CN104893580A - Nano anti-fouling fiber paint - Google Patents
Nano anti-fouling fiber paint Download PDFInfo
- Publication number
- CN104893580A CN104893580A CN201510271543.1A CN201510271543A CN104893580A CN 104893580 A CN104893580 A CN 104893580A CN 201510271543 A CN201510271543 A CN 201510271543A CN 104893580 A CN104893580 A CN 104893580A
- Authority
- CN
- China
- Prior art keywords
- parts
- maleic anhydride
- acrylic resin
- fiber coating
- chlorinated rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to nano anti-fouling fiber paint. The nano anti-fouling fiber paint comprises cement, a waterproof agent, asphalt, stannous chloride, cuprous oxide, maleic anhydride, short fibers, chlorinated rubber, acrylic resin and vinyl resin. The nano anti-fouling fiber paint comprises the following components in parts by weight: 65 to 90 parts of cement, 30 to 50 parts of a waterproof agent, 30 to 55 parts of asphalt, 20 to 30 parts of stannous chloride, 25 to 40 parts of cuprous oxide, 10 to 15 parts of maleic anhydride, 5 to 12 parts of short fibers, 10 to 12 parts of chlorinated rubber, 7 to 10 parts of acrylic resin and 6 to 10 parts of vinyl resin. The nano anti-fouling fiber paint has characteristics of pollution resistance, water resistance, low price and long service life.
Description
Technical field
The invention belongs to building field, relate to a kind of nano antifouling fiber coating.
Background technology
At present, in construction industry, the top in many houses or side due to its body plan part many, figure is complicated, so its tightness is poor, easy any standing water on top, interior wall get damp, mouldy, bring very large puzzlement to resident family, common water-proof material, although can solve a problem promptly, it is easily aging, and heat-resisting tolerance to cold is poor, water resistance is poor, often needs repeatedly to brush.
House is stained to be referred to house and stands all day to expose to the weather and be corroded and the attachment of dirt, is tarnished in house.The stained meeting in house brings very large puzzlement to resident family.As traditional Organotin antifouling paints because poisonous, be prohibited from using.For preventing the stained loss caused in house, hereby have developed a kind of nano antifouling fiber coating and be coated on room body to increase house fouling resistance ability, the specific function of combining nano filamentary material, need the prerequisite of environmental protection at coatings industry under, the long-acting nontoxic main development direction that will become soil resistant fibre coating containing the soil resistant fibre coating of some nano-scale component and the soil resistant fibre coating of nanometer scale.
Summary of the invention
The technical problem to be solved in the present invention is: overcoming anti-fouling material anti-fouling effect in prior art, to be difficult to meet house moulding changeable, complex structure, easily aging, heat-resisting tolerance to cold is poor to make house waterproof construction, water resistance is poor, often need the technical problem of repeatedly brushing, the nano antifouling fiber coating that a kind of antifouling, waterproof, low price, materials'use life-span are long is provided.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of nano antifouling fiber coating, it is characterized in that: comprise cement, water-resisting agent, pitch, tin protochloride, Red copper oxide, maleic anhydride, staple fibre, chlorinated rubber, acrylic resin and vinyl resins.Its feed components comprises cement 65-90 part, water-resisting agent 30-50 part, pitch 30-55 part, tin protochloride 20-30 part, Red copper oxide 25-40 part, maleic anhydride 10-15 part, staple fibre 5-12 part, chlorinated rubber 10-12 part, acrylic resin 7-10 part and vinyl resins 6-10 part by weight.
As preferably, described nano antifouling fiber coating, it is characterized in that: its feed components by weight, comprises cement 80 parts, water-resisting agent 35 parts, pitch 30 parts, tin protochloride 22 parts, 36 parts, Red copper oxide, maleic anhydride 10 parts, 7 parts, staple fibre, chlorinated rubber 12 parts, acrylic resin 7 parts and vinyl resins 7 parts.
Above-mentioned nano antifouling fiber coating is prepared by following method:
(1) form even to cement, water-resisting agent and asphalt mixing according to formula;
(2) in described step (1), add tin protochloride, Red copper oxide, be again stirred to evenly;
(3) maleic anhydride, staple fibre, chlorinated rubber, acrylic resin and vinyl resins are heated, and stir;
(4) mixture that described step (3) is obtained is poured in the obtained mixture of described step (2), again stir, obtained nano antifouling coating.
As preferably, the Heating temperature in described step (3) is 80-90 degree Celsius.
The invention has the beneficial effects as follows, a kind of nano antifouling fiber coating of the present invention that there is antifouling, waterproof, low price, materials'use life-span long feature.
Embodiment
A kind of nano antifouling fiber coating of the present invention, is characterized in that: comprise cement, water-resisting agent, pitch, tin protochloride, Red copper oxide, maleic anhydride, chlorinated rubber, acrylic resin and vinyl resins.Its feed components comprises cement 65-90 part, water-resisting agent 30-50 part, pitch 30-55 part, tin protochloride 20-30 part, Red copper oxide 25-40 part, maleic anhydride 10-15 part, staple fibre 5-12 part, chlorinated rubber 10-12 part, acrylic resin 7-10 part and vinyl resins 6-10 part by weight.
As preferably, described nano antifouling fiber coating, it is characterized in that: its feed components by weight, comprises cement 80 parts, water-resisting agent 35 parts, pitch 30 parts, tin protochloride 22 parts, 36 parts, Red copper oxide, maleic anhydride 10 parts, 7 parts, staple fibre, chlorinated rubber 12 parts, acrylic resin 7 parts and vinyl resins 7 parts.
Above-mentioned nano antifouling fiber coating is prepared by following method:
(1) form even to cement, water-resisting agent and asphalt mixing according to formula;
(2) in described step (1), add tin protochloride, Red copper oxide, be again stirred to evenly;
(3) maleic anhydride, staple fibre, chlorinated rubber, acrylic resin and vinyl resins are heated, and stir;
(4) mixture that described step (3) is obtained is poured in the obtained mixture of described step (2), again stir, obtained nano antifouling fiber coating.
As preferably, the Heating temperature in described step (3) is 80-90 degree Celsius.
Claims (4)
1. a nano antifouling fiber coating, it is characterized in that: comprise cement, water-resisting agent, pitch, tin protochloride, Red copper oxide, maleic anhydride, staple fibre, chlorinated rubber, acrylic resin and vinyl resins, its feed components comprises cement 65-90 part, water-resisting agent 30-50 part, pitch 30-55 part, tin protochloride 20-30 part, Red copper oxide 25-40 part, maleic anhydride 10-15 part, staple fibre 5-12 part, chlorinated rubber 10-12 part, acrylic resin 7-10 part and vinyl resins 6-10 part by weight.
2. nano antifouling fiber coating as claimed in claim 1, it is characterized in that: its feed components by weight, comprises cement 80 parts, water-resisting agent 35 parts, pitch 30 parts, tin protochloride 22 parts, 36 parts, Red copper oxide, maleic anhydride 10 parts, 7 parts, staple fibre, chlorinated rubber 12 parts, acrylic resin 7 parts and vinyl resins 7 parts.
3. the nano antifouling fiber coating as described in claim 1-2, feature is: it is prepared by following method:
(1) form even to cement, water-resisting agent and asphalt mixing according to formula;
(2) in described step (1), add tin protochloride, Red copper oxide, be again stirred to evenly;
(3) maleic anhydride, staple fibre, chlorinated rubber, acrylic resin and vinyl resins are heated, and stir;
(4) mixture that described step (3) is obtained is poured in the obtained mixture of described step (2), again stir, obtained nano antifouling fiber coating.
4. nano antifouling fiber coating as claimed in claim 3, is characterized in that: the Heating temperature in described step (3) is 80-90 degree Celsius.