CN103740227A - 一种耐火涂料 - Google Patents

一种耐火涂料 Download PDF

Info

Publication number
CN103740227A
CN103740227A CN201310719411.1A CN201310719411A CN103740227A CN 103740227 A CN103740227 A CN 103740227A CN 201310719411 A CN201310719411 A CN 201310719411A CN 103740227 A CN103740227 A CN 103740227A
Authority
CN
China
Prior art keywords
parts
aluminium dihydrogen
refractory paint
unsaturated polyester
diphenyletherformalde
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310719411.1A
Other languages
English (en)
Other versions
CN103740227B (zh
Inventor
朱恒横
张国胜
胡兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PROVINCE JINDUN PAINT Co Ltd
Original Assignee
ANHUI PROVINCE JINDUN PAINT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI PROVINCE JINDUN PAINT Co Ltd filed Critical ANHUI PROVINCE JINDUN PAINT Co Ltd
Priority to CN201310719411.1A priority Critical patent/CN103740227B/zh
Publication of CN103740227A publication Critical patent/CN103740227A/zh
Application granted granted Critical
Publication of CN103740227B publication Critical patent/CN103740227B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂25-40份，聚乙烯醇缩醛改性酚醛树脂12-20份，间苯型不饱和聚酯树脂10-15份，间二甲苯6-10份，乙苯10-14份，硫代二丙酸二月桂酯3-7份，炭黑2-4份，三聚磷酸二氢铝6-9份，二氨基二苯基砜2-6份；其中三聚磷酸二氢铝的吸油值为25-30%。本发明中，所述耐火涂料的耐火性能好，防腐性能优异，使用寿命长，且成本较低。

Description

一种耐火涂料
技术领域
本发明涉及涂料技术领域，尤其涉及一种耐火涂料。
背景技术
耐高温涂料是指在一定时限内，一定温度段内，能够经受高温环境氧化腐蚀的涂料，从而保护被涂物能在高温下正常工作，用于可燃性基材表面，能降低被涂材料表面的可燃性、阻滞火灾的迅速蔓延，或用于非可燃性基材表面，用以提高被涂材料耐火极限的一种特种涂料，防火涂料涂覆在基材表面，除具有阻燃作用以外，还具有防锈、防水、防腐、耐磨和耐热性能，其涂层具有坚韧性、着色性、黏附性、易干性和一定的光泽，可广泛应用于钢铁制造、冶金、石油工业、天然气开采、航空航天等工业领域，目前虽已生产出多种耐火涂料仍满足不了需求，如何制备一种耐火性能好，防腐性能优异，使用寿命长的耐火性能的涂料成为目前需要解决的技术问题。
发明内容
本发明提出了一种耐火涂料，所述耐火涂料的耐火性能好，防腐性能优异，使用寿命长，且成本较低。
本发明提出的一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂25-40份，聚乙烯醇缩醛改性酚醛树脂12-20份，间苯型不饱和聚酯树脂10-15份，间二甲苯6-10份，乙苯10-14份，硫代二丙酸二月桂酯3-7份，炭黑2-4份，三聚磷酸二氢铝6-9份，二氨基二苯基砜2-6份；其中三聚磷酸二氢铝的吸油值为25-30%。
在具体实施方式中，二苯醚甲醛树脂的重量份可以为25、25.4、27、27.4、28、30、33、34、36、37、39、40，聚乙烯醇缩醛改性酚醛树脂的重量份可以12、12.3、13、15、15.7、16、18、19、19.2、20，间苯型不饱和聚酯树脂的重量份可以10、10.5、11、11.6、12、12.2、13、14、14.6、15，间二甲苯的重量份可以6、6.5、7、7.4、8、8.8、9、9.2、9.5、10，乙苯的重量份可以10、10.2、11、11.6、12、12.5、13、13.7、14，硫代二丙酸二月桂酯的重量份可以3、3.2、3.5、3.7、4、4.2、4.6、4.8、5、5.6、6、7，炭黑的重量份可以2、2.4、2.6、3、3.3、3.6、3.8、4，三聚磷酸二氢铝的重量份可以6、6.2、6.4、7、7.2、7.7、8、8.2、8.5、8.7、9，二氨基二苯基砜的重量份可以2、2.4、2.8、3、3.3、3.7、4、4.4、4.6、5、5.6、6。
在具体实施方式中，三聚磷酸二氢铝的吸油值可以为25%、25.7%、26%、26.8%、27%、28%、28.7%、29%、29.3%、29.7%、30%。
优选地，二苯醚甲醛树脂、聚乙烯醇缩醛改性酚醛树脂及间苯型不饱和聚酯树脂的重量比为6:（3-4）：2。
优选地，所述炭黑粒径为40-90nm。
优选地，三聚磷酸二氢铝中，P2O5的含量为60-70%,Al2O3的含量为20-30%。
优选地，其原料按重量份包括：二苯醚甲醛树脂30-35份，聚乙烯醇缩醛改性酚醛树脂15-17份，间苯型不饱和聚酯树脂12-13份，间二甲苯8-9份，乙苯12-14份，硫代二丙酸二月桂酯5-6份，炭黑3-4份，三聚磷酸二氢铝7-8份，二氨基二苯基砜3-5份。
优选地，其原料按重量份包括：二苯醚甲醛树脂36份，聚乙烯醇缩醛改性酚醛树脂15份，间苯型不饱和聚酯树脂12份，间二甲苯8份，乙苯13份，硫代二丙酸二月桂酯6份，炭黑4份，三聚磷酸二氢铝7份，二氨基二苯基砜4份。
本发明中，使用二苯醚甲醛树脂、聚乙烯醇缩醛改性酚醛树脂及间苯型不饱和聚酯树脂作为耐火涂料的基材，控制三者比例处于一定的范围内，可明显增强涂料的耐火性能，甲苯与间二甲苯为耐火涂料的有机溶剂，控制两者在原料中的含量，可使耐火涂料的稀释、平稳挥发效果好，并形成较平滑的涂膜，炭黑的耐摩擦性能好，与硫代二丙酸二月桂酯及三聚磷酸二氢铝共同作用，可在显著提高新型耐磨涂料与基底的附着性能的前提下，大大增强耐火涂料防腐性能及其使用寿命，本发明中，所述耐火涂料的耐火性能好，防腐性能优异，使用寿命长，且成本较低。
具体实施方式
实施例1
本实施例中，一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂36份，聚乙烯醇缩醛改性酚醛树脂15份，间苯型不饱和聚酯树脂12份，间二甲苯8份，乙苯13份，硫代二丙酸二月桂酯6份，炭黑4份，三聚磷酸二氢铝7份，二氨基二苯基砜4份；其中三聚磷酸二氢铝的吸油值为26.8%，P2O5的含量为60%,Al2O3的含量为30%，炭黑粒径为40-90nm。
实施例2
本实施例中，一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂30份，聚乙烯醇缩醛改性酚醛树脂15.7份，间苯型不饱和聚酯树脂12.2份，间二甲苯8.8份，乙苯11.6份，硫代二丙酸二月桂酯4.2份，炭黑3.3份，三聚磷酸二氢铝7.7份，二氨基二苯基砜3.3份；其中三聚磷酸二氢铝的吸油值为26.8%，P2O5的含量为65%,Al2O3的含量为25%，炭黑粒径为40-90nm。
实施例3
本实施例中，一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂27.4份，聚乙烯醇缩醛改性酚醛树脂19份，间苯型不饱和聚酯树脂11.6份，间二甲苯9.2份，乙苯11份，硫代二丙酸二月桂酯5份，炭黑2.6份，三聚磷酸二氢铝8.2份，二氨基二苯基砜2.4份；其中三聚磷酸二氢铝的吸油值为26%，P2O5的含量为63%,Al2O3的含量为27%，炭黑粒径为40-90nm。
实施例4
本实施例中，一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂39份，聚乙烯醇缩醛改性酚醛树脂12.3份，间苯型不饱和聚酯树脂14.6份，间二甲苯6.5份，乙苯13.7份，硫代二丙酸二月桂酯3.2份，炭黑3.8份，三聚磷酸二氢铝6.2份，二氨基二苯基砜5.6份；其中三聚磷酸二氢铝的吸油值为29.7%，P2O5的含量为66%,Al2O3的含量为22%，炭黑粒径为40-90nm。
实施例5
本实施例中，一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂36份，聚乙烯醇缩醛改性酚醛树脂13份，间苯型不饱和聚酯树脂14份，间二甲苯7.4份，乙苯12.5份，硫代二丙酸二月桂酯3.7份，炭黑3.6份，三聚磷酸二氢铝7份，二氨基二苯基砜4.4份；其中三聚磷酸二氢铝的吸油值为29%，P2O5的含量为70%,Al2O3的含量为20%，炭黑粒径为40-90nm。
实施例6
本实施例中，一种耐火涂料，其原料按重量份包括：二苯醚甲醛树脂25份，聚乙烯醇缩醛改性酚醛树脂19.2份，间苯型不饱和聚酯树脂10.5份，间二甲苯9.5份，乙苯10.2份，硫代二丙酸二月桂酯5.6份，炭黑2份，三聚磷酸二氢铝8.7份，二氨基二苯基砜2份；其中三聚磷酸二氢铝的吸油值为25%，P2O5的含量为65%,Al2O3的含量为28%，炭黑粒径为40-90nm。
在实施例1-6中，使用二苯醚甲醛树脂、聚乙烯醇缩醛改性酚醛树脂及间苯型不饱和聚酯树脂作为耐火涂料的基材，控制三者比例处于一定的范围内，可明显增强涂料的耐火性能，甲苯与间二甲苯为耐火涂料的有机溶剂，控制两者在原料中的含量，可使耐火涂料的稀释、平稳挥发效果好并形成较平滑的涂膜，炭黑的耐摩擦性能好，与硫代二丙酸二月桂酯及三聚磷酸二氢铝共同作用，可在显著提高新型耐磨涂料与基底的附着性能的前提下，大大增强耐火涂料防腐性能及其使用寿命，本发明中，所述耐火涂料的耐火性能好，防腐性能优异，使用寿命长，且成本较低。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (6)

1.一种耐火涂料，其特征在于，其原料按重量份包括：二苯醚甲醛树脂25-40份，聚乙烯醇缩醛改性酚醛树脂12-20份，间苯型不饱和聚酯树脂10-15份，间二甲苯6-10份，乙苯10-14份，硫代二丙酸二月桂酯3-7份，炭黑2-4份，三聚磷酸二氢铝6-9份，二氨基二苯基砜2-6份；其中三聚磷酸二氢铝的吸油值为25-30%。
2.根据权利要求1所述的耐火材料，其特征在于，二苯醚甲醛树脂、聚乙烯醇缩醛改性酚醛树脂及间苯型不饱和聚酯树脂的重量比为6:（3-4）：2。
3.根据权利要求1所述的耐火涂料，其特征在于，所述炭黑粒径为40-90nm。
4.根据权利要求1所述的耐火涂料，其特征在于，三聚磷酸二氢铝中，P2O5的含量为60-70%,Al2O3的含量为20-30%。
5.根据权利要求1所述的耐火涂料，其特征在于，其原料按重量份包括：二苯醚甲醛树脂30-35份，聚乙烯醇缩醛改性酚醛树脂15-17份，间苯型不饱和聚酯树脂12-13份，间二甲苯8-9份，乙苯12-14份，硫代二丙酸二月桂酯5-6份，炭黑3-4份，三聚磷酸二氢铝7-8份，二氨基二苯基砜3-5份。
6.根据权利要求5所述的耐火涂料，其特征在于，其原料按重量份包括：二苯醚甲醛树脂36份，聚乙烯醇缩醛改性酚醛树脂15份，间苯型不饱和聚酯树脂12份，间二甲苯8份，乙苯13份，硫代二丙酸二月桂酯6份，炭黑4份，三聚磷酸二氢铝7份，二氨基二苯基砜4份。
CN201310719411.1A 2013-12-23 2013-12-23 一种耐火涂料 Active CN103740227B (zh)