CN103602244B - A kind of multi-functional environment-protection water-repellent paint - Google Patents
A kind of multi-functional environment-protection water-repellent paint Download PDFInfo
- Publication number
- CN103602244B CN103602244B CN201310580469.2A CN201310580469A CN103602244B CN 103602244 B CN103602244 B CN 103602244B CN 201310580469 A CN201310580469 A CN 201310580469A CN 103602244 B CN103602244 B CN 103602244B
- Authority
- CN
- China
- Prior art keywords
- parts
- repellent paint
- functional environment
- waterproof
- protection water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of multi-functional environment-protection water-repellent paint, made by the raw material of following parts by weight: sulfonate 1.7-3.4 part of ferricyanate 2.3-4.5 part, polyether Glycols 3-8 part, vanillic aldehyde 4-7 part, calcium chloride 0.8-1.9 part, mica powder 5-10 part, furane resins 2.5-3.8 part, phenol formaldehyde condensate and oxirane-epoxy butane copolymer 3.2-4.7 part. The present invention is compared with existing water-repellent paint, the present invention is applicable to the waterproof of the buildings such as basement, toilet, kitchen, pond, when use without heating, reduce environmental pollution, have that cost is low, constructing operation is simple, can be on the basal plane of moist or dry various material construction waterproof functional, nontoxic, long service life is a kind of comparatively ideal waterproof material.
Description
Technical field
The present invention relates to a kind of multi-functional environment-protection water-repellent paint, belong to building material field.
Background technology
Due to advocating of environmental protection, water paint has become the hot product in market, and the development and application of China's water-repellent paint starts from 60 yearsGeneration, once developed in early days product taking various chemical industry leftover bits and pieces as raw material, all stop development because capability and performance is unstable. For the moment samePhase, China, for improve asphalt configuration water-repellent paint aspect with high polymer, plays chess and has carried out relatively large work. In the sixtiesThere is neoprene in the phase--asphalt waterproofing paint, and there is reclaimed rubber in the initial stage seventies--asphalt waterproofing paint, and in workIn journey, obtain more successfully application. Along with the stable development of China's synthesized polymer material industry, with various high-quality synthetic rubber andSynthetic resin is the water-repellent paint of raw material development, in succession comes into operation: as Two-component Waterproof Polyurethane Coating, third in the eightiesLight water-repellent paint, cationic chloroprene latex asphalt waterproofing paint and the silicon rubber waterproof coating etc. of alkene esters of gallic acid, rubber asphalt classIn China's waterproofing work application, just occupying increasing proportion with synthetic high score subclass water-repellent paint. Taking asphalt as main,Carry out the technological approaches of modification with high polymer, in the existing longer history of China, its raw material sources is extensive, and cost is lower, is suitable forIn the general waterproofing work of the large face light of amount; Taking synthesized polymer material as the main coating of making, performance is more excellent, but price is higher.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is to provide a kind of multi-functional environment-protection waterproof to be coated withMaterial, steady quality, reduces environmental pollution, cheap.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of multi-functional environment-protection water-repellent paint,
Raw material by following parts by weight is made: ferricyanate 2.3-4.5 part, polyether Glycols 3-8 part, vanillic aldehyde 4-7 part,The sulfonate 1.7-3.4 of calcium chloride 0.8-1.9 part, mica powder 5-10 part, furane resins 2.5-3.8 part, phenol formaldehyde condensatePart and oxirane-epoxy butane copolymer 3.2-4.7 part.
Optimize, above-mentioned multi-functional environment-protection water-repellent paint, made by the raw material of following parts by weight:
3.7 parts of ferricyanates, 6 parts of polyether Glycols, 6.5 parts of vanillic aldehydes, 1.2 parts, calcium chloride, 8 parts of mica powders, furans3.9 parts of 2.5 parts, the sulfonate of 3.2 parts of resins, phenol formaldehyde condensate and oxirane-epoxy butane copolymers.
The present invention is compared with existing water-repellent paint, and the present invention is applicable to the anti-of the buildings such as basement, toilet, kitchen, pondWater, without heating, reduces environmental pollution when use, has that cost is low, constructing operation is simple, can be moist or dry multipleOn the basal plane of material, construction waterproof is functional, nontoxic, and long service life is a kind of comparatively ideal waterproof material.
Detailed description of the invention
Embodiment 1
The present invention is a kind of multi-functional environment-protection water-repellent paint, is made up of the raw material of following parts by weight:
3.7 parts of ferricyanates, 6 parts of polyether Glycols, 6.5 parts of vanillic aldehydes, 1.2 parts, calcium chloride, 8 parts of mica powders, furans3.9 parts of 2.5 parts, the sulfonate of 3.2 parts of resins, phenol formaldehyde condensate and oxirane-epoxy butane copolymers.
Embodiment 2
The present invention is a kind of multi-functional environment-protection water-repellent paint, is made up of the raw material of following parts by weight:
2.3 parts of ferricyanates, 3 parts of polyether Glycols, 4 parts of vanillic aldehydes, 0.8 part, calcium chloride, 5 parts of mica powders, furans tree3.2 parts of 1.7 parts, the sulfonate of 2.5 parts, fat, phenol formaldehyde condensate and oxirane-epoxy butane copolymers.
Embodiment 3
The present invention is a kind of multi-functional environment-protection water-repellent paint, is made up of the raw material of following parts by weight:
4.5 parts of ferricyanates, 8 parts of polyether Glycols, 7 parts of vanillic aldehydes, 1.9 parts, calcium chloride, 10 parts of mica powders, furans4.7 parts of 3.4 parts, the sulfonate of 3.8 parts of resins, phenol formaldehyde condensate and oxirane-epoxy butane copolymers.
The present invention is compared with existing water-repellent paint, and the present invention is applicable to the anti-of the buildings such as basement, toilet, kitchen, pondWater, without heating, reduces environmental pollution when use, has that cost is low, constructing operation is simple, can be moist or dry multipleOn the basal plane of material, construction waterproof is functional, nontoxic, and long service life is a kind of comparatively ideal waterproof material.
Certainly, above-mentioned explanation is not limitation of the present invention, the present invention be also not limited to above-mentioned for example, the art generalLogical technical staff, in essential scope of the present invention, variation, remodeling, interpolation or the replacement made, all should belong to of the present inventionProtection domain.
Claims (2)
1. a multi-functional environment-protection water-repellent paint, is characterized in that: the raw material by following parts by weight is made:
Ferricyanate 2.3-4.5 part, polyether Glycols 3-8 part, vanillic aldehyde 4-7 part, calcium chloride 0.8-1.9 part, mica powderSulfonate 1.7-3.4 part and the oxirane-epoxy butane of 5-10 part, furane resins 2.5-3.8 part, phenol formaldehyde condensate are commonPolymers 3.2-4.7 part.
2. multi-functional environment-protection water-repellent paint according to claim 1, is characterized in that:
Raw material by following parts by weight is made: 3.7 parts of ferricyanates, 6 parts of polyether Glycols, 6.5 parts of vanillic aldehydes, chlorination2.5 parts, the sulfonate of 1.2 parts of calcium, 8 parts of mica powders, 3.2 parts of furane resins, phenol formaldehyde condensate and oxirane-epoxy fourth3.9 parts of alkyl copolymers.