CN103555228B - 一种消失模铸造用冷胶的生产方法 - Google Patents

一种消失模铸造用冷胶的生产方法 Download PDF

Info

Publication number
CN103555228B
CN103555228B CN201310470547.3A CN201310470547A CN103555228B CN 103555228 B CN103555228 B CN 103555228B CN 201310470547 A CN201310470547 A CN 201310470547A CN 103555228 B CN103555228 B CN 103555228B
Authority
CN
China
Prior art keywords
initiator
reactor
monomer
cold glue
production method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310470547.3A
Other languages
English (en)
Other versions
CN103555228A (zh
Inventor
崔刚
杨洋
张晓忠
肖青国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shared New Materials Shandong Co ltd
Original Assignee
NINGXIA KOCEL CHEMICALS CO Ltd
Kocel Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGXIA KOCEL CHEMICALS CO Ltd, Kocel Group Co Ltd filed Critical NINGXIA KOCEL CHEMICALS CO Ltd
Priority to CN201310470547.3A priority Critical patent/CN103555228B/zh
Publication of CN103555228A publication Critical patent/CN103555228A/zh
Application granted granted Critical
Publication of CN103555228B publication Critical patent/CN103555228B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种冷胶的生产方法，尤其是涉及一种消失模铸造用冷胶的生产方法，该方法包括如下步骤：将引发剂溶于溶剂配制成溶液，将配制好的溶液加1/6-1/4至反应釜中，搅拌、向反应釜中加入单体，升温至反应釜内回流后计时保温、每隔25-40分钟补加1/6-1/4配制好的引发剂溶液，当引发剂溶液加完后，继续反应、单体逐渐聚合发粘，取样品检测粘度，当粘度在15000-20000mPa·s时，除去未反应的单体、将0.1-0.2%的引发剂溶于25-30%溶剂，加入反应釜中，搅拌保温30-60分钟后放料即可；本发明提供一种粘结速度快、粘结强度高、合成工艺简单、价格低廉的可满足消失模铸造正常生产使用。

Description

一种消失模铸造用冷胶的生产方法
技术领域
本发明涉及一种冷胶的生产方法，尤其是涉及一种消失模铸造用冷胶的生产方法。
背景技术
消失模铸造，又称实型铸造，是将与铸件尺寸形状相似的石蜡或泡沫模型粘结组合成模型簇，刷涂耐火涂料并烘干后，埋在干石英砂中振动造型，在负压下浇注，使模型气化，液体金属占据模型位置，凝固冷却后形成铸件的新型铸造方法。因为复杂而不能整体发泡成型的模样，一般将其分成若干部分分别发泡成型，再粘合成整体。另外，整体模样进行浇铸也需粘结浇道口等配件。
消失模铸造用粘结剂是在白模粘结面上涂胶，通过白模表面的黏附、内聚和化学键作用，固化产生足够的粘接强度， 将模片粘接在一起。按照消失模粘结剂的形态将其分为固体胶和液体胶，通常将液体胶称为冷胶。
到目前为止，还没有一种粘结速度快、粘结强度高、合成工艺简单的冷胶。
发明内容
本发明的目的是克服现有技术的缺陷，提供一种粘结速度快、粘结强度高、合成工艺简单、价格低廉的可满足消失模铸造正常生产使用的一种消失模铸造用冷胶的生产方法。
本发明通过如下方式实现：
一种消失模铸造用冷胶的生产方法，其特征在于：该方法包括如下步骤：
a、将0.2-0.3%的引发剂溶于20-29%溶剂配制成溶液，将配制好的溶液加1/6-1/4至反应釜中，搅拌；
b、向反应釜中加入40-54%的单体，升温至反应釜内回流后计时保温；
c、每隔25-40分钟补加1/6-1/4配制好的引发剂溶液，当引发剂溶液加完后，继续反应；
d、单体逐渐聚合发粘，取样品检测粘度，当粘度在15000-20000mPa·s时，除去未反应的单体；
e、将0.1-0.2%的引发剂溶于25-30%溶剂，加入反应釜中，搅拌保温30-60分钟后放料即可；
所述单体为醋酸乙烯酯、丙烯酸丁酯、甲基丙烯酸甲酯、丙烯酸、甲基丙烯酸羟乙酯，所述溶剂为无刺激性气味的低沸点溶剂如甲醇、乙醇，所述引发剂为有机过氧化物引发剂或偶氮类引发剂。
本发明有如下效果：
1）合成所需原材料种类多样，价格低廉，容易获得：本发明提供的冷胶的生产方法如下：将0.2-0.3%的引发剂溶于20-29%溶剂配制成溶液，将配制好的溶液加1/6-1/4至反应釜中，搅拌；向反应釜中加入40-54%的单体，升温至反应釜内回流后计时保温；每隔25-40分钟补加1/6-1/4配制好的引发剂溶液，当引发剂溶液加完后，继续反应；单体逐渐聚合发粘，取样品检测粘度，当粘度在15000-20000mPa·s时，除去未反应的单体；将0.1-0.2%的引发剂溶于25-30%溶剂，加入反应釜中，搅拌保温30-60分钟后放料即可；所述单体为醋酸乙烯酯、丙烯酸丁酯、甲基丙烯酸甲酯、丙烯酸、甲基丙烯酸羟乙酯，所述溶剂为低沸点溶剂如甲醇、乙醇，所述引发剂为有机过氧化物引发剂或偶氮类引发剂。
2）本发明提供的冷胶生产合成工艺简单，合成要求不高；冷胶生产所用的设备为常用设备，无特殊要求。
3）本发明提供的冷胶使用效果好，因所使用溶剂为低沸点溶剂，常温易挥发，因此粘结速度快;冷胶合成过程中单体之间发生缩聚反应形成高分子量的有机物,具有粘结强度高的特点。
4）合成的冷胶850℃灼烧无残留，在浇注过程中形成气体排出,不会残留在金属液中对铸件造成危害，可满足消失模铸造要求。
具体实施方式
实施例一：一种消失模铸造用冷胶的生产方法，该方法包括如下步骤：
a、将0.2%的偶氮二异丁氰溶于20%甲醇配制成引发剂-甲醇溶液，将配制好的溶液加1/4至反应釜中，搅拌。
b、向反应釜中加入50%的醋酸乙烯酯，升温反应釜内甲醇开始回流，计时保温。
c、每隔35分钟补加1/4配制好的引发剂-甲醇溶液，当引发剂-甲醇溶液加完后，继续反应。 
d、醋酸乙烯酯单体逐渐聚合发粘，取样品检测粘度，粘度为16000mPa·s（25℃），除去未反应的单体。
e、将0.1%的偶氮二异丁氰溶于29.7%甲醇，加入反应釜中，搅拌保温30分钟后放料。
实施例二：一种消失模铸造用冷胶的生产方法，该方法包括如下步骤：
a、将0.3%的偶氮二异庚氰溶于25%甲醇配制成引发剂-甲醇溶液，将配制好的溶液加1/5至反应釜中，搅拌。
b、向反应釜中加入45%的丙烯酸丁酯，升温，温度升至开始回流后计时保温。
c、每隔30分钟补加1/5配制好的引发剂-甲醇溶液，当引发剂-甲醇溶液加完后，继续反应。 
d、丙烯酸丁酯单体逐渐聚合发粘，取样品检测粘度，粘度为18000mPa·s（25℃），除去未反应的单体。
e、将0.15%的偶氮二异庚氰溶于29.55%甲醇，加入反应釜中，搅拌保温40分钟后放料。
实施例三：一种消失模铸造用冷胶的生产方法，该方法包括如下步骤：
a、将0.25%的过氧化二苯甲酰溶于28%乙醇配制成引发剂-乙醇溶液，将配制好的溶液加1/6至反应釜中，搅拌。
b、向反应釜中加入42%的甲基丙烯酸甲酯，升温至反应釜开始回流后计时保温。
c、每隔20分钟补加1/6配制好的引发剂-乙醇溶液，当引发剂-乙醇溶液加完后，继续反应。 
d、甲基丙烯酸甲酯单体逐渐聚合发粘，取样品检测粘度，粘度为15000Pa·s（25℃）时，除去未反应单体。
e、将0.15%的过氧化二苯甲酰溶于29.6%乙醇，加入反应釜中，搅拌保温50分钟后放料。
实施例四：一种消失模铸造用冷胶的生产方法，该方法包括如下步骤：
a、将0.2%的过氧化叔丁醇溶于29.7%乙醇配制成引发剂-乙醇溶液，将配制好的溶液加1/5至反应釜中，搅拌。
b、向反应釜中加入45%的丙烯酸，升温至反应釜开始回流后计时保温。
c、每隔25分钟补加1/5配制好的引发剂-乙醇溶液，当引发剂-乙醇溶液加完后，继续反应。 
d、丙烯酸单体逐渐聚合发粘，取样品检测粘度，粘度为17000Pa·s（25℃）时，除去未反应单体。
e、将0.10%的过氧化叔丁醇溶于25%乙醇，加入反应釜中，搅拌保温45分钟后放料。
实施例五：一种消失模铸造用冷胶的生产方法，该方法包括如下步骤：
a、将0.18%的偶氮二异丁腈溶于29%甲醇配制成引发剂-甲醇溶液，将配制好的溶液加1/4至反应釜中，搅拌。
b、向反应釜中加入42%的甲基丙烯酸羟乙酯，升温至反应釜开始回流后计时保温。
c、每隔30分钟补加1/4配制好的引发剂-甲醇溶液，当引发剂-甲醇溶液加完后，继续反应。 
d、丙烯酸单体逐渐聚合发粘，取样品检测粘度，粘度为15000Pa·s（25℃）时，除去未反应单体。
e、将0.12%的偶氮二异丁腈溶于28.7%甲醇，加入反应釜中，搅拌保温40分钟后放料。

Claims (2)

1.一种消失模铸造用冷胶的生产方法，其特征在于：该方法包括如下步骤：
a、将0.2-0.3%的引发剂溶于20-29%溶剂配制成溶液，将配制好的溶液加1/6-1/4至反应釜中，搅拌；
b、向反应釜中加入40-54%的单体，升温至反应釜内回流后计时保温；
c、每隔25-40分钟补加1/6-1/4配制好的引发剂溶液，当引发剂溶液加完后，继续反应；
d、单体逐渐聚合发粘，取样品检测粘度，当粘度在15000-20000mPa·s时，除去未反应的单体；
e、将0.1-0.2%的引发剂溶于25-30%溶剂，加入反应釜中，搅拌保温30-60分钟后放料即可，所述单体为醋酸乙烯酯、丙烯酸丁酯、甲基丙烯酸甲酯、丙烯酸、甲基丙烯酸羟乙酯中的任意一种。
2.如权利要求1所述的一种消失模铸造用冷胶的生产方法，其特征在于：所述溶剂为具有无刺激性气味的低沸点的甲醇或乙醇，所述引发剂为有机过氧化物引发剂或偶氮类引发剂。
CN201310470547.3A 2013-10-11 2013-10-11 一种消失模铸造用冷胶的生产方法 Active CN103555228B (zh)