CN103726617B - Build roofing and plant green three layers of pre-control root thorn method - Google Patents
Build roofing and plant green three layers of pre-control root thorn method Download PDFInfo
- Publication number
- CN103726617B CN103726617B CN201310707267.XA CN201310707267A CN103726617B CN 103726617 B CN103726617 B CN 103726617B CN 201310707267 A CN201310707267 A CN 201310707267A CN 103726617 B CN103726617 B CN 103726617B
- Authority
- CN
- China
- Prior art keywords
- paving
- coiled material
- root resistance
- resistance carbon
- root
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of roofing of building and plant green three layers of pre-control root thorn method, comprise the step such as base treatment, spraying rubber cement, paving aluminium tin pewter coiled material, the paving of complex copper tire base SBS modified asphalt waterproof coiled material, root resistance carbon place mat.Easy construction of the present invention, root resistance control thorn performance is good.
Description
Technical field
The present invention relates to adjustment roofing and plant green technology roofing root-resistant puncturing method.
Background technology
Along with the continuous deterioration of climatic environment, air layer pollutes more and more serious, and the haze frequency of occurrences is more and more higher, carbonization concentration is more and more closeer, land resources is fewer and feweri, and urban heat land effect is more and more obvious, thus advances construction roofing to plant green technology and seems more and more important.The national U.S. of west prosperity, Germany, Britain's roofing are planted green area and are occupied larger specific gravity, and south China roofing is planted and greenly also occupied certain ratio.But plant green technology roofing root-resistant puncturing technology at construction roofing and be still technical difficult point, do not have to solve very well, green construction 2-3 planted by some roofings, its roofing carries out seepage, basic reason roofing root system of plant is through concrete plank layer, have to keep in repair, expend fund, manually, affect using function and effect.
Summary of the invention
Green three layers of pre-control root thorn method planted by the construction roofing that the object of the present invention is to provide a kind of root resistance control to sting performance good.
Technical solution of the present invention is:
Green three layers of pre-control root thorn method planted by a kind of roofing of building, and it is characterized in that: comprise the following steps:
(1) base treatment: after roofing basal plane is formed, sweep off floating dust, cuts redundance, fills up recessed portion, then carries out levelling with mortar, makes roofing smooth, and the degree of deviation is ± 2mm;
(2) spray rubber cement: adopt 325# cement: water: 901 glue=1:0.3:0.2 weight ratio mixing, stir, then even application is on toft face, and thickness is 3mm;
(3) paving aluminium tin pewter coiled material: when after rubber cement spraying, paving aluminium tin pewter coiled material, during paving, paving from top to bottom, sealing overlap joint >=5cm, carries out nip drum 1-2 time from top to bottom with Ф 20mm steel pipe after place mat, is convenient to closely knit; Sealing is welded: adopt electric welding machine to carry out sealing welding;
(4) complex copper tire base SBS modified asphalt waterproof coiled material paving: brush away aluminium tin pewter coiled material surface and float layer, foreign material; Then brushing basal plane agent: bituminous neoprene bonding adhesive is added gasoline and dilutes, stir, evenly brushes on aluminium tin pewter coiled material with round brush, at normal temperatures, brushes and within latter 4 hours, starts to carry out paving complex copper tire base SBS modified asphalt waterproof coiled material;
Complex copper tire base SBS modified asphalt waterproof coiled material adopts hot melt to carry out paving, unreels while heating edge paving during paving; Hot melt edge sealing: heated by complex copper tire base SBS modified asphalt waterproof coiled material lap-joint fired heater, makes both be connected firmly while hot, and overflow pitch for degree with edge, it is tight that end receives head sealing compound pointing;
To calm the anger compacting: after the paving of complex copper tire base SBS modified asphalt waterproof coiled material, carry out nip drum from top to bottom with Ф 20cm steel pipe, air is extruded, bondingly with aluminium tin pewter coiled material become overall;
(5) root resistance carbon place mat:
Root resistance carbon configures: root resistance carbon is made up of charcoal, lime, clay three kinds of materials, and configuration part by weight 3:1:1, proportionally mixes, even mix, form root resistance carbon;
Root resistance carbon place mat, at the root resistance carbon-coating that copper tire base SBS modified asphalt waterproof coiled material surface uniform place mat 0.5cm is thick, sprays water after paving, every m
2water spray 0.3kg, after surface is solid, rolls with hollow steel and carries out compacting from top to bottom;
Root resistance carbon face is protected, root resistance carbon-coating surface, brushing one deck pitch, and covers one deck geotextiles.
Charcoal in root resistance carbon is the powdery of particle diameter <1mm; Lime is pulverized limestone, and sieves with eyelet Ф <1mm steel sieve, removing impurity, and clay dries for passing through or dries, and carries out pulverizing or pulverizing, and sieves with eyelet Ф <1mm steel sieve, removing impurity.
Easy construction of the present invention, root resistance control thorn performance is good.
First floor of the present invention is closed root resistance puncture layer, adopt aluminium tin pewter coiled material, this tensile strength of material >=20Mpa, fracture elongation >=30%, root-resistant puncturing is tested sharp root system and is not punctured for more than 10 years, is up to state standards, low-temperature tenderness-30, Ф 20mm drum, by damaging impact flawless or perforation.By aluminium tin pewter coiled material, root system, on concrete pavement or on plank surface layer and on other surface layer, is directly carried out prevention puncture by place mat, and this one deck is closure root resistance puncture layer.
The second layer is flexible closure, and half initiative resists root resistance puncture layer, when after roofing basal plane place mat aluminium tin pewter coiled material, and place mat complex copper tire base SBS modified asphalt waterproof coiled material, this material soluble content>=2900g/m
2, pulling force>=800 IV/50mm, fracture elongation>=40%, root-resistant puncturing is tested sharp root system and is not punctured for more than 8 years, heat resistance 105 DEG C, low temperature flexibility-25 DEG C, this material has closure root resistance performance, and root resistance dynamics is not as good as aluminium tin pewter coiled material, but this material has a kind of pitch chemicals, when phytem enters this layer, during contact pitch, there is burn phytem function, play root resistance puncture effect.
Third layer is antagonism root resistance puncture layer.When after second layer complex copper tire SBS modified asphalt waterproof coiled material place mat, the root resistance carbon that place mat one deck 0.5cm is thick, root resistance carbon presses 1:1:3 proportional arrangement by lime, clay, charcoal, when root system enters this layer, being forced property grows round about, must not enter lower floor, because charcoal and plant phytem have antagonism, and charcoal has stability, the time, longer root resistance effect was better, was an antagonistic root resistance puncture measure.
Adopt above three layers of root resistance puncture measure, form three layers of root resistance lancing system, carry out and have complementary advantages.
Below in conjunction with embodiment, the invention will be further described.
Detailed description of the invention
Green three layers of pre-control root thorn method planted by a kind of roofing of building, and comprise the following steps:
(1) base treatment: after roofing basal plane is formed, sweep off floating dust, cuts redundance, fills up recessed portion, then carries out levelling with mortar, makes roofing smooth, and the degree of deviation is ± 2mm;
(2) spray rubber cement: adopt 325# cement: water: 901 glue=1:0.3:0.2 weight ratio mixing, stir, then even application is on toft face, and thickness is 3mm;
(3) paving aluminium tin pewter coiled material: when after rubber cement spraying, paving aluminium tin pewter coiled material, during paving, paving from top to bottom, sealing overlap joint >=5cm, carries out nip drum 1-2 time from top to bottom with Ф 20mm steel pipe after place mat, is convenient to closely knit; Sealing is welded: adopt electric welding machine to carry out sealing welding;
(4) complex copper tire base SBS modified asphalt waterproof coiled material paving: brush away aluminium tin pewter coiled material surface and float layer, foreign material; Then brushing basal plane agent: bituminous neoprene bonding adhesive is added gasoline and dilutes, bituminous neoprene bonding adhesive and gasoline weight ratio are 10:2, stir, evenly brush on aluminium tin pewter coiled material with round brush, at normal temperatures, brush and within latter 4 hours, start to carry out paving complex copper tire base SBS modified asphalt waterproof coiled material;
Complex copper tire base SBS modified asphalt waterproof coiled material adopts hot melt to carry out paving, unreels while heating edge paving during paving; Hot melt edge sealing: heated by complex copper tire base SBS modified asphalt waterproof coiled material lap-joint fired heater, makes both be connected firmly while hot, and overflow pitch for degree with edge, it is tight that end receives head sealing compound pointing;
To calm the anger compacting: after the paving of complex copper tire base SBS modified asphalt waterproof coiled material, carry out nip drum from top to bottom with Ф 20cm steel pipe, air is extruded, bondingly with aluminium tin pewter coiled material become overall;
(5) root resistance carbon place mat:
Root resistance carbon configures: root resistance carbon is made up of charcoal, lime, clay three kinds of materials, and configuration part by weight 3:1:1, proportionally mixes, even mix, form root resistance carbon;
Root resistance carbon place mat, at the root resistance carbon-coating that copper tire base SBS modified asphalt waterproof coiled material surface uniform place mat 0.5cm is thick, sprays water after paving, every m
2water spray 0.3kg, after surface is solid, rolls with hollow steel and carries out compacting from top to bottom;
Root resistance carbon face is protected, root resistance carbon-coating surface, brushing one deck pitch, and covers one deck geotextiles.
Charcoal in root resistance carbon is the powdery of particle diameter <1mm; Lime is pulverized limestone, and sieves with eyelet Ф <1mm steel sieve, removing impurity, and clay dries for passing through or dries, and carries out pulverizing or pulverizing, and sieves with eyelet Ф <1mm steel sieve, removing impurity.
Claims (2)
1. green three layers of pre-control root thorn method planted by construction roofing, it is characterized in that: comprise the following steps:
(1) base treatment: after roofing basal plane is formed, sweep off floating dust, cuts redundance, fills up recessed portion, then carries out levelling with mortar, makes roofing smooth, and the degree of deviation is ± 2mm;
(2) spray rubber cement: adopt 325# cement: water: 901 glue=1:0.3:0.2 weight ratio mixing, stir, then even application is on toft face, and thickness is 3mm;
(3) paving aluminium tin pewter coiled material: when after rubber cement spraying, paving aluminium tin pewter coiled material, during paving, paving from top to bottom, sealing overlap joint >=5cm, carries out nip drum 1-2 time from top to bottom with Ф 20mm steel pipe after place mat, is convenient to closely knit; Sealing is welded: adopt electric welding machine to carry out sealing welding;
(4) complex copper tire base SBS modified asphalt waterproof coiled material paving: brush away aluminium tin pewter coiled material surface and float layer, foreign material; Then brushing basal plane agent: bituminous neoprene bonding adhesive is added gasoline and dilutes, stir, evenly brushes on aluminium tin pewter coiled material with round brush, at normal temperatures, brushes and within latter 4 hours, starts to carry out paving complex copper tire base SBS modified asphalt waterproof coiled material;
Complex copper tire base SBS modified asphalt waterproof coiled material adopts hot melt to carry out paving, unreels while heating edge paving during paving; Hot melt edge sealing: heated by complex copper tire base SBS modified asphalt waterproof coiled material lap-joint fired heater, makes both be connected firmly while hot, and overflow pitch for degree with edge, it is tight that end receives head sealing compound pointing;
To calm the anger compacting: after the paving of complex copper tire base SBS modified asphalt waterproof coiled material, carry out nip drum from top to bottom with Ф 20cm steel pipe, air is extruded, bondingly with aluminium tin pewter coiled material become overall;
(5) root resistance carbon place mat:
Root resistance carbon configures: root resistance carbon is made up of charcoal, lime, clay three kinds of materials, and configuration part by weight 3:1:1, proportionally mixes, even mix, form root resistance carbon;
Root resistance carbon place mat, at the root resistance carbon-coating that copper tire base SBS modified asphalt waterproof coiled material surface uniform place mat 0.5cm is thick, sprays water after paving, every m
2water spray 0.3kg, after surface is solid, rolls with hollow steel and carries out compacting from top to bottom;
Root resistance carbon face is protected, root resistance carbon-coating surface, brushing one deck pitch, and covers one deck geotextiles.
2. green three layers of pre-control root thorn method planted by construction roofing according to claim 1, it is characterized in that: the charcoal in root resistance carbon is the powdery of particle diameter <1mm; Lime is pulverized limestone, and sieves with eyelet Ф <1mm steel sieve, removing impurity, and clay dries for passing through or dries, and carries out pulverizing or pulverizing, and sieves with eyelet Ф <1mm steel sieve, removing impurity.