CN103666715A - Semisynthesis cutting fluid and preparation method thereof - Google Patents
Semisynthesis cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN103666715A CN103666715A CN201310654099.2A CN201310654099A CN103666715A CN 103666715 A CN103666715 A CN 103666715A CN 201310654099 A CN201310654099 A CN 201310654099A CN 103666715 A CN103666715 A CN 103666715A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid ester
- cutting fluid
- good
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A semisynthesis cutting fluid is prepared from the following raw materials in parts by weight: 5 - 7 parts of boric acid ester, 3 - 4 of parts of phosphate, 10 - 12 parts of diethylene glycol, 3 - 4 parts of triazine, 1 - 2 parts of cellulose hydroxyethyl ether, 30 - 34 parts of 10# aviation hydraulic oil, 3 - 4 of parts of triethylene glycol dimethyl ether, 2- 3 parts of ammonium molybdate, 1 - 2 parts of trimethylolpropane, 1 - 2 parts of sodium dodecyl benzene sulfonate, 6 - 8 parts of an assistant and 200 parts of water; through the use of the boric acid ester, the phosphate, the10# aviation hydraulic oil and other lubricants, the semisynthesis cutting fluid is not only good in lubrication, and can form a protective film on the metal surface, increases extreme pressure resistance, is not easy to wear the metal surface, is good in cleaning performance, is friendly to the environment, has good anti corruption performance, is not easy to go bad and smell, is stable in dispersion and not easy to coagulation, is good in sedimentation performance, is long in the use time, has very good protection effects on workpieces and equipment, and after use, is simple in waste liquid treatment.
Description
Technical field
The present invention relates to cutting fluid technical field, relate in particular to a kind of semi-synthetic cutting fluid and preparation method thereof.
Background technology
Cutting fluid should possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature.Cutting fluid can be divided into two classes, oil soluble cutting fluid and water-soluble metalworking liquid at present.General oil soluble cutting fluid lubrication performance is good, but poor cooling performance, and contain large amount of organic, contaminate environment.Although some water-soluble metalworking liquid cooling performances are good, there is again the poor problem of oilness and rust-proof effect, therefore research and development have concurrently oilness, cooling, rust-preventing characteristic, easy cleaning, nontoxic, tasteless, non-corrosive to human body, to equipment not burn into the non-staining cutting fluid of environment is just seemed to very important.
Summary of the invention
The object of the present invention is to provide a kind of semi-synthetic cutting fluid and preparation method thereof, this cutting fluid has that oilness is good, environmental protection, feature that extreme pressure wear resistance is good.
Technical scheme of the present invention is as follows:
A semi-synthetic cutting fluid, is characterized in that being made by the raw material of following weight part: boric acid ester 5-7, phosphoric acid ester 3-4, Diethylene Glycol 10-12, triazine 3-4, natrosol 1-2, Number 10 aviation hydraulic oil 30-34, TRIGLYME 3-4, ammonium molybdate 2-3, TriMethylolPropane(TMP) 1-2, Sodium dodecylbenzene sulfonate 1-2, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, aluminum nitride powder 0.1-0.2, boric acid 2-3, morpholine 1-2, water glass 1-2, silane coupling agent KH-5601-2, Potassium Persulphate 1-2, peach gum 3-4, water 20-24; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described semi-synthetic cutting fluid, is characterized in that comprising the following steps: water, natrosol, Sodium dodecylbenzene sulfonate are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add boric acid ester, phosphoric acid ester, Diethylene Glycol, Number 10 aviation hydraulic oil, TRIGLYME, TriMethylolPropane(TMP), auxiliary agent, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.
Beneficial effect of the present invention
Semi-synthetic cutting fluid of the present invention is by being used the lubricants such as boric acid ester, phosphoric acid ester, Number 10 aviation hydraulic oil, and not only oilness is good, and can also form in metallic surface protective membrane; improve extreme pressure wear resistance, be difficult for wear metal surface, and cleaning performance is good; environmentally friendly; have the anti-performance that addles preferably, not perishable smelly, stably dispersing is difficult for cohesion; settling property is good; duration of service is long, workpiece and equipment is had to the effect of good protection, uses liquid waste disposal simple.
Embodiment
A semi-synthetic cutting fluid, by following weight part (kilogram) raw material make: boric acid ester 6, phosphoric acid ester 3.5, Diethylene Glycol 11, triazine 3.5, natrosol 1.5, Number 10 aviation hydraulic oil 32, TRIGLYME 3.5, ammonium molybdate 2.5, TriMethylolPropane(TMP) 1.5, Sodium dodecylbenzene sulfonate 1.5, auxiliary agent 7, water 200; Described auxiliary agent by following weight part (kilogram) raw material make: polyoxyethylene sorbitan monooleate 2, aluminum nitride powder 0.1, boric acid 2, morpholine 1, water glass 2, silane coupling agent KH-5601, Potassium Persulphate 1, peach gum 3, water 20; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described semi-synthetic cutting fluid, comprises the following steps: water, natrosol, Sodium dodecylbenzene sulfonate are mixed, be heated to 45 ℃; Under 3500 revs/min of stirrings, add boric acid ester, phosphoric acid ester, Diethylene Glycol, Number 10 aviation hydraulic oil, TRIGLYME, TriMethylolPropane(TMP), auxiliary agent, continue to be heated to 75 ℃, stir 13 minutes; Add other remaining components, continue to stir 20 minutes, obtain.
The semi-synthetic cutting fluid testing data that this embodiment obtains is as follows:
Claims (2)
1. a semi-synthetic cutting fluid, is characterized in that being made by the raw material of following weight part: boric acid ester 5-7, phosphoric acid ester 3-4, Diethylene Glycol 10-12, triazine 3-4, natrosol 1-2, Number 10 aviation hydraulic oil 30-34, TRIGLYME 3-4, ammonium molybdate 2-3, TriMethylolPropane(TMP) 1-2, Sodium dodecylbenzene sulfonate 1-2, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, aluminum nitride powder 0.1-0.2, boric acid 2-3, morpholine 1-2, water glass 1-2, silane coupling agent KH-560 1-2, Potassium Persulphate 1-2, peach gum 3-4, water 20-24; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
2. the preparation method of semi-synthetic cutting fluid according to claim 1, is characterized in that comprising the following steps: water, natrosol, Sodium dodecylbenzene sulfonate are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add boric acid ester, phosphoric acid ester, Diethylene Glycol, Number 10 aviation hydraulic oil, TRIGLYME, TriMethylolPropane(TMP), auxiliary agent, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.