CN103602162A - Novel waterproof coating - Google Patents
Novel waterproof coating Download PDFInfo
- Publication number
- CN103602162A CN103602162A CN201310492446.6A CN201310492446A CN103602162A CN 103602162 A CN103602162 A CN 103602162A CN 201310492446 A CN201310492446 A CN 201310492446A CN 103602162 A CN103602162 A CN 103602162A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coating
- zinc oxide
- weight
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel waterproof coating which is prepared by the following raw materials by weight: 3.5-7.6 parts of styrene-acrylic emulsion, 1.3-2.8 parts of zinc oxide, 1.5-2.6 parts of triethanolamine, 2.1-3.5 parts of dibutyl phthalate, 5-10 parts of deionized water, 2.3-3.5 parts of polyoxyethylene octylphenol ether, 1.5-2.8 parts of abietic acid polyoxyethylene ester, and 1.5-3.7 parts of sodium dodecyl benzene sulfonate. Compared with existing waterproof coatings, the coating of the invention has unique waterproofness, and stable chemical properties, is safe and environment-friendly, has certain anticorrosion performance, can be coated directly, and is convenient for operation.
Description
Technical field
The present invention relates to a kind of waterproof coating, belong to building material field.
Background technology
The waterproof problem of buildings is not only related to people's work, living environment, and has influence on the work-ing life of buildings.Therefore, it is that people thirst for the problem solving always.Early stage people make water-proof material with tar felt, pitch.While using this material not only to construct, energy consumption is high, and environmental pollution is serious, poor adhesive force, and also its weathering resistance is poor, and easily harden and embrittlement winter, the fusing of being easily clamminess summer.Therefore there is constructional difficulties, work-ing life is short and water resistance is poor problem in this water-proof material.People have developed the asphalt waterproofing material with synthetic resins, modified synthetic rubber, as materials such as chloroprene rubber pitch, isoprene-isobutylene rubber pitch and reclaimed rubber rubber asphalts.Though these water-proof materials have brought the convenience in construction, it still can not solve the problem that asphalt waterproofing material weathering resistance is poor, work-ing life is short and water resistance is poor.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is, a kind of waterproof coating is provided, and good water-proof effect is manufactured easyly, and cost is low, and the life-span is long.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of waterproof coating,
Raw material by following parts by weight is made: benzene emulsion 3.5-7.6 part, zinc oxide 1.3-2.8 part, trolamine 1.5-2.6 part, dibutyl phthalate 2.1-3.5 part, deionized water 5-10 part, polyoxyethylene octylphenol ether 2.3-3.5 part, sylvic acid polyoxyethylene ester 1.5-2.8 part and Sodium dodecylbenzene sulfonate 1.5-3.7 part.
Optimize, above-mentioned waterproof coating, by the raw material of following parts by weight, made:
3.2 parts of 5.6 parts of benzene emulsions, 2.2 parts, zinc oxide, 1.8 parts of trolamines, 2.6 parts of dibutyl phthalates, 8 parts of deionized waters, 2.7 parts of polyoxyethylene octylphenol ethers, 2.1 parts of sylvic acid polyoxyethylene ester and Sodium dodecylbenzene sulfonatees.
The present invention compares with existing waterproof paint, has unique water resistance, stable chemical performance, and safety and environmental protection, has certain antiseptic property, and directly brushing, easy to operate.
Embodiment
embodiment 1
The present invention is a kind of waterproof coating, by the raw material of following parts by weight, is made:
3.2 parts of 5.6 parts of benzene emulsions, 2.2 parts, zinc oxide, 1.8 parts of trolamines, 2.6 parts of dibutyl phthalates, 8 parts of deionized waters, 2.7 parts of polyoxyethylene octylphenol ethers, 2.1 parts of sylvic acid polyoxyethylene ester and Sodium dodecylbenzene sulfonatees.
embodiment 2
The present invention is a kind of waterproof coating, by the raw material of following parts by weight, is made:
1.5 parts of 3.5 parts of benzene emulsions, 1.3 parts, zinc oxide, 1.5 parts of trolamines, 2.1 parts of dibutyl phthalates, 5 parts of deionized waters, 2.3 parts of polyoxyethylene octylphenol ethers, 1.5 parts of sylvic acid polyoxyethylene ester and Sodium dodecylbenzene sulfonatees.
embodiment 3
The present invention is a kind of waterproof coating, by the raw material of following parts by weight, is made:
3.7 parts of 7.6 parts of benzene emulsions, 2.8 parts, zinc oxide, 2.6 parts of trolamines, 3.5 parts of dibutyl phthalates, 10 parts of deionized waters, 3.5 parts of polyoxyethylene octylphenol ethers, 2.8 parts of sylvic acid polyoxyethylene ester and Sodium dodecylbenzene sulfonatees.
The present invention compares with existing waterproof paint, has unique water resistance, stable chemical performance, and safety and environmental protection, has certain antiseptic property, and directly brushing, easy to operate.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. a waterproof coating, is characterized in that: the raw material by following parts by weight is made:
Benzene emulsion 3.5-7.6 part, zinc oxide 1.3-2.8 part, trolamine 1.5-2.6 part, dibutyl phthalate 2.1-3.5 part, deionized water 5-10 part, polyoxyethylene octylphenol ether 2.3-3.5 part, sylvic acid polyoxyethylene ester 1.5-2.8 part and Sodium dodecylbenzene sulfonate 1.5-3.7 part.
2. waterproof coating according to claim 1, is characterized in that:
Raw material by following parts by weight is made: 3.2 parts of 5.6 parts of benzene emulsions, 2.2 parts, zinc oxide, 1.8 parts of trolamines, 2.6 parts of dibutyl phthalates, 8 parts of deionized waters, 2.7 parts of polyoxyethylene octylphenol ethers, 2.1 parts of sylvic acid polyoxyethylene ester and Sodium dodecylbenzene sulfonatees.