CN102533012A - Water-proof coating and preparation method thereof - Google Patents
Water-proof coating and preparation method thereof Download PDFInfo
- Publication number
- CN102533012A CN102533012A CN201010584775XA CN201010584775A CN102533012A CN 102533012 A CN102533012 A CN 102533012A CN 201010584775X A CN201010584775X A CN 201010584775XA CN 201010584775 A CN201010584775 A CN 201010584775A CN 102533012 A CN102533012 A CN 102533012A
- Authority
- CN
- China
- Prior art keywords
- percent
- water
- proof coating
- plasticizer
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a water-proof coating and a preparation method thereof. The water-proof coating comprises the following raw materials in percentage by weight: 60-70 percent of a bonding agent, 20-30 percent of stone dust, 3-5 percent of titanium pigment, 1-3 percent of a plasticizer and 1-3 percent of an anti-foaming agent, wherein the bonding agent is polyvinyl alcohol; the plasticizer is dibutyl phthalate; and the anti-foaming agent is dimethyl silicone oil. The method comprises the following steps of: putting the weighed bonding agent into a container with a stirrer; adding the stone dust, titanium pigment, plasticizer and anti-foaming agent in sequence; and fully stirring and mixing uniformly. The water-proof coating has the beneficial effects of simple process, low energy-saving cost, high water-proof performance, convenience for construction, no flow, freeness from foam phenomenon, high-temperature resistance, cold resistance, high viscosity, good water sealing effect, high aging resistance, capability of seeping into the surface of a porous inorganic material, high adhesion with an inorganic substrate, superior wear resistance, superior aging resistance, and the like.
Description
Technical field
The present invention relates to the chemistry painting industry field, relate in particular to a kind of waterproof paint and preparation method thereof.
Background technology
The exterior coating kind is more, and the especially appearance of macromolecule emulsion is for this coating has increased many new variety.Its waterproof, resistance of oxidation have certain degree ground to strengthen, and decorate properties also is good.Yet can rainproof effectively, antiscour; And can keep the coating variety of long term less its excellent properties; Therefore often see that decorating and brush neat and artistic buildings often cannot stand wind and rain and wash away and corrode with moisture and color is mottled, the meeting that has is because of coating lost efficacy, the metope erosion is leaked and caused that electric insulation destroys and cause getting an electric shock and catching fire.
Coating is coated in the buildings that is exposed in the atmosphere, is to protect them to avoid the infringement of weather and play the decorative appearance effect.Regrettably, usually the appearance rust is dirty to become ugly very soon because of producing to scribble the outward appearance of buildings of coating.Quite serious surface corrosion can take place with other structural parts in the pipeline of steel and iron, but structurally still very firm.When rainy, above iron rust can drip to rainwater, form a kind of ugly brown stain, be difficult to remove.
At present; Mostly adopt in pitch or the pitch as waterproof paint in construction industry to add emulsified rubber, though pitch is cheap, its waterproof ability is poor; Easy ageing be full of cracks in a short time; And, tangible irregular slit can occur, thereby waterproof layer was lost efficacy because the ground non-uniform settling is flexible with heat.
Summary of the invention
In order to overcome above defective, the technical problem that the present invention will solve is: waterproof paint that a kind of technology is simple, cost is low and preparation method thereof is provided.
In order to overcome the defective that exists in the background technology; The technical solution adopted for the present invention to solve the technical problems is: a kind of waterproof paint comprises the tackiness agent of 60-70% weight, the stone flour of 20-30% weight, the white titanium pigment of 3-5% weight, the softening agent of 1-3%, the skimmer of 1-3%.
According to another preferred embodiment, waterproof paint comprises that further said tackiness agent is a Z 150PH.
According to another preferred embodiment, waterproof paint comprises that further said softening agent is a Witcizer 300.
According to another preferred embodiment, waterproof paint comprises that further said skimmer is a dimethyl silicone oil.
A kind of preparation method of waterproof paint places the container that has whisking appliance with load weighted tackiness agent, adds stone flour, white titanium pigment, softening agent, skimmer then successively, fully mixes.
The invention has the beneficial effects as follows: technology is simple, and energy-conservation cost is low, and water resistance is good, and easy construction; Do not trickle no bubble phenomenon, high temperature resistant, anti-severe cold; Viscosity is high, and sealed waterproof effect is good, and resistance of aging is strong; Can penetrate into the porous inorganic material surface, and good sticking power arranged, have fine qualities such as wear-resisting, ageing-resistant with organic ground.
Embodiment
In conjunction with the preferred embodiments the present invention is done further detailed explanation now.
Embodiment one
The raw material weight proportioning does
Tackiness agent 66%
Stone flour 26%
White titanium pigment 4%
Softening agent 2%
Skimmer 2%
The specific operation process process is following:
Load weighted tackiness agent is placed the container that has whisking appliance, add stone flour, white titanium pigment, softening agent, skimmer then successively, fully mix.
Embodiment two
The raw material weight proportioning does
Tackiness agent 70%
Stone flour 23%
White titanium pigment 3%
Softening agent 3%
Skimmer 1%
The specific operation process process is following:
Load weighted tackiness agent is placed the container that has whisking appliance, add stone flour, white titanium pigment, softening agent, skimmer then successively, fully mix.
With above-mentioned foundation desirable embodiment of the present invention is enlightenment, and through above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this invention technological thought.The technical scope of this invention is not limited to the content on the specification sheets, must confirm its technical scope according to the claim scope.
Claims (5)
1. a waterproof paint is characterized in that: comprise the tackiness agent of 60-70% weight, the stone flour of 20-30% weight, the white titanium pigment of 3-5% weight, the softening agent of 1-3%, the skimmer of 1-3%.
2. waterproof paint as claimed in claim 1 is characterized in that: said tackiness agent is a Z 150PH.
3. waterproof paint as claimed in claim 1 is characterized in that: said softening agent is a Witcizer 300.
4. waterproof paint as claimed in claim 1 is characterized in that: said skimmer is a dimethyl silicone oil.
5. the preparation method of a waterproof paint is characterized in that: load weighted tackiness agent is placed the container that has whisking appliance, add stone flour, white titanium pigment, softening agent, skimmer then successively, fully mix.