CN103726617A - Building roof afforestation three-layer root thorn precontrol method - Google Patents
Building roof afforestation three-layer root thorn precontrol method Download PDFInfo
- Publication number
- CN103726617A CN103726617A CN201310707267.XA CN201310707267A CN103726617A CN 103726617 A CN103726617 A CN 103726617A CN 201310707267 A CN201310707267 A CN 201310707267A CN 103726617 A CN103726617 A CN 103726617A
- Authority
- CN
- China
- Prior art keywords
- paving
- coiled material
- root
- root resistance
- resistance carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a building roof afforestation three-layer root thorn precontrol method. The method includes the steps of substrate processing, mucilage spraying, aluminum-tin-antimony alloy coil laying, composite copper tire based SBS modified asphalt waterproof coil laying, root-resisting carbon laying and the like. The building roof afforestation three-layer root thorn precontrol method is convenient in construction and good in root-resisting thorn-controlling performance.
Description
Technical field
The present invention relates to adjust roofing and plant green technology roofing root-resistant puncturing method.
Background technology
Along with the continuous deterioration of climatic environment, air layer pollutes more and more serious, and the haze frequency of occurrences is more and more higher, carbonization concentration is more and more closeer, land resources is fewer and feweri, and urban heat land effect is more and more obvious, thereby advance to build roofing and plant green technology and seem more and more important.The national U.S. of west prosperity, Germany, Britain's roofing are planted green area and are occupied larger specific gravity, and south China roofing is planted green certain ratio of also occupying.But at construction roofing, plant green technology roofing root-resistant puncturing technology and be still technical difficult point, do not have finely to solve, some roofings are planted green construction 2-3, its roofing carries out seepage, basic reason roofing root system of plant is through concrete plank layer, have to keep in repair, expend fund, artificial, function and effect are used in impact.
Summary of the invention
The object of the present invention is to provide the good construction roofing of a kind of root resistance control thorn performance to plant green three layers of pre-control root thorn method.
Technical solution of the present invention is:
Construction roofing is planted green three layers of pre-control root thorn method, it is characterized in that: comprise the following steps:
(1) base treatment: after roofing basal plane forms, sweep off floating dust, cut redundance, fill up recessed portion, then carry out levelling with mortar, make roofing smooth, the degree of deviation is ± 2mm;
(2) spraying rubber cement: adopt 325# cement: water: 901 glue=1:0.3:0.2 weight ratio is mixed, and stirs, and is then evenly sprayed on toft face, and thickness is 3mm;
(3) paving aluminium tin pewter coiled material: after rubber cement spraying, paving aluminium tin pewter coiled material, during paving, paving from top to bottom, sealing overlap joint >=5cm, carries out nip drum 1-2 time from top to bottom with Ф 20mm steel pipe after place mat, is convenient to closely knit; Sealing is welded: adopt electric welding machine to carry out sealing welding;
(4) complex copper tire base SBS modified asphalt waterproof coiled material paving: brush away the floating layer of aluminium tin pewter coiled material surface, foreign material; Then brushing basal plane agent: add gasoline to dilute neoprene asphalt adhesive, stir, evenly brush on aluminium tin pewter coiled material with round brush, at normal temperatures, brush and start to carry out paving complex copper tire base SBS modified asphalt waterproof coiled material for latter 4 hours;
Complex copper tire base SBS modified asphalt waterproof coiled material adopts hot melt to carry out paving, the heating edge paving while unreeling during paving; Hot melt edge sealing: complex copper tire JiSBS modified asphalt waterproof coiled material lap-joint is heated with fired heater, make while hot both be connected firmly, take edge overflows pitch as degree, and it is tight with sealing compound pointing that end is received head;
The compacting of calming the anger: after the paving of complex copper tire base SBS modified asphalt waterproof coiled material,, air is extruded, with the bonding integral body that becomes of aluminium tin pewter coiled material from the upper supreme nip drum that carries out with Ф 20cm steel pipe;
(5) root resistance carbon place mat:
Root resistance carbon configuration: root resistance carbon is comprised of charcoal, lime, three kinds of materials of clay, configuration part by weight 3:1:1, proportionally mixes, and evenly mix, forms root resistance carbon;
Root resistance carbon place mat, at the thick root resistance carbon-coating of copper tire base SBS modified asphalt waterproof coiled material surface uniform place mat 0.5cm, sprays water after paving, every m
2water spray 0.3kg, after surface is solid, rolls and carries out from top to bottom compacting with hollow steel;
The protection of root resistance carbon face, root resistance carbon-coating surface, brushing one deck pitch, and cover one deck geotextiles.
Charcoal in root resistance carbon is the powdery of particle diameter <1mm; Lime is pulverized limestone, and sieves with eyelet Ф <1mm steel sieve, removes impurity, and clay is through shining soil or drying, and pulverizes or pulverize, and with eyelet Ф <1mm steel, sieves and sieves, and removes impurity.
Easy construction of the present invention, root resistance control thorn performance is good.
First floor of the present invention is closed root resistance puncture layer, adopt aluminium tin pewter coiled material, this tensile strength of material >=20Mpa, fracture elongation >=30%, root-resistant puncturing is tested sharp root system and is not punctured above for 10 years, is up to state standards, and low-temperature tenderness-30, Ф 20mm drum, by damaging impact flawless or perforation.By aluminium tin pewter coiled material, place mat, on concrete pavement or on plank surface layer and on other surface layer, directly stops puncture by root system, and this one deck is closure root resistance puncture layer.
The second layer is flexible sealing, and half initiative is resisted root resistance puncture layer, after roofing basal plane place mat aluminium tin pewter coiled material, and place mat complex copper tire base SBS modified asphalt waterproof coiled material, this material solubility content>=2900g/m
2, pulling force>=800 IV/50mm, fracture elongation>=40%, root-resistant puncturing is tested sharp root system and is not punctured above for 8 years, 105 ℃ of heat resistances, low temperature flexibility-25 ℃, this material has closure root resistance performance, and root resistance dynamics is not as good as aluminium tin pewter coiled material, but this material has a kind of pitch chemicals, when phytem enters this layer, during contact pitch, there is burn phytem function, play root resistance puncture effect.
The 3rd layer is antagonism root resistance puncture layer.After second layer complex copper tire SBS modified asphalt waterproof coiled material place mat, the root resistance carbon that place mat one deck 0.5cm is thick, root resistance carbon is pressed 1:1:3 proportional arrangement by lime, clay, charcoal, when root system enters this layer, being forced to property is grown round about, must not enter lower floor, because charcoal and plant phytem have antagonism, and charcoal has stability, the time, longer root resistance effect was better, was an antagonistic root resistance puncture measure.
Adopt above three layers of root resistance puncture measure, form three layers of root resistance lancing system, carry out and have complementary advantages.
Below in conjunction with embodiment, the invention will be further described.
The specific embodiment
Construction roofing is planted green three layers of pre-control root thorn method, comprises the following steps:
(1) base treatment: after roofing basal plane forms, sweep off floating dust, cut redundance, fill up recessed portion, then carry out levelling with mortar, make roofing smooth, the degree of deviation is ± 2mm;
(2) spraying rubber cement: adopt 325# cement: water: 901 glue=1:0.3:0.2 weight ratio is mixed, and stirs, and is then evenly sprayed on toft face, and thickness is 3mm;
(3) paving aluminium tin pewter coiled material: after rubber cement spraying, paving aluminium tin pewter coiled material, during paving, paving from top to bottom, sealing overlap joint >=5cm, carries out nip drum 1-2 time from top to bottom with Ф 20mm steel pipe after place mat, is convenient to closely knit; Sealing is welded: adopt electric welding machine to carry out sealing welding;
(4) complex copper tire base SBS modified asphalt waterproof coiled material paving: brush away the floating layer of aluminium tin pewter coiled material surface, foreign material; Then brushing basal plane agent: add gasoline to dilute neoprene asphalt adhesive, neoprene asphalt adhesive and gasoline weight ratio are 10:2, stir, with round brush, evenly brush on aluminium tin pewter coiled material, at normal temperatures, brush and within latter 4 hours, start to carry out paving complex copper tire base SBS modified asphalt waterproof coiled material;
Complex copper tire base SBS modified asphalt waterproof coiled material adopts hot melt to carry out paving, the heating edge paving while unreeling during paving; Hot melt edge sealing: complex copper tire JiSBS modified asphalt waterproof coiled material lap-joint is heated with fired heater, make while hot both be connected firmly, take edge overflows pitch as degree, and it is tight with sealing compound pointing that end is received head;
The compacting of calming the anger: after the paving of complex copper tire base SBS modified asphalt waterproof coiled material,, air is extruded, with the bonding integral body that becomes of aluminium tin pewter coiled material from the upper supreme nip drum that carries out with Ф 20cm steel pipe;
(5) root resistance carbon place mat:
Root resistance carbon configuration: root resistance carbon is comprised of charcoal, lime, three kinds of materials of clay, configuration part by weight 3:1:1, proportionally mixes, and evenly mix, forms root resistance carbon;
Root resistance carbon place mat, at the thick root resistance carbon-coating of copper tire base SBS modified asphalt waterproof coiled material surface uniform place mat 0.5cm, sprays water after paving, every m
2water spray 0.3kg, after surface is solid, rolls and carries out from top to bottom compacting with hollow steel;
The protection of root resistance carbon face, root resistance carbon-coating surface, brushing one deck pitch, and cover one deck geotextiles.
Charcoal in root resistance carbon is the powdery of particle diameter <1mm; Lime is pulverized limestone, and sieves with eyelet Ф <1mm steel sieve, removes impurity, and clay is through shining soil or drying, and pulverizes or pulverize, and with eyelet Ф <1mm steel, sieves and sieves, and removes impurity.
Claims (2)
1. construction roofing is planted green three layers of pre-control root thorn method, it is characterized in that: comprise the following steps:
(1) base treatment: after roofing basal plane forms, sweep off floating dust, cut redundance, fill up recessed portion, then carry out levelling with mortar, make roofing smooth, the degree of deviation is ± 2mm;
(2) spraying rubber cement: adopt 325# cement: water: 901 glue=1:0.3:0.2 weight ratio is mixed, and stirs, and is then evenly sprayed on toft face, and thickness is 3mm;
(3) paving aluminium tin pewter coiled material: after rubber cement spraying, paving aluminium tin pewter coiled material, during paving, paving from top to bottom, sealing overlap joint >=5cm, carries out nip drum 1-2 time from top to bottom with Ф 20mm steel pipe after place mat, is convenient to closely knit; Sealing is welded: adopt electric welding machine to carry out sealing welding;
(4) complex copper tire base SBS modified asphalt waterproof coiled material paving: brush away the floating layer of aluminium tin pewter coiled material surface, foreign material; Then brushing basal plane agent: add gasoline to dilute neoprene asphalt adhesive, stir, evenly brush on aluminium tin pewter coiled material with round brush, at normal temperatures, brush and start to carry out paving complex copper tire base SBS modified asphalt waterproof coiled material for latter 4 hours;
Complex copper tire base SBS modified asphalt waterproof coiled material adopts hot melt to carry out paving, the heating edge paving while unreeling during paving; Hot melt edge sealing: complex copper tire JiSBS modified asphalt waterproof coiled material lap-joint is heated with fired heater, make while hot both be connected firmly, take edge overflows pitch as degree, and it is tight with sealing compound pointing that end is received head;
The compacting of calming the anger: after the paving of complex copper tire base SBS modified asphalt waterproof coiled material,, air is extruded, with the bonding integral body that becomes of aluminium tin pewter coiled material from the upper supreme nip drum that carries out with Ф 20cm steel pipe;
(5) root resistance carbon place mat:
Root resistance carbon configuration: root resistance carbon is comprised of charcoal, lime, three kinds of materials of clay, configuration part by weight 3:1:1, proportionally mixes, and evenly mix, forms root resistance carbon;
Root resistance carbon place mat, at the thick root resistance carbon-coating of copper tire base SBS modified asphalt waterproof coiled material surface uniform place mat 0.5cm, sprays water after paving, every m
2water spray 0.3kg, after surface is solid, rolls and carries out from top to bottom compacting with hollow steel;
The protection of root resistance carbon face, root resistance carbon-coating surface, brushing one deck pitch, and cover one deck geotextiles.
2. construction roofing according to claim 1 is planted green three layers of pre-control root thorn method, it is characterized in that: the charcoal in root resistance carbon is the powdery of particle diameter <1mm; Lime is pulverized limestone, and sieves with eyelet Ф <1mm steel sieve, removes impurity, and clay is through shining soil or drying, and pulverizes or pulverize, and with eyelet Ф <1mm steel, sieves and sieves, and removes impurity.