CN103666720A - Stable semi-synthetic cutting fluid and preparation method thereof - Google Patents
Stable semi-synthetic cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN103666720A CN103666720A CN201310654370.2A CN201310654370A CN103666720A CN 103666720 A CN103666720 A CN 103666720A CN 201310654370 A CN201310654370 A CN 201310654370A CN 103666720 A CN103666720 A CN 103666720A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting fluid
- good
- water
- sorbitan monooleate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A stable semi-synthetic cutting fluid is prepared from the following raw materials in parts by weight: 2-3 parts of sodium petroleum sulfonate, 4-5 parts of sorbitan monooleate, 2-3 parts of fatty alcohol polyoxyethylene ether, 1-2 parts of coconut oil diethanol amide, 4-5 parts of butylcarbitol, 10-12 parts of polyether, 1-2 parts of turkey red oil, 14-17 parts of castor oil, 6-8 parts of an auxiliary agent and 200 parts of water. The cutting fluid provided by the invention is excellent in emulsion property, can keep stable and have no sedimentation for a long time, and is good in hard water resistance, good in foam inhibiting property, good in water solubility, free of coacervation and free of caking; and the cutting fluid is good in lubricity and cleaning property, good in antirust property and fast in cooling, is suitable for medium/high-speed cutting, is substantially improved the service life and helps to substantially prolong the service life of machines.
Description
Technical field
The present invention relates to cutting fluid technical field, relate in particular to a kind of semi-synthetic cutting fluid and preparation method thereof of stablizing.
Background technology
Cutting fluid should possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature.Cutting fluid can be divided into two classes, oil soluble cutting fluid and water-soluble metalworking liquid at present.General oil soluble cutting fluid lubrication performance is good, but poor cooling performance, and contain large amount of organic, contaminate environment.Although some water-soluble metalworking liquid cooling performances are good, there is again the poor problem of oilness and rust-proof effect, therefore research and development have concurrently oilness, cooling, rust-preventing characteristic, easy cleaning, nontoxic, tasteless, non-corrosive to human body, to equipment not burn into the non-staining cutting fluid of environment is just seemed to very important.
Summary of the invention
The object of the present invention is to provide a kind of semi-synthetic cutting fluid and preparation method thereof of stablizing, this cutting fluid has stable not sedimentation, and oilness is good, the feature that cleaning is good.
Technical scheme of the present invention is as follows:
Stablize a semi-synthetic cutting fluid, it is characterized in that being made by the raw material of following weight part: petroleum sodium sulfonate 2-3, sorbitan monooleate 4-5, fatty alcohol-polyoxyethylene ether 2-3, coconut oil diethanol amide 1-2, diethylene glycol monobutyl ether 4-5, polyethers 10-12, alizarin assistant 1-2, Viscotrol C 14-17, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, nano aluminum nitride 0.1-0.2, citric acid 1-2, tripoly phosphate sodium STPP 2-3, ammonium persulphate 1-2, silane coupling agent KH-5601-2, Sodium orthomolybdate 1-2, peach gum 2-3, water 20-24; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The described preparation method who stablizes semi-synthetic cutting fluid, is characterized in that comprising the following steps: water, petroleum sodium sulfonate, sorbitan monooleate, fatty alcohol-polyoxyethylene ether, coconut oil diethanol amide, alizarin assistant are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add diethylene glycol monobutyl ether, polyethers, Viscotrol C, auxiliary agent, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.
Beneficial effect of the present invention
Cutting fluid emulsifying property of the present invention is excellent, can not sedimentation of stable for extended periods of time, and anti-performance of hard water is good, suds suppressing properties is good, and good water solubility is not condensed, is not lumpd; And oilness and cleaning good, good antirust property, speed of cooling is fast, is applicable to high speed cutting, has greatly extended cutting fluid and mechanical work-ing life.
Embodiment
Stablize a semi-synthetic cutting fluid, by following weight part (kilogram) raw material make: petroleum sodium sulfonate 2.5, sorbitan monooleate 4.5, fatty alcohol-polyoxyethylene ether 2.5, coconut oil diethanol amide 1.5, diethylene glycol monobutyl ether 4.5, polyethers 11, alizarin assistant 1.5, Viscotrol C 16, auxiliary agent 7, water 200; Described auxiliary agent by following weight part (kilogram) raw material make: polyoxyethylene sorbitan monooleate 2, nano aluminum nitride 0.1, citric acid 1, tripoly phosphate sodium STPP 3, ammonium persulphate 2, silane coupling agent KH-5602, Sodium orthomolybdate 2, peach gum 3, water 20-24; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The described preparation method who stablizes semi-synthetic cutting fluid, comprises the following steps: water, petroleum sodium sulfonate, sorbitan monooleate, fatty alcohol-polyoxyethylene ether, coconut oil diethanol amide, alizarin assistant are mixed, be heated to 45 ℃; Under 3500 revs/min of stirrings, add diethylene glycol monobutyl ether, polyethers, Viscotrol C, auxiliary agent, continue to be heated to 75 ℃, stir 13 minutes; Add other remaining components, continue to stir 20 minutes, obtain.
This embodiment obtains, and to stablize semi-synthetic cutting fluid testing data as follows:
Claims (2)
1. stablize a semi-synthetic cutting fluid, it is characterized in that being made by the raw material of following weight part: petroleum sodium sulfonate 2-3, sorbitan monooleate 4-5, fatty alcohol-polyoxyethylene ether 2-3, coconut oil diethanol amide 1-2, diethylene glycol monobutyl ether 4-5, polyethers 10-12, alizarin assistant 1-2, Viscotrol C 14-17, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, nano aluminum nitride 0.1-0.2, citric acid 1-2, tripoly phosphate sodium STPP 2-3, ammonium persulphate 1-2, silane coupling agent KH-560 1-2, Sodium orthomolybdate 1-2, peach gum 2-3, water 20-24; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
2. stablize according to claim 1 the preparation method of semi-synthetic cutting fluid, it is characterized in that comprising the following steps: water, petroleum sodium sulfonate, sorbitan monooleate, fatty alcohol-polyoxyethylene ether, coconut oil diethanol amide, alizarin assistant are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add diethylene glycol monobutyl ether, polyethers, Viscotrol C, auxiliary agent, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.