CN103554689A - 用于汽车胶管的低硬度三元乙丙橡胶组合物 - Google Patents

用于汽车胶管的低硬度三元乙丙橡胶组合物 Download PDF

Info

Publication number
CN103554689A
CN103554689A CN201310542670.1A CN201310542670A CN103554689A CN 103554689 A CN103554689 A CN 103554689A CN 201310542670 A CN201310542670 A CN 201310542670A CN 103554689 A CN103554689 A CN 103554689A
Authority
CN
China
Prior art keywords
parts
epdm
low
rubber
rubber hose
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310542670.1A
Other languages
English (en)
Inventor
张洪起
胡金明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Pengling Rubber Hose Co Ltd
Original Assignee
Tianjin Pengling Rubber Hose Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Pengling Rubber Hose Co Ltd filed Critical Tianjin Pengling Rubber Hose Co Ltd
Priority to CN201310542670.1A priority Critical patent/CN103554689A/zh
Publication of CN103554689A publication Critical patent/CN103554689A/zh
Pending legal-status Critical Current

Abstract

本发明一种用于汽车胶管的低硬度三元乙丙橡胶组合物，其组份及质量份数为：100份三元乙丙橡胶4770R，90～130份快压出炭黑N550，68～98份石蜡油3912，5份氧化锌，1份硬脂酸，1份防老剂RD，2份促进剂DTDM，1.6份促进剂TMTD，1份促进剂BZ，1.6份硫磺。通过对以上配方所得结果分析，此发明专利的三元乙丙橡胶配方即满足了在低硬度情况下的胶管弯曲效果，也同时保证了胶料在120℃时的热老化性能。

Description

用于汽车胶管的低硬度三元乙丙橡胶组合物
技术领域
本发明发明涉及橡胶配方技术领域，特别是一种用于汽车胶管的低硬度三元乙丙橡胶组合物。
背景技术
随着汽车行业的发展，汽车发动机舱体越来越小，要求舱体的温度也逐渐升高，对于制品的使用温度也越来越高，所以对于一些产品的要求就会有所提高。在如此狭小的空间中一些适用于弯曲性能良好的直型胶管相应产生，由于此类产品为了提高其弯曲过程中的使用要求，从而在设计时即将其硬度要求由原来的70±5A降低至60±5A。
对于此类产品另外的性能要求如下：
1、满足硬度60±5A；
2、材料性能满足GB/T2491-09；
3、弯曲试验，使用胶管外径8倍芯轴，胶管弯曲后，弯曲后外径/原外径的值大于0.7；
对于上述要求就需要有一种低硬度的三元乙丙橡胶组合物来满足该产品的性能及使用要求。
发明内容
本发明在三元乙丙橡胶为主体材料的基础上，配以硫磺硫化体系来实现以上要求的。本发明的技术方案如下：
一种用于汽车胶管的低硬度三元乙丙橡胶组合物，其组份及质量份数如下：
原材料 质量份数
三元乙丙橡胶4770R 100
快压出炭黑N550 90～130
石蜡油3912 68～98
氧化锌 5
硬脂酸 1
防老剂RD 1
促进剂DTDM 2
促进剂TMTD 1.6
促进剂BZ 1
硫磺 1.6
本发明中通过对调整碳黑、石蜡油以的用量来满足产品使用要求见下表，且生产后的产品外观无瑕疵，其余原材料使用量均不变。
性能表
Figure BDA0000408569050000021
具体实施方式
实施例1：
质量份单位：克
Figure BDA0000408569050000022
Figure BDA0000408569050000031
按所列配方中原材料及用量进行混炼加工：橡胶、原材料称量-一段密炼-一段开炼-下片-二段密炼-二段开炼-下片-硫化胶片-按标准裁取式样-进行试验检测。
下面是三元乙丙橡胶性能检测结果：
Figure BDA0000408569050000032
以上材料采用销钉式挤出机挤出，饱和热蒸汽硫化，然后进行弯曲试验：
实施例2：
质量份单位：克
Figure BDA0000408569050000034
Figure BDA0000408569050000041
按所列配方中原材料及用量进行混炼加工：橡胶、原材料称量-一段密炼-一段开炼-下片-二段密炼-二段开炼-下片-硫化胶片-按标准裁取式样-进行试验检测。
下面是三元乙丙橡胶性能检测结果：
以上材料采用销钉式挤出机挤出，饱和热蒸汽硫化，然后进行弯曲试验：
Figure BDA0000408569050000043
实施例3：
质量份单位：克
原材料 质量份数
三元乙丙橡胶4770R 100
快压出炭黑N550 130
石蜡油3912 98
氧化锌 1
硬脂酸 5
防老剂RD 1
促进剂DTDM 2
促进剂TMTD 2
促进剂BZ 1.6
硫磺 1
合计 341.6
按所列配方中原材料及用量进行混炼加工：橡胶、原材料称量-一段密炼-一段开炼-下片-二段密炼-二段开炼-下片-硫化胶片-按标准裁取式样-进行试验检测。
下面是三元乙丙橡胶性能检测结果：
Figure BDA0000408569050000061
以上材料采用销钉式挤出机挤出，饱和热蒸汽硫化，然后进行弯曲试验：
Figure BDA0000408569050000062
实施例4：
质量份单位：克
原材料 质量份数
三元乙丙橡胶4770R 100
快压出炭黑N550 90
石蜡油3912 68
氧化锌 1
硬脂酸 5
防老剂RD 1
促进剂DTDM 2.5
促进剂TMTD 2
促进剂BZ 1.6
硫磺 1
合计 272.1
按所列配方中原材料及用量进行混炼加工：橡胶、原材料称量-一段密炼-一段开炼-下片-二段密炼-二段开炼-下片-硫化胶片-按标准裁取式样-进行试验检测。
下面是三元乙丙橡胶性能检测结果：
Figure BDA0000408569050000063
以上材料采用销钉式挤出机挤出，饱和热蒸汽硫化，然后进行弯曲试验：
Figure BDA0000408569050000072
实施例5
质量份单位：克
原材料 质量份数
三元乙丙橡胶4770R 100
快压出炭黑N550 90
石蜡油3912 98
氧化锌 1
硬脂酸 5
防老剂RD 1
促进剂DTDM 5
促进剂TMTD 2
促进剂BZ 1.6
硫磺 1
合计 304.6
按所列配方中原材料及用量进行混炼加工：橡胶、原材料称量-一段密炼-一段开炼-下片-二段密炼-二段开炼-下片-硫化胶片-按标准裁取式样-进行试验检测。
下面是三元乙丙橡胶性能检测结果：
Figure BDA0000408569050000073
Figure BDA0000408569050000081
以上材料采用销钉式挤出机挤出，饱和热蒸汽硫化，然后进行弯曲试验：
Figure BDA0000408569050000082
通过对以上配方所得结果分析，此发明专利的三元乙丙橡胶配方即满足了在低硬度情况下的胶管弯曲效果，也同时保证了胶料在120℃时的热老化性能。
本发明提出的低硬度三元乙丙橡胶组合物，已通过以上进行了详细描述，相关技术人员明显能在不脱离本发明内容、精神和范围内对本文所述的配方和制备方法进行改动或适当变更与组合来实现本发明技术。特别需要指出的是，所有相类似的替换和改动对本领域技术人员来说是显而易见的，他们都被视为包括在本发明精神、范围和内容中。

Claims (1)

1.一种用于汽车胶管的低硬度三元乙丙橡胶组合物，其组份及质量份数如下：
Figure FDA0000408569040000011
CN201310542670.1A 2013-11-05 2013-11-05 用于汽车胶管的低硬度三元乙丙橡胶组合物 Pending CN103554689A (zh)