CN103602229B - A kind of cracking resistance water-repellent paint - Google Patents
A kind of cracking resistance water-repellent paint Download PDFInfo
- Publication number
- CN103602229B CN103602229B CN201310580168.XA CN201310580168A CN103602229B CN 103602229 B CN103602229 B CN 103602229B CN 201310580168 A CN201310580168 A CN 201310580168A CN 103602229 B CN103602229 B CN 103602229B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- repellent paint
- cracking resistance
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of cracking resistance water-repellent paint, made by the raw material of following parts by weight: acetylacetone,2,4-pentanedione selenium 2.3-4.8 part, water-based unsaturated polyester (UP) acrylate resin 3.2-4.6 part, defoamer 1.3-3.3 part, cyclohexanone 1.3-2.6 part, bentonite 2.3-5 part, two phenethyl phenol polyethenoxy ether 2.3-4 part, long-chain fatty alcohol APEO 1.5-2.8 part and propandiol butyl ether 1.5-3 part. The present invention, compared with existing water-repellent paint, is applicable to the waterproof of the buildings such as basement, toilet, kitchen, pond, when use, without heating, reduces environmental pollution, has the advantages such as cost is low, constructing operation is simple; Cohesive force is strong, and cracking resistance has improved waterproof effect; Can be on the basal plane of moist or dry various material construction waterproof functional, nontoxic, long service life, is a kind of comparatively ideal waterproof material.
Description
Technical field
The present invention relates to a kind of cracking resistance water-repellent paint, belong to building material field.
Background technology
Due to advocating of environmental protection, water paint has become the hot product in market, and the development and application of China's water-repellent paint starts from 60 yearsGeneration, once developed in early days product taking various chemical industry leftover bits and pieces as raw material, all stop development because capability and performance is unstable. For the moment samePhase, China, for improve asphalt configuration water-repellent paint aspect with high polymer, plays chess and has carried out relatively large work. In the sixtiesThere is neoprene in the phase--asphalt waterproofing paint, and there is reclaimed rubber in the initial stage seventies--asphalt waterproofing paint, and in workIn journey, obtain more successfully application. Along with the stable development of China's synthesized polymer material industry, with various high-quality synthetic rubber andSynthetic resin is the water-repellent paint of raw material development, in succession comes into operation: as Two-component Waterproof Polyurethane Coating, third in the eightiesLight water-repellent paint, cationic chloroprene latex asphalt waterproofing paint and the silicon rubber waterproof coating etc. of alkene esters of gallic acid, rubber asphalt classIn China's waterproofing work application, just occupying increasing proportion with synthetic high score subclass water-repellent paint. Taking asphalt as main,Carry out the technological approaches of modification with high polymer, in the existing longer history of China, its raw material sources is extensive, and cost is lower, is suitable forIn the general waterproofing work of the large face light of amount; Taking synthesized polymer material as the main coating of making, performance is more excellent, but price is higher;Due to building distortion, thereby body of wall be full of cracks causes coating surface cracking, reduces waterproof effect.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is, a kind of cracking resistance water-repellent paint is provided,Cohesive force is strong, good water-proof effect, and cracking resistance, reduces environmental pollution, with low cost.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of cracking resistance water-repellent paint,
Raw material by following parts by weight is made: acetylacetone,2,4-pentanedione selenium 2.3-4.8 part, water-based unsaturated polyester (UP) acrylate resin3.2-4.6 part, defoamer 1.3-3.3 part, cyclohexanone 1.3-2.6 part, bentonite 2.3-5 part, two phenethyl phenol polyoxy secondAlkene ether 2.3-4 part, long-chain fatty alcohol APEO 1.5-2.8 part and propandiol butyl ether 1.5-3 part.
Optimize, above-mentioned cracking resistance water-repellent paint, made by the raw material of following parts by weight:
4.4 parts, acetylacetone,2,4-pentanedione selenium, 3.6 parts of water-based unsaturated polyester (UP) acrylate resins, 2.5 parts of defoamers, cyclohexanone 1.8Part, 3.6 parts of bentonites, 3.3 parts of two phenethyl phenol polyethenoxy ethers, 2.7 parts of long-chain fatty alcohol APEOs and propane diols1.9 parts of butyl ether.
The present invention, compared with existing water-repellent paint, is applicable to the waterproof of the buildings such as basement, toilet, kitchen, pond, makesUsed time, without heating, reduces environmental pollution, has the advantages such as cost is low, constructing operation is simple; Cohesive force is strong, and cracking resistance is carriedHigh waterproof effect; Can be on the basal plane of moist or dry various material construction waterproof functional, nontoxic, use the longevityLife is long, is a kind of comparatively ideal waterproof material.
Detailed description of the invention
Embodiment 1
The present invention is a kind of cracking resistance water-repellent paint, is made up of the raw material of following parts by weight:
4.4 parts, acetylacetone,2,4-pentanedione selenium, 3.6 parts of water-based unsaturated polyester (UP) acrylate resins, 2.5 parts of defoamers, cyclohexanone 1.8Part, 3.6 parts of bentonites, 3.3 parts of two phenethyl phenol polyethenoxy ethers, 2.7 parts of long-chain fatty alcohol APEOs and propane diols1.9 parts of butyl ether.
Embodiment 2
The present invention is a kind of cracking resistance water-repellent paint, is made up of the raw material of following parts by weight:
2.3 parts, acetylacetone,2,4-pentanedione selenium, 3.2 parts of water-based unsaturated polyester (UP) acrylate resins, 1.3 parts of defoamers, cyclohexanone 1.3Part, 2.3 parts of bentonites, 2.3 parts of two phenethyl phenol polyethenoxy ethers, 1.5 parts of long-chain fatty alcohol APEOs and propane diols1.5 parts of butyl ether.
Embodiment 3
The present invention is a kind of cracking resistance water-repellent paint, is made up of the raw material of following parts by weight:
4.8 parts, acetylacetone,2,4-pentanedione selenium, 4.6 parts of water-based unsaturated polyester (UP) acrylate resins, 3.3 parts of defoamers, cyclohexanone 2.6Part, 5 parts of bentonites, 4 parts of two phenethyl phenol polyethenoxy ethers, 2.8 parts of long-chain fatty alcohol APEOs and propandiol butyl ether3 parts.
The present invention, compared with existing water-repellent paint, is applicable to the waterproof of the buildings such as basement, toilet, kitchen, pond, makesUsed time, without heating, reduces environmental pollution, has the advantages such as cost is low, constructing operation is simple; Cohesive force is strong, and cracking resistance is carriedHigh waterproof effect; Can be on the basal plane of moist or dry various material construction waterproof functional, nontoxic, use the longevityLife is long, is a kind of comparatively ideal waterproof material.
Certainly, above-mentioned explanation is not limitation of the present invention, the present invention be also not limited to above-mentioned for example, the art generalLogical technical staff, in essential scope of the present invention, variation, remodeling, interpolation or the replacement made, all should belong to of the present inventionProtection domain.
Claims (2)
1. a cracking resistance water-repellent paint, is characterized in that: the raw material by following parts by weight is made:
Acetylacetone,2,4-pentanedione selenium 2.3-4.8 part, water-based unsaturated polyester (UP) acrylate 3.2-4.6 part, defoamer 1.3-3.3 part, cyclohexanone 1.3-2.6 part, bentonite 2.3-5 part, two phenethyl phenol polyethenoxy ether 2.3-4 part, long-chain fatty alcohol APEO 1.5-2.8 part and propandiol butyl ether 1.5-3 part.
2. cracking resistance water-repellent paint according to claim 1, is characterized in that:
Raw material by following parts by weight is made: 1.9 parts of 4.4 parts, acetylacetone,2,4-pentanedione selenium, 3.6 parts of water-based unsaturated polyester (UP) acrylates, 2.5 parts of defoamers, 1.8 parts of cyclohexanone, 3.6 parts of bentonites, 3.3 parts of two phenethyl phenol polyethenoxy ethers, 2.7 parts of long-chain fatty alcohol APEOs and propandiol butyl ethers.