CN103692366B - 一种超疏水抗堵塞砂纸复胶及其制备方法 - Google Patents

一种超疏水抗堵塞砂纸复胶及其制备方法 Download PDF

Info

Publication number
CN103692366B
CN103692366B CN201310675667.7A CN201310675667A CN103692366B CN 103692366 B CN103692366 B CN 103692366B CN 201310675667 A CN201310675667 A CN 201310675667A CN 103692366 B CN103692366 B CN 103692366B
Authority
CN
China
Prior art keywords
component
filler
adhesive
hydrophobic
sand paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310675667.7A
Other languages
English (en)
Other versions
CN103692366A (zh
Inventor
关广利
卢高波
冷成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU FENGMANG COMPOSITE MATERIAL S&T GROUP CO Ltd
Original Assignee
JIANGSU FENGMANG COMPOSITE MATERIAL S&T GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU FENGMANG COMPOSITE MATERIAL S&T GROUP CO Ltd filed Critical JIANGSU FENGMANG COMPOSITE MATERIAL S&T GROUP CO Ltd
Priority to CN201310675667.7A priority Critical patent/CN103692366B/zh
Publication of CN103692366A publication Critical patent/CN103692366A/zh
Application granted granted Critical
Publication of CN103692366B publication Critical patent/CN103692366B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种超疏水抗堵塞砂纸复胶，包含甲、乙、丙、丁四种组分；甲组分由胶黏剂和溶剂组成；乙组分由填料和溶剂组成；丙组分由爽滑剂和溶剂组成；丁组分由颜料和疏水促进剂组成。一种超疏水抗堵塞砂纸复胶的制备方法，先按照甲组分中的胶黏剂和乙组分中的填料成分分别配置胶黏剂和填料，再分别将甲组分的胶黏剂、乙组分的填料和丙组分的爽滑剂与溶剂按照重量比例分别配制，将丁组分的颜料与疏水促进剂按重量比例配制，最后按甲、乙、丙、丁四种组分的比例将四种组分混合并且搅拌均匀。本发明提高砂纸的疏水性能，并且使砂纸具有防静电、抗堵塞以及寿命长的特点。

Description

一种超疏水抗堵塞砂纸复胶及其制备方法
技术领域
本发明属于材料领域，涉及一种涂附磨具的复胶，尤其是一种超疏水抗堵塞砂纸复胶及其制备方法。
背景技术
在涂附磨具行业中，砂纸是一种广泛使用的打磨工具，砂纸具有使用方便、价格低廉等特点。目前砂纸的制作方法一般为：在纸基上涂覆上底胶，然后把磨料植入底胶上，最后在磨料上涂覆一层复胶层，其中底胶或复胶层一般只通过合成树脂再加几种辅助材料制作而成。用这种方法制成复胶的涂附磨具，在使用过程中容易产生静电，且砂纸在使用起来打磨木材、金属等表面时候，容易被堵塞，导致磨削效果降低；尤其是这种方法制成的复胶容易被水沾湿，从而影响砂纸的打磨效果以及寿命，因此需要进一步改进。
发明内容
本发明所要解决的技术问题是，克服现有技术的缺点，提供一种超疏水抗堵塞砂纸复胶及其制备方法，提高砂纸的疏水性能，并且使砂纸具有防静电、抗堵塞以及寿命长的特点，能够提高砂纸的利用效率。
为了解决以上技术问题，本发明提供一种超疏水抗堵塞砂纸复胶及其制备方法：
一种超疏水抗堵塞砂纸复胶，包含甲、乙、丙、丁四种组分，甲、乙、丙、丁四种组分的总量比例为：100:10-50:20-40:15-55；
甲组分由70%-90%胶黏剂和10%-30%溶剂组成；乙组分由填料40%-80%和溶剂20%-60%组成；丙组分由40%-80%爽滑剂和20%-60%溶剂组成；丁组分由颜料70%-90%和10%-30%疏水促进剂组成。
一种超疏水抗堵塞砂纸复胶的制备方法，先按照甲组分中的胶黏剂和乙组分中的填料成分分别配置胶黏剂和填料，再分别将甲组分的胶黏剂、乙组分的填料和丙组分的爽滑剂与溶剂按照重量比例分别配制，将丁组分的颜料与疏水促进剂按重量比例配制，最后按甲、乙、丙、丁四种组分的比例将四种组分混合并且搅拌均匀。
本发明进一步限定的技术方案是：
前述甲组分的胶黏剂为酚醛树脂，环氧树脂，聚氨酯，白乳胶或聚乙烯醇中的至少一种。
前述乙组分的填料为滑石粉，石棉粉，陶土粉，碳酸钙粉，长石粉或方解石粉中的至少一种。
前述丙组分的爽滑剂为滑石粉，硬脂酸锌，硬脂酸镁，硬脂酸铝或蜡乳液中的任一种。
前述丁组分的颜料为氧化铁颜料或水性颜料中的任一种。
前述甲、乙、丙组分的溶剂为甲醇、乙醇、乙二醇、甲苯、丙酮、溶剂油或水中的任一种；丁组分的疏水促进剂为水性蜡乳液。
本发明的有益效果是：本发明在砂纸的复胶丁组分中添加了疏水促进剂，可以形成超疏水层，提高砂纸的疏水性，防止砂纸被水沾湿，提高砂纸的寿命；本发明的复胶丙组分中添加了抗静电剂，可以有效防止砂纸在研磨过程中产生经典，影响砂纸的打磨效果；本发明的复胶可以使砂纸表面光洁干燥，砂纸散热快且耐久度高，用于木材、金属等打磨时具有良好的抗堵塞的性能。
具体实施方式
实施例1
本实施例提供的一种超疏水抗堵塞砂纸复胶，包含甲、乙、丙、丁四种组分，甲、乙、丙、丁四种组分的总量比例为：100:10:40:50；
甲组分由70%胶黏剂和30%溶剂组成；乙组分由填料80%和溶剂20%组成；丙组分由40%爽滑剂和60%溶剂组成；丁组分由颜料70%和30%疏水促进剂组成。
甲组分的胶黏剂为环氧树脂；乙组分的填料为陶土粉和碳酸钙粉的混合物；丙组分的爽滑剂为硬脂酸锌；丁组分的颜料为氧化铁颜料；甲、乙、丙组分的溶剂为乙醇；丁组分的疏水促进剂为水性蜡乳液。
该超疏水抗堵塞砂纸复胶的制备方法，先按照甲组分中的胶黏剂和乙组分中的填料成分分别配置胶黏剂和填料，再分别将甲组分的胶黏剂、乙组分的填料和丙组分的爽滑剂与溶剂按照重量比例分别配制，将丁组分的颜料与疏水促进剂按重量比例配制，最后按甲、乙、丙、丁四种组分的比例将四种组分混合并且搅拌均匀。
实施例2
本实施例提供的一种超疏水抗堵塞砂纸复胶，包含甲、乙、丙、丁四种组分，甲、乙、丙、丁四种组分的总量比例为：100:50:20:15；
甲组分由90%胶黏剂和10%溶剂组成；乙组分由填料60%和溶剂40%组成；丙组分由80%爽滑剂和20%溶剂组成；丁组分由颜料90%和10%疏水促进剂组成。
甲组分的胶黏剂为聚氨酯和白乳胶的混合物；乙组分的填料为石棉粉；丙组分的爽滑剂为硬脂酸铝；丁组分的颜料为水性颜料；甲、乙、丙组分的溶剂为甲苯；丁组分的疏水促进剂为水性蜡乳液。
该超疏水抗堵塞砂纸复胶的制备方法，先按照甲组分中的胶黏剂和乙组分中的填料成分分别配置胶黏剂和填料，再分别将甲组分的胶黏剂、乙组分的填料和丙组分的爽滑剂与溶剂按照重量比例分别配制，将丁组分的颜料与疏水促进剂按重量比例配制，最后按甲、乙、丙、丁四种组分的比例将四种组分混合并且搅拌均匀。
实施例3
本实施例提供的一种超疏水抗堵塞砂纸复胶，包含甲、乙、丙、丁四种组分，甲、乙、丙、丁四种组分的总量比例为：100:35:30:55；
甲组分由80%胶黏剂和20%溶剂组成；乙组分由填料40%和溶剂60%组成；丙组分由50%爽滑剂和50%溶剂组成；丁组分由颜料80%和20%疏水促进剂组成。
甲组分的胶黏剂为聚乙烯醇；乙组分的填料为方解石粉；丙组分的爽滑剂为蜡乳液；丁组分的颜料为氧化铁颜料；甲、乙、丙组分的溶剂为溶剂油；丁组分的疏水促进剂为水性蜡乳液。
该超疏水抗堵塞砂纸复胶的制备方法，先按照甲组分中的胶黏剂和乙组分中的填料成分分别配置胶黏剂和填料，再分别将甲组分的胶黏剂、乙组分的填料和丙组分的爽滑剂与溶剂按照重量比例分别配制，将丁组分的颜料与疏水促进剂按重量比例配制，最后按甲、乙、丙、丁四种组分的比例将四种组分混合并且搅拌均匀。
除上述实施例外，本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案，均落在本发明要求的保护范围。

Claims (2)

1.一种超疏水抗堵塞砂纸复胶，其特征在于：包含甲、乙、丙、丁四种组分，所述甲、乙、丙、丁四种组分的总量比例为：100:10-50:20-40:15-55；
所述甲组分由70%-90%胶黏剂和10%-30%溶剂组成；所述乙组分由填料40%-80%和溶剂20%-60%组成；所述丙组分由40%-80%爽滑剂和20%-60%溶剂组成；所述丁组分由颜料70%-90%和10%-30%疏水促进剂组成；
所述甲组分的胶黏剂为酚醛树脂，环氧树脂，聚氨酯，白乳胶或聚乙烯醇中的至少一种；
所述乙组分的填料为滑石粉，石棉粉，陶土粉，碳酸钙粉，长石粉或方解石粉中的至少一种；
所述丙组分的爽滑剂为滑石粉，硬脂酸锌，硬脂酸镁，硬脂酸铝或蜡乳液中的任一种；
所述丁组分的颜料为氧化铁颜料或水性颜料中的任一种；
所述甲、乙、丙组分的溶剂为甲醇、乙醇、乙二醇、甲苯、丙酮、溶剂油或水中的任一种；所述丁组分的疏水促进剂为水性蜡乳液。
2.根据权利要求1所述的超疏水抗堵塞砂纸复胶的制备方法，其特征在于：先按照甲组分中的胶黏剂和乙组分中的填料成分分别配置胶黏剂和填料，再分别将甲组分的胶黏剂、乙组分的填料和丙组分的爽滑剂与溶剂按照重量比例分别配制，将丁组分的颜料与疏水促进剂按重量比例配制，最后按甲、乙、丙、丁四种组分的比例将四种组分混合并且搅拌均匀。
CN201310675667.7A 2013-12-13 2013-12-13 一种超疏水抗堵塞砂纸复胶及其制备方法 Active CN103692366B (zh)