CN103710864A - 一种等规聚丙烯长纤维多层复合吸音棉及其制备方法 - Google Patents
一种等规聚丙烯长纤维多层复合吸音棉及其制备方法 Download PDFInfo
- Publication number
- CN103710864A CN103710864A CN201310600019.5A CN201310600019A CN103710864A CN 103710864 A CN103710864 A CN 103710864A CN 201310600019 A CN201310600019 A CN 201310600019A CN 103710864 A CN103710864 A CN 103710864A
- Authority
- CN
- China
- Prior art keywords
- parts
- isotactic polypropylene
- powder
- surface layer
- sound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种等规聚丙烯长纤维多层复合吸音棉，由顶面层、背面层，及夹装于顶面层与背面层之间的纤维棉层构成，顶面层、背面层采用无纺布材料，无纺布由下列重量份的原料通过熔喷法制成：等规聚丙烯100、2,4,6-三氯-1,3,5-三嗪1-2、粉煤灰3-4、ACM-24PVC抗冲改性剂1-2、间苯二甲酸二甲酯10-12、聚对苯二甲酸丙二醇酯4-6、聚丙烯酸钠1-2、活性炭粉10-12、硅溶胶2-3、明矾6-7、膨润土12-15、木槿皮10-12、白茅根2-3、茜草2-3、向日葵根1-2、助剂4-5；本发明制得的吸音棉具有阻燃性优异，抗拉强度及延展度高，且生产原料绿色环保，工艺简单，工业化可实施性强。
Description
技术领域
本发明涉及非织造布技术，具体涉及一种等规聚丙烯长纤维多层复合吸音棉及其制备方法。
背景技术
噪声直接影响人们的身心健康和生活质量的提高，长期处于噪声环境中，会引起听力损失甚至可能诱发一些疾病。要远离噪声，我们能做的就是吸音和隔音。吸音棉，可以将生活中所产生的中高频噪声振动能转换为吸音棉内部的细旦纤维的动能并导成热能而消失，达到吸音降噪的功能。
吸音棉可以用多层无纺布叠合，或者搭配其它材料，制成吸音、隔音材料。无纺布是将纺织短纤维或者长丝进行定向或随机撑列，形成纤网结构，呈现出许多细小的间隙，这种间隙可看作孔隙，具有吸附功能，因此，吸音棉可视为多孔材料，具有良好的吸音、隔热保暖性能。吸音棉作为一种衬垫材料广泛运用于建筑、电器、汽车、机械等行业，主要起到隔音的作用。但是现有的吸音棉产品及其制造方法均存在较多的不足，主要表现为：制作工艺不环保；吸音效果一般；耐化学腐蚀性低，无法满足特殊场所使用要求；耐温等级低；没有进行阻燃处理；产品粘结度不够、易散、拉力强度差；外观及平整度不够，厚度较大偏差等。
发明内容
本发明的目的就是提供一种等规聚丙烯长纤维多层复合吸音棉及其制备方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种等规聚丙烯长纤维多层复合吸音棉，由顶面层、背面层，及夹装于顶面层与背面层之间的纤维棉层构成，所述的顶面层、背面层采用无纺布材料，其特征在于所述的无纺布由下列重量份的原料通过熔喷法制成：等规聚丙烯100、2,4,6-三氯-1,3,5-三嗪1-2、粉煤灰3-4、ACM-24PVC抗冲改性剂1-2、间苯二甲酸二甲酯10-12、聚对苯二甲酸丙二醇酯4-6、聚丙烯酸钠1-2、活性炭粉10-12、硅溶胶2-3、明矾6-7、膨润土12-15、木槿皮10-12、白茅根2-3、茜草2-3、向日葵根1-2、助剂4-5。
所述的助剂由下列重量份原料制成：纳米碳1-2、高岭土8-10、天青石1-2、防老剂TPPD 1-2、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯2-3、乙二醇2-3、玉石1-2、乙撑双硬脂酰胺2-3、一缩二乙二醇二苯甲酸酯32-33、没食子酸丙酯1-2、薏仁油1-2、二硼化钒2-3、表儿茶素2-3；制备方法是将高岭土、天青石、玉石送入煅烧炉中在720-740℃下煅烧2-3小时，然后，取出，送入10-15%的盐酸溶液中浸泡2-3小时，过滤，得滤渣，用清水洗净，烘干、研磨成400-600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
所述的等规聚丙烯长纤维多层复合吸音棉的制备方法，其特征在于包括以下步骤：
（1）、将木槿皮、白茅根、茜草、向日葵根合并粉碎220-280目粉末，然后，向所得的粉末鼓风使其翻腾，向翻腾的粉末中喷雾状硅溶胶，使二者充分混合；
（2）、将膨润土送入炭化炉中，在580-650℃下煅烧处理3-4小时，取出，粉碎成粉末；
（3）、将等规聚丙烯加热至熔融状态，加入步骤（1）、（2）物料，充分搅拌均匀；
（4）、向步骤（3）物料中加入其它剩余成分，充分搅拌，混合均匀，通过喷嘴喷丝制成无纺布。
本发明有以下有益效果：本发明将等规聚丙烯、2,4,6-三氯-1,3,5-三嗪、粉煤灰、ACM-24PVC抗冲改性剂复合制得的吸音棉具有阻燃性优异，抗拉强度及延展度高，且生产原料绿色环保，工艺简单，工业化可实施性强，产品质量稳定可靠，吸音效果佳。
具体实施方式
所述的等规聚丙烯长纤维多层复合吸音棉，由顶面层、背面层，及夹装于顶面层与背面层之间的纤维棉层构成，所述的顶面层、背面层采用无纺布材料，其特征在于所述的无纺布由下列重量份的原料通过熔喷法制成：等规聚丙烯100、2,4,6-三氯-1,3,5-三嗪1-2、粉煤灰3-4、ACM-24PVC抗冲改性剂1-2、间苯二甲酸二甲酯10-12、聚对苯二甲酸丙二醇酯4-6、聚丙烯酸钠1-2、活性炭粉10-12、硅溶胶2-3、明矾6-7、膨润土12-15、木槿皮10-12、白茅根2-3、茜草2-3、向日葵根1-2、助剂4-5。
所述的助剂由下列重量份（公斤）原料制成：纳米碳1、高岭土8、天青石1、防老剂TPPD 1、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯2、乙二醇2、玉石1、乙撑双硬脂酰胺2、一缩二乙二醇二苯甲酸酯32、没食子酸丙酯2、薏仁油1、二硼化钒2、表儿茶素2；制备方法是将高岭土、天青石、玉石送入煅烧炉中在720-740℃下煅烧2-3小时，然后，取出，送入10-15%的盐酸溶液中浸泡2-3小时，过滤，得滤渣，用清水洗净，烘干、研磨成400-600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
制备方法包括以下步骤：
（1）、将木槿皮、白茅根、茜草、向日葵根合并粉碎220-280目粉末，然后，向所得的粉末鼓风使其翻腾，向翻腾的粉末中喷雾状硅溶胶，使二者充分混合；
（2）、将膨润土送入炭化炉中，在580-650℃下煅烧处理3-4小时，取出，粉碎成粉末；
（3）、将等规聚丙烯加热至熔融状态，加入步骤（1）、（2）物料，充分搅拌均匀；
（4）、向步骤（3）物料中加入其它剩余成分，充分搅拌，混合均匀，通过喷嘴喷丝制成无纺布。
经测试，所得材料的纤维直径分布为1.64-1.89μm，撕裂强度为549N/m，热传导系数为4.318-6.302W/(m2·℃)，降噪系数为0.863-0.877。
Claims (2)
1.一种等规聚丙烯长纤维多层复合吸音棉，由顶面层、背面层，及夹装于顶面层与背面层之间的纤维棉层构成，所述的顶面层、背面层采用无纺布材料，其特征在于所述的无纺布由下列重量份的原料通过熔喷法制成：等规聚丙烯100、2,4,6-三氯-1,3,5-三嗪1-2、粉煤灰3-4、ACM-24PVC抗冲改性剂1-2、间苯二甲酸二甲酯10-12、聚对苯二甲酸丙二醇酯4-6、聚丙烯酸钠1-2、活性炭粉10-12、硅溶胶2-3、明矾6-7、膨润土12-15、木槿皮10-12、白茅根2-3、茜草2-3、向日葵根1-2、助剂4-5；所述的助剂由下列重量份原料制成：纳米碳1-2、高岭土8-10、天青石1-2、防老剂TPPD 1-2、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯2-3、乙二醇2-3、玉石1-2、乙撑双硬脂酰胺2-3、一缩二乙二醇二苯甲酸酯32-33、没食子酸丙酯1-2、薏仁油1-2、二硼化钒2-3、表儿茶素2-3；制备方法是将高岭土、天青石、玉石送入煅烧炉中在720-740℃下煅烧2-3小时，然后，取出，送入10-15%的盐酸溶液中浸泡2-3小时，过滤，得滤渣，用清水洗净，烘干、研磨成400-600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
2.根据权利要求1所述的等规聚丙烯长纤维多层复合吸音棉的制备方法，其特征在于包括以下步骤：
（1）、将木槿皮、白茅根、茜草、向日葵根合并粉碎220-280目粉末，然后，向所得的粉末鼓风使其翻腾，向翻腾的粉末中喷雾状硅溶胶，使二者充分混合；
（2）、将膨润土送入炭化炉中，在580-650℃下煅烧处理3-4小时，取出，粉碎成粉末；
（3）、将等规聚丙烯加热至熔融状态，加入步骤（1）、（2）物料，充分搅拌均匀；
（4）、向步骤（3）物料中加入其它剩余成分，充分搅拌，混合均匀，通过喷嘴喷丝制成无纺布。