CN103642391A - Crack resistant waterproof paint - Google Patents
Crack resistant waterproof paint Download PDFInfo
- Publication number
- CN103642391A CN103642391A CN201310580597.7A CN201310580597A CN103642391A CN 103642391 A CN103642391 A CN 103642391A CN 201310580597 A CN201310580597 A CN 201310580597A CN 103642391 A CN103642391 A CN 103642391A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof paint
- crack resistant
- resistant waterproof
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a crack resistant waterproof paint. The crack resistant waterproof paint comprises following raw materials, by weight, 1.5 to 3.7 parts of tetrabutylammonium bromide, bisphenol A, 3 to 5.5 parts of N-methylethanolamine, 1.5 to 2.6 parts of decabromodiphenyl ether, 2.2 to 2.9 parts of amino resin, 1.5 to 4 parts of asphalt, 2.3 to 3.6 parts of phenethyl phenol polyoxyethylene ether phosphate ester, 1.5 to 2.5 parts of alkylamine polyoxyethylene ether phosphate ester, and 2.1 to 3.5 parts of polyoxyethylene sorbitan fatty acid ester. Compared with existing waterproof paints, the crack resistant waterproof paint is suitable for water repellent treatment of buildings such as basements, toilets, kitchens, and pools. The crack resistant waterproof paint does not need to be heated for using; environmental pollution is reduced; the crack resistant waterproof paint possesses advantages such as low cost, easy construction operation, high bonding force, and crack resistance; waterproof effect is improved; and the crack resistant waterproof paint can be used for construction on wet or dry base surfaces made of a plurality of materials possesses no toxicity, is long in service life, and is an ideal waterproof material.
Description
Technical field
The waterproof paint that the present invention relates to a kind of cracking resistance, belongs to building material field.
Background technology
Due to advocating of environmental protection, water-borne coatings has become the hot product in market, and the development and application of China's waterproof paint started from for the 60's, once take in early days various chemical industry tankage as raw material development product, all because capability and performance is unstable, stops development.In the same period, China, for improve petroleum pitch configuration waterproof paint aspect with superpolymer, plays chess and has carried out relatively large work.There is chloroprene rubber in 60 mid-nineties 90s--asphalt waterproofing paint, and there is regenerated rubber in the initial stage in the 70's--asphalt waterproofing paint, and in engineering, obtain more successfully application.Steady progression along with China's synthesized polymer material industry, take the waterproof paint that various high-quality synthetic rubber and synthetic resins is raw material development, in the 80's, in succession come into operation: as the light waterproof paint of Two-component Waterproof Polyurethane Coating, esters of acrylic acid, cationic chloroprene latex asphalt waterproofing paint and silicon rubber waterproof coating etc., rubber asphalt class and synthetic high score subclass waterproof paint, in China's waterproofing work application, are just occupying increasing proportion.Take petroleum pitch as main, carry out the technological approaches of modification with superpolymer, in the existing longer history of China, its raw material sources is extensive, and cost is lower, the general waterproofing work of large light of the amount of being applicable to; Take synthesized polymer material as the main coating of making, and performance is more excellent, but price is higher; Due to building distortion, thereby body of wall be full of cracks causes coating surface cracking, reduces waterproof effect.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is, a kind of waterproof paint of cracking resistance is provided, cohesive force is strong, good water-proof effect, cracking resistance, reduces environmental pollution, and cost is low.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of waterproof paint of cracking resistance,
Raw material by following parts by weight is made: Tetrabutyl amonium bromide 1.5-3.7 part, dihydroxyphenyl propane, N-Mono Methyl Ethanol Amine 3-5.5 part, decabromodiphynly oxide 1.5-2.6 part, aminoresin 2.2-2.9 part, pitch 1.5-4 part, styroyl phenol polyethenoxy ether phosphate 2.3-3.6 part, ethoxylated fatty amines phosphoric acid ester 1.5-2.5 part and polyoxyethylene sorbitan fatty acid ester 2.1-3.5 part.
Optimize, the waterproof paint of above-mentioned cracking resistance, by the raw material of following parts by weight, made:
2.8 parts of 2.8 parts of Tetrabutyl amonium bromides, dihydroxyphenyl propane, 4.6 parts of N-Mono Methyl Ethanol Amines, 2.2 parts of decabromodiphynly oxides, 2.7 parts, aminoresin, 3.2 parts of pitches, 2.7 parts of styroyl phenol polyethenoxy ether phosphates, 1.9 parts of ethoxylated fatty amines phosphoric acid ester and polyoxyethylene sorbitan fatty acid esters.
The present invention compares with existing waterproof paint, is applicable to the waterproof of the buildings such as vault, toilet, kitchen, pond simultaneously, during use, without heating, reduces environmental pollution, has the advantages such as cost is low, constructing operation is simple; Cohesive force is strong, and cracking resistance has improved waterproof effect; Can be on the basal plane of moist or dry various material construction waterproof functional, nontoxic, long service life, is a kind of comparatively ideal water-proof material.
Embodiment
embodiment 1
The present invention is a kind of waterproof paint of cracking resistance, by the raw material of following parts by weight, is made:
2.8 parts of 2.8 parts of Tetrabutyl amonium bromides, dihydroxyphenyl propane, 4.6 parts of N-Mono Methyl Ethanol Amines, 2.2 parts of decabromodiphynly oxides, 2.7 parts, aminoresin, 3.2 parts of pitches, 2.7 parts of styroyl phenol polyethenoxy ether phosphates, 1.9 parts of ethoxylated fatty amines phosphoric acid ester and polyoxyethylene sorbitan fatty acid esters.
embodiment 2
The present invention is a kind of waterproof paint of cracking resistance, by the raw material of following parts by weight, is made:
2.1 parts of 1.5 parts of Tetrabutyl amonium bromides, dihydroxyphenyl propane, 3 parts of N-Mono Methyl Ethanol Amines, 1.5 parts of decabromodiphynly oxides, 2.2 parts, aminoresin, 1.5 parts of pitches, 2.3 parts of styroyl phenol polyethenoxy ether phosphates, 1.5 parts of ethoxylated fatty amines phosphoric acid ester and polyoxyethylene sorbitan fatty acid esters.
embodiment 3
The present invention is a kind of waterproof paint of cracking resistance, by the raw material of following parts by weight, is made:
3.5 parts of 3.7 parts of Tetrabutyl amonium bromides, dihydroxyphenyl propane, 5.5 parts of N-Mono Methyl Ethanol Amines, 2.6 parts of decabromodiphynly oxides, 2.9 parts, aminoresin, 4 parts of pitches, 3.6 parts of styroyl phenol polyethenoxy ether phosphates, 2.5 parts of ethoxylated fatty amines phosphoric acid ester and polyoxyethylene sorbitan fatty acid esters.
The present invention compares with existing waterproof paint, is applicable to the waterproof of the buildings such as vault, toilet, kitchen, pond simultaneously, during use, without heating, reduces environmental pollution, has the advantages such as cost is low, constructing operation is simple; Cohesive force is strong, and cracking resistance has improved waterproof effect; Can be on the basal plane of moist or dry various material construction waterproof functional, nontoxic, long service life, is a kind of comparatively ideal water-proof material.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. a waterproof paint for cracking resistance, is characterized in that: the raw material by following parts by weight is made:
Tetrabutyl amonium bromide 1.5-3.7 part, dihydroxyphenyl propane, N-Mono Methyl Ethanol Amine 3-5.5 part, decabromodiphynly oxide 1.5-2.6 part, aminoresin 2.2-2.9 part, pitch 1.5-4 part, styroyl phenol polyethenoxy ether phosphate 2.3-3.6 part, ethoxylated fatty amines phosphoric acid ester 1.5-2.5 part and polyoxyethylene sorbitan fatty acid ester 2.1-3.5 part.
2. the waterproof paint of cracking resistance according to claim 1, is characterized in that:
Raw material by following parts by weight is made: 2.8 parts of 2.8 parts of Tetrabutyl amonium bromides, dihydroxyphenyl propane, 4.6 parts of N-Mono Methyl Ethanol Amines, 2.2 parts of decabromodiphynly oxides, 2.7 parts, aminoresin, 3.2 parts of pitches, 2.7 parts of styroyl phenol polyethenoxy ether phosphates, 1.9 parts of ethoxylated fatty amines phosphoric acid ester and polyoxyethylene sorbitan fatty acid esters.
?