CN101328389A - 纳米级环保型彩色水性防水涂装材料 - Google Patents
纳米级环保型彩色水性防水涂装材料 Download PDFInfo
- Publication number
- CN101328389A CN101328389A CNA200810142603XA CN200810142603A CN101328389A CN 101328389 A CN101328389 A CN 101328389A CN A200810142603X A CNA200810142603X A CN A200810142603XA CN 200810142603 A CN200810142603 A CN 200810142603A CN 101328389 A CN101328389 A CN 101328389A
- Authority
- CN
- China
- Prior art keywords
- agent
- nano
- coating material
- friendly type
- type color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及到一种涂装材料,尤其涉及到一种纳米级环保型彩色水性防水涂装材料。其以弹性乳液为基料,添加防霉剂、重质碳酸钙、成膜助剂、增塑剂、消泡剂、增稠剂、防冻剂、润湿剂、流平剂和钛白粉各种剂料,其还添加有纳米硅浆料和纳米钛浆料为原料品,将上述的原料品通过分散机,经过搅拌工序和研磨工序后得到涂装材料成品。其有益效果是:通过添加纳米二氧化硅、纳米二氧化钛和纳米氧化锌,降低了紫外线对产品的降解能力,因为纳米是最小的计量单位,紫外线很难将其降解,产品的使用寿命可达三十年以上。而选用的生产原料均为环保型,在生产和施工过程中,没有废水、废气以及废渣,没有任何污染。
Description
技术领域
本发明涉及到一种涂装材料,尤其涉及到一种纳米级环保型彩色水性防水涂装材料。
背景技术
传统的防水、涂装材料大部分对生产和施工环境及人员产生污染和危害,使用期较短,目前防水及外墙涂装材料都具有使用寿命短,不耐老化,易变色等不足之处。
如中国专利申请号为200510002575.8,名称为‘多功能防水涂料’的文件中所述:其包括弹性丙烯酸酯合成乳液、水、硅溶胶、钛白粉、重质碳酸钙、硅灰石粉、粉煤灰漂剂、防腐杀菌剂、消泡剂、流平剂、增稠剂、增塑剂、柔软剂、PH值调节剂等,还添加了粉煤灰漂珠、纳米空心微珠、反光剂、柔软剂等进行科学配比制成。不过这只是部分解决了易老化和使用寿命短的问题,并没有完全解决现有涂装材料的不足之处。
基于现有涂装材料的不足之处,本发明人设计了一种新的“纳米级环保型彩色水性防水涂装材料”。
发明内容
本发明针对上述现有技术的不足所要解决的技术问题是:提供一种完全解决现有涂装材料不足之处的纳米级环保型彩色水性防水涂装材料。
本发明解决其技术问题所采用的技术方案是:
一种纳米级环保型彩色水性防水涂装材料,以弹性乳液为基料,添加防霉剂、重质碳酸钙、成膜助剂、增塑剂、消泡剂、增稠剂、防冻剂、润湿剂、流平剂和钛白粉各种剂料,其还添加有纳米硅浆料和纳米钛浆料为原料品,将上述的原料品通过分散机,经过搅拌工序和研磨工序后得到涂装材料成品。
所述的原料品通过分散机,在常温常压下通过200-1000的搅拌2小时后再经过研磨机研磨30分钟得到涂装材料成品。
所述的原料品还添加有分散剂、颜料、柔软剂、PH值调节剂和白云母粉。分散剂用于促进分散过程,获得精细的微粒尺寸,使颜料在树脂溶液中呈稳定状态;颜料可以根据使用者的不同需要调制不同颜色的涂料;柔软剂用于使涂料具有良好的柔软性与丰厚感,不会有黏腻的手感,使涂料制品的稳定性高和具有良好的机械力稳定性;PH值调节剂用于调节涂料的PH值;白云母粉用于减少紫外线或其它光和热对漆膜的破坏,增加涂层的耐酸、碱和电绝缘性能,提高涂层的抗冻性、抗腐蚀性、坚韧性和密实性、降低涂层的透气性,防止斑点和龟裂。
所述的原料品还添加有工业香精,工业香精用于中和涂料本身的刺激性味道。。
所述的各成分含量为:弹性乳液:37%-45%,分散剂:0.4%,防霉剂:0.15%,重质碳酸钙:34.55%-42.55%,颜料:1%,成膜助剂:1.5%,增塑剂:4%,消泡剂:0.8%,增稠剂:0.5%,防冻剂:1.4%,润湿剂:0.1%,流平剂:0.6%,钛白粉(金红石型):5%,白云母粉:4%,纳米二氧化硅:0.5%,纳米二氧化钛:0.3%,纳米氧化锌:0.2%。
另一优选方式是:所述的各成分含量为:弹性乳液:38.55%,分散剂:0.4%,防霉剂:0.15%,重质碳酸钙:600目41%,颜料:1%,成膜助剂:1.5%,增塑剂:4%,消泡剂:0.8%,增稠剂:0.5%,防冻剂:1.4%,润湿剂:0.1%,流平剂:0.6%,钛白粉(金红石型):5%,白云母粉:4%,纳米二氧化硅:0.5%,纳米二氧化钛:0.3%,纳米氧化锌:0.2%。
本发明为水性单组份,通过施工固化后形成没有接缝的整体防水层,在任何复杂的基层表面适应性强,对复杂部位施工有明显优越性,采用喷涂方式施工,既方便又缩短工期,适应各种部位及基面防水。
本发明是以聚合物弹性乳液为基料,与多种高分子化工原料和少量纳米级材料在常温常压下聚合反应而产生的一种新型环保水性乳胶防水涂装材料,通过添加纳米二氧化硅、纳米二氧化钛和纳米氧化锌改变了产品的使用功能和品质,通过纳米二氧化硅改性,形成双疏效应,提高自洁力,通过纳米二氧化钛改性降低紫外线对漆膜分子链的降解能力,通过二氧化锌改性,提高漆膜的防腐防霉能力,降低了紫外线对产品的降解能力,因为纳米是最小的计量单位,紫外线很难将其降解,因此产品的使用寿命可达三十年以上。而选用的生产原料均为环保型,在生产和施工过程中,没有废水、废汽和废渣,没有任何污染。
本发明纳米级环保型彩色水性防水涂装材料的有益效果是:
通过添加纳米二氧化硅、纳米二氧化钛和纳米氧化锌,降低了紫外线对产品的降解能力,因为纳米是最小的计量单位,紫外线很难将其降解,产品的使用寿命可达三十年以上。而选用的生产原料均为环保型,在生产和施工过程中,没有废水、废汽以及废渣,没有任何污染。具体具有以下优点:
1、耐老化性能优良,在紫外线、热、光、氧作用下性能稳定,材料使用寿命长,一般可达30年以上。
2、粘接力强,材料与水泥基面粘接强度可达0.8m Pa以上,对各种基材有较好的粘接能力,在水泥、玻璃、陶瓷、石棉瓦、塑料、彩钢板及原有防水材料基面等基材上均可施工,每平方米1.5KG。
3、材料延伸性能好,延伸率可达330%以上,因此抗裂性能优异,还具有优良的抗冻性和低温柔性。
4、施工性能好,不起泡,成膜效果好,固化快,表干1-2小时,实干6小时,可以缩短工期。
5、本产品为无毒材料,施工简单,无污染,对基层含湿量要求不严,含水率小于20%均可施工。
6、不限工场,在任何规则或不规则开头基面喷涂或刷、刮,都能形成连续不断的橡胶防水层,在施工现场水可做溶剂,用水稀释产品达到喷涂浓度,采用喷涂工艺施工水不参加反应,挥发后可形成整体涂膜。
7、本产品色泽鲜艳,具有反射功能,彻底改变了防水涂装的黑色面貌,能起到隔热、保温和装饰美化的作用。
8、本产品还可以作为粘接剂和密封膏。
具体实施方式
本发明是这样实施的:
实施例一:
弹性乳液:400kg 防霉剂:1.5kg
分散剂:4kg 重质碳酸钙:600目420kg
颜料:10kg 流平剂:6kg
成膜助剂:15kg 钛白粉(金红石型):50kg
增塑剂:40kg 白云母粉:40kg
消泡剂:8kg 内米二氧化硅:5kg
增稠剂:5kg 内米二氧化钛:3kg
防冻剂:14kg 内米氧化锌:2kg
润湿剂:1kg
上述材料通过分散机,在常温常压下通过500转/分的搅拌2小时再经过研磨机研磨30分钟即可。
本发明经测试的参数如下:基料:丙烯酸共聚物,手感光滑舒适,与基面有良好的附着力,耐洗刷性佳,使墙面倍感亮丽,适用内外墙装修。既绿色环保又施工方便,产品质量符合LC/T645-1996国家行业标准,主要技术指标参照JIS-A6008,JIS-6021国际标准,使用寿命达到30年以上,通过了十环认证,ISO9001认证,是国家环保局与财政局认可产品。
以上所述,仅是本发明一种纳米级环保型彩色水性防水涂装材料的较佳实施例而已,并非对本发明的技术范围作任何限制,凡是依据本发明的技术实质对上面实施例所作的任何细微修改、等同变化与修饰,均仍属于本发明技术内容的范围内。
Claims (7)
1、一种纳米级环保型彩色水性防水涂装材料,以弹性乳液为基料,添加防霉剂、重质碳酸钙、成膜助剂、增塑剂、消泡剂、增稠剂、防冻剂、润湿剂、流平剂和钛白粉各种剂料,本发明的特征在于:其还添加有纳米二氧化硅和纳米二氧化钛成为原料品;
纳米二氧化硅改性,形成双疏效应,提高自洁力;
纳米二氧化钛改性降低紫外线对漆膜分子链的降解能力;
将上述的原料品通过分散机,经过搅拌工序和研磨工序后得到涂装材料成品。
2、根据权利要求1所述的纳米级环保型彩色水性防水涂装材料,其特征在于所述的原料品还添加有纳米氧化锌,二氧化锌用于改性,提高漆膜的防腐防霉能力,降低紫外线对涂料的降解能力。
3、根据权利要求1或2所述的纳米级环保型彩色水性防水涂装材料,其特征在于所述的原料品通过分散机,在常温常压下通过200-1000转/分的搅拌2小时后再经过研磨机研磨30分钟得到涂装材料成品。
4、根据权利要求1或2所述的纳米级环保型彩色水性防水涂装材料,其特征在于所述的原料品还添加有分散剂、颜料、柔软剂、PH值调节剂和白云母粉,分散剂用于促进分散过程,获得精细的微粒尺寸,使颜料在树脂溶液中呈稳定状态;颜料可以根据使用者的不同需要调制不同颜色的涂料;柔软剂用于使涂料具有良好的柔软性与丰厚感,不会有黏腻的手感,使涂料制品的稳定性高和具有良好的机械力稳定性;PH值调节剂用于调节涂料的PH值;白云母粉用于减少紫外线或其它光和热对漆膜的破坏,增加涂层的耐酸、碱和电绝缘性能,提高涂层的抗冻性、抗腐蚀性、坚韧性和密实性、降低涂层的透气性,防止斑点和龟裂。
5、根据权利要求1或2所述的纳米级环保型彩色水性防水涂装材料,其特征在于所述的原料品还添加有工业香精,工业香精用于中和涂料本身的刺激性味道。
6、根据权利要求4所述的纳米级环保型彩色水性防水涂装材料,其特征在于所述的各成分含量为:
弹性乳液:37%-45%,分散剂:0.4%,防霉剂:0.15%,重质碳酸钙:34.55%-42.55%,颜料:1%,成膜助剂:1.5%,增塑剂:4%,消泡剂:0.8%,增稠剂:0.5%,防冻剂:1.4%,润湿剂:0.1%,流平剂:0.6%,钛白粉(金红石型):5%,白云母粉:4%,纳米二氧化硅:0.5%,纳米二氧化钛:0.3%,纳米氧化锌:0.2%。
7、根据权利要求5所述的纳米级环保型彩色水性防水涂装材料,其特征在于所述的各成分含量为:
弹性乳液:38.55%,分散剂:0.4%,防霉剂:0.15%,重质碳酸钙:600目41%,颜料:1%,成膜助剂:1.5%,增塑剂:4%,消泡剂:0.8%,增稠剂:0.5%,防冻剂:1.4%,润湿剂:0.1%,流平剂:0.6%,钛白粉(金红石型):5%,白云母粉:4%,纳米二氧化硅:0.5%,纳米二氧化钛:0.3%,纳米氧化锌:0.2%。