CN103770181B - 一种仿龙凤檀重竹地板加工工艺 - Google Patents

一种仿龙凤檀重竹地板加工工艺 Download PDF

Info

Publication number
CN103770181B
CN103770181B CN201310276863.7A CN201310276863A CN103770181B CN 103770181 B CN103770181 B CN 103770181B CN 201310276863 A CN201310276863 A CN 201310276863A CN 103770181 B CN103770181 B CN 103770181B
Authority
CN
China
Prior art keywords
amount
primer
paint
floor
roll
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310276863.7A
Other languages
English (en)
Other versions
CN103770181A (zh
Inventor
林垂伍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Zhenzhou Science And Technology Co Innovation Co ltd
Original Assignee
Jiangxi Nanfeng Zhenyu Industry Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangxi Nanfeng Zhenyu Industry Group Co Ltd filed Critical Jiangxi Nanfeng Zhenyu Industry Group Co Ltd
Priority to CN201310276863.7A priority Critical patent/CN103770181B/zh
Publication of CN103770181A publication Critical patent/CN103770181A/zh
Application granted granted Critical
Publication of CN103770181B publication Critical patent/CN103770181B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种竹制品竹条的加工方法，尤其涉及一种仿龙凤檀重竹地板加工工艺。一种仿龙凤檀重竹地板加工工艺，其特征在于包括以下步骤：选片、分片、砂光、精砂、调漆、上多层漆，烘干等。使用本发明所述的加工工艺后，能够在重竹地板的表面产生仿龙凤檀木纹的木地板的效果，既满足了消费者对地板花纹和色调的要求，又利用可再生性高的竹木资源，大大减少了对木材的砍伐，对环境保护具有突出的贡献。

Description

一种仿龙凤檀重竹地板加工工艺
技术领域
本发明涉及一种竹地板加工工艺，尤其涉及一种仿龙凤檀重竹地板加工工艺。
背景技术
实木地板由于各种木质的颜色花样不同而呈现各种形态，深受消费者喜欢。但是实木地板需要消耗大量木材，木材资源短缺，成木生长周期长，长期大量砍伐对环境造成较大影响。而毛竹因其生长周期短，资源丰富，可再生性高，毛竹运用于地板领域已经越来越普及，推崇以竹代木，现在甚至以竹胜木。现有的重竹地板因竹木色调比较单一，现有工艺基本只能加工出本色、碳化、虎纹三种色调，难以满足消费者的需求。
发明内容
为了解决以上问题，本发明提供一种竹地板加工工艺，能够制造出仿龙凤檀木地板色调的竹地板。
本发明的技术方案如下。
一种仿龙凤檀重竹地板加工工艺，其特征在于包括以下步骤。
（1）选用经碳化的重竹地板方料进行分片，分片后的胚板经水分平衡烘干、养生、分选后，用砂光机进行砂光，砂光后对胚板的四端加工出公母槽，对胚板的背面开背槽，然后喷封边漆、进行精砂。
（2）在水性底漆中加入黄色、红色、黑色、棕色色精搅匀，水性底漆与黄色、红色、黑色、棕色色精的配比为24:3:2:1:2，搅匀后呈龙凤檀色，将龙凤檀色混合漆用滚涂机滚涂至地板正面，经过烘干机烘半干后，再在地板正面滚涂一层弹性底漆，然后经过烘干机烘半干。
（3）使用滚涂机在地板表面滚涂一层透明腻子漆，腻子漆用量为28~32g/㎡，经烘干机烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，然后再滚涂一层透明腻子漆，腻子漆用量为33~37g/㎡，经烘干机烘半干后，在地板背面涂上背涂漆，烘半干后使用砂光机对地板正面进行砂光，采用320目砂带。
（4）继续使用滚涂机在地板表面滚涂一层透明腻子漆，腻子漆用量为16~20g/㎡，经烘干机烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，然后再滚涂一层耐磨底漆，耐磨底漆用量为18~22g/㎡，烘半干后，再滚涂一层透明底漆，透明底漆用量为16~18g/㎡，烘半干后，再滚涂一层透明底漆，透明底漆用量为15~17g/㎡，烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，再滚涂一层砂光底漆，砂光底漆用量为11~14g/㎡，烘半干后，使用砂光机对地板正面进行砂光，采用400目砂带，再滚涂一层60度面漆，面漆用量为6~8g/㎡，烘半干后，再滚涂一层40度耐磨面漆，耐磨面漆用量为6~8g/㎡，最后经过烘干机彻底烘干，使成品表面油漆亮光度达到25~35度。
作为本发明的进一步优选方案，步骤（3）中所述腻子漆用量第一次为30g/㎡，第二次为35g/㎡。
作为本发明的进一步优选方案，步骤（4）中所述腻子漆用量为18g/㎡，所述耐磨底漆用量为20g/㎡，所述透明底漆第一次用量为17g/㎡，第二次用量为16g/㎡，所述砂光底漆用量为12g/㎡，所述面漆用量为7g/㎡，所述耐磨面漆用量为7g/㎡。
使用本发明所述的加工工艺后，能够在重竹地板的表面产生仿龙凤檀木纹的木地板的效果，既满足了消费者对地板花纹和色调的要求，又利用可再生性高的竹木资源，大大减少了对木材的砍伐，对环境保护具有突出的贡献。
具体实施方式
下面通过具体实施例对本发明作进一步的详细说明。
实施例一。
一种仿龙凤檀重竹地板加工工艺，其特征在于包括以下步骤。
（1）选用经碳化的重竹地板方料进行分片，分片后的胚板经水分平衡烘干、养生、分选后，用砂光机进行砂光，砂光后对胚板的四端加工出公母槽，对胚板的背面开背槽，然后喷封边漆、进行精砂。
（2）在水性底漆中加入黄色、红色、黑色、棕色色精搅匀，水性底漆与黄色、红色、黑色、棕色色精的配比为24:3:2:1:2，搅匀后呈龙凤檀色，将龙凤檀色混合漆用滚涂机滚涂至地板正面，经过烘干机烘半干后，再在地板正面滚涂一层弹性底漆，然后经过烘干机烘半干。
（3）使用滚涂机在地板表面滚涂一层透明腻子漆，腻子漆用量为28~32g/㎡，经烘干机烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，然后再滚涂一层透明腻子漆，腻子漆用量为33~37g/㎡，经烘干机烘半干后，在地板背面涂上背涂漆，烘半干后使用砂光机对地板正面进行砂光，采用320目砂带。
（4）继续使用滚涂机在地板表面滚涂一层透明腻子漆，腻子漆用量为16~20g/㎡，经烘干机烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，然后再滚涂一层耐磨底漆，耐磨底漆用量为18~22g/㎡，烘半干后，再滚涂一层透明底漆，透明底漆用量为16~18g/㎡，烘半干后，再滚涂一层透明底漆，透明底漆用量为15~17g/㎡，烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，再滚涂一层砂光底漆，砂光底漆用量为11~14g/㎡，烘半干后，使用砂光机对地板正面进行砂光，采用400目砂带，再滚涂一层60度面漆，面漆用量为6~8g/㎡，烘半干后，再滚涂一层40度耐磨面漆，耐磨面漆用量为6~8g/㎡，最后经过烘干机彻底烘干，使成品表面油漆亮光度达到25~35度。
实施例二。
步骤（5）中所述腻子漆用量第一次为30g/㎡，第二次为35g/㎡。
步骤（6）中所述腻子漆用量为18g/㎡，所述耐磨底漆用量为20g/㎡，所述透明底漆第一次用量为17g/㎡，第二次用量为16g/㎡，所述砂光底漆用量为12g/㎡，所述面漆用量为7g/㎡，所述耐磨面漆用量为7g/㎡。
其他步骤与实施例一相同。
实施例三。
步骤（5）中所述腻子漆用量第一次为32g/㎡，第二次为37g/㎡。
步骤（6）中所述腻子漆用量为20g/㎡，所述耐磨底漆用量为22g/㎡，所述透明底漆第一次用量为18g/㎡，第二次用量为17g/㎡，所述砂光底漆用量为14g/㎡，所述面漆用量为8g/㎡，所述耐磨面漆用量为8g/㎡。
其他步骤与实施例一相同。

Claims (3)

1.一种仿龙凤檀重竹地板加工工艺，其特征在于包括以下步骤：
（1）选用经碳化的重竹地板方料进行分片，分片后的胚板经水分平衡烘干、养生、分选后，用砂光机进行砂光，砂光后对胚板的四端加工出公母槽，对胚板的背面开背槽，然后喷封边漆、进行精砂；
（2）在水性底漆中加入黄色、红色、黑色、棕色色精搅匀，水性底漆与黄色、红色、黑色、棕色色精的质量配比为24:3:2:1:2，搅匀后呈龙凤檀色，将龙凤檀色混合漆用滚涂机滚涂至地板正面，经过烘干机烘半干后，再在地板正面滚涂一层弹性底漆，然后经过烘干机烘半干；
（3）使用滚涂机在地板表面滚涂一层透明腻子漆，腻子漆用量为28~32g/㎡，经烘干机烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，然后再滚涂一层透明腻子漆，腻子漆用量为33~37g/㎡，经烘干机烘半干后，在地板背面涂上背涂漆，烘半干后使用砂光机对地板正面进行砂光，采用320目砂带；
（4）继续使用滚涂机在地板表面滚涂一层透明腻子漆，腻子漆用量为16~20g/㎡，经烘干机烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，然后再滚涂一层耐磨底漆，耐磨底漆用量为18~22g/㎡，烘半干后，再滚涂一层透明底漆，透明底漆用量为16~18g/㎡，烘半干后，再滚涂一层透明底漆，透明底漆用量为15~17g/㎡，烘半干后，使用砂光机对地板正面进行砂光，采用320目砂带，再滚涂一层砂光底漆，砂光底漆用量为11~14g/㎡，烘半干后，使用砂光机对地板正面进行砂光，采用400目砂带，再滚涂一层60度面漆，面漆用量为6~8g/㎡，烘半干后，再滚涂一层40度耐磨面漆，耐磨面漆用量为6~8g/㎡，最后经过烘干机彻底烘干，使成品表面油漆亮光度达到25~35度。
2.根据权利要求1所述的一种仿龙凤檀重竹地板加工工艺，其特征在于：步骤（3）中所述腻子漆用量第一次为30g/㎡，第二次为35g/㎡。
3.根据权利要求1所述的一种仿龙凤檀重竹地板加工工艺，其特征在于：步骤（4）中所述腻子漆用量第一次为18g/㎡，所述耐磨底漆用量为20g/㎡，所述透明底漆第一次用量为17g/㎡，第二次用量为16g/㎡，所述砂光底漆用量为12g/㎡，所述面漆用量为7g/㎡，所述耐磨面漆用量为7g/㎡。
CN201310276863.7A 2013-07-04 2013-07-04 一种仿龙凤檀重竹地板加工工艺 Active CN103770181B (zh)