CN103724049A - 一种多孔保温砖 - Google Patents

一种多孔保温砖 Download PDF

Info

Publication number
CN103724049A
CN103724049A CN201310670988.8A CN201310670988A CN103724049A CN 103724049 A CN103724049 A CN 103724049A CN 201310670988 A CN201310670988 A CN 201310670988A CN 103724049 A CN103724049 A CN 103724049A
Authority
CN
China
Prior art keywords
parts
insulating brick
porous heat
heat insulation
calcium carbonate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310670988.8A
Other languages
English (en)
Inventor
李本明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO WUWEI INSULATION MATERIAL Co Ltd
Original Assignee
QINGDAO WUWEI INSULATION MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO WUWEI INSULATION MATERIAL Co Ltd filed Critical QINGDAO WUWEI INSULATION MATERIAL Co Ltd
Priority to CN201310670988.8A priority Critical patent/CN103724049A/zh
Publication of CN103724049A publication Critical patent/CN103724049A/zh
Pending legal-status Critical Current

Abstract

本发明公布了建筑材料领域的一种多孔保温砖，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩50～100份、水玻璃35～85份、锂基膨润土10～40份、煅烧高岭土5～25份、碳酸钙3～10份、海泡石5～10份。所述多孔保温砖长、宽、高的长度比为10～20:5～10:2～5。该多孔保温砖与传统的膨胀珍珠岩保温砖相比具有更好的保温性能，机械强度和耐水性也得到进一步地提高，是一种值得推广的保温材料。

Description

一种多孔保温砖
技术领域
本发明属于建筑材料领域，具体涉及一种多孔保温砖。
背景技术
工业化的进程给我们带来了社会的进步、生产力的大幅提高，但同时也引发了一系列的能源危机。随着对能源开采的逐年加剧，地球上的化石、燃料等不可再生资源已经渐渐枯竭，能源危机的警钟已经敲响。近几年来，能源问题引起了世界各国越来越多的关注，并被列入了人类面临的四大生存问题之一。
各类热工设备及建筑的保温绝热，是节能的重要措施。保温绝热材料是节能的物质基础，性能优良的保温绝热材料和良好的保温技术，在工业保温中往往可起到事半功倍的效果。
传统膨胀珍珠岩保温材料是以膨胀珍珠岩为骨料，水玻璃、磷酸盐等为粘结剂在高温下焙烧而成，或者通过添加水泥等固化剂在60～120℃条件下静置固化得到。传统保温材料的保温效果、机械强度和防水性都可以进一步的提高。
发明内容
    本发明提供了一种多孔保温砖及其制备方法。
一种多孔保温砖，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩50～100份、水玻璃35～85份、锂基膨润土10～40份、煅烧高岭土5～25份、碳酸钙3～10份、海泡石5～10份。
进一步地，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩50～60份、水玻璃35～55份、锂基膨润土15～20份、煅烧高岭土5～10份、碳酸钙3～6份、海泡石5～10份。
所述多孔保温砖的生产工艺包括以下步骤：
（1）按照所述配比称取膨胀珍珠岩、锂基膨润土、煅烧高岭土、碳酸钙、海泡石，加入搅拌机中搅拌均匀,接着加入水，继续搅拌30min；
（2）继续向上述混合物中加入所述配比的水玻璃，搅拌均匀；
（3）将搅拌均匀的浆料倒入模具中，利用压力机压成所需形状的保温砖；
（4）将上述已成型的保温砖放入微波炉中膨化16～30min，接着取出静置冷却，即得所需多孔保温砖。
进一步地， 所述多孔保温砖的长、宽、高长度比为10～20:5～10:2～5。
进一步地， 所述多孔保温砖的长、宽、高长度比4:2:1。
进一步地，其中步骤（1）中水料比为0.4～0.6。
    通过该方法制得的多孔保温砖与传统的膨胀珍珠岩保温砖相比具有更好的保温性能，机械强度和耐水性也得到进一步地提高，是一种值得推广的保温材料。
具体实施方式
实施例1
一种多孔保温砖，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩50份、水玻璃35份、锂基膨润土18份、煅烧高岭土5份、碳酸钙6份、海泡石8份。
该多孔保温砖的生产工艺包括以下步骤：
（1）按照所述配比称取膨胀珍珠岩、锂基膨润土、煅烧高岭土、碳酸钙、海泡石，加入搅拌机中搅拌均匀,接着加入水，继续搅拌30min，其中水料比为0.55:1；
（2）继续向上述混合物中加入所述配比的水玻璃，搅拌均匀；
（3）将搅拌均匀的浆料倒入模具中，利用压力机压成所需形状的保温砖，其中已成型的保温砖的长、宽、高长度分别为240mm×120mm×60mm；
（4）将上述已成型的保温砖放入微波炉中膨化20min，接着取出静置冷却，即得所需多孔保温砖。
实施例2
一种多孔保温砖，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩60份、水玻璃45份、锂基膨润土20份、煅烧高岭土10份、碳酸钙6份、海泡石5份。
该多孔保温砖的生产工艺包括以下步骤：
（1）按照所述配比称取膨胀珍珠岩、锂基膨润土、煅烧高岭土、碳酸钙、海泡石，加入搅拌机中搅拌均匀,接着加入水，继续搅拌30min，其中水料比为0.45:1；
（2）继续向上述混合物中加入所述配比的水玻璃，搅拌均匀；
（3）将搅拌均匀的浆料倒入模具中，利用压力机制成所需形状的保温砖，其中已成型的保温砖的长、宽、高长度分别为240mm×115mm×53mm；
（4）将上述已成型的保温砖放入微波炉中膨化30min，接着取出静置冷却,即得所需多孔保温砖。
实施例3
一种多孔保温砖，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩55份、水玻璃45份、锂基膨润土18份、煅烧高岭土8份、碳酸钙4份、海泡石8份。
该多孔保温砖的生产工艺包括以下步骤：
（1）按照所述配比称取膨胀珍珠岩、锂基膨润土、煅烧高岭土、碳酸钙、海泡石，加入搅拌机中搅拌均匀,接着加入水，继续搅拌30min，其中水料比为0.6:1；
（2）继续向上述混合物中加入所述配比的水玻璃，搅拌均匀；
（3）将搅拌均匀的浆料倒入模具中，利用压力机制成所需形状的保温砖，其中已成型的保温砖的长、宽、高长度分别为240mm×120mm×60mm；
（4）将上述已成型的保温砖放入微波炉中膨化18min，接着取出静置冷却,即得所需多孔保温砖。

Claims (6)

1.一种多孔保温砖，其特征在于，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩50～100份、水玻璃35～85份、锂基膨润土10～40份、煅烧高岭土5～25份、碳酸钙3～10份、海泡石5～10份。
2.根据权利要求1所述的一种多孔保温砖，其特征在于，按重量计，所述多孔保温砖包括下述组分：膨胀珍珠岩50～60份、水玻璃35～55份、锂基膨润土15～20份、煅烧高岭土5～10份、碳酸钙3～6份、海泡石5～10份。
3.根据权利要求1所述的一种多孔保温砖，其特征在于，所述多孔保温砖的生产工艺包括以下步骤：
（1）按照所述配比称取膨胀珍珠岩、锂基膨润土、煅烧高岭土、碳酸钙、海泡石，加入搅拌机中搅拌均匀,接着加入水，继续搅拌30min；
（2）继续向上述混合物中加入所述配比的水玻璃，搅拌均匀；
（3）将搅拌均匀的浆料倒入模具中，利用压力机压成所需形状的保温砖；
（4）将上述已成型的保温砖放入微波炉中膨化16～30min，接着取出静置冷却，即得所需多孔保温砖。
4.根据权利要求3所述的一种多孔保温砖，其特征在于， 所述多孔保温砖的长、宽、高长度比为10～20:5～10:2～5。
5.根据权利要求3所述的一种多孔保温砖，其特征在于， 所述多孔保温砖的长、宽、高长度比4:2:1。
6.根据权利要求3所述的一种多孔保温砖，其特征在于，其中步骤（1）中水料比为0.4～0.6。 
CN201310670988.8A 2013-12-12 2013-12-12 一种多孔保温砖 Pending CN103724049A (zh)