CN103602907A - 一种粉末冶金回转支承及其制备方法 - Google Patents

一种粉末冶金回转支承及其制备方法 Download PDF

Info

Publication number
CN103602907A
CN103602907A CN201310469322.6A CN201310469322A CN103602907A CN 103602907 A CN103602907 A CN 103602907A CN 201310469322 A CN201310469322 A CN 201310469322A CN 103602907 A CN103602907 A CN 103602907A
Authority
CN
China
Prior art keywords
powder
sintering
under
hour
chromium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310469322.6A
Other languages
English (en)
Other versions
CN103602907B (zh
Inventor
胡光荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu coastal agricultural science and Technology Development Co Ltd
Original Assignee
TONGLING XINCHUANG FLUID TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING XINCHUANG FLUID TECHNOLOGY Co Ltd filed Critical TONGLING XINCHUANG FLUID TECHNOLOGY Co Ltd
Priority to CN201310469322.6A priority Critical patent/CN103602907B/zh
Publication of CN103602907A publication Critical patent/CN103602907A/zh
Application granted granted Critical
Publication of CN103602907B publication Critical patent/CN103602907B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种粉末冶金回转支承，其特征在于，由下列重量份的原料制成：石墨0.8-1.2、硅1.6-1.8、锰1.1-1.3、铬2.6-2.8、铝11.7-12.1、钼1.5-1.7、硼化铬0.2-0.3、ZrO20.4-0.5、SiO20.3-0.5、微晶蜡3.2-3.4、碳化钨0.2-0.3、TiC0.2-0.4、铁粉92-94、助剂1-2；本发明的优点是采用特殊的原料配比，使生产出的回转支承性能指标高，光泽度好，稳定性好，结构韧性、刚度、硬度、耐疲劳性能、抗拉强度性能优良，不易出现断裂等现象，使用寿命长，适用范围广。

Description

一种粉末冶金回转支承及其制备方法
技术领域
本发明涉及粉末冶金领域，特别是一种粉末冶金回转支承及其制备方法。
背景技术
回转支承是一种能够承受综合载荷的大型轴承，可以同时承受较大的轴向、径向负荷和倾覆力矩。回转支承又叫转盘轴承，有些人也称其为：旋转支撑承、 回旋支承。回转支承在现实工业中应用很广泛，被人们称为：“机器的关节”，是两物体之间需作相对回转运动，又需同时承受轴向力、径向力、倾翻力矩的机械所必需的重要传动部件。随着机械行业的迅速发展，回转支承在船舶设备、工程机械、轻工机械、冶金机械、医疗机械、工业机械等行业得到了广泛的应用。
粉末冶金是制取金属粉末或用金属粉末(或金属粉末与非金属粉末的混合物)作为原料，经过成形和烧结，制取金属材料、复合材料以及各种类型制品的工业技术。目前，粉末冶金技术已被广泛应用于交通、机械、电子、航空航天、兵器、生物、新能源、信息和核工业等领域，成为新材料科学中最具发展活力的分支之一。粉末冶金技术具备显著节能、省材、性能优异、产品精度高且稳定性好等一系列优点，非常适合于大批量生产。另外，部分用传统铸造方法和机械加工方法无法制备的材料和复杂零件也可用粉末冶金技术制造，因而备受工业界的重视。粉末冶金结构件制品材料成分不受熔炼限制，既可以加入合金成分，也可以加入其它结构组分，并且在相当大的范围内根据要求进行调整，进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高，既能减少人员，又能提高效率，进而节约成本。粉末冶金技术能取代传统的制造工艺，为广大传统企业节约成本。
所以研究各种机械零部件的粉末冶金的配方，适应不同的需要，具有重要的意义。
发明内容
本发明的目的是提供一种韧性大、塑性高、质量稳定的粉末冶金回转支承及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种粉末冶金回转支承，由下列重量份的原料制成：石墨0.8-1.2、硅1.6-1.8、锰1.1-1.3、铬2.6-2.8、铝11.7-12.1、钼1.5-1.7、硼化铬0.2-0.3、ZrO20.4-0.5、SiO2 0.3-0.5、微晶蜡3.2-3.4、碳化钨0.2-0.3、TiC0.2-0.4、铁粉92-94、助剂1-2；
所述助剂由下列重量份的原料制成：铁粉3-4、高岭土2-3、纳米碳1-2、氟化锆1-2、明矾2-3、海藻酸钠2-3、三聚磷酸钠1-2、刚玉粉2-3、硫酸铜1-2、硬酯酸钙1-2、乙烯基三乙氧基硅烷2-3；制备方法是将铁粉、高岭土、氟化锆、明矾、海藻酸钠、三聚磷酸钠、刚玉粉、硫酸铜混合，研磨成200-300目粉末，然后加入乙烯基三乙氧基硅烷混合均匀，在10-15Mpa下压制成坯料，然后，送入920-950℃下煅烧3-4小时，冷却后，粉碎成300-400目粉末，与其它剩余成分混合，加热至60-70℃，在1200-1500转/分下搅拌1-2小时，即得。
本发明所述粉末冶金回转支承，由以下具体步骤制成：
（1）将锰、铬、铝、钼、铁粉、ZrO2混合，加入适量水中，送入球磨机中球磨，得到250-400目粉末，然后，喷雾干燥、烘干，在8-11Mpa压力下压制成块状，然后在氮气保护气氛下600-650℃进行烧结8-10小时，将烧结后的物料粉碎后过200-400目筛；
（2）将其它剩余成分混合均匀；
（3）将步骤（1）、（2）物料在55-65℃下混合搅拌均匀65-95分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以9-12℃/分钟速率升温至350-450℃条件下烧结1-2小时；然后以5-7℃/分钟速率升温至1075-1160℃条件下烧结2-3小时；最后空气中冷却至室温即可。
本发明的优点是采用特殊的原料配比，使生产出的回转支承性能指标高，光泽度好，稳定性好，结构韧性、刚度、硬度、耐疲劳性能、抗拉强度性能优良，不易出现断裂等现象，使用寿命长，适用范围广。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种粉末冶金回转支承，由下列重量份（公斤）的原料制成：石墨0.8、硅1.6、锰1.1、铬2.6、铝11.7、钼1.5、硼化铬0.2、ZrO20.4、SiO2 0.3、微晶蜡3.2、碳化钨0.2、TiC0.2、铁粉92、助剂1；
所述助剂由下列重量份（公斤）的原料制成：铁粉3、高岭土2、纳米碳2、氟化锆1、明矾2、海藻酸钠3、三聚磷酸钠1、刚玉粉3、硫酸铜1、硬酯酸钙1、乙烯基三乙氧基硅烷3；制备方法是将铁粉、高岭土、氟化锆、明矾、海藻酸钠、三聚磷酸钠、刚玉粉、硫酸铜混合，研磨成200-300目粉末，然后加入乙烯基三乙氧基硅烷混合均匀，在10-15Mpa下压制成坯料，然后，送入920-950℃下煅烧3-4小时，冷却后，粉碎成300-400目粉末，与其它剩余成分混合，加热至60-70℃，在1200-1500转/分下搅拌1-2小时，即得。
本发明所述粉末冶金回转支承，由以下具体步骤制成：
（1）将锰、铬、铝、钼、铁粉、ZrO2混合，加入适量水中，送入球磨机中球磨，得到250-400目粉末，然后，喷雾干燥、烘干，在8-11Mpa压力下压制成块状，然后在氮气保护气氛下600-650℃进行烧结8-10小时，将烧结后的物料粉碎后过200-400目筛；
（2）将其它剩余成分混合均匀；
（3）将步骤（1）、（2）物料在55-65℃下混合搅拌均匀65-95分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以9-12℃/分钟速率升温至350-450℃条件下烧结1-2小时；然后以5-7℃/分钟速率升温至1075-1160℃条件下烧结2-3小时；最后空气中冷却至室温即可。
经过检测，本发明的硬度：HRC130；抗拉强度：880MPa 。

Claims (2)

1.一种粉末冶金回转支承，其特征在于，由下列重量份的原料制成：石墨0.8-1.2、硅1.6-1.8、锰1.1-1.3、铬2.6-2.8、铝11.7-12.1、钼1.5-1.7、硼化铬0.2-0.3、ZrO20.4-0.5、SiO2 0.3-0.5、微晶蜡3.2-3.4、碳化钨0.2-0.3、TiC0.2-0.4、铁粉92-94、助剂1-2；
所述助剂由下列重量份的原料制成：铁粉3-4、高岭土2-3、纳米碳1-2、氟化锆1-2、明矾2-3、海藻酸钠2-3、三聚磷酸钠1-2、刚玉粉2-3、硫酸铜1-2、硬酯酸钙1-2、乙烯基三乙氧基硅烷2-3；制备方法是将铁粉、高岭土、氟化锆、明矾、海藻酸钠、三聚磷酸钠、刚玉粉、硫酸铜混合，研磨成200-300目粉末，然后加入乙烯基三乙氧基硅烷混合均匀，在10-15Mpa下压制成坯料，然后，送入920-950℃下煅烧3-4小时，冷却后，粉碎成300-400目粉末，与其它剩余成分混合，加热至60-70℃，在1200-1500转/分下搅拌1-2小时，即得。
2.根据权利要求1所述粉末冶金回转支承，其特征在于，由以下具体步骤制成：
（1）将锰、铬、铝、钼、铁粉、ZrO2混合，加入适量水中，送入球磨机中球磨，得到250-400目粉末，然后，喷雾干燥、烘干，在8-11Mpa压力下压制成块状，然后在氮气保护气氛下600-650℃进行烧结8-10小时，将烧结后的物料粉碎后过200-400目筛；
（2）将其它剩余成分混合均匀；
（3）将步骤（1）、（2）物料在55-65℃下混合搅拌均匀65-95分钟后，装入模具，压制成坯；
（4）将压坯放在烧结炉中，以9-12℃/分钟速率升温至350-450℃条件下烧结1-2小时；然后以5-7℃/分钟速率升温至1075-1160℃条件下烧结2-3小时；最后空气中冷却至室温即可。
CN201310469322.6A 2013-10-10 2013-10-10 一种粉末冶金回转支承及其制备方法 Expired - Fee Related CN103602907B (zh)