CN104120019A - Novel water-based rust-resistant corrosion-resistant wear-resistant cutting fluid and preparation method thereof - Google Patents
Novel water-based rust-resistant corrosion-resistant wear-resistant cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN104120019A CN104120019A CN201410305916.8A CN201410305916A CN104120019A CN 104120019 A CN104120019 A CN 104120019A CN 201410305916 A CN201410305916 A CN 201410305916A CN 104120019 A CN104120019 A CN 104120019A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting fluid
- resistant
- water
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a novel water-based rust-resistant corrosion-resistant wear-resistant cutting fluid. The invention is characterized in that the cutting fluid is prepared from the following raw materials in parts by weight: 2-3 parts of phytate, 1-2 parts of calcium propionate, 3-4 parts of emulsified silicone oil, 2.5-3.5 parts of castor oil polyethenoxy ether, 3-4 parts of sulfurized oleic acid, 1.5-2.5 parts of sodium carbonate, 3-4 parts of tall oil, 4-5 parts of NP-6, 5-7 parts of assistant and 200 parts of deionized water. According to the reasonable formula, the sulfurized oleic acid is used as the extreme pressure antiwear agent, the phytate is used as the water-soluble rust inhibitor, the calcium propionate is added as the preservative, and the surfactant and assistant are matched, so that the cutting fluid has the advantages of favorable permeability, favorable cleaning property, high cooling rate, favorable lubricating property, favorable rust corrosion, corrosion and odor resistance and low cost, and is easy to store, simple to operate and suitable for processing multiple metals.
Description
Technical field
The present invention relates to cutting fluid field, particularly wear-resisting cutting fluid of a kind of novel water-based antirust, anti-corrosive and preparation method thereof.
Background technology
Cutting fluid is that a kind of metal that is used in is cut, cuts, grinds in the course of processing, be used for the industrial type fluid of Cooling and Lubricator cutter and workpiece, comprise the oil base cutting fluid that contains mineral oil and additive, contain polyoxyethylene glycol or polypropylene glycol as the glycol-based cutting fluid of main ingredient, and the water-based cutting fluid of water phase surfactant mixture form.Oil base cutting fluid is poor at the cooling performance of cutting point, oil base cutting fluid can be polluted workpiece or instrument, need to further clean with organic solvent, unfriendly to environment, performance is poor aspect the dispersion stabilization of viscosity stability in cutting operation of glycol-based cutting fluid and water-based cutting fluid and abrasive material.Cutting fluid of the present invention is formed through the compound compatibility of science by several functions auxiliary agent, possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature simultaneously, overcome the easily difficult dilution in smelly, winter in summer of traditional soap base emulsion, rust-proof effect poor defect, lathe paint is also had no adverse effects, be applicable to cutting and the mill processing of ferrous metal, belong to leading current abrasive product.
Summary of the invention
The object of this invention is to provide wear-resisting cutting fluid of a kind of novel water-based antirust, anti-corrosive and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
The wear-resisting cutting fluid of novel water-based antirust, anti-corrosive, is made by the raw material of following weight part: myo-Inositol hexaphosphate 2-3, calcium propionate 1-2, silicone emulsion 3-4, castor oil polyoxyethylene ether 2.5-3.5, sulfuration oleic acid 3-4, sodium carbonate 1.5-2.5, Yatall MA 3-4, NP-6 4-5, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made by the raw material of following weight part: artificial diamond's stone flour 2-3, corundum 1-2, vinyl cyanide 1-2, Oleum Bupleuri 3-4, Lauryl Alcohol ester 2-3, rosin alcohol 2-3, hexamethyldisiloxane 1-1.5, Sodium dodecylbenzene sulfonate 3.5-4, water 50-54; First preparation method adds artificial diamond's stone flour, corundum, Oleum Bupleuri, Sodium dodecylbenzene sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The wear-resisting cutting fluid of a kind of novel water-based antirust, anti-corrosive of the present invention, by following concrete steps, made:
(1) silicone emulsion, Yatall MA, NP-6 are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
Excellent effect of the present invention is: the present invention fills a prescription rationally, add sulfuration oleic acid as extreme pressure anti-wear agent, myo-Inositol hexaphosphate is as water soluble anti-rust agent and add calcium propionate as sanitas, and the coordinating of tensio-active agent and auxiliary agent, the present invention has good perviousness, cleaning, and speed of cooling is fast, oilness and good antirust property, anticorrosion deodorization are easily preserved, simple to operate, with low cost, be applicable to various metals processing.
Embodiment
Below by specific examples, the present invention is described in detail.
The wear-resisting cutting fluid of novel water-based antirust, anti-corrosive, by following weight part (kilogram) raw material make: myo-Inositol hexaphosphate 2, calcium propionate 1, silicone emulsion 3, castor oil polyoxyethylene ether 2.5, sulfuration oleic acid 3, sodium carbonate 1.5, Yatall MA 3, NP-6 4, auxiliary agent 5, deionized water 200;
Described auxiliary agent by following weight part (kilogram) raw material make: artificial diamond's stone flour 2, corundum 1, vinyl cyanide 1, Oleum Bupleuri 3, Lauryl Alcohol ester 2, rosin alcohol 2, hexamethyldisiloxane 1, Sodium dodecylbenzene sulfonate 3.5, water 50; First preparation method adds artificial diamond's stone flour, corundum, Oleum Bupleuri, Sodium dodecylbenzene sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
The wear-resisting cutting fluid of a kind of novel water-based antirust, anti-corrosive of the present invention, by following concrete steps, made:
(1) silicone emulsion, Yatall MA, NP-6 are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
After tested, cutting fluid of the present invention can reach following technical requirements:
Claims (2)
1. the wear-resisting cutting fluid of novel water-based antirust, anti-corrosive, it is characterized in that, by the raw material of following weight part, made: myo-Inositol hexaphosphate 2-3, calcium propionate 1-2, silicone emulsion 3-4, castor oil polyoxyethylene ether 2.5-3.5, sulfuration oleic acid 3-4, sodium carbonate 1.5-2.5, Yatall MA 3-4, NP-6 4-5, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made by the raw material of following weight part: artificial diamond's stone flour 2-3, corundum 1-2, vinyl cyanide 1-2, Oleum Bupleuri 3-4, Lauryl Alcohol ester 2-3, rosin alcohol 2-3, hexamethyldisiloxane 1-1.5, Sodium dodecylbenzene sulfonate 3.5-4, water 50-54; First preparation method adds artificial diamond's stone flour, corundum, Oleum Bupleuri, Sodium dodecylbenzene sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
2. the wear-resisting cutting fluid of a kind of novel water-based antirust, anti-corrosive according to claim 1, is characterized in that, by following concrete steps, is made:
(1) silicone emulsion, Yatall MA, NP-6 are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.