CN103537682A - 一种复合金属轴承材料及其制备方法 - Google Patents
一种复合金属轴承材料及其制备方法 Download PDFInfo
- Publication number
- CN103537682A CN103537682A CN201310472222.9A CN201310472222A CN103537682A CN 103537682 A CN103537682 A CN 103537682A CN 201310472222 A CN201310472222 A CN 201310472222A CN 103537682 A CN103537682 A CN 103537682A
- Authority
- CN
- China
- Prior art keywords
- sintering
- under
- hour
- parts
- metal bearing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种复合金属轴承材料,其特征在于,由下列重量份的原料制成:铝8.4-8.7、锌1.4-1.7、硅2.1-2.3、Cr3.7-3.9、Mn1.1-1.3、Te0.3-0.5、Yb0.1-0.2、ZnO0.2-0.4、氧化硼0.2-0.3、纳米膨润土1.2-1.4、铁粉83-85、助剂1-2;本发明利用粉末冶金技术制备复合金属轴承材料,制造工艺简单易行,生产成本低,生产效率高,而且本发明材料疲劳强度好、耐磨性能好,能够承受很高的载荷,可替代部分昂贵的材料。
Description
技术领域
本发明涉及粉末冶金领域,特别是一种复合金属轴承材料及其制备方法。
背景技术
粉末冶金是制取金属粉末或用金属粉末(或金属粉末与非金属粉末的混合物)作为原料,经过成形和烧结,制取金属材料、复合材料以及各种类型制品的工业技术。目前,粉末冶金技术已被广泛应用于交通、机械、电子、航空航天、兵器、生物、新能源、信息和核工业等领域,成为新材料科学中最具发展活力的分支之一。粉末冶金技术具备显著节能、省材、性能优异、产品精度高且稳定性好等一系列优点,非常适合于大批量生产。另外,部分用传统铸造方法和机械加工方法无法制备的材料和复杂零件也可用粉末冶金技术制造,因而备受工业界的重视。粉末冶金结构件制品材料成分不受熔炼限制,既可以加入合金成分,也可以加入其它结构组分,并且在相当大的范围内根据要求进行调整,进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高,既能减少人员,又能提高效率,进而节约成本。粉末冶金技术能取代传统的制造工艺,为广大传统企业节约成本。
所以研究各种机械零部件的粉末冶金的配方,适应不同的需要,具有重要的意义。
发明内容
本发明的目的是提供一种复合金属轴承材料及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种复合金属轴承材料,由下列重量份的原料制成:铝8.4-8.7、锌1.4-1.7、硅2.1-2.3、Cr3.7-3.9、Mn1.1-1.3、Te0.3-0.5、Yb0. 1-0.2、ZnO 0.2-0.4、氧化硼0.2-0.3、纳米膨润土1.2-1.4、铁粉83-85、助剂1-2;
所述助剂由下列重量份的原料制成:铁粉3-4、高岭土2-3、纳米碳1-2、氟化锆1-2、明矾2-3、海藻酸钠2-3、三聚磷酸钠1-2、刚玉粉2-3、硫酸铜1-2、硬酯酸钙1-2、乙烯基三乙氧基硅烷2-3;制备方法是将铁粉、高岭土、氟化锆、明矾、海藻酸钠、三聚磷酸钠、刚玉粉、硫酸铜混合,研磨成200-300目粉末,然后加入乙烯基三乙氧基硅烷混合均匀,在10-15Mpa下压制成坯料,然后,送入920-950℃下煅烧3-4小时,冷却后,粉碎成300-400目粉末,与其它剩余成分混合,加热至60-70℃,在1200-1500转/分下搅拌1-2小时,即得。
本发明所述复合金属轴承材料,由以下具体步骤制成:
(1)将铝、锌、Cr、Mn、Te、Yb、ZnO、铁粉混合,加入适量水中,送入球磨机中球磨,得到250-400目粉末,然后,喷雾干燥、烘干,在8-10Mpa压力下压制成块状,然后在氮气保护气氛下600-650℃进行烧结8-10小时,将烧结后的物料粉碎后过200-400目筛;
(2)将其它剩余成分混合均匀;
(3)将步骤(1)、(2)物料在55-65℃下混合搅拌均匀65-85分钟后,装入模具,压制成坯;
(4)将压坯放在烧结炉中,以6-8℃/分钟速率升温至800-850℃条件下烧结1.5-2小时;然后以5-7℃/分钟速率升温至1100-1150℃条件下烧结2-3小时;再以8-12℃/分钟速率降温至450-550℃条件下烧结1-2小时,最后空气中冷却至室温即可。
本发明利用粉末冶金技术制备复合金属轴承材料,制造工艺简单易行,生产成本低,生产效率高,而且本发明材料疲劳强度好、耐磨性能好,能够承受很高的载荷,可替代部分昂贵的材料。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种复合金属轴承材料,由下列重量份(公斤)的原料制成:铝8.4、锌1.4、硅2.1、Cr3.7、Mn1.1、Te0.3、Yb0. 1、ZnO 0.2、氧化硼0.2、纳米膨润土1.2、铁粉83、助剂1;
所述助剂由下列重量份(公斤)的原料制成:铁粉3、高岭土2、纳米碳2、氟化锆1、明矾2、海藻酸钠3、三聚磷酸钠1、刚玉粉3、硫酸铜1、硬酯酸钙1、乙烯基三乙氧基硅烷3;制备方法是将铁粉、高岭土、氟化锆、明矾、海藻酸钠、三聚磷酸钠、刚玉粉、硫酸铜混合,研磨成200-300目粉末,然后加入乙烯基三乙氧基硅烷混合均匀,在10-15Mpa下压制成坯料,然后,送入920-950℃下煅烧3-4小时,冷却后,粉碎成300-400目粉末,与其它剩余成分混合,加热至60-70℃,在1200-1500转/分下搅拌1-2小时,即得。
本发明所述复合金属轴承材料,由以下具体步骤制成:
(1)将铝、锌、Cr、Mn、Te、Yb、ZnO、铁粉混合,加入适量水中,送入球磨机中球磨,得到250-400目粉末,然后,喷雾干燥、烘干,在8-10Mpa压力下压制成块状,然后在氮气保护气氛下600-650℃进行烧结8-10小时,将烧结后的物料粉碎后过200-400目筛;
(2)将其它剩余成分混合均匀;
(3)将步骤(1)、(2)物料在55-65℃下混合搅拌均匀65-85分钟后,装入模具,压制成坯;
(4)将压坯放在烧结炉中,以6-8℃/分钟速率升温至800-850℃条件下烧结1.5-2小时;然后以5-7℃/分钟速率升温至1100-1150℃条件下烧结2-3小时;再以8-12℃/分钟速率降温至450-550℃条件下烧结1-2小时,最后空气中冷却至室温即可。
经过检测,本发明复合金属轴承材料的硬度:HRC50;抗拉强度:380MPa 。
Claims (2)
1.一种复合金属轴承材料,其特征在于,由下列重量份的原料制成:铝8.4-8.7、锌1.4-1.7、硅2.1-2.3、Cr3.7-3.9、Mn1.1-1.3、Te0.3-0.5、Yb0. 1-0.2、ZnO 0.2-0.4、氧化硼0.2-0.3、纳米膨润土1.2-1.4、铁粉83-85、助剂1-2;
所述助剂由下列重量份的原料制成:铁粉3-4、高岭土2-3、纳米碳1-2、氟化锆1-2、明矾2-3、海藻酸钠2-3、三聚磷酸钠1-2、刚玉粉2-3、硫酸铜1-2、硬酯酸钙1-2、乙烯基三乙氧基硅烷2-3;制备方法是将铁粉、高岭土、氟化锆、明矾、海藻酸钠、三聚磷酸钠、刚玉粉、硫酸铜混合,研磨成200-300目粉末,然后加入乙烯基三乙氧基硅烷混合均匀,在10-15Mpa下压制成坯料,然后,送入920-950℃下煅烧3-4小时,冷却后,粉碎成300-400目粉末,与其它剩余成分混合,加热至60-70℃,在1200-1500转/分下搅拌1-2小时,即得。
2.根据权利要求1所述复合金属轴承材料,其特征在于,由以下具体步骤制成:
(1)将铝、锌、Cr、Mn、Te、Yb、ZnO、铁粉混合,加入适量水中,送入球磨机中球磨,得到250-400目粉末,然后,喷雾干燥、烘干,在8-10Mpa压力下压制成块状,然后在氮气保护气氛下600-650℃进行烧结8-10小时,将烧结后的物料粉碎后过200-400目筛;
(2)将其它剩余成分混合均匀;
(3)将步骤(1)、(2)物料在55-65℃下混合搅拌均匀65-85分钟后,装入模具,压制成坯;
(4)将压坯放在烧结炉中,以6-8℃/分钟速率升温至800-850℃条件下烧结1.5-2小时;然后以5-7℃/分钟速率升温至1100-1150℃条件下烧结2-3小时;再以8-12℃/分钟速率降温至450-550℃条件下烧结1-2小时,最后空气中冷却至室温即可。