CN103696284A - Special pearlescent paste for Suzhou embroideries as well as preparation method and application of special pearlescent paste - Google Patents
Special pearlescent paste for Suzhou embroideries as well as preparation method and application of special pearlescent paste Download PDFInfo
- Publication number
- CN103696284A CN103696284A CN201310717633.XA CN201310717633A CN103696284A CN 103696284 A CN103696284 A CN 103696284A CN 201310717633 A CN201310717633 A CN 201310717633A CN 103696284 A CN103696284 A CN 103696284A
- Authority
- CN
- China
- Prior art keywords
- pearly
- special
- suzhou
- embroidery
- lustre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses special pearlescent paste for Suzhou embroideries. The special pearlescent paste for the Suzhou embroideries is characterized by comprising the following components in percentage by weight: 10-20% of pearl powder, 40-50% of an adhesive, 1-10% of ethylene glycol, 0.5-5% of a thickener and 10-40% of deionized water. Embroideries such as the Suzhou embroideries dyed by using the paste have more than two types of colored light, so that the embroideries have various pearly color and luster in natural light and lamp light, space secondary color generated through mutual fusion of silk light with different hues after section printing and section dyeing and an artistic effect of twinkling flexible beauty and printing embroidery combination; and after dyeing and finishing, the sludge pollution is not caused, and the sludge treatment working procedure is omitted.
Description
Technical field
The invention belongs to dye printing technical field, be specifically related to liquid paste and its production and use for a kind of dye printing.
Background technology
Rubber cement can be divided into common rubber cement and special rubber cement according to purposes.The slurry that common rubber cement is just used for general stamp, does not require and reaches special effect.Itself generally can be divided into interspongioplastic substance, PVA glue, color printing slurry and Lacquer finish slurry.Interspongioplastic substance be imprinted on cloth itself be transparent can covering power without appointing, being only applicable to light cloth printing uses, advantage is because the content of resin own is high, therefore firmness is better than PVA glue, mix with PVA glue to use and not only can improve firmness, can also increase gloss and elasticity, but covering power is poor; And PVA glue itself is the use that can be used in white stamp of white, strong covering power, the content of itself titanium dioxide of PVA glue is high, so firmness is poor; The two combination thus, to add the interspongioplastic substance of 70% left and right can be color printing slurry for the dark cloth stamp of enameling to 30% left and right PVA glue, can reduce the consumption of mill base with color printing slurry, can reach again good color and luster saturation degree and colored covering power; Because some rubber cement intrinsic brightness is not very high, can stamp on its surface one deck Lacquer finish slurry, Lacquer finish slurry is mainly a kind of slurry that improves stamp product surface brightness.
Pearl essence with its to human body and skin have no side effect, magical and gloss lucuriant in design nature.September 7 in 2011, disclosed Chinese patent application ZL201110038391.2 disclosed pearly-lustre rubber cement and its preparation method and application for a kind of environment-friendly type textile printing, and described rubber cement is counted with the percentage by weight of its component: the super soft adhesive 49-39% of environment-friendly type; Particle size range is at the rutile-type silvery white pearl essence 15-25% of 5-25um; Particle size range is at the anatase titanium dioxide silvery white pearl essence 25-15% of 10-60um; Ethylene glycol 4-6%; Dispersant 1-2%; Levelling agent 1-3%; Antimildew and antibacterial auxiliary agent 1-2%; Negative ion far-infrared powder 2-4%; Thickener 2-4%.This pearly-lustre rubber cement generally uses on textiles, and effect is remarkable.Yet, this environment-friendly type textile printing is the printing and dyeing for embroidery product such as Suzhou embroiderys with pearly-lustre rubber cement, pearly-lustre rubber cement wire mark and the embroidery of independent, monochromatic silk thread, cannot reach the stereoeffect of the embroidery product such as Suzhou embroidery separately, so affected the artistic expression of embroidery product.The present invention comes therefrom.
Summary of the invention
The object of the invention is to provide the special-purpose pearly-lustre slurry of a kind of Suzhou embroidery, the special-purpose pearly-lustre slurry of this Suzhou embroidery is exclusively used in the printing and dyeing of Suzhou embroidery product and uses, solve in prior art pearly-lustre rubber cement wire mark and the embroidery of independent, monochromatic silk thread separately, cannot reach the problems such as the stereoeffect of the embroidery product such as Suzhou embroidery and optical effect.
In order to solve these problems of the prior art, technical scheme of the present invention is:
The special-purpose pearly-lustre slurry of Suzhou embroidery, is characterized in that the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery is counted with the percentage by weight of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery is counted with the percentage by weight of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery is counted with the percentage by weight of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery is counted with the percentage by weight of its component:
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery is counted with the percentage by weight of its component:
Preferred technical scheme is: described adhesive is VS-0071 adhesive; Described pearl essence is rutile-type pearl essence; Described mite-proofing and antimicrobial auxiliary agent is SCJ-998 mite-proofing and antimicrobial finishing agent; Described thickener is PUP-82 thickener.
Preferred technical scheme is: the special-purpose pearly-lustre slurry of described Suzhou embroidery is counted with the percentage by weight of its component:
The preparation method who another object of the present invention is to provide the special-purpose pearly-lustre slurry of a kind of described Suzhou embroidery, is characterized in that said method comprising the steps of:
According to formula consumption, pearl essence, adhesive, ethylene glycol, thickener, deionized water are mixed to the composite special-purpose pearly-lustre slurry of described Suzhou embroidery that obtains.
Of the present invention have an object to be to provide the application of the special-purpose pearly-lustre slurry of a kind of described Suzhou embroidery in the monochromatic wire mesh of Suzhou embroidery India and China.
After the special-purpose pearly-lustre slurry of Suzhou embroidery of the present invention is used in Suzhou embroidery product, Suzhou embroidery product has two kinds of above coloured light.The special-purpose pearly-lustre slurry of described Suzhou embroidery is in conjunction with pearly-lustre rubber cement wire mark and traditional embroidery skill and technique, need to again prepare with look and picture according to Suzhou embroidery silk thread, find after tested, the special-purpose pearly-lustre slurry of this Suzhou embroidery and Duan Yin, section is dyed silk thread embroidery combination, embroidery product is at natural daylight, the various pearly-lustre color and lusters that manifest under light, Duan Yin, section is dyed the mercerising of rear different form and aspect, mutually merge the space secondary colour producing, agile U.S. of material flicker and seal are embroidered in conjunction with the artistic effect presenting simultaneously, all independent pearly-lustre rubber cement wire marks and independent, monochromatic silk thread embroidery is beyond one's reach at all.Although it is exactly a production process layer by layer that pearlite slurry wire mark and Duan Yin, section are dyed the process of silk thread embroidery, but owing to adopting the difference of the special-purpose pearly-lustre slurry of Suzhou embroidery, cause whole embroidery product to have stereoeffect and optical effect, this is to retouch in original text, embroidery process and cannot embody all the time simultaneously before conventional embroidery.
The special-purpose pearly-lustre slurry of Suzhou embroidery role is the effect of the place mat skill of handling needles of making a draft, and plays from start to finish again setoff, retouching effect, and makes picture have more appeal with Duan Yin, in section dying the alternately used of silk thread.The mentality of designing of the special-purpose pearly-lustre slurry of Suzhou embroidery of the present invention is tightly around Suzhou embroidery product, the simulation Suzhou embroidery skill of handling needles of just take when layout is basic skill, with high order, counting silk screen prints layer by layer, utilize the stable chemical property of the different particle diameter of pearl essence and distinctive optical interference, visual pearlescent effect, flash metal luster effect, goniochromatic effect, color transfer effect, additional color effect, three dimensions effect, background contrast effect, make it with Duan Yin, section dye silk thread embroidery in conjunction with time, wire mark pearly-lustre rubber cement again on the silk thread of the different skill of handling needles, it is because rising and falling, uneven and appear before one's eyes, the special visual effect reflecting and be obviously different from conventional manual rough sketch, digital spray printing.The floor file of pearly-lustre rubber cement wire mark, it is the same that original text is retouched in the craft of embroidering with routine, digit printing is done the front original text method of embroidery, but pearly-lustre rubber cement wire mark, before embroidery, is not only the effect of embroidering front rough sketch with routine of having played, the silk thread from material pearly-lustre rubber cement, Duan Yin, the section of making aspect are dyed; Wire mark and embroidery from technological layer; From view picture works, print, embroider in conjunction with the artistic effect presenting; Displaying from color matching to whole works is an integral body all the time.
The invention belongs to the manual wire mark of pearly-lustre rubber cement, manual silk thread embroidery field, Suzhou, be specifically related to a kind of with pearly-lustre rubber cement fabrography and silk thread with monochromatic silk thread and Duan Yin, the printing and dyeing of section dyeing technique, as manual wire mark and the field of embroidering and combining., pearlite slurry wire mark pattern approximate with two kinds of coloured light, skill and technique wire mark with complete simulating hand embroidery stitching method, by luminous effect, visual impact with embroidering and replacing, superpose rear generation, the artistic appeal of its works is that routine is embroidered, pearlite slurry wire mark works are beyond one's reach at all.
The special-purpose pearly-lustre slurry of most preferred Suzhou embroidery is counted with the percentage by weight of component: VS-0071 adhesive 48.8%; Deionized water 30%; Rutile-type pearl essence 15%; Ethylene glycol 4%; SCJ-998 mite-proofing and antimicrobial finishing agent 1%; PUP-82 thickener 1.2%.Wherein rutile-type pearl essence, SCJ-998 mite-proofing and antimicrobial finishing agent are commercially available.
The particle diameter of rutile-type pearl essence is that particle size range is at 5-25 μ m.Preferred technical scheme is: described thickener is selected from the PUP-82 thickener of Dongguan Chang Lian new material Science and Technology Co., Ltd..
Wherein PUP-82 thickener is the listing product of Dongguan Chang Lian new material Science and Technology Co., Ltd., is mainly used in water paint, and the thickener of DISPERSE DYES system is applicable to the various types of resins such as pure third, phenylpropyl alcohol, vinegar third, polyurethane.PUP-82 is different from general thickener, is high thickening product, be mainly to emphasize that thickening effect, feature are larger to low-shear viscosity contribution, and be strong false modeling product, in the last interpolation of formulation for coating material, fully disperse to stir to play thickening power.
The whole dyeing and finishing process of the special-purpose pearly-lustre slurry of Suzhou embroidery of the present invention, without any sludge creation, has also reduced this procedure of Treatment of Sludge, has avoided the generation of pollutant.
With respect to scheme of the prior art, advantage of the present invention is:
The special-purpose pearly-lustre slurry of Suzhou embroidery of the present invention goes for the printing and dyeing of the embroidery product such as Suzhou embroidery, through test, confirm, after the embroidery product such as this slurry printing and dyeing Suzhou embroidery, there is two or more coloured light, the mercerising of different form and aspect after making embroidery product have various pearly-lustre color and lusters, Duan Yin, section under natural daylight, light to dye, mutually merges agile U.S. of the space secondary colour that produces, material flicker and prints the artistic effect of embroidering in conjunction with present simultaneously.In addition, after dyeing and finishing, can not produce mud and pollute, avoid Treatment of Sludge operation.
Accompanying drawing explanation
Below in conjunction with drawings and Examples, the invention will be further described:
Fig. 1 is for being used the wire mark process chart of the special-purpose pearly-lustre slurry of Suzhou embroidery;
Fig. 2 is for being used another wire mark process chart of the special-purpose pearly-lustre slurry of Suzhou embroidery; .
The specific embodiment
Below in conjunction with specific embodiment, such scheme is described further.Should be understood that these embodiment do not limit the scope of the invention for the present invention is described.The implementation condition adopting in embodiment can be done further adjustment according to the condition of concrete producer, and not marked implementation condition is generally the condition in normal experiment.
The preparation of the special-purpose pearly-lustre slurry of embodiment 1 Suzhou embroidery
The raw material adopting and formula are as follows:
Wherein PUP-82 thickener is purchased from Dongguan Chang Lian new material Science and Technology Co., Ltd.; SCJ-998 mite-proofing and antimicrobial finishing agent is market product, VS-0071 adhesive is purchased from Jiahe, Suzhou textile auxiliary factory, pearl essence adhesive VS-0071 is applicable to active, Disperse Printing, after coordinating stamp with pearl essence, still keep the peculiar gloss of pearl essence powder and brightness, and can obtain gem-pure pattern, lines.
Preparation method is as follows:
In first in proportion deionized water being poured into easily, during turn/min of low speed 1000, add VS-0071 adhesive to stir 5min, add thickener PUP-82 after thickening, change 2850 turn/min at a high speed, add ethylene glycol, SCJ-998 mite-proofing and antimicrobial finishing agent to stir 10min, finally add rutile-type pearl essence stir 3min the special-purpose pearly-lustre slurry of Suzhou embroidery.
After measured, all indexs of this slurry all meet national requirements for environmental protection, and the special-purpose pearly-lustre slurry of Suzhou embroidery is undertaken the printing of and detected by national silk and dress-goods Quality Supervision and Inspection Center at silk fabric, and dry fastness reaches 4 grades.
The preparation of the special-purpose pearly-lustre slurry of embodiment 2 Suzhou embroiderys
The raw material adopting and formula are as follows:
Wherein PUP-82 thickener is purchased from Dongguan Chang Lian new material Science and Technology Co., Ltd.; SCJ-998 mite-proofing and antimicrobial finishing agent is market product, and VS-0071 adhesive is purchased from Jiahe, Suzhou textile auxiliary factory.
Preparation method is as follows:
In first in proportion deionized water being poured into easily, during turn/min of low speed 1000, add VS-0071 adhesive to stir 5min, add thickener PUP-82 after thickening, change 2850 turn/min at a high speed, add ethylene glycol, SCJ-998 mite-proofing and antimicrobial finishing agent to stir 10min, finally add rutile-type pearl essence stir 3min the special-purpose pearly-lustre slurry of Suzhou embroidery.
After measured, all indexs of this slurry all meet national requirements for environmental protection, and the special-purpose pearly-lustre slurry of Suzhou embroidery is undertaken the printing of and detected by national silk and dress-goods Quality Supervision and Inspection Center at silk fabric, and dry fastness reaches 4 grades.
The preparation of the special-purpose pearly-lustre slurry of embodiment 3 Suzhou embroiderys
The raw material adopting and formula are as follows:
Wherein PUP-82 thickener is purchased from Dongguan Chang Lian new material Science and Technology Co., Ltd.; SCJ-998 mite-proofing and antimicrobial finishing agent is market product, and VS-0071 adhesive is purchased from Jiahe, Suzhou textile auxiliary factory.
Preparation method is as follows:
In first in proportion deionized water being poured into easily, during turn/min of low speed 1000, add VS-0071 adhesive to stir 5min, add thickener PUP-82 after thickening, change 2850 turn/min at a high speed, add ethylene glycol, SCJ-998 mite-proofing and antimicrobial finishing agent to stir 10min, finally add rutile-type pearl essence stir 3min the special-purpose pearly-lustre slurry of Suzhou embroidery.
After measured, all indexs of this slurry all meet national requirements for environmental protection, and the special-purpose pearly-lustre slurry of Suzhou embroidery is undertaken the printing of and detected by national silk and dress-goods Quality Supervision and Inspection Center at silk fabric, and dry fastness reaches 4 grades.
The preparation of the special-purpose pearly-lustre slurry of embodiment 4 Suzhou embroiderys
The raw material adopting and formula are as follows:
Wherein PUP-82 thickener is purchased from Dongguan Chang Lian new material Science and Technology Co., Ltd.; SCJ-998 mite-proofing and antimicrobial finishing agent is market product, and VS-0071 adhesive is purchased from Jiahe, Suzhou textile auxiliary factory.
Preparation method is as follows:
In first in proportion deionized water being poured into easily, during turn/min of low speed 1000, add VS-0071 adhesive to stir 5min, add thickener PUP-82 after thickening, change 2850 turn/min at a high speed, add ethylene glycol, SCJ-998 mite-proofing and antimicrobial finishing agent to stir 10min, finally add rutile-type pearl essence stir 3min the special-purpose pearly-lustre slurry of Suzhou embroidery.
After measured, all indexs of this slurry all meet national requirements for environmental protection, and the special-purpose pearly-lustre slurry of Suzhou embroidery is undertaken the printing of and detected by national silk and dress-goods Quality Supervision and Inspection Center at silk fabric, and dry fastness reaches 4 grades.
The preparation of the special-purpose pearly-lustre slurry of embodiment 5 Suzhou embroiderys
The raw material adopting and formula are as follows:
Wherein PUP-82 thickener is purchased from Dongguan Chang Lian new material Science and Technology Co., Ltd.; SCJ-998 mite-proofing and antimicrobial finishing agent is market product, and VS-0071 adhesive is purchased from Jiahe, Suzhou textile auxiliary factory.
Preparation method is as follows:
In first in proportion deionized water being poured into easily, during turn/min of low speed 1000, add VS-0071 adhesive to stir 5min, add thickener PUP-82 after thickening, change 2850 turn/min at a high speed, add ethylene glycol, SCJ-998 mite-proofing and antimicrobial finishing agent to stir 10min, finally add rutile-type pearl essence stir 3min the special-purpose pearly-lustre slurry of Suzhou embroidery.
After measured, all indexs of this slurry all meet national requirements for environmental protection, and the special-purpose pearly-lustre slurry of Suzhou embroidery is undertaken the printing of and detected by national silk and dress-goods Quality Supervision and Inspection Center at silk fabric, and dry fastness reaches 4 grades.
When the special-purpose pearly-lustre slurry of Suzhou embroidery carries out the printing and dyeing of the embroidery product such as Suzhou embroidery, whole technique is comprised of two parts, and one, preparation: the special-purpose slurry of picture design → pearly-lustre rubber cement color matching → Suzhou embroidery pearly-lustre preparation → art silk is matched colors; Two, operation: usually need to have two kinds of process sequences according to drawing in operation: 1. wire mark → embroidery → wire mark → embroidery → finished product; 2. embroidery → wire mark → embroidery → wire mark → finished product.
Application examples 1
As shown in Figure 1, implementing process: wire mark → embroidery → wire mark → embroidery → finished product.
Picture design: will need wire mark part, with the skill and technique design of imitative tambour needle;
Slurry title: adopt the special-purpose pearlite slurry of Suzhou embroidery to match colors;
Wire type: the monochromatic silk thread of Suzhou embroidery;
Meshcount: 100 orders;
Operation sequence: wire mark → embroidery → wire mark → embroidery → finished product.
Finished product assessment: because works are with pearly-lustre rubber cement, the special-purpose slurry of Suzhou embroidery pearly-lustre shop fixtures, the sub-light, the special-purpose slurry of the Suzhou embroidery pearly-lustre interference light effect that present with pearly-lustre rubber cement during embroidery, have been taken into account again, after embroidering with the utmost point, wire mark is embroidered again again, complicated is stacked, make mercerising, pearly-lustre in the unreal sense of the special mercerising of middle appeared before one's eyes vision alternate with each other, simple pearly-lustre rubber cement, the special-purpose slurry of Suzhou embroidery pearly-lustre wire mark, the artistic effect that it is special especially that the embroidery of pure silk line is beyond one's reach at all.
Application examples 2
As shown in Figure 2, implementing process: embroidery → wire mark → embroidery → wire mark → finished product;
Picture design: will need wire mark part, with the skill and technique design of imitative tambour needle;
Slurry title: adopt the special-purpose pearlite slurry of Suzhou embroidery to match colors;
Wire type: Suzhou embroidery section prints silk thread;
Meshcount: 100 orders;
Operation sequence: embroidery → wire mark → embroidery → wire mark → finished product.
Finished product assessment: and silk thread with Duan Yin, after section dying is made embroidery shop fixtures, again with pearly-lustre rubber cement, the special-purpose slurry of Suzhou embroidery pearly-lustre wire mark, embroider again, taken into account especially between the secondary color interspersing each other, mutually set off, complementary color and echoed and the luminous effect relation of reflecting, after making it to fold thoroughly, more can present distinctive visual space and mix unreal look, this is that wire mark, embroidery all cannot lean on separately this professional skill and technique, material to reach in the past.Particularly be significantly that the color, color and luster, the form and aspect that after the silk thread embroidery after dying of Duan Yin, section, present are very abundant, secondary color, secondary color, complementary color are many and not messy, all silk looks are all unified in the mercerising that intelligence is full, in addition the interference of light luminous effect that the special use of Suzhou embroidery pearly-lustre is starched, different angles view and admire the works that it print to embroider combination time, its artistic effect is peculiar, and abundant color is that conventional embroidery cannot match in excellence or beauty.
Above-mentioned example is only explanation technical conceive of the present invention and feature, and its object is to allow person skilled in the art can understand content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalent transformations that Spirit Essence is done according to the present invention or modification, within all should being encompassed in protection scope of the present invention.
Claims (9)
1. the special-purpose pearly-lustre slurry of Suzhou embroidery, is characterized in that the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
2. the special-purpose pearly-lustre slurry of Suzhou embroidery according to claim 1, is characterized in that the special-purpose pearly-lustre slurry of described Suzhou embroidery comprises with the weight percent meter of its component:
3. the special-purpose pearly-lustre slurry of Suzhou embroidery according to claim 1, is characterized in that the special-purpose pearly-lustre slurry of described Suzhou embroidery counts with the percentage by weight of its component:
4. the special-purpose pearly-lustre slurry of Suzhou embroidery according to claim 1, is characterized in that the special-purpose pearly-lustre slurry of described Suzhou embroidery counts with the percentage by weight of its component:
5. the special-purpose pearly-lustre slurry of Suzhou embroidery according to claim 1, is characterized in that the special-purpose pearly-lustre slurry of described Suzhou embroidery counts with the percentage by weight of its component:
6. the special-purpose pearly-lustre slurry of Suzhou embroidery according to claim 5, is characterized in that described adhesive is T-608 adhesive; Described pearl essence is rutile-type pearl essence; Described mite-proofing and antimicrobial finishing agent is SCJ-998 mite-proofing and antimicrobial finishing agent; Described thickener is PUP-82 thickener.
7. the special-purpose pearly-lustre slurry of Suzhou embroidery according to claim 1, is characterized in that the special-purpose pearly-lustre slurry of described Suzhou embroidery counts with the percentage by weight of its component:
8. a preparation method for the special-purpose pearly-lustre slurry of the Suzhou embroidery described in claim 1～7 any one, is characterized in that said method comprising the steps of:
According to formula consumption, pearl essence, adhesive, ethylene glycol, thickener, deionized water are mixed to the composite special-purpose pearly-lustre slurry of described Suzhou embroidery that obtains.
9. the special-purpose pearly-lustre slurry of the Suzhou embroidery described in claim 1～7 any one is in the application of the monochromatic wire mesh of Suzhou embroidery India and China.