CN103726299A - 蓄热保暖织物整理剂的制备方法 - Google Patents
蓄热保暖织物整理剂的制备方法 Download PDFInfo
- Publication number
- CN103726299A CN103726299A CN201310625688.8A CN201310625688A CN103726299A CN 103726299 A CN103726299 A CN 103726299A CN 201310625688 A CN201310625688 A CN 201310625688A CN 103726299 A CN103726299 A CN 103726299A
- Authority
- CN
- China
- Prior art keywords
- medical stone
- molybdenum oxide
- powder
- finishing agent
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种蓄热保暖织物整理剂的制备方法,包括如下步骤:在装有直径为1-1.5mm锆球的砂磨机中依次加入65-70质量份氧化钼和麦饭石混合纳米粉体、25-30质量份水性丙烯酸树脂、55-60质量份水、2-3质量份聚丙烯酸钠、7-9质量份羟丙基甲基纤维素,用14500-15000转/分钟的转速分散6-8小时,制得蓄热保暖织物整理剂;所述氧化钼和麦饭石混合纳米粉体中,氧化钼纳米粉体和麦饭石纳米粉体的质量百分含量分别为75-80%和20-25%,且氧化钼和麦饭石混合纳米粉体的平均粒径≤10nm。在面料厚度和结构不改变的情况下,只要在洗衣服或洗面料时少许添加本发明制备的蓄热保暖织物整理剂浸泡烘干或洗涤烘干即可实现保暖功能。
Description
技术领域
本发明涉及蓄热保暖织物整理剂的制备方法。
背景技术
现有的保暖内衣、保暖纺织品等都是采用面料的多层结构,使用起来有很大的局限性,人穿了也很臃肿,不容易洗,也不耐用。
发明内容
本发明的目的在于提供一种蓄热保暖织物整理剂的制备方法,在面料厚度和结构不改变的情况下,只要在洗衣服或洗面料时少许添加本发明制备的蓄热保暖织物整理剂浸泡烘干或洗涤烘干即可实现保暖功能。
为实现上述目的,本发明的技术方案是设计一种蓄热保暖织物整理剂的制备方法,包括如下步骤:
在装有直径为1-1.5mm锆球的砂磨机中依次加入65-70质量份氧化钼和麦饭石混合纳米粉体、25-30质量份水性丙烯酸树脂、55-60质量份水、2-3质量份聚丙烯酸钠、7-9质量份羟丙基甲基纤维素,用14500-15000转/分钟的转速分散6-8小时,制得蓄热保暖织物整理剂;
所述氧化钼和麦饭石混合纳米粉体中,氧化钼纳米粉体和麦饭石纳米粉体的质量百分含量分别为75-80%和20-25%,且氧化钼和麦饭石混合纳米粉体的平均粒径≤10nm。
本发明的优点和有益效果在于:提供一种蓄热保暖织物整理剂的制备方法,在面料厚度和结构不改变的情况下,只要在洗衣服或洗面料时少许添加本发明制备的蓄热保暖织物整理剂浸泡烘干或洗涤烘干即可实现保暖功能。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种蓄热保暖织物整理剂的制备方法,包括如下步骤:
在装有直径为1.5mm锆球的砂磨机中依次加入70质量份氧化钼和麦饭石混合纳米粉体、30质量份水性丙烯酸树脂、60质量份水、3质量份聚丙烯酸钠、9质量份羟丙基甲基纤维素,用15000转/分钟的转速分散8小时,制得蓄热保暖织物整理剂;
所述氧化钼和麦饭石混合纳米粉体中,氧化钼纳米粉体和麦饭石纳米粉体的质量百分含量分别为80%和20%,且氧化钼和麦饭石混合纳米粉体的平均粒径≤10nm。
实施例2
一种蓄热保暖织物整理剂的制备方法,包括如下步骤:
在装有直径为1mm锆球的砂磨机中依次加入65质量份氧化钼和麦饭石混合纳米粉体、25质量份水性丙烯酸树脂、55质量份水、2质量份聚丙烯酸钠、7质量份羟丙基甲基纤维素,用14500转/分钟的转速分散6小时,制得蓄热保暖织物整理剂;
所述氧化钼和麦饭石混合纳米粉体中,氧化钼纳米粉体和麦饭石纳米粉体的质量百分含量分别为75%和25%,且氧化钼和麦饭石混合纳米粉体的平均粒径≤10nm。
实施例3
一种蓄热保暖织物整理剂的制备方法,包括如下步骤:
在装有直径为1.3mm锆球的砂磨机中依次加入66质量份氧化钼和麦饭石混合纳米粉体、28质量份水性丙烯酸树脂、57质量份水、2.3质量份聚丙烯酸钠、7.9质量份羟丙基甲基纤维素,用14800转/分钟的转速分散7小时,制得蓄热保暖织物整理剂;
所述氧化钼和麦饭石混合纳米粉体中,氧化钼纳米粉体和麦饭石纳米粉体的质量百分含量分别为78%和22%,且氧化钼和麦饭石混合纳米粉体的平均粒径≤10nm。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.蓄热保暖织物整理剂的制备方法,其特征在于,包括如下步骤:
在装有直径为1-1.5mm锆球的砂磨机中依次加入65-70质量份氧化钼和麦饭石混合纳米粉体、25-30质量份水性丙烯酸树脂、55-60质量份水、2-3质量份聚丙烯酸钠、7-9质量份羟丙基甲基纤维素,用14500-15000转/分钟的转速分散6-8小时,制得蓄热保暖织物整理剂;
所述氧化钼和麦饭石混合纳米粉体中,氧化钼纳米粉体和麦饭石纳米粉体的质量百分含量分别为75-80%和20-25%,且氧化钼和麦饭石混合纳米粉体的平均粒径≤10nm。