CN103790026A - 一种防紫外线抗静电织物的整理方法 - Google Patents

一种防紫外线抗静电织物的整理方法 Download PDF

Info

Publication number
CN103790026A
CN103790026A CN201410032207.7A CN201410032207A CN103790026A CN 103790026 A CN103790026 A CN 103790026A CN 201410032207 A CN201410032207 A CN 201410032207A CN 103790026 A CN103790026 A CN 103790026A
Authority
CN
China
Prior art keywords
fabric
parts
dispersant
coupling agent
sorting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201410032207.7A
Other languages
English (en)
Inventor
黄锋
顾向军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd
Original Assignee
NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd filed Critical NANTONG HUITONG TEXTILE EQUIPMENT CO Ltd
Priority to CN201410032207.7A priority Critical patent/CN103790026A/zh
Publication of CN103790026A publication Critical patent/CN103790026A/zh
Withdrawn legal-status Critical Current

Abstract

一种防紫外线抗静电织物的整理方法，包括以下步骤：（1）按重量份数计称取以下原料：水杨酸苯酯10-15份，聚氨乙烯多胺30-55份，偶联剂1-3份，分散剂0.5-1.2份，硫酸基甜菜碱10-15份，聚氧乙烯烷基醚20-30份；（2）将称取的水杨酸苯酯、聚氨乙烯多胺、硫酸基甜菜碱和聚氧乙烯烷基醚混合均匀，然后加入偶联剂和分散剂得浸渍液；（3）将织物在上述浸渍液中进行一浸一轧；（4）将处理后的织物置于烘箱中干燥。本发明将防紫外线和抗静电处理同时进行，不仅简化了操作步骤，降低了能源损耗，所得织物的功能之间互不影响，满足人们的日常需求。

Description

一种防紫外线抗静电织物的整理方法
技术领域
本发明涉及纺织品的整理方法领域，尤其涉及一种防紫外线抗静电织物的整理方法。 
背景技术
随着科技的进步，人们生活水平得到提高，大家对纺织品的要求也越来越高，希望其满足人们在不同环境中的不同需求。近几年紫外灼伤皮肤，增加了人们患皮肤癌的几率，即使使用防晒用品，但保护的区域也是有限的。织物因为纤维本身的电导率低，纤维与摩擦面之间产生高介电常数的中间层，再加上纤维光滑，所以容易产生静电，经常出现“裙绕腿”的现象。研发多功能织物，以便满足人们生活工作需要。 
发明内容
针对现有技术的不足，本发明提供了一种防紫外线抗静电织物的整理方法。 
为解决现有技术问题，本发明采取的技术方案为：一种防紫外线抗静电织物的整理方法，包括以下步骤： 
（1）按重量份数计称取以下原料：水杨酸苯酯10-15份，聚氨乙烯多胺30-55份，偶联剂1-3份，分散剂0.5-1.2份，硫酸基甜菜碱10-15份，聚氧乙烯烷基醚20-30份；
（2）将称取的水杨酸苯酯、聚氨乙烯多胺、硫酸基甜菜碱和聚氧乙烯烷基醚混合均匀，然后加入偶联剂和分散剂，继续搅拌20-30分钟，调成质量分数为15%-65%、pH为5-6的浸渍液；
（3）将织物在上述浸渍液中进行一浸一轧，压力为1.5-2.2kg/cm2，轧液率为30%-60%；
（4）将处理后的织物置于烘箱中干燥，温度为115-160℃条件下烘焙0.5-2小时。
作为优选的是，所述偶联剂为硅烷偶联剂。 
作为优选的是，所述分散剂为聚丙烯酸钠分散剂。 
作为优选的是，所述分散剂粘度为200-280mPa·s。 
本发明的有益效果：本发明将防紫外线和抗静电处理同时进行，不仅简化了操作步骤，降低了能源损耗，所得织物的功能之间互不影响，满足人们的日常需求。 
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。 
实施例1 
一种防紫外线抗静电织物的整理方法，包括以下步骤：
（1）按重量份数计称取以下原料：水杨酸苯酯10份，聚氨乙烯多胺30份，偶联剂1份，分散剂0.5份，硫酸基甜菜碱10份，聚氧乙烯烷基醚20份；
（2）将称取的水杨酸苯酯、聚氨乙烯多胺、硫酸基甜菜碱和聚氧乙烯烷基醚混合均匀，然后加入偶联剂和分散剂，继续搅拌20分钟，调成质量分数为15%、pH为5的浸渍液；
（3）将织物在上述浸渍液中进行一浸一轧，压力为1.5kg/cm2，轧液率为30%；
（4）将处理后的织物置于烘箱中干燥，温度为115℃条件下烘焙0.5小时。
作为优选的是，所述偶联剂为硅烷偶联剂。 
作为优选的是，所述分散剂为聚丙烯酸钠分散剂。 
作为优选的是，所述分散剂粘度为200mPa·s。 
实施例2 
一种防紫外线抗静电织物的整理方法，包括以下步骤：
（1）按重量份数计称取以下原料：水杨酸苯酯15份，聚氨乙烯多胺55份，偶联剂3份，分散剂1.2份，硫酸基甜菜碱15份，聚氧乙烯烷基醚30份；
（2）将称取的水杨酸苯酯、聚氨乙烯多胺、硫酸基甜菜碱和聚氧乙烯烷基醚混合均匀，然后加入偶联剂和分散剂，继续搅拌30分钟，调成质量分数为65%、pH为6的浸渍液；
（3）将织物在上述浸渍液中进行一浸一轧，压力为2.2kg/cm2，轧液率为60%；
（4）将处理后的织物置于烘箱中干燥，温度为160℃条件下烘焙2小时。
作为优选的是，所述偶联剂为硅烷偶联剂。 
作为优选的是，所述分散剂为聚丙烯酸钠分散剂。 
作为优选的是，所述分散剂粘度为280mPa·s。 
实施例3 
一种防紫外线抗静电织物的整理方法，包括以下步骤：
（1）按重量份数称取的以下原料：水杨酸苯酯12份，聚氨乙烯多胺42份，偶联剂2份，分散剂1.0份，硫酸基甜菜碱12份，聚氧乙烯烷基醚25份；
（2）将称取的水杨酸苯酯、聚氨乙烯多胺、硫酸基甜菜碱和聚氧乙烯烷基醚混合均匀，然后加入偶联剂和分散剂，继续搅拌25分钟，调成质量分数为45%、pH为5.5的浸渍液； 
（3）将织物在上述浸渍液中进行一浸一轧，压力为2.0kg/cm2，轧液率为50%；             
（4）将处理后的织物置于烘箱中干燥，温度为120℃条件下烘焙1.2小时。
作为优选的是，所述偶联剂为硅烷偶联剂。 
作为优选的是，所述分散剂为聚丙烯酸钠分散剂。 
作为优选的是，所述分散剂粘度为250mPa·s。 
将未整理的织物与本发明整理的织物进行防紫外线和抗静电性能检测，所用检测方法参照国家标准，所得结果如下表所示： 
Figure 2014100322077100002DEST_PATH_IMAGE001
通过表中数据可看出，本发明的防紫外线抗静电织物的防紫外线和抗静电能力均良好。
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。 

Claims (4)

1. 一种防紫外线抗静电织物的整理方法，其特征在于包括以下步骤：
（1）按重量份数计称取以下原料：水杨酸苯酯10-15份，聚氨乙烯多胺30-55份，偶联剂1-3份，分散剂0.5-1.2份，硫酸基甜菜碱10-15份，聚氧乙烯烷基醚20-30份；
（2）将称取的水杨酸苯酯、聚氨乙烯多胺、硫酸基甜菜碱和聚氧乙烯烷基醚混合均匀，然后加入偶联剂和分散剂，继续搅拌20-30分钟，调成质量分数为15%-65%、pH为5-6的浸渍液；
（3）将织物在上述浸渍液中进行一浸一轧，压力为1.5-2.2kg/cm2，轧液率为30%-60%；
（4）将处理后的织物置于烘箱中干燥，温度为115-160℃条件下烘焙0.5-2小时。
2. 根据权利要求1所述的一种防紫外线抗静电织物的整理方法，其特征在于：所述偶联剂为硅烷偶联剂。
3. 根据权利要求1所述的一种防紫外线抗静电织物的整理方法，其特征在于：所述分散剂为聚丙烯酸钠分散剂。
4. 根据权利要求1所述的一种防紫外线抗静电织物的整理方法，其特征在于：所述分散剂粘度为200-280mPa·s。
CN201410032207.7A 2014-01-24 2014-01-24 一种防紫外线抗静电织物的整理方法 Withdrawn CN103790026A (zh)