CN103726300A - 织物保暖整理剂的制备方法 - Google Patents
织物保暖整理剂的制备方法 Download PDFInfo
- Publication number
- CN103726300A CN103726300A CN201310641332.3A CN201310641332A CN103726300A CN 103726300 A CN103726300 A CN 103726300A CN 201310641332 A CN201310641332 A CN 201310641332A CN 103726300 A CN103726300 A CN 103726300A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- finishing agent
- mass
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种织物保暖整理剂的制备方法,包括如下步骤:1)在装有直径为5-6mm锆球的砂磨机中依次加入25-30质量份氧化钼纳米粉体、15-20质量份麦饭石纳米粉体、5-8质量份水性丙烯酸树脂、20-25质量份水,用14100-14500转/分钟的转速分散5-6小时;2)再依次加入3-6质量份聚乙二醇、7-9质量份聚乙烯吡咯烷酮,以13000-13500转/分钟的转速分散5-6小时,制得织物保暖整理剂。本发明提供的织物保暖整理剂的制备方法,使织物添加该织物保暖整理剂浸泡烘干或洗涤烘干即可实现保暖功能。
Description
技术领域
本发明涉及织物保暖整理剂的制备方法。
背景技术
现有技术中,虽有防紫外线功能的织物整理剂报道,但尚无具有蓄热蓄热保暖功能和防紫外线功能的织物整理剂公开。
发明内容
本发明的目的在于提供一种织物保暖整理剂的制备方法,使织物添加该织物保暖整理剂浸泡烘干或洗涤烘干即可实现保暖功能。
为实现上述目的,本发明的技术方案是设计一种织物保暖整理剂的制备方法,包括如下步骤:
1)在装有直径为5-6mm锆球的砂磨机中依次加入25-30质量份氧化钼纳米粉体、15-20质量份麦饭石纳米粉体、5-8质量份水性丙烯酸树脂、20-25质量份水,用14100-14500转/分钟的转速分散5-6小时;
2)再依次加入3-6质量份聚乙二醇、7-9质量份聚乙烯吡咯烷酮,以13000-13500转/分钟的转速分散5-6小时,制得织物保暖整理剂。
本发明的优点和有益效果在于:提供一种织物保暖整理剂的制备方法,使织物添加该织物保暖整理剂浸泡烘干或洗涤烘干即可实现保暖功能。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种织物保暖整理剂的制备方法,包括如下步骤:
1)在装有直径为6mm锆球的砂磨机中依次加入30质量份氧化钼纳米粉体、20质量份麦饭石纳米粉体、8质量份水性丙烯酸树脂、25质量份水,用14500转/分钟的转速分散6小时;
2)再依次加入6质量份聚乙二醇、9质量份聚乙烯吡咯烷酮,以13500转/分钟的转速分散6小时,制得织物保暖整理剂。
实施例2
一种织物保暖整理剂的制备方法,包括如下步骤:
1)在装有直径为5mm锆球的砂磨机中依次加入25质量份氧化钼纳米粉体、15质量份麦饭石纳米粉体、5质量份水性丙烯酸树脂、20质量份水,用14100转/分钟的转速分散5小时;
2)再依次加入3质量份聚乙二醇、7质量份聚乙烯吡咯烷酮,以13000转/分钟的转速分散5小时,制得织物保暖整理剂。
实施例3
一种织物保暖整理剂的制备方法,包括如下步骤:
1)在装有直径为5.6mm锆球的砂磨机中依次加入28质量份氧化钼纳米粉体、17质量份麦饭石纳米粉体、5.8质量份水性丙烯酸树脂、23质量份水,用14300转/分钟的转速分散5.5小时;
2)再依次加入3.6质量份聚乙二醇、7.9质量份聚乙烯吡咯烷酮,以13300转/分钟的转速分散5.5小时,制得织物保暖整理剂。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.织物保暖整理剂的制备方法,其特征在于,包括如下步骤:
1)在装有直径为5-6mm锆球的砂磨机中依次加入25-30质量份氧化钼纳米粉体、15-20质量份麦饭石纳米粉体、5-8质量份水性丙烯酸树脂、20-25质量份水,用14100-14500转/分钟的转速分散5-6小时;
2)再依次加入3-6质量份聚乙二醇、7-9质量份聚乙烯吡咯烷酮,以13000-13500转/分钟的转速分散5-6小时,制得织物保暖整理剂。