CN103639560A - 一种6063铝合金的盐浴钎焊工艺过程 - Google Patents

一种6063铝合金的盐浴钎焊工艺过程 Download PDF

Info

Publication number
CN103639560A
CN103639560A CN201310611596.4A CN201310611596A CN103639560A CN 103639560 A CN103639560 A CN 103639560A CN 201310611596 A CN201310611596 A CN 201310611596A CN 103639560 A CN103639560 A CN 103639560A
Authority
CN
China
Prior art keywords
brazing
salt bath
product
aluminum alloy
aluminium alloys
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310611596.4A
Other languages
English (en)
Inventor
郇文杰
王海伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Lantu Culture Communication Co Ltd Shinan Branch
Original Assignee
Qingdao Lantu Culture Communication Co Ltd Shinan Branch
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Lantu Culture Communication Co Ltd Shinan Branch filed Critical Qingdao Lantu Culture Communication Co Ltd Shinan Branch
Priority to CN201310611596.4A priority Critical patent/CN103639560A/zh
Publication of CN103639560A publication Critical patent/CN103639560A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种钎焊工艺过程，尤其是一种6063铝合金的盐浴钎焊工艺过程。其步骤包括焊前准备、加热、保温、冷却、焊后处理。用此工艺焊接的6063铝合金制件具有良好的机械性能和力学性能。它操作步骤简单、方便、易于掌握，温度为恒温控制，加热均匀、迅速，焊缝质量高，而且一次能完成大量钎缝焊接，生产效率高，是一种品质优良的6063铝合金的盐浴钎焊工艺过程。

Description

一种6063铝合金的盐浴钎焊工艺过程
技术领域
本发明涉及一种钎焊工艺，尤其是一种6063铝合金的盐浴钎焊工艺过程。
背景技术
6063铝合金广泛用于建筑铝门窗、幕墙的框架，具有高塑性、高强度、优良的抗腐蚀性能，适宜压力加工。但由于其熔化温度较低，故其钎焊性差，致使6063铝合金的应用受到很大局限。
发明内容
本发明旨在解决上述问题，提供了6063铝合金的盐浴钎焊工艺过程，它温度为恒温控制，加热均匀、迅速，焊缝质量高，其采用的技术方案如下：
一种6063铝合金的盐浴钎焊工艺过程，工艺步骤依次为：
a) 焊前准备：将基体金属6063铝合金和钎料在60℃温度下用5%（质量分数）的氢氧化钠溶液浸泡1-2分钟除掉表面杂质和油污，再用大量水冲洗、干燥后将制件用夹具夹持好；
b) 加热：将装有钎剂的盐浴槽放入氮气保护的炉中加热，升温至560℃；
c) 保温：将提前装备好的制件放入盐浴槽中保温一定时间；
d) 冷却：将制件取出冷却；
e) 焊后处理：将制件放入沸水中冲洗除去工件表面残留钎剂，再放入盛有5%硝酸溶液的酸洗槽中浸洗5-15分钟，最后放入清水中冲洗，干燥。
附图说明
图1：本发明的盐浴钎焊工艺过程。
具体实施方式
下面结合附图和实例对本发明作进一步说明：
如图1所示，一种6063铝合金的盐浴钎焊工艺过程，所述的钎焊工艺步骤依次为：
a) 焊前准备：将基体金属6063铝合金和钎料在60℃温度下用5%（质量分数）的氢氧化钠溶液浸泡1-2分钟除掉表面杂质和油污，再用大量水冲洗、干燥后将制件用夹具夹持好；
b) 加热：将装有钎剂的盐浴槽放入氮气保护的炉中加热，升温至560℃；
c) 保温：将提前装备好的制件放入盐浴槽中保温一定时间；
d) 冷却：将制件取出冷却；
e) 焊后处理：将制件放入沸水中冲洗除去工件表面残留钎剂，再放入盛有5%硝酸溶液的酸洗槽中浸洗5-15分钟，最后放入清水中冲洗，干燥。
上面以举例方式对本发明进行了说明，但本发明不限于上述具体实施例，凡基于本发明所做的任何改动或变型均属于本发明要求保护的范围。

Claims (1)

1.一种6063铝合金的盐浴钎焊工艺过程，其特征在于，工艺步骤依次为：
a) 焊前准备：将基体金属6063铝合金和钎料在60℃温度下用5%（质量分数）的氢氧化钠溶液浸泡1-2分钟除掉表面杂质和油污，再用大量水冲洗、干燥后将制件用夹具夹持好；
b) 加热：将装有钎剂的盐浴槽放入氮气保护的炉中加热，升温至560℃；
c) 保温：将提前装备好的制件放入盐浴槽中保温一定时间；
d) 冷却：将制件取出冷却；
e) 焊后处理：将制件放入沸水中冲洗除去工件表面残留钎剂，再放入盛有5%硝酸溶液的酸洗槽中浸洗5-15分钟，最后放入清水中冲洗，干燥。
CN201310611596.4A 2013-11-28 2013-11-28 一种6063铝合金的盐浴钎焊工艺过程 Pending CN103639560A (zh)