CN103756066A - 一种氯丁橡胶汽车配件用防护套料 - Google Patents

一种氯丁橡胶汽车配件用防护套料 Download PDF

Info

Publication number
CN103756066A
CN103756066A CN201310680828.1A CN201310680828A CN103756066A CN 103756066 A CN103756066 A CN 103756066A CN 201310680828 A CN201310680828 A CN 201310680828A CN 103756066 A CN103756066 A CN 103756066A
Authority
CN
China
Prior art keywords
parts
chloroprene rubber
powder
protective sleeve
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310680828.1A
Other languages
English (en)
Inventor
韦中祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Jinying Machinery Science & Technology Development Co Ltd
Original Assignee
Wuhu Jinying Machinery Science & Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Jinying Machinery Science & Technology Development Co Ltd filed Critical Wuhu Jinying Machinery Science & Technology Development Co Ltd
Priority to CN201310680828.1A priority Critical patent/CN103756066A/zh
Publication of CN103756066A publication Critical patent/CN103756066A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种氯丁橡胶汽车配件用防护套料，它是由下述重量份的原料组成的：氯丁橡胶S40V90-100、焦宝石粉3-4、碳酸锆钾1-2、四氯间苯二甲腈2-3、聚乙烯醇缩丁醛酯2-3、柠檬酸1-2、N,N-二乙基苯胺1-2、交联剂TAC0.2-0.4、氧化铝1-2、石墨粉10-18、防老剂A1-2、硫磺0.9-1.2、已二酸二异癸酯5-7、氧化镁0.4-1、复合填料20-26，本发明的氯丁橡胶汽车配件用防护套料具有很好的拉伸强度、断裂伸长率高、耐水耐老化性强，使用寿命长，综合性能好。

Description

一种氯丁橡胶汽车配件用防护套料
技术领域
    本发明主要涉及汽车配件领域，尤其涉及一种氯丁橡胶汽车配件用防护套料。
背景技术
氯丁橡胶有良好的物理机械性能，耐油，耐热，耐燃，耐日光，耐臭氧，耐酸碱，耐化学试剂。缺点是耐寒性和贮存稳定性较差。具有较高的拉伸强度、伸长率和可逆的结晶性，粘接性好。耐老化、耐热。耐油、耐化学腐蚀性优异。耐候性和耐臭氧老化仅次于乙丙橡胶和丁基橡胶。耐热性与丁腈橡胶相当，分解温度230～260℃，短期可耐120～150℃，在80～100℃可长期使用，具有一定的阻燃性。耐油性仅次于丁腈橡胶。耐无机酸、碱腐蚀性良好。耐寒性稍差，电绝缘性不佳。生胶储存稳定性差，会产生“自硫”现象，门尼黏度增大，因此使用各种助剂复配来改善氯丁橡胶的综合性能，可以扩大其使用范围。
发明内容
本发明目的就是提供一种氯丁橡胶汽车配件用防护套料。
本发明是通过以下技术方案实现的：
一种氯丁橡胶汽车配件用防护套料，它是由下述重量份的原料组成的：
氯丁橡胶S40V 90-100、焦宝石粉3-4、碳酸锆钾1-2、四氯间苯二甲腈2-3、聚乙烯醇缩丁醛酯2-3、柠檬酸1-2、N,N-二乙基苯胺1-2、交联剂 TAC0.2-0.4、氧化铝1-2、石墨粉10-18、防老剂A1-2、硫磺0.9-1.2、已二酸二异癸酯5-7、氧化镁0.4-1、复合填料20-26；
所述的复合填料是由下述重量份的原料组成的：
黑土40-45、万年灰6-10、粉煤灰10-13、苏打粉2-3、双咪唑烷基脲1-2、六甲氧甲基三聚氰胺树脂2-3、水适量；
将上述苏打粉加入到2-3倍水中，搅拌均匀后加入万年灰，在40-50℃下加热搅拌至水干，加入六甲氧甲基三聚氰胺树脂，200-300转/分搅拌分散3-5分钟，得预混料；将上述黑土和粉煤灰混合，在600-700℃下煅烧1-2小时后与上述预混料混合，磨粉，过筛，即得所述复合填料。
一种氯丁橡胶汽车配件用防护套料的制备方法，包括以下步骤：
将上述氯丁橡胶S40V与已二酸二异癸酯、N,N-二乙基苯胺、聚乙烯醇缩丁醛酯混合，加入密炼机，在温度为85-90℃下混炼2-3分钟；
再加入石墨粉、复合填料、焦宝石粉、碳酸锆钾、四氯间苯二甲腈，在温度为85-90℃下，混炼4-6分钟；
再加入剩余各原料，在温度为55-60℃下混炼2-3分钟，即得所述氯丁橡胶汽车配件用防护套料。
本发明的优点是：
本发明的氯丁橡胶汽车配件用防护套料具有很好的拉伸强度、断裂伸长率高、耐水耐老化性强，使用寿命长，综合性能好。
具体实施方式
实施例1
一种氯丁橡胶汽车配件用防护套料，它是由下述重量份（公斤）的原料组成的：
氯丁橡胶S40V 100、焦宝石粉3、碳酸锆钾1、四氯间苯二甲腈3、聚乙烯醇缩丁醛酯3、柠檬酸1、N,N-二乙基苯胺1、交联剂 TAC0.4、氧化铝1、石墨粉18、防老剂A2、硫磺1.2、已二酸二异癸酯7、氧化镁0.4、复合填料26；
所述的复合填料是由下述重量份的原料组成的：
黑土45、万年灰10、粉煤灰13、苏打粉3、双咪唑烷基脲2、六甲氧甲基三聚氰胺树脂3、水适量；
将上述苏打粉加入到3倍水中，搅拌均匀后加入万年灰，在50℃下加热搅拌至水干，加入六甲氧甲基三聚氰胺树脂，300转/分搅拌分散5分钟，得预混料；将上述黑土和粉煤灰混合，在700℃下煅烧2小时后与上述预混料混合，磨粉，过筛，即得所述复合填料。
一种氯丁橡胶汽车配件用防护套料的制备方法，包括以下步骤：
将上述氯丁橡胶S40V与已二酸二异癸酯、N,N-二乙基苯胺、聚乙烯醇缩丁醛酯混合，加入密炼机，在温度为90℃下混炼3分钟；
再加入石墨粉、复合填料、焦宝石粉、碳酸锆钾、四氯间苯二甲腈，在温度为90℃下，混炼4分钟；
再加入剩余各原料，在温度为60℃下混炼3分钟，即得所述氯丁橡胶汽车配件用防护套料。
性能测试：
拉伸强度：17.3MPa；
断裂伸长率：386%；
耐油性：20#机油100℃×70h，断裂伸长率保持率72.5%、抗拉强度保持率73.2%；
耐臭氧：25℃、24h、臭氧浓度0.025%，无开裂；
耐老化：120℃、150h，抗拉强度保持率89.7%，断裂伸长率保持率78.3%；
耐寒实验：（-40℃、4h）:无裂纹。

Claims (2)

1.一种氯丁橡胶汽车配件用防护套料，其特征在于它是由下述重量份的原料组成的：
氯丁橡胶S40V 90-100、焦宝石粉3-4、碳酸锆钾1-2、四氯间苯二甲腈2-3、聚乙烯醇缩丁醛酯2-3、柠檬酸1-2、N,N-二乙基苯胺1-2、交联剂 TAC0.2-0.4、氧化铝1-2、石墨粉10-18、防老剂A1-2、硫磺0.9-1.2、已二酸二异癸酯5-7、氧化镁0.4-1、复合填料20-26；
所述的复合填料是由下述重量份的原料组成的：
黑土40-45、万年灰6-10、粉煤灰10-13、苏打粉2-3、双咪唑烷基脲1-2、六甲氧甲基三聚氰胺树脂2-3、水适量；
将上述苏打粉加入到2-3倍水中，搅拌均匀后加入万年灰，在40-50℃下加热搅拌至水干，加入六甲氧甲基三聚氰胺树脂，200-300转/分搅拌分散3-5分钟，得预混料；将上述黑土和粉煤灰混合，在600-700℃下煅烧1-2小时后与上述预混料混合，磨粉，过筛，即得所述复合填料。
2.一种如权利要求1所述的氯丁橡胶汽车配件用防护套料的制备方法，其特征在于包括以下步骤：
将上述氯丁橡胶S40V与已二酸二异癸酯、N,N-二乙基苯胺、聚乙烯醇缩丁醛酯混合，加入密炼机，在温度为85-90℃下混炼2-3分钟；
再加入石墨粉、复合填料、焦宝石粉、碳酸锆钾、四氯间苯二甲腈，在温度为85-90℃下，混炼4-6分钟；
再加入剩余各原料，在温度为55-60℃下混炼2-3分钟，即得所述氯丁橡胶汽车配件用防护套料。
CN201310680828.1A 2013-12-13 2013-12-13 一种氯丁橡胶汽车配件用防护套料 Pending CN103756066A (zh)