CN103725395A - Water-soluble highly-clean cutting fluid and preparation method thereof - Google Patents
Water-soluble highly-clean cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN103725395A CN103725395A CN201310670840.4A CN201310670840A CN103725395A CN 103725395 A CN103725395 A CN 103725395A CN 201310670840 A CN201310670840 A CN 201310670840A CN 103725395 A CN103725395 A CN 103725395A
- Authority
- CN
- China
- Prior art keywords
- water
- cutting fluid
- parts
- nano
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-soluble highly-clean cutting fluid. The cutting fluid is prepared from the following raw materials in parts by weight: 3-4 parts of nonylphenol polyoxyethylene ether, 1-2 part(s) of diethanol amine, 3-4 parts of boric acid, 1-2 part (s) of octocapric acid, 1-2 part(s) of sodium benzoate, 12-15 parts of soybean oil, 3-4 parts of dodecenylsuccinic acid, 1-2 part(s) of benzotriazole, 1-2 part(s) of triethanolamine, 1-2 part(s) of polytetrafluoroethylene, 3-4 parts of methyl methacrylate, 1-2 part(s) of nano-graphite, 6-8 parts of an additive and 200 parts of water. Since the nano-graphite is adopted, so that the cutting fluid has an excellent lubricating effect and wearing resistance, and the abrasion of a cutter is reduced; moreover, the cutting fluid is not required to be replaced or discharged in the process of metal processing, the cutting fluid does not metamorphose when being used for a long time, and can be kept clear and transparent for a long time; therefore, the problems of foreign mixed oil resistance of the cutting fluid and the settlement and recycle of impurities such as iron power grinding mud, grinding slag and the like are solved.
Description
Technical field
The present invention relates to cutting fluid field, relate in particular to a kind of water-soluble abrasive cutting fluid and preparation method thereof.
Background technology
Cutting fluid should possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature.Cutting fluid can be divided into two classes, oil soluble cutting fluid and water-soluble metalworking liquid at present.General oil soluble cutting fluid lubrication performance is good, but poor cooling performance, and contain large amount of organic, contaminate environment.Although some water-soluble metalworking liquid cooling performances are good, there is again the poor problem of oilness and rust-proof effect, therefore research and development have concurrently oilness, cooling, rust-preventing characteristic, easy cleaning, nontoxic, tasteless, non-corrosive to human body, to equipment not burn into the non-staining cutting fluid of environment is just seemed to very important.
Summary of the invention
The object of the present invention is to provide a kind of water-soluble abrasive cutting fluid and preparation method thereof, this cutting fluid lubrication is good, long-term clean never degenerates, resistance to extreme pressure is good.
Technical scheme of the present invention is as follows:
A water-soluble abrasive cutting fluid, is characterized in that being made by the raw material of following weight part: polyoxyethylene nonylphenol ether 3-4, diethanolamine 1-2, boric acid 3-4, pungent capric acid 1-2, Sodium Benzoate 1-2, soybean oil 12-15, dodecenylsuccinic acid 3-4, benzotriazole 1-2, trolamine 1-2, tetrafluoroethylene 1-2, methyl methacrylate 3-4, nano-graphite 1-2, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: ammonium oxide 1-2, morpholine 2-3, nano aluminum nitride 0.1-0.2, water glass 1-2, borax 2-3,2-amino-2-methyl-1-propanol 1-2, polyoxyethylene sorbitan monooleate 2-3, peach gum 2-3, ammonium persulphate 1-2, water 20-24; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described water-soluble abrasive cutting fluid, is characterized in that comprising the following steps: water, polyoxyethylene nonylphenol ether boric acid, nano-graphite are mixed, be heated to 40-50 ℃; Add soybean oil, tetrafluoroethylene, methyl methacrylate, auxiliary agent, under 1000-1200 rev/min of stirring, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-20 minute, obtain.
Beneficial effect of the present invention
Cutting fluid of the present invention has been used nano-graphite, there is excellent lubricant effect and wear resistance, reduced tool wear, and without changing, do not discharge cutting fluid in process of metal working, life-time service never degenerates, it is as clear as crystal for a long time that cutting fluid keeps, and the sedimentation that effectively solves the impurity such as the anti-external assorted oil of cutting fluid and iron powder mill mud, mill slag is reclaimed.
Embodiment
A water-soluble abrasive cutting fluid, by following weight part (kilogram) raw material make: polyoxyethylene nonylphenol ether 3.5, diethanolamine 1.5, boric acid 3.5, pungent capric acid 1.5, Sodium Benzoate 1.5, soybean oil 14, dodecenylsuccinic acid 3.5, benzotriazole 1.5, trolamine 1.5, tetrafluoroethylene 1.5, methyl methacrylate 3.5, nano-graphite 1.5, auxiliary agent 7, water 200; Described auxiliary agent by following weight part (kilogram) raw material make: ammonium oxide 1, morpholine 2, nano aluminum nitride 0.1, water glass 1, borax 2,2-amino-2-methyl-1-propanol 2, polyoxyethylene sorbitan monooleate 3, peach gum 2, ammonium persulphate 1, water 20; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described water-soluble abrasive cutting fluid, comprises the following steps: water, polyoxyethylene nonylphenol ether boric acid, nano-graphite are mixed, be heated to 45 ℃; Add soybean oil, tetrafluoroethylene, methyl methacrylate, auxiliary agent, under 1100 revs/min of stirrings, continue to be heated to 75 ℃, stir 13 minutes; Add other remaining components, continue to stir 18 minutes, obtain.
The water-soluble abrasive cutting fluid testing data that this embodiment obtains is as follows:
Claims (2)
1. a water-soluble abrasive cutting fluid, is characterized in that being made by the raw material of following weight part: polyoxyethylene nonylphenol ether 3-4, diethanolamine 1-2, boric acid 3-4, pungent capric acid 1-2, Sodium Benzoate 1-2, soybean oil 12-15, dodecenylsuccinic acid 3-4, benzotriazole 1-2, trolamine 1-2, tetrafluoroethylene 1-2, methyl methacrylate 3-4, nano-graphite 1-2, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: ammonium oxide 1-2, morpholine 2-3, nano aluminum nitride 0.1-0.2, water glass 1-2, borax 2-3,2-amino-2-methyl-1-propyl alcohol 1-2, polyoxyethylene sorbitan monooleate 2-3, peach gum 2-3, ammonium persulphate 1-2, water 20-24; Preparation method be ammonium persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
2. the preparation method of water-soluble abrasive cutting fluid according to claim 1, is characterized in that comprising the following steps: water, polyoxyethylene nonylphenol ether boric acid, nano-graphite are mixed, be heated to 40-50 ℃; Add soybean oil, tetrafluoroethylene, methyl methacrylate, auxiliary agent, under 1000-1200 rev/min of stirring, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-20 minute, obtain.