CN103571075A - 一种pvc护套橡皮 - Google Patents
一种pvc护套橡皮 Download PDFInfo
- Publication number
- CN103571075A CN103571075A CN201210251713.6A CN201210251713A CN103571075A CN 103571075 A CN103571075 A CN 103571075A CN 201210251713 A CN201210251713 A CN 201210251713A CN 103571075 A CN103571075 A CN 103571075A
- Authority
- CN
- China
- Prior art keywords
- pvc sheath
- sheath rubber
- pvc
- parts
- mass parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种PVC护套橡皮，该护套橡皮的组成及配比包括，质量份计：PVC树脂 50～70份；稳定剂 5～10份；吸酸剂 3.0～3.5份；增塑剂 40～60份；填充剂 50～100份；润滑剂 1.2～2.0份；加工助剂 0.5～1.0份；高色素碳黑1.0～1.5份；改性橡胶30～50份；复合硫化剂10～12份。本发明采用橡胶来改性PVC塑料,再用热空气硫化方式把PVC热塑性护套硫化成热固性橡胶，以增加PVC电缆的柔软性能、提高耐温等级；并能防铬铁烫及热延伸试验。
Description
技术领域
本发明涉及一种电缆用的护套橡皮，特别涉及一种PVC护套橡皮。
背景技术
在电线电缆的绝缘和护套材料中，PVC比较便宜，机械性能优良，加工方便，使得它长久以来成为电线电缆行业使用数量最多的材料。20世纪末以来，PVC 材料的环境问题被广泛认识，一些发达国家已提出了限制或全面禁止使用PVC 电缆的法令建议。
虽然用无卤料取代PVC材料的呼声越来越高，但是PVC 本身具有价格低廉，阻燃性好，加工设备、工艺简单，硬度可调范围广，电绝缘性好，耐油、耐化学试剂等优势，因此短期内还无法被取代，短期内在世界范围完全禁止PVC的使用并不现实。
把PVC护套改性为XLPVC，即交联PVC，就是热固性橡皮，有重大的应用价值。
发明内容
本发明的目的在于克服已有技术的不足，提供一种PVC护套橡皮。
实现本发明目的的技术方案为：一种PVC护套橡皮，所述护套橡皮的组成及配比包括，质量份计：
上述的一种PVC护套橡皮，所述PVC树脂为悬浮法通用型PVC树脂。
上述的一种PVC护套橡皮，所述稳定剂为通用型钙锌复合稳定剂。
上述的一种PVC护套橡皮，所述吸酸剂为轻质氧化镁。
上述的一种PVC护套橡皮，所述增塑剂为对苯二甲酸二辛酯和环氧大豆油的混合物，在配方总组分中，对苯二甲酸二辛酯为20～30质量份，环氧大豆油为20～30质量份。
上述的一种PVC护套橡皮，所述填充剂为重质碳酸钙。
上述的一种PVC护套橡皮，所述润滑剂为硬脂酸和石蜡的混合物，在配方总组分中，硬脂酸为0.5～1.0质量份，石蜡为0.7～1.0质量份。
上述的一种PVC护套橡皮，所述加工助剂为丙烯酸酯共聚物ACR 401。
上述的一种PVC护套橡皮，所述改性橡胶为NBR与CPE中的一种单用或二种共用，在配方总组分中，NBR为0～50质量份，CPE为0～30质量份。
上述的一种PVC护套橡皮，所述复合硫化剂为宜兴南方镁盐有限公司生产的NFCP-P。
采用了上述技术方案后，本发明具有以下的有益效果：（1）本发明采用橡胶来改性PVC塑料，方法简单，成本低，效果好；（2）本发明采用热空气硫化方式：在烘箱中160 ℃*10 min 把PVC热塑性护套硫化成热固性橡胶；（3）因为硫化成热固性橡胶，就增加了PVC电缆的柔软性能、提高了耐温等级；（4）也因为硫化成热固性橡胶，电缆的PVC护套就能防铬铁烫及热延伸试验。
具体实施方式
（实施例1）
本实施例的一种PVC护套橡皮的组成、配比份数及型号见表一：
表一
本实施例中：
混炼胶片的性能：
门尼粘度M(1+4)100℃为：73Mv
硫变仪上 160 ℃*15 min 的最高转矩 MH为：3.2 N.m
硫变仪上 160 ℃*15 min 的工艺焦烧时间t10 为：0.80 min
硫变仪上 160 ℃*15 min 的工艺正硫化时间t90为：7.50 min
在烘箱中：160 ℃*10 min 硫化后测试
抗张强度为：16.6 N/mm2
伸长率为：320 %
永久变形为：3 %
热延伸试验：硫化后在烘箱中：200 ℃*15 min 后测试
载荷下伸长率为：50 %
冷却后伸长率为：5 %
（实施例2）
本实施例的一种PVC护套橡皮的组成、配比份数及型号见表二：
表二
本实施例中：
混炼胶片的性能：
门尼粘度M(1+4)100℃为：78Mv
硫变仪上 160 ℃*15 min 的最高转矩 MH为：3.5 N.m
硫变仪上 160 ℃*15 min 的工艺焦烧时间t10 为：0.90 min
硫变仪上 160 ℃*15 min 的工艺正硫化时间t90为：8.20 min
在烘箱中：160 ℃*10 min 硫化后测试
抗张强度为：14.4 N/mm2
伸长率为：300 %
永久变形为：10 %
热延伸试验：硫化后在烘箱中：200 ℃*15 min 后测试
载荷下伸长率为：70 %
冷却后伸长率为：10 %
（实施例3）
本实施例的一种PVC护套橡皮的组成、配比份数及型号见表三：
表三
本实施例中：
混炼胶片的性能：
门尼粘度M(1+4)100℃为：85Mv
硫变仪上 160 ℃*15 min 的最高转矩 MH为：4.3 N.m
硫变仪上 160 ℃*15 min 的工艺焦烧时间t10 为：1.05 min
硫变仪上 160 ℃*15 min 的工艺正硫化时间t90为：8.70 min
在烘箱中：160 ℃*10 min 硫化后测试
抗张强度为：14.2 N/mm2
伸长率为：300 %
永久变形为：20 %
热延伸试验：硫化后在烘箱中：200 ℃*15 min 后测试
载荷下伸长率为：80 %
冷却后伸长率为：15 %
（实施例4）
本实施例的一种PVC护套橡皮的组成、配比份数及型号见表四：
表四
本实施例中：
混炼胶片的性能：
门尼粘度M(1+4)100℃为：94Mv
硫变仪上 160 ℃*15 min 的最高转矩 MH为：5.3 N.m
硫变仪上 160 ℃*15 min 的工艺焦烧时间t10 为：1.20 min
硫变仪上 160 ℃*15 min 的工艺正硫化时间t90为：9.10 min
在烘箱中：160 ℃*10 min 硫化后测试
抗张强度为：12.3 N/mm2
伸长率为：290 %
永久变形为：22 %
热延伸试验：硫化后在烘箱中：200 ℃*15 min 后测试
载荷下伸长率为：90 %
冷却后伸长率为：20 %
以上所述的具体实施例，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种PVC护套橡皮，其特征在于：所述护套橡皮的组成及配比包括，质量份计：
2.根据权利要求1所述的一种PVC护套橡皮，其特征在于：所述PVC树脂为悬浮法通用型PVC树脂。
3.根据权利要求1所述的一种PVC护套橡皮，其特征在于：所述稳定剂为通用型钙锌复合稳定剂。
4.根据权利要求1所述的一种PVC护套橡皮，其特征在于：所述吸酸剂为轻质氧化镁。
5.根据权利要求1所述的一种PVC护套橡皮，其特征在于：所述增塑剂为对苯二甲酸二辛酯和环氧大豆油的混合物，在配方总组分中，对苯二甲酸二辛酯为20～30质量份，环氧大豆油为20～30质量份。
6.根据权利要求1所述的一种PVC护套橡皮，其特征在于：所述填充剂为重质碳酸钙。
7.根据权利要求1所述的一种PVC护套橡皮，其特征在于:所述润滑剂为硬脂酸和石蜡的混合物，在配方总组分中，硬脂酸为0.5～1.0质量份，石蜡为0.7～1.0质量份。
8.根据权利要求1所述的一种PVC护套橡皮，其特征在于:所述加工助剂为丙烯酸酯共聚物ACR 401。
9.根据权利要求1所述的一种PVC护套橡皮，其特征在于:所述改性橡胶为NBR与CPE中的一种单用或二种共用，在配方总组分中，NBR为0～50质量份，CPE为0～30质量份。
10.根据权利要求1所述的一种PVC护套橡皮，其特征在于:所述复合硫化剂为宜兴南方镁盐有限公司生产的NFCP-P。