CN103666685A - 一种防锈油及其制备方法 - Google Patents
一种防锈油及其制备方法 Download PDFInfo
- Publication number
- CN103666685A CN103666685A CN201310636591.7A CN201310636591A CN103666685A CN 103666685 A CN103666685 A CN 103666685A CN 201310636591 A CN201310636591 A CN 201310636591A CN 103666685 A CN103666685 A CN 103666685A
- Authority
- CN
- China
- Prior art keywords
- parts
- fatty acid
- acid ester
- stir
- mixed solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种防锈油及其制备方法，其中防锈油以重量组分计包括：醇酸树脂6-10份，氧化石油脂钡皂4-8份，蓖麻油2-6份，石油磺酸钙8-15份，司盘800.5-1份，聚甘油脂肪酸酯0.2-0.8份，邻苯二甲酸二丁酯1-5份，石油磺酸钠1-5份；制备方法为将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到60-80℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌10-20分钟，将石油磺酸钙和石油磺酸钠加入到以上得到的混合液中，保持70-80℃，搅拌10-20分钟。本发明提供的防锈油稳定性良好，防锈周期长。
Description
技术领域
本发明属于化工防锈剂领域，特别涉及一种防锈油及其制备方法。
背景技术
腐蚀是使紧固件破坏的主要形式之一，对汽车、摩托车以及各种车辆、机械会造成很大的损失。据统计，每年由于金属腐蚀所造成的直接经济损失约占国民经济总产值的2%-4%。为避免锈蚀、减少损失，人们采用了各种各样的方法，用防锈油脂来 最新防锈油保护金属紧固件，便是目前最常见的防护方法之一。螺纹紧固件多种多样，从普通螺栓、螺母、螺钉，到高强度、高性能、高精度、高附加值和非标异形件，他们的防锈包装方法却基本相同。对于表面氧化、磷化、发黑的螺纹紧固件多数都是采用表面涂、浸防锈油外，外加用塑料包装的方式。防锈油脂是在石油类基本组分中加入一种或多种防锈添加剂及其辅助添加剂组成，它使用方便，成本低廉，效果好，操作简单，紧固件行业都在大量使用。
目前现有的防锈油效果一般，防锈周期较短，不能够进行较长时期的防锈。
发明内容
本发明的目的在于为了克服以上现有技术的不足而提供一种防锈油及其制备方法。
本发明是通过以下技术手段实现的：
一种防锈油，以重量组分计包括：醇酸树脂6-10份，氧化石油脂钡皂4-8份，蓖麻油2-6份，石油磺酸钙8-15份，司盘80 0.5-1份，聚甘油脂肪酸酯0.2-0.8份，邻苯二甲酸二丁酯1-5份，石油磺酸钠1-5份。
所述的防锈油，优选可以为以重量组分计包括：醇酸树脂8-10份，氧化石油脂钡皂5-7份，蓖麻油3-5份，石油磺酸钙10-13份，司盘80 0.6-0.8份，聚甘油脂肪酸酯0.3-0.5份，邻苯二甲酸二丁酯2-4份，石油磺酸钠2-4份。
一种以上所述的防锈油的制备方法，可以按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到60-80℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌10-20分钟；
（3）将石油磺酸钙和石油磺酸钠加入到步骤（2）得到的混合液中，保持70-80℃，搅拌10-20分钟。
本发明提供的防锈油有机稳定性良好，腐蚀试验与盐水浸渍试验都合格，湿热试验能够达到50天以上，防锈周期能达到30天以上。
具体实施方式：
实施例1
一种防锈油，以重量组分计包括：醇酸树脂6份，氧化石油脂钡皂4份，蓖麻油2份，石油磺酸钙8份，司盘80 0.5份，聚甘油脂肪酸酯0.2份，邻苯二甲酸二丁酯1份，石油磺酸钠1份。
以上所述的防锈油按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到60℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌10分钟；
（3）将石油磺酸钙和石油磺酸钠加入到步骤（2）得到的混合液中，保持70℃，搅拌10分钟。
实施例2
一种防锈油，以重量组分计包括：醇酸树脂8份，氧化石油脂钡皂5份，蓖麻油3份，石油磺酸钙10份，司盘80 0.6份，聚甘油脂肪酸酯0.3份，邻苯二甲酸二丁酯2份，石油磺酸钠2份。
以上所述的防锈油按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到65℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌12分钟；
（3）将石油磺酸钙和石油磺酸钠加入到步骤（2）得到的混合液中，保持75℃，搅拌15分钟。
实施例3
一种防锈油，以重量组分计包括：醇酸树脂9份，氧化石油脂钡皂6份，蓖麻油4份，石油磺酸钙12份，司盘80 0.7份，聚甘油脂肪酸酯0.4份，邻苯二甲酸二丁酯3份，石油磺酸钠3份。
以上所述的防锈油按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到70℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌15分钟；
（3）将石油磺酸钙和石油磺酸钠加入到步骤（2）得到的混合液中，保持76℃，搅拌15分钟。
实施例4
一种防锈油，以重量组分计包括：醇酸树脂10份，氧化石油脂钡皂7份，蓖麻油5份，石油磺酸钙13份，司盘80 0.8份，聚甘油脂肪酸酯0.5份，邻苯二甲酸二丁酯4份，石油磺酸钠4份。
以上所述的防锈油按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到75℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌20分钟；
（3）将石油磺酸钙和石油磺酸钠加入到步骤（2）得到的混合液中，保持78℃，搅拌20分钟。
实施例5
一种防锈油，以重量组分计包括：醇酸树脂10份，氧化石油脂钡皂8份，蓖麻油6份，石油磺酸钙15份，司盘80 1份，聚甘油脂肪酸酯0.8份，邻苯二甲酸二丁酯5份，石油磺酸钠5份。
以上所述的防锈油按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到80℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌20分钟；
（3）将石油磺酸钙和石油磺酸钠加入到步骤（2）得到的混合液中，保持80℃，搅拌20分钟。
对以上实施例制备得到的防锈油进行性能测试，结果见下表：
| 项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 |
| 有机稳定性 | 稳定 | 稳定 | 稳定 | 稳定 | 稳定 |
| 腐蚀试验 | 合格 | 合格 | 合格 | 合格 | 合格 |
| 湿热试验 | 50天 | 52天 | 55天 | 53天 | 51天 |
| 盐水浸渍试验 | 合格 | 合格 | 合格 | 合格 | 合格 |
| 防锈周期 | 30天 | 32天 | 33天 | 33天 | 31天 |
从以上数据可以看出，本发明提供的防锈油有机稳定性良好，腐蚀试验与盐水浸渍试验都合格，湿热试验能够达到50天以上，防锈周期能达到30天以上。
Claims (3)
1. 一种防锈油，其特征在于，以重量组分计包括：醇酸树脂6-10份，氧化石油脂钡皂4-8份，蓖麻油2-6份，石油磺酸钙8-15份，司盘80 0.5-1份，聚甘油脂肪酸酯0.2-0.8份，邻苯二甲酸二丁酯1-5份，石油磺酸钠1-5份。
2. 根据权利要求1所述的防锈油，其特征在于，以重量组分计包括：醇酸树脂8-10份，氧化石油脂钡皂5-7份，蓖麻油3-5份，石油磺酸钙10-13份，司盘80 0.6-0.8份，聚甘油脂肪酸酯0.3-0.5份，邻苯二甲酸二丁酯2-4份，石油磺酸钠2-4份。
3. 一种权利要求1或2所述的防锈油的制备方法，其特征在于，按照以下步骤进行制备：
（1）按照重量份称取各组分；
（2）将醇酸树脂、氧化石油脂钡皂、蓖麻油和邻苯二甲酸二丁酯加热到60-80℃，搅拌均匀，加入司盘80和聚甘油脂肪酸酯搅拌至混合液均匀分散，继续搅拌10-20分钟；
（3）将石油磺酸钙和石油磺酸钠加入到步骤（2）得到的混合液中，保持70-80℃，搅拌10-20分钟。