CN103666268A - Method for manufacturing fire-proof floor - Google Patents
Method for manufacturing fire-proof floor Download PDFInfo
- Publication number
- CN103666268A CN103666268A CN201310625634.1A CN201310625634A CN103666268A CN 103666268 A CN103666268 A CN 103666268A CN 201310625634 A CN201310625634 A CN 201310625634A CN 103666268 A CN103666268 A CN 103666268A
- Authority
- CN
- China
- Prior art keywords
- parts
- board
- air drying
- fire
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a fire-proof floor. The method sequentially comprises the following steps: (a) sawing a piece of board according to the size need, and naturally air drying the board; (b) in part by weight, putting 235 parts of water, 1.5 parts of a wetting agent, 5 parts of a SN-5040 dispersing agent, 12 parts of ethanediol, 1 part of cellulose, 1.5 parts of NXZ defoaming agent, 50 parts of titanium dioxide, 300 parts of ammonium polyphosphate, 70 parts of melamine, 60 parts of pentaerythritol, 1 part of brightener, 250 parts of emulsion 816, 100 parts of elastic emulsion 963, 17 parts of dodecanol ester, 1.5 parts of preservative, 6 parts of thickener and 2 parts of flatting agent into a stirrer for stirring for 1 hour; (c) then uniformly coating the manufactured mixed liquid on the surface of the board; (d) finally, putting the board into a reaction kettle, pressurizing at 3 MPa, taking out after 5-8 hours, and naturally air drying the board. According to the method for manufacturing the fire-proof floor, the surface of the board is coated with a coating layer with excellent flame-retarded effect, and the board is subjected to high-pressure treatment so as to obtain an ideal fire-proof effect. The production cost is relatively low, and the floor is easily popularized.
Description
Technical field
The present invention relates to a kind of manufacture craft of floor, is specifically a kind of making method of fireproof floorboard.
Background technology
At present the floor on decoration market has had the features such as warming, attractive in appearance, but floor as inflammable in house ornamentation, its fire performance is ignored by people always, also have more antiflaming floor, but actual effect is not satisfactory on market.
Summary of the invention
Technical problem to be solved by this invention is just to provide a kind of making method of fireproof floorboard, and the fireproof floorboard that this making method is made has good fire performance.
For achieving the above object, the present invention adopts following technical scheme: a kind of making method of fireproof floorboard, is characterized in that: comprise the following steps successively:
A) first by size, need to saw out a sheet material, natural air drying;
B) then by weight by 235 parts, water, 1.5 parts of wetting agents, 5 parts of SN-5040 dispersion agents, 12 parts of ethylene glycol, 1 part of Mierocrystalline cellulose, 1.5 parts of NXZ defoamers, 50 parts of titanium dioxides, 300 parts of ammonium polyphosphates, 70 parts of trimeric cyanamides, 60 parts of tetramethylolmethanes, 1 part, whitening agent, 816250 parts of emulsions, 963100 parts of elastic emulsions, 17 parts, lauryl alcohol fat, 1.5 parts of sanitass, 6 parts of thickening materials, 2 parts of flow agents, put into agitator and stir 1 hour;
C) then the mixed solution of making is coated in to plate surface uniformly;
D) finally sheet material is put into reactor, pressurization 3MPa, spends 5-8 hour and takes out, natural air drying.
The making method of fireproof floorboard of the present invention, by applying the splendid coating of flame retardant effect at plate surface, through autoclaving, can obtain comparatively desirable flameproof effect, and production cost is relatively low, is easy to promote.
Embodiment
The making method embodiment 1 of fireproof floorboard of the present invention, comprises the following steps successively:
A) first by size, need to saw out a sheet material, natural air drying;
B) then by weight by 235 parts, water, 1.5 parts of wetting agents, 5 parts of SN-5040 dispersion agents, 12 parts of ethylene glycol, 1 part of Mierocrystalline cellulose, 1.5 parts of NXZ defoamers, 50 parts of titanium dioxides, 300 parts of ammonium polyphosphates, 70 parts of trimeric cyanamides, 60 parts of tetramethylolmethanes, 1 part, whitening agent, 816250 parts of emulsions, 963100 parts of elastic emulsions, 17 parts, lauryl alcohol fat, 1.5 parts of sanitass, 6 parts of thickening materials, 2 parts of flow agents, put into agitator and stir 1 hour;
C) then the mixed solution of making is coated in to plate surface uniformly;
D) finally sheet material is put into reactor, pressurization 3MPa, spends 5-8 hour and takes out, natural air drying.
The making method of fireproof floorboard of the present invention is simple to operate, and the floor of processing through the method has good fire resistance, can guarantee the attractive in appearance of floor itself again simultaneously, and cost is lower, is easy to promote.
Above-described embodiment is to explanation of the present invention, is not limitation of the invention, any scheme after simple transformation of the present invention is all belonged to protection scope of the present invention.
Claims (1)
1. a making method for fireproof floorboard, is characterized in that: comprise the following steps successively:
A) first by size, need to saw out a sheet material, natural air drying;
B) then by weight by 235 parts, water, 1.5 parts of wetting agents, 5 parts of SN-5040 dispersion agents, 12 parts of ethylene glycol, 1 part of Mierocrystalline cellulose, 1.5 parts of NXZ defoamers, 50 parts of titanium dioxides, 300 parts of ammonium polyphosphates, 70 parts of trimeric cyanamides, 60 parts of tetramethylolmethanes, 1 part, whitening agent, 816250 parts of emulsions, 963100 parts of elastic emulsions, 17 parts, lauryl alcohol fat, 1.5 parts of sanitass, 6 parts of thickening materials, 2 parts of flow agents, put into agitator and stir 1 hour;
C) then the mixed solution of making is coated in to plate surface uniformly;
D) finally sheet material is put into reactor, pressurization 3MPa, spends 5-8 hour and takes out, natural air drying.