CN1035480C - 复合聚苯乙烯高效防腐涂料及制造方法 - Google Patents

复合聚苯乙烯高效防腐涂料及制造方法 Download PDF

Info

Publication number
CN1035480C
CN1035480C CN91110808A CN91110808A CN1035480C CN 1035480 C CN1035480 C CN 1035480C CN 91110808 A CN91110808 A CN 91110808A CN 91110808 A CN91110808 A CN 91110808A CN 1035480 C CN1035480 C CN 1035480C
Authority
CN
China
Prior art keywords
polystyrene
liquid
paint
coating
butyl acetate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN91110808A
Other languages
English (en)
Other versions
CN1072705A (zh
Inventor
王巧生
肖珩
吴荫顺
张荣良
英广恕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Shijingshan Environmental Protection Coating Factory
University of Science and Technology Beijing USTB
Original Assignee
Beijing Shijingshan Environmental Protection Coating Factory
University of Science and Technology Beijing USTB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Shijingshan Environmental Protection Coating Factory, University of Science and Technology Beijing USTB filed Critical Beijing Shijingshan Environmental Protection Coating Factory
Priority to CN91110808A priority Critical patent/CN1035480C/zh
Publication of CN1072705A publication Critical patent/CN1072705A/zh
Application granted granted Critical
Publication of CN1035480C publication Critical patent/CN1035480C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明属于表面处理领域中含聚苯乙烯的涂覆材料及制造方法，特别是用于钢铁构件、厂房、地下管线等设施的防腐涂料。该涂料主要含聚苯乙烯、煤焦油沥青、醋酸丁脂、古马隆树脂，经过特定的处理，加热、充分搅拌混合后，不仅具有良好的防腐性能，而且能够有效合理地回收利用废旧聚苯乙烯泡沫塑料，使废聚苯乙烯再生利用，成为防止大气、土壤腐蚀的理想涂料。

Description

复合聚苯乙烯高效防腐涂料及制造方法
本发明属于表面处理领域中含聚苯乙烯的涂复材料，特别是用于钢铁构件、厂房、地下管线等设施的防腐涂料。
随着国民经济的发展，我国以聚苯乙烯泡沫塑料为主的包装材料发展很快，年产量已达几十万吨，这些材料主要用于家用电器、仪器、仪表的防震包装，以及快餐食品盒，且都是一次性使用，用后的废品越积越多，不仅堆放场地面积大，而且容易燃烧，不利于安全生产。若将大量的废弃料烧掉，会造成大气污染，因此废弃聚苯乙烯泡沫已成为一大公害。目前，已有一些专利文献报道，利用废旧聚苯乙烯泡沫塑料经过简单改性，可以得到清漆、外墙涂料、快干漆、防水涂料等，尽管这些涂料具有一定的防腐作用，但有的漆膜附着力不好，在大气、土壤环境中防腐性能并不理想。
本发明的目的在于有效合理地回收利用废弃聚苯乙烯泡沫塑料，使废聚苯乙烯再生利用制成能够防大气、土壤腐蚀的涂料。
实现本发明目的的步骤是：
1.配制A液。将废旧聚苯乙烯泡沫塑料洗净，破碎，溶于二氯丙烷或二甲苯溶剂中，按30-34wt％溶解，同时搅拌，液体组成是聚苯乙烯∶溶剂＝(30-34)∶(70-66)。
2.配制B液。按重量百分比，将50-70％煤焦油沥青加热至熔化，沥青温度为200-220℃，缓冷至180-200℃，加入200号溶剂汽油10-15％，边兑入边搅拌，温度降至130-140℃，加入二氯丙烷或二甲苯20-35％，缓冷至90-95℃，搅拌保温，制成含50-70％煤焦油沥青的B液。
3.配制混合液。按重量百分比，加入A液40-48％，B液10-6％，再加入醋酸丁酯1-0.5％，古马隆树脂1-0.5％，铁红18-15％，滑石粉18-20％，锌黄8-3％，二丁酯2-1％，在40-60℃进行充分混合搅拌。
4.将搅拌均匀的物料送入研磨机进行研磨分散2-2.5小时，可加2-6％的少量溶剂调整粘度。
5.检验细度(≤80)及粘度(80-150秒)，合格后，分装为成品。
本发明具备以下优点：
1.利用废旧泡沫塑料为主要成膜物质，本身成本低，同时解决了城市环境污染的难题。
2.本涂料为单组分，克服了双组分涂料在配比、固化等因素引起的质量问题。特别是给现场施工、操作人员带来很大的方便。
3.本涂料为底漆面漆一体化，使用方便，操作简单。
4.本涂料为原浆型重防腐涂料，一次成膜厚，干燥速度快，是大气、地下管线防腐的理想涂料。
5.本涂料除有一般涂料性能外，还具有抗老化、耐盐雾、耐微生物浸蚀等特性。
下面结合实施例进一步说明本发明的实现过程和特点：
按上述生产制造步骤配制A液，聚苯乙烯∶溶剂＝32∶68。配制B液，煤焦油沥青60％，200号汽油14％，二氯丙烷26％。取A液44kg、B液10kg、加入醋酸丁酯1kg、古马隆树脂1kg、铁红15kg、滑石粉18kg、锌黄5kg、二丁酯2kg，在45℃进行充分混合搅拌，搅拌均匀的物料送入研磨机进行研磨分散2小时，加4kg溶剂调整粘度。
经质量监督检验证明，该涂料具有以下技术特点：
序号     项目   计量单位   技术指标   备注
  1   漆膜外观   平整光滑 底漆及各色面漆
  2 粘度(涂4粘度计)     S     ≥60
  3 细度(刮板计)     μm     ≤80
  4 遮盖力     ％/m2     ≤150
  5 干燥时间  表干实干     minh     ≤25≤6
  6 固体含量     ％     ≥70
  7 柔韧性     mm     1
  8 附着力(划圈法)     级     1
  9 摆杆硬度     ≥0.4
  10 冲击强度     kg cm     50
  11 耐水性     浸24h     无变化
  12 盐雾(168h)     级     1  3.5％NaCl40±2℃
  13 湿热(168h)     级     1  96＋2％47±1℃
  14 耐霉菌     级     0
  15 耐老化     Y     10  300h
  16 耐碱性     20d     无变化  NaOH
  17 耐酸性     30d     无变化 25％H2SO410％HCl

Claims (2)

1.一种利用聚苯乙烯塑料泡沫制成的涂料，特别是用于防大气土壤腐蚀的涂料，其特征在于涂料成分(按重量的百分比)为，含30-34％聚苯乙烯的A液40-48％，含50-70％煤焦油沥青的B液10-6％，醋酸丁酯1-0.5％，古马隆树脂1-0.5％，铁红18-15％，滑石粉18-20％，锌黄8-3％，二丁酯2-1％。
2.一种如权利要求1所述涂料的制备方法，其特征在于：
(1)将废旧聚苯乙烯泡沫塑料洗净，破碎，按30-34％(重量百分比)溶于二氯丙烷或二甲苯中，同时搅拌制成A液；
(2)将50-70％煤焦油沥青加热至熔化，沥青温度为200-220℃，缓冷至180°-200℃，加入200号溶剂汽油10-15％，边兑入边搅拌，温度降至130-140℃，加入溶剂二氯丙烷或二甲苯，20-35％，缓冷至90°-95℃，搅拌保温，制成B液；
(3)混合A、B液，再加入醋酸丁酯、古马隆树脂、铁红、滑石粉、锌黄、二丁酯，在40-60℃进行充分混合搅拌；
(4)搅拌后进行研磨分散2-2.5小时，加溶剂调整粘度。
CN91110808A 1991-11-23 1991-11-23 复合聚苯乙烯高效防腐涂料及制造方法 Expired - Fee Related CN1035480C (zh)