CN103725389B - A kind of ferrous metal processing cutting fluid and preparation method thereof - Google Patents
A kind of ferrous metal processing cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN103725389B CN103725389B CN201310653463.3A CN201310653463A CN103725389B CN 103725389 B CN103725389 B CN 103725389B CN 201310653463 A CN201310653463 A CN 201310653463A CN 103725389 B CN103725389 B CN 103725389B
- Authority
- CN
- China
- Prior art keywords
- cutting fluid
- water
- ferrous metal
- metal processing
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Does is a kind of ferrous metal processing cutting fluid, made up of the raw material of following weight part: ricinolic acid 4-5, dimethyl silicone oil 12-14, styroyl phenol polyethenoxy ether 2-4, molybdenumdisulphide 3-4, clorafin 6-8, tween 80? 1-2, lauryl alcohol 4-5, auxiliary agent 6-8, water 200.Cutting fluid of the present invention employs the lubricant such as dimethyl silicone oil, molybdenumdisulphide and kinds of surface promoting agent, cutting fluid is non-foaming, good stability, and oilness, cooling and cleaning are excellent, do not corrode ferrous metal, non-corrosive, cutting fluid keeps as clear as crystal for a long time, and biodegradability is good, can be used for high speed cutting, workpiece burn can not be caused, smoke event.
Description
Technical field
The present invention relates to cutting fluid field, particularly relate to a kind of ferrous metal processing cutting fluid and preparation method thereof.
Background technology
Cutting fluid should possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature.Current cutting fluid can be divided into two classes, oil soluble cutting fluid and water-soluble metalworking liquid.General oil soluble cutting fluid lubrication performance is good, but poor cooling performance, and containing large amount of organic, contaminate environment.Although some water-soluble metalworking liquid cooling performances are good, there is again the problem of oilness and rust-proof effect difference, therefore research and development have concurrently oilness, cooling, rust-preventing characteristic, easy cleaning, nontoxic, tasteless, non-corrosive to human body, to equipment not burn into the non-staining cutting fluid of environment is just seemed very important.
Summary of the invention
The object of the present invention is to provide a kind of ferrous metal to process cutting fluid and preparation method thereof, this cutting fluid lubrication is good, and speed of cooling is fast.
Technical scheme of the present invention is as follows:
A kind of ferrous metal processing cutting fluid, is characterized in that being made up of the raw material of following weight part: ricinolic acid 4-5, dimethyl silicone oil 12-14, styroyl phenol polyethenoxy ether 2-4, molybdenumdisulphide 3-4, clorafin 6-8, tween 80 1-2, lauryl alcohol 4-5, auxiliary agent 6-8, water 200; Described auxiliary agent is made up of the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, nano aluminum nitride 0.1-0.2, bicarbonate of ammonia 2-3, thanomin 1-2, cm-chitosan 2-3, butyl 1-2, propylene glycol 5-8, peach gum 2-3, water glass 1-2, urea 3-4, ammonium persulphate 1-2, water 20-24; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 DEG C, stirring reaction 1-2 hour, to obtain final product.
The preparation method of described ferrous metal processing cutting fluid, is characterized in that comprising the following steps: by water, dimethyl silicone oil, styroyl phenol polyethenoxy ether, tween 80 mixing, be heated to 40-50 DEG C; Add ricinolic acid, clorafin, auxiliary agent, continue to be heated to 70-80 DEG C, stir 10-15 minute; Add other remaining components, continue to stir 10-15 minute, to obtain final product.
Beneficial effect of the present invention
Cutting fluid of the present invention employs the lubricant such as dimethyl silicone oil, molybdenumdisulphide and kinds of surface promoting agent, cutting fluid is non-foaming, good stability, and oilness, cooling and cleaning are excellent, do not corrode ferrous metal, non-corrosive, cutting fluid keeps as clear as crystal for a long time, and biodegradability is good, can be used for high speed cutting, workpiece burn can not be caused, smoke event.
Embodiment
A kind of ferrous metal processing cutting fluid, is made up of the raw material of following weight part (kilogram): ricinolic acid 4.5, dimethyl silicone oil 13, styroyl phenol polyethenoxy ether 3, molybdenumdisulphide 3.5, clorafin 7, tween 80 1.5, lauryl alcohol 4.5, auxiliary agent 7, water 200; Described auxiliary agent is made up of the raw material of following weight part (kilogram): polyoxyethylene sorbitan monooleate 3, nano aluminum nitride 0.1, bicarbonate of ammonia 3, thanomin 1, cm-chitosan 2, butyl 1, propylene glycol 8, peach gum 3, water glass 1, urea 4, ammonium persulphate 2, water 20; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 DEG C, stirring reaction 1-2 hour, to obtain final product.
The preparation method of described ferrous metal processing cutting fluid, comprises the following steps: by water, dimethyl silicone oil, styroyl phenol polyethenoxy ether, tween 80 mixing, be heated to 45 DEG C; Add ricinolic acid, clorafin, auxiliary agent, continue to be heated to 75 DEG C, stir 13 minutes; Add other remaining components, continue stirring 13 minutes, to obtain final product.
The ferrous metal processing cutting fluid testing data that this embodiment obtains is as follows:
Claims (1)
1. a ferrous metal processing cutting fluid, is characterized in that being made up of the raw material of following weight part: ricinolic acid 4-5, dimethyl silicone oil 12-14, styroyl phenol polyethenoxy ether 2-4, molybdenumdisulphide 3-4, clorafin 6-8, tween 80 1-2, lauryl alcohol 4-5, auxiliary agent 6-8, water 200; Described auxiliary agent is made up of the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, nano aluminum nitride 0.1-0.2, bicarbonate of ammonia 2-3, thanomin 1-2, cm-chitosan 2-3, butyl 1-2, propylene glycol 5-8, peach gum 2-3, water glass 1-2, urea 3-4, ammonium persulphate 1-2, water 20-24; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 DEG C, stirring reaction 1-2 hour, to obtain final product;
The preparation method of described ferrous metal processing cutting fluid comprises the following steps: by water, dimethyl silicone oil, styroyl phenol polyethenoxy ether, tween 80 mixing, be heated to 40-50 DEG C; Add ricinolic acid, clorafin, auxiliary agent, continue to be heated to 70-80 DEG C, stir 10-15 minute; Add other remaining components, continue to stir 10-15 minute, to obtain final product.