CN103710124A - Anti-superhigh hard water microemulsified magnesium alloy cutting fluid and preparation method therefor - Google Patents
Anti-superhigh hard water microemulsified magnesium alloy cutting fluid and preparation method therefor Download PDFInfo
- Publication number
- CN103710124A CN103710124A CN201310654191.9A CN201310654191A CN103710124A CN 103710124 A CN103710124 A CN 103710124A CN 201310654191 A CN201310654191 A CN 201310654191A CN 103710124 A CN103710124 A CN 103710124A
- Authority
- CN
- China
- Prior art keywords
- cutting fluid
- parts
- water
- microemulsified
- magnesium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Provided is an anti-superhigh hard water microemulsified magnesium alloy cutting fluid. The cutting fluid is prepared from the following raw materials, by weight, 5-6 parts of boric acid, 1-2 parts of triethanolamine, 10-12 parts of ethylene glycol monobutyl ether, 1-2 parts of nano exfoliated graphite, 1-2 parts of potassium humate, 4-5 parts of 2-methyl-1,3-propylene glycol, 2-4 parts of polyethylene glycol, 1-2 parts of alkyl succinate sodium sulfonate, 20-23 parts of kerosene, 6-8 parts of auxiliary agents and 200 parts of water. Through application of nano exfoliated graphite, the cutting fluid has good lubricating property and extreme pressure wear resistance, and has a function of adsorbing bacteria, and the cutting fluid keeps clear. Through application of potassium humate, the cutting fluid has dispersion and chelating functions. Through application of polyethylene glycol and surfactants cooperatively, the cutting fluid is stable, not easy to assemble, and easy to observe. The service life is prolonged. The cutting fluid has excellent cleaning property.
Description
Technical field
The present invention relates to cutting fluid technical field, relate in particular to a kind of anti-superelevation hard water microemulsified magnesium alloy cutting fluid and preparation method thereof.
Background technology
Cutting fluid should possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature.Cutting fluid can be divided into two classes, oil soluble cutting fluid and water-soluble metalworking liquid at present.General oil soluble cutting fluid lubrication performance is good, but poor cooling performance, and contain large amount of organic, contaminate environment.Although some water-soluble metalworking liquid cooling performances are good, there is again the poor problem of oilness and rust-proof effect, therefore research and development have concurrently oilness, cooling, rust-preventing characteristic, easy cleaning, nontoxic, tasteless, non-corrosive to human body, to equipment not burn into the non-staining cutting fluid of environment is just seemed to very important.
Summary of the invention
The object of the present invention is to provide a kind of anti-superelevation hard water microemulsified magnesium alloy cutting fluid and preparation method thereof, this cutting fluid has good, the anti-high hardness of oilness, feature that extreme pressure anti-wear is good.
Technical scheme of the present invention is as follows:
A kind of anti-superelevation hard water microemulsified magnesium alloy cutting fluid, it is characterized in that being made by the raw material of following weight part: boric acid 5-6, trolamine 1-2, ethylene glycol monobutyl ether 10-12, nano swelling graphite 1-2, potassium humate 1-2,2-methyl isophthalic acid, ammediol 4-5, polyoxyethylene glycol 2-4, dialkyl succinylsuccinate ester sodium sulfonate 1-2, kerosene 20-23, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, aluminum nitride powder 0.1-0.2, boric acid 2-3, morpholine 1-2, water glass 1-2, silane coupling agent KH-5601-2, Potassium Persulphate 1-2, peach gum 3-4, water 20-24; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described anti-superelevation hard water microemulsified magnesium alloy cutting fluid, is characterized in that comprising the following steps: water, dialkyl succinylsuccinate ester sodium sulfonate, potassium humate are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add boric acid, ethylene glycol monobutyl ether, 2-methyl isophthalic acid, ammediol, polyoxyethylene glycol, kerosene, auxiliary agent, continue to be heated to 70-80 ℃, stirs 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.
Beneficial effect of the present invention
Cutting fluid of the present invention, by using nano swelling graphite, not only has good oilness, extreme pressure wear resistance, also has the effect of absorption bacterium, makes cutting fluid keep limpid; By using potassium humate to there is dispersion, sequestering action, be used in conjunction with polyoxyethylene glycol and tensio-active agent, make cutting fluid stable, be difficult for cohesion, be easy to observe, also extended work-ing life; The present invention simultaneously also has excellent cleaning.
Embodiment
A kind of anti-superelevation hard water microemulsified magnesium alloy cutting fluid, by following weight part (kilogram) raw material make: boric acid 5.5, trolamine 1.5, ethylene glycol monobutyl ether 11, nano swelling graphite 1.5, potassium humate 1.5,2-methyl isophthalic acid, ammediol 4.5, polyoxyethylene glycol 3, dialkyl succinylsuccinate ester sodium sulfonate 1.5, kerosene 21, auxiliary agent 7, water 200; Described auxiliary agent by following weight part (kilogram) raw material make: polyoxyethylene sorbitan monooleate 2, aluminum nitride powder 0.1, boric acid 2, morpholine 1, water glass 2, silane coupling agent KH-560 1, Potassium Persulphate 1, peach gum 3, water 20; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described anti-superelevation hard water microemulsified magnesium alloy cutting fluid, comprises the following steps: water, dialkyl succinylsuccinate ester sodium sulfonate, potassium humate are mixed, be heated to 45 ℃; Under 3500 revs/min of stirrings, add boric acid, ethylene glycol monobutyl ether, 2-methyl isophthalic acid, ammediol, polyoxyethylene glycol, kerosene, auxiliary agent, continue to be heated to 75 ℃, stirs 13 minutes; Add other remaining components, continue to stir 20 minutes, obtain.
The anti-superelevation hard water microemulsified magnesium alloy cutting fluid testing data that this embodiment obtains is as follows:
Claims (2)
1. an anti-superelevation hard water microemulsified magnesium alloy cutting fluid, it is characterized in that being made by the raw material of following weight part: boric acid 5-6, trolamine 1-2, ethylene glycol monobutyl ether 10-12, nano swelling graphite 1-2, potassium humate 1-2,2-methyl isophthalic acid, ammediol 4-5, polyoxyethylene glycol 2-4, dialkyl succinylsuccinate ester sodium sulfonate 1-2, kerosene 20-23, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, aluminum nitride powder 0.1-0.2, boric acid 2-3, morpholine 1-2, water glass 1-2, silane coupling agent KH-560 1-2, Potassium Persulphate 1-2, peach gum 3-4, water 20-24; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
2. the preparation method of anti-superelevation hard water microemulsified magnesium alloy cutting fluid according to claim 1, is characterized in that comprising the following steps: water, dialkyl succinylsuccinate ester sodium sulfonate, potassium humate are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add boric acid, ethylene glycol monobutyl ether, 2-methyl isophthalic acid, ammediol, polyoxyethylene glycol, kerosene, auxiliary agent, continue to be heated to 70-80 ℃, stirs 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.