CN103627887B - 消除低碳低合金耐热钢碳化物析出的热处理方法 - Google Patents

消除低碳低合金耐热钢碳化物析出的热处理方法 Download PDF

Info

Publication number
CN103627887B
CN103627887B CN201310700365.0A CN201310700365A CN103627887B CN 103627887 B CN103627887 B CN 103627887B CN 201310700365 A CN201310700365 A CN 201310700365A CN 103627887 B CN103627887 B CN 103627887B
Authority
CN
China
Prior art keywords
low
ferrite
resisting steel
processing method
thermal processing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310700365.0A
Other languages
English (en)
Other versions
CN103627887A (zh
Inventor
王晓军
胡永平
李连贵
周仲成
李宝臣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia North Heavy Industries Group Co Ltd
Original Assignee
Inner Mongolia North Heavy Industries Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia North Heavy Industries Group Co Ltd filed Critical Inner Mongolia North Heavy Industries Group Co Ltd
Priority to CN201310700365.0A priority Critical patent/CN103627887B/zh
Publication of CN103627887A publication Critical patent/CN103627887A/zh
Application granted granted Critical
Publication of CN103627887B publication Critical patent/CN103627887B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种消除低碳低合金耐热钢碳化物析出的热处理方法，属于钢铁冶金领域。本发明对0.10C-1.10Cr-0.30Mo-0.20V耐热钢零件加热进行奥氏体化，然后将零件预冷至700℃～750℃，进行水冷，5s/100mm～7s/100mm，空冷时间：1s/100mm～2s/100mm，再水冷，9s/100mm～12s/100mm，得到少量铁素体+贝氏体的显微组织，抑制碳化物的析出。本发明由于对零件加热进行奥氏体化，然后预冷至一定温度后，采用快速冷却方式通过铁素体析出的温度区间，得到少量铁素体+贝氏体的显微组织，有效抑制碳化物的析出。

Description

消除低碳低合金耐热钢碳化物析出的热处理方法
技术领域：
本发明涉及一种消除低碳低合金耐热钢碳化物析出的热处理方法，属于钢铁冶金领域。
背景技术：
对于0.10C-1.10Cr-0.30Mo-0.20V耐热钢，零件加热进行奥氏体化后，在600℃～700℃之间冷却速度小于8℃/s，生成大量铁素体组织，在随后冷却到室温的过程中，铁素体中的碳含量将由0.0218%减小到0%，碳化物从铁素体中析出，从而金相组织中出现大量碳化物。
发明内容：
本发明的目的在于提供一种消除低碳低合金耐热钢碳化物析出的热处理方法。
技术解决方案：
本发明方法步骤如下：
1）对0.10C-1.10Cr-0.30Mo-0.20V耐热钢零件加热进行奥氏体化。
2）将步骤1）后的零件预冷至700℃～750℃，进行水冷，水冷时间：5s/100mm～7s/100mm，然后进行空冷，空冷时间：1s/100mm～2s/100mm，再水冷，水冷时间：9s/100mm～12s/100mm，得到少量铁素体+贝氏体的显微组织，抑制碳化物的析出。
本发明进一步：零件预冷至720℃～750℃。
本发明从控制0.10C-1.10Cr-0.30Mo-0.20V耐热钢碳化物析出着手，对零件加热进行奥氏体化，然后预冷至一定温度后，采用快速冷却方式通过铁素体析出的温度区间，得到少量铁素体组织，有效抑制碳化物的析出。
附图说明
图1为本发明工艺图；
图2本发明金相组织照片；
图3为现有技术金相组织照片图。
具体实施方式：
实施例1
本发明对于0.10C-1.10Cr-0.30Mo-0.20V耐热钢，按照图1工艺进行奥氏体化，奥氏体化温度为980±10℃，均、保温时间2h/100mm,然后将零件预冷至700℃～750℃，比铁素体组织转变温度上线高，躲过铁素体组织转变区进行水冷，水冷时间：5s/100mm～7s/100mm，然后进行空冷，空冷时间：1s/100mm～2s/100mm，再水冷，水冷时间：9s/100mm～12s/100mm，得到少量铁素体+贝氏体的显微组织，在随后冷却到室温的过程中，铁素体中的碳含量将由0.0218%减小到0%，碳化物从铁素体中析出；由于组织中铁素体含量少，故从铁素体中析出的碳化物数量少，从而抑制碳化物的析出。
实施例2
本发明对于0.10C-1.10Cr-0.30Mo-0.20V耐热钢，按照图1工艺进行奥氏体化，奥氏体化温度为980±10℃，均、保温时间2h/100mm,然后将零件预冷至720℃～750℃，比铁素体组织转变温度上线高，躲过铁素体组织转变区进行水冷，水冷时间：5s/100mm～7s/100mm，然后进行空冷，空冷时间：1s/100mm～2s/100mm，再水冷，水冷时间：9s/100mm～12s/100mm，得到少量铁素体+贝氏体的显微组织，在随后冷却到室温的过程中，铁素体中的碳含量将由0.0218%减小到0%，碳化物从铁素体中析出；由于组织中铁素体含量少，故从铁素体中析出的碳化物数量少，从而抑制碳化物的析出。

Claims (1)

1.消除低碳低合金耐热钢碳化物析出的热处理方法，其特征在于，方法步骤如下：1）对0.10C-1.10Cr-0.30Mo-0.20V 耐热钢零件加热进行奥氏体化；2）将步骤1）后的零件预冷至700℃～750℃，进行水冷，水冷时间：5s/100mm～7s/100mm，然后进行空冷，空冷时间：1s/100mm ～2s/100mm ，再水冷，水冷时间：9s/100mm ～12s/100mm，得到少量铁素体+贝氏体的显微组织，抑制碳化物的析出。
CN201310700365.0A 2013-08-28 2013-12-19 消除低碳低合金耐热钢碳化物析出的热处理方法 Active CN103627887B (zh)