CN103737678A - 一种单板密实化胶合方法 - Google Patents

一种单板密实化胶合方法 Download PDF

Info

Publication number
CN103737678A
CN103737678A CN201310675121.1A CN201310675121A CN103737678A CN 103737678 A CN103737678 A CN 103737678A CN 201310675121 A CN201310675121 A CN 201310675121A CN 103737678 A CN103737678 A CN 103737678A
Authority
CN
China
Prior art keywords
veneer
densification
powder
montmorillonite
rubber powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310675121.1A
Other languages
English (en)
Other versions
CN103737678B (zh
Inventor
彭万喜
李凯夫
傅锦辉
张仲凤
邓和平
李东立
肖云飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Hongsen New Material Technology Co., Ltd
Original Assignee
Central South University of Forestry and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Central South University of Forestry and Technology filed Critical Central South University of Forestry and Technology
Priority to CN201310675121.1A priority Critical patent/CN103737678B/zh
Publication of CN103737678A publication Critical patent/CN103737678A/zh
Application granted granted Critical
Publication of CN103737678B publication Critical patent/CN103737678B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合。本发明是一种易于实现、操作方便、生产成本低的单板密实化胶合方法。

Description

一种单板密实化胶合方法
技术领域
本发明涉及一种单板密实化胶合方法，具体地说，涉及一种利用低密度人工林木材单板制造高档胶合板、单板层积材的方法。
背景技术
人工林，是采用人工播种、栽植或扦插等方法和技术措施营造培育而成的森林，是世界林产化工的主要原材料林，特别是中国、巴西、南非、印度等大量种植人工林，其中我国人工林已达5325万公顷，居世界第一位，仅桉树人工林面积达到170万ha2，杨树人工林面积达到700多万ha2，已形成南“桉”北“杨”人工林群落。人工林树干通直，纹理美观，生物量高，可广泛应用于木质复合材料、制浆造纸等领域。其中胶合板、单板层积材是人工林木材高效高值加工的有效途径。然而，人工林木材易干缩湿胀、易皱缩，在胶合板、单板层积材使用中，单板含水率发生变化时，单板尺寸发生变化，促使胶钉、化学结合键断裂，产品出现分层，严重影响产品使用价值。
为了克服这种现象，发明人历时两代人，耗资近千万，全面分析《一种碎料胶合板及其制造方法》（申请号：88105263）、《用废单板生产胶合板的方法》（申请号：90107378.4）、《一种生产密实性强化单板层积材的方法》（申请号：200410064530.9）等近400项发明专利的基础上，本发明申请人创新胶合板、单板层积材的单板干燥、胶黏剂制备、施胶三个工序，实现单板密实化胶合，为提高人工林木材附加值与增加农民收入提供技术支撑。
发明内容
本发明所要解决的技术问题是提供一种易于实现、操作方便、生产成本低的单板密实化胶合方法。
为了解决上述技术问题，本发明采用的单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合，（1）、不改变单板干燥设备与工序参数基础上，将单板干燥含水率控制在40％～70％范围；其中单板树种是密度低于0.7g/cm3的人工林桉树、杨树、桐树、杉树、槭树的任意一种或多种，单板是旋切加工的，厚度为0.3～20mm；（2）、按照质量比m脲醛树脂胶粉：m三聚氰胺胶粉：m过硼酸钠：m蒙脱石：m钛酸乙酯：m二氧化钛：m轻质碳酸钙：m面粉=100：0.5～2.5：1.2～3.8：0.8～1.7：0.1～1.1：2～5.7：3～7：3～15，将脲醛树脂胶粉、三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉进行均匀混合，在室温、压力0.9MPa～1.3MPa、挤压时间1min～5min下压制成块，然后再粉碎至100目～240目固体胶粉，其中脲醛树脂胶粉的甲醛释放量<30mg/100g，三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉的纯度>95％；（3）、将固体胶粉放入胶槽之中，然后将单板放在胶槽上，接通直流电，使其两极间电压50KV～80KV，保持20s～60s，当施胶量达到8％～10％时断电，取出单板，完成施胶，然后按照胶合板、单板层积材正常组批、冷压、热压及后续工序下，完成单板密实化胶合。
采用上述技术方案的单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合，易于实现，操作方便，生产成本低，创新胶合板、单板层积材的单板干燥、胶黏剂制备、施胶三个工序，实现单板密实化胶合，为提高人工林木材附加值与增加农民收入提供技术支撑，同时实现低密度树种资源经济较大化利用，可增加果农收入，对构建和谐社会具有重要意义。该发明将能产生显著的经济与社会效益，具有很好的推广价值。
本发明是一种易于实现、操作方便、生产成本低的单板密实化胶合方法。
附图说明
图1是本发明的工艺装置图。
图1中：1-正极，2-木单板，3-静电胶槽，4-负极
具体实施方式
通过下面给出的本发明的具体实施例可以进一步清楚地理解本发明，但下述实施例并不是对本发明的限定。
实施例1：
参见图1，一种单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合，（1）不改变单板干燥设备与工序参数基础上，将单板干燥含水率控制在40％范围；其中单板树种是密度低于0.7g/cm3的人工林桉树、杨树、桐树、杉树、槭树的任意一种或多种，单板是旋切加工的，厚度为0.3mm；（2）按照质量比m脲醛树脂胶粉：m三聚氰胺胶粉：m过硼酸钠：m蒙脱石：m钛酸乙酯：m二氧化钛：m轻质碳酸钙：m面粉=100：0.5：1.2：1.7：1.1：2：5：3，将脲醛树脂胶粉、三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉进行均匀混合，在室温、压力1.2MPa、挤压时间4min下压制成块，然后再粉碎至100目固体胶粉，其中脲醛树脂胶粉的甲醛释放量<30mg/100g，三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉的纯度>95％；（3）将固体胶粉放入胶槽之中，然后将单板放在胶槽上，接通直流电，使其两极间电压50KV，保持60s，当施胶量达到8％时断电，取出单板，完成施胶，然后按照胶合板、单板层积材正常组批、冷压、热压及后续工序下，完成单板密实化胶合。
实施例2：
参见图1，一种单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合，（1）不改变单板干燥设备与工序参数基础上，将单板干燥含水率控制在50％范围；其中单板树种是密度低于0.7g/cm3的人工林桉树、杨树、桐树、杉树、槭树的任意一种或多种，单板是旋切加工的，厚度为8mm；（2）按照质量比m脲醛树脂胶粉：m三聚氰胺胶粉：m过硼酸钠：m蒙脱石：m钛酸乙酯：m二氧化钛：m轻质碳酸钙：m面粉=100：1.0：2.0：1.5：0.5：3.5：7：8，将脲醛树脂胶粉、三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉进行均匀混合，在室温、压力1.0MPa、挤压时间3min下压制成块，然后再粉碎至180目固体胶粉，其中脲醛树脂胶粉的甲醛释放量<30mg/100g，三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉的纯度>95％；（3）将固体胶粉放入胶槽之中，然后将单板放在胶槽上，接通直流电，使其两极间电压60KV，保持50s，当施胶量达到9％时断电，取出单板，完成施胶，然后按照胶合板、单板层积材正常组批、冷压、热压及后续工序下，完成单板密实化胶合。
实施例3：
参见图1，一种单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合，（1）不改变单板干燥设备与工序参数基础上，将单板干燥含水率控制在60％范围；其中单板树种是密度低于0.7g/cm3的人工林桉树、杨树、桐树、杉树、槭树的任意一种或多种，单板是旋切加工的，厚度为12mm；（2）按照质量比m脲醛树脂胶粉：m三聚氰胺胶粉：m过硼酸钠：m蒙脱石：m钛酸乙酯：m二氧化钛：m轻质碳酸钙：m面粉=100：2.0：2.8：1.0：0.9：4.5：3：10，将脲醛树脂胶粉、三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉进行均匀混合，在室温、压力0.9MPa、挤压时间5min下压制成块，然后再粉碎至200目固体胶粉，其中脲醛树脂胶粉的甲醛释放量<30mg/100g，三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉的纯度>95％；（3）将固体胶粉放入胶槽之中，然后将单板放在胶槽上，接通直流电，使其两极间电压70KV，保持30s，当施胶量达到9％时断电，取出单板，完成施胶，然后按照胶合板、单板层积材正常组批、冷压、热压及后续工序下，完成单板密实化胶合。
实施例4：
参见图1，一种单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合，（1）不改变单板干燥设备与工序参数基础上，将单板干燥含水率控制在70％范围；其中单板树种是密度低于0.7g/cm3的人工林桉树、杨树、桐树、杉树、槭树的任意一种或多种，单板是旋切加工的，厚度为20mm；（2）按照质量比m脲醛树脂胶粉：m三聚氰胺胶粉：m过硼酸钠：m蒙脱石：m钛酸乙酯：m二氧化钛：m轻质碳酸钙：m面粉=100：2.5：3.8：0.8：0.1：5.7：4：15，将脲醛树脂胶粉、三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉进行均匀混合，在室温、压力1.3MPa、挤压时间1min下压制成块，然后再粉碎至240目固体胶粉，其中脲醛树脂胶粉的甲醛释放量<30mg/100g，三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉的纯度>95％；（3）将固体胶粉放入胶槽之中，然后将单板放在胶槽上，接通直流电，使其两极间电压80KV，保持20s，当施胶量达到10％时断电，取出单板，完成施胶，然后按照胶合板、单板层积材正常组批、冷压、热压及后续工序下，完成单板密实化胶合。

Claims (1)

1.一种单板密实化胶合方法，在不改变胶合板、单板层积材主要生产工序的基础上，只同时改变单板干燥、胶黏剂制备、施胶三个工序及参数，实施单板密实化胶合，其特征是：
（1）、不改变单板干燥设备与工序参数基础上，将单板干燥含水率控制在40％～70％范围；其中单板树种是密度低于0.7g/cm3的人工林桉树、杨树、桐树、杉树、槭树的任意一种或多种，单板是旋切加工的，厚度为0.3～20mm；
（2）、按照质量比m脲醛树脂胶粉：m三聚氰胺胶粉：m过硼酸钠：m蒙脱石：m钛酸乙酯：m二氧化钛：m轻质碳酸钙：m面粉=100：0.5～2.5：1.2～3.8：0.8～1.7：0.1～1.1：2～5.7：3～7：3～15，将脲醛树脂胶粉、三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉进行均匀混合，在室温、压力0.9MPa～1.3MPa、挤压时间1min～5min下压制成块，然后再粉碎至100目～240目固体胶粉，其中脲醛树脂胶粉的甲醛释放量<30mg/100g，三聚氰胺胶粉、过硼酸钠、蒙脱石、钛酸乙酯、二氧化钛、轻质碳酸钙和面粉的纯度>95％；
（3）、将固体胶粉放入胶槽之中，然后将单板放在胶槽上，接通直流电，使其两极间电压50KV～80KV，保持20s～60s，当施胶量达到8％～10％时断电，取出单板，完成施胶，然后按照胶合板、单板层积材正常组批、冷压、热压及后续工序下，完成单板密实化胶合。
CN201310675121.1A 2013-12-11 2013-12-11 一种单板密实化胶合方法 Active CN103737678B (zh)