，3%-10%；⑤减水剂，0.05%-0.1%；⑥纳米钛酸钡粉体，5%-15%；⑦纳米铁酸铋粉体，3%-10%；⑧含银浆液，0.01%-0.05%，该发明一种可感知压强的混凝土块将压电材料/铁电材料与传统水泥等融合在一起，使得混凝土块在具有传统建筑材料的耐压、保温、高硬度的同时，又具有了压电/铁电特性，为测试建筑材料的机械特性提供了便利。
Description
技术领域
本发明涉及一种混凝土块及生产工艺，特别涉及一种可感知压强的混凝土块。
背景技术
混凝土块是建筑中必用的一种建筑材料，起到抗压、稳定、隔断的作用。混凝土块的耐压程度是决定建筑安全的最重要的因素，因此，测试混凝土块的耐压值是建筑材料测试中必做的一项。传统的方法比较麻烦，而且测量数值容易出现偏差，随着电子技术和纳米技术飞速发展，如何将两种先进的技术融合到传统的建筑材料测试中成为当前的研究热点。发明内容
本发明为了实现上述将电子技术、纳米技术与建筑材料测试相结合的构想，提供了一种将压电材料融合到建筑材料中，利用压电材料的压电特性测试建筑材料耐压值的可感知压强的混凝土块，为了测量更加准确，在添加传统压电材料钛酸钡粉体后，还添加了除具有压电特性还有优异的铁电性能铁酸铋粉体。
本发明是通过如下技术方案实现的：
本发明一种可感知压强的混凝土块是由以下重量百分比的原料制成，
①水泥 30%—40%
②水 20%-25%
③细砂 25%—35%
④小粒径的可发性聚苯乙烯颗粒 3%-10%
⑤减水剂 0.05%-0.1%
⑥纳米钛酸钡粉体 5%-15%
⑦纳米铁酸铋粉体 3%-10%
⑧含银浆液 0.01%-0.05%。
上述本发明一种可感知压强的混凝土块，所述水泥粒径、细砂粒径、聚苯乙烯颗粒粒径均在1μm以下。
上述本发明一种可感知压强的混凝土块，所述减水剂为聚羧酸系高性能减水剂。
上述本发明一种可感知压强的混凝土块，所述纳米钛酸钡粉体与纳米铁酸铋粉体均为结晶完全后的压电陶瓷粉体，其粒径均在100nm以下。
上述本发明一种可感知压强的混凝土块，所述含银浆液为20μm的细强闪银浆。
上述本发明一种可感知压强的混凝土块，采用以下步骤制备，
①按所述比例将水、减水剂搅拌均匀，制成A料；
②按所述比例将水泥、细砂、纳米钛酸钡粉体、纳米铁酸铋粉体搅拌均匀，制成B料；
③将A料与B料混合均匀并搅拌10-15分钟，搅拌过程中，慢慢加入聚苯乙烯颗粒，制的浆料；
④将浆料灌入到模具中，并施加0.5MPa左右的压力；
⑤将模具封好口后，静止放置24小时以上；
⑥取出混凝土块，将含银浆液以点状的形式涂抹在混凝土块上；
⑦将混凝土块置于200℃的环境中保温1小时；
⑧在点状银浆上接上探针，将探针与数字电桥连接，对混凝土块施加一定的压力，通过
数字电桥读出数据，计算压强值，与所施加的压强值作对比。
本发明的有益效果是：该发明一种可感知压强的混凝土块将压电材料/铁电材料与传统水泥等融合在一起，使得混凝土块在具有传统建筑材料的耐压、保温、高硬度的同时，又具有了压电/铁电特性，为测试建筑材料的机械特性提供了便利。
具体实施方式
实施例1：
本实施例的一种可感知压强的混凝土块是由以下重量百分比的原料制成，
① 水泥 30%；
②水 20%；
③ 细砂25%；
④小粒径的可发性聚苯乙烯颗粒 3%；
⑤ 减水剂 0.05%；
⑥ 纳米钛酸钡粉体 5%；
⑦ 纳米铁酸铋粉体 3%；
⑧ 含银浆液 0.01%；
所述水泥粒径、细砂粒径、聚苯乙烯颗粒粒径均在1μm以下；所述减水剂为聚羧酸系高性能减水剂；所述纳米钛酸钡粉体与纳米铁酸铋粉体均为结晶完全后的压电陶瓷粉体，其粒径均在100nm以下；所述含银浆液为20μm的细强闪银浆。
采用以下步骤制备：
①按所述比例将水、减水剂搅拌均匀，制成A料；
②按所述比例将水泥、细砂、纳米钛酸钡粉体、纳米铁酸铋粉体搅拌均匀，制成B料；
③将A料与B料混合均匀并搅拌10-15分钟，搅拌过程中，慢慢加入聚苯乙烯颗粒，制的浆料；
④将浆料灌入到模具中，并施加0.5MPa左右的压力；
⑤将模具封好口后，静止放置24小时以上；
⑥取出混凝土块，将含银浆液以点状的形式涂抹在混凝土块上；
⑦将混凝土块置于200℃的环境中保温1小时；
⑧在点状银浆上接上探针，将探针与数字电桥连接，对混凝土块施加一定的压力，通过
数字电桥读出数据，计算压强值，与所施加的压强值作对比。
实施例2：
本实施例一种可感知压强的混凝土块是由以下重量百分比的原料制成，
①水泥 35%；
② 水 22%；
③ 细砂 30%；
④小粒径的可发性聚苯乙烯颗粒 7%；
⑤ 减水剂 0.08%；
⑥ 纳米钛酸钡粉体 10%；
⑦ 纳米铁酸铋粉体 7%；
⑧ 含银浆液 0.04%；
所述水泥粒径、细砂粒径、聚苯乙烯颗粒粒径均在1μm以下；所述减水剂为聚羧酸系高性能减水剂；所述纳米钛酸钡粉体与纳米铁酸铋粉体均为结晶完全后的压电陶瓷粉体，其粒径均在100nm以下；所述含银浆液为20μm的细强闪银浆。
其余与实施例1相同。
实施例3：
本实施例一种可感知压强的混凝土块是由以下重量百分比的原料制成，
① 水泥 40%；
② 水 25%；
③ 细砂 35%；
④小粒径的可发性聚苯乙烯颗粒 10%；
⑤ 减水剂 0.1%；
⑥ 纳米钛酸钡粉体 15%；
⑦纳米铁酸铋粉体 10%；
⑧银浆液 0.05%；
所述水泥粒径、细砂粒径、聚苯乙烯颗粒粒径均在1μm以下；所述减水剂为聚羧酸系高性能减水剂；所述纳米钛酸钡粉体与纳米铁酸铋粉体均为结晶完全后的压电陶瓷粉体，其粒径均在100nm以下；所述含银浆液为20μm的细强闪银浆。
其余与实施例1相同。
Claims (6)
1.一种可感知压强的混凝土块，其特征在于：是由以下重量百分比的原料制成，
①水泥 30%—40%；
水 20%-25%；
细砂 25%—35%；
小粒径的可发性聚苯乙烯颗粒 3%-10%；
减水剂 0.05%-0.1%；
纳米钛酸钡粉体 5%-15%；
纳米铁酸铋粉体 3%-10%；
含银浆液 0.01%-0.05%。
2.根据权利要求1所述的一种可感知压强的混凝土块，其特征是：所述水泥粒径、细砂粒径、聚苯乙烯颗粒粒径均在1μm以下。
3.根据权利要求1所述的一种可感知压强的混凝土块，其特征是：所述减水剂为聚羧酸系高性能减水剂。
4.根据权利要求1所述的一种可感知压强的混凝土块，其特征是：所述纳米钛酸钡粉体与纳米铁酸铋粉体均为结晶完全后的压电陶瓷粉体，其粒径均在100nm以下。
5.根据权利要求1所述的一种可感知压强的混凝土块，其特征是：所述含银浆液为20μm的细强闪银浆。
6.根据权利要求1所述的一种可感知压强的混凝土块，其特征是：采用以下步骤制备，
①按所述比例将水、减水剂搅拌均匀，制成A料；
②按所述比例将水泥、细砂、纳米钛酸钡粉体、纳米铁酸铋粉体搅拌均匀，制成B料；
③将A料与B料混合均匀并搅拌10-15分钟，搅拌过程中，慢慢加入聚苯乙烯颗粒，制得浆料；
④将浆料灌入到模具中，并施加0.5MPa左右的压力；
⑤将模具封好口后，静止放置24小时以上；
⑥取出混凝土块，将含银浆液以点状的形式涂抹在混凝土块上；
⑦将混凝土块置于200℃的环境中保温1小时；
⑧在点状银浆上接上探针，将探针与数字电桥连接，对混凝土块施加一定的压力，通过数字电桥读出数据，计算压强值，与所施加的压强值作对比。