CN103525345A - Flocking bonding agent - Google Patents
Flocking bonding agent Download PDFInfo
- Publication number
- CN103525345A CN103525345A CN201310469062.2A CN201310469062A CN103525345A CN 103525345 A CN103525345 A CN 103525345A CN 201310469062 A CN201310469062 A CN 201310469062A CN 103525345 A CN103525345 A CN 103525345A
- Authority
- CN
- China
- Prior art keywords
- parts
- materials
- bonding agent
- ethanol
- diluted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A flocking bonding agent is characterized by comprising the components by weight: 25-50 parts of methyl acrylate, 6-10 parts of hydroxy-propyl acrylate, 260-300 parts of ethyl acrylate, 9-15 parts of acrylic acid, 6-10 parts of N-methacrylamide, 90-120 parts of E-S1 epoxy resin, 1-5 parts of benzoyl peroxide, 1-3 parts of N,N-dimethyl benzylamine, and 50-80 parts of vinyl acetate. The solid materials are dissolved by ethanol at the temperature of 70-75 DEG C and then are diluted into a 15% ethanol solution, all the materials are added and are subjected to a stirring reaction for 12-22 hours at the room temperature, and the product is obtained. The flocking bonding agent has the advantages of easily-obtained raw materials, low cost, green environmental protection, convenient use, and good effect.
Description
Technical field
The invention belongs to a kind of tackiness agent.
Background technology
Tackiness agent (Bonding agent) is one of most important subsidiary material, and in package handling, application is very extensive.Tackiness agent is the sticking material of tool, by its viscosity, two kinds of separated materials can be linked together.The kind of tackiness agent is a lot.1. natural glue it be taken from the material of occurring in nature.Comprise the biological adhesives such as starch, protein, dextrin, gelatin, shellac, hide glue, rosin; Also comprise the mineral binders such as pitch.2. artificial tackiness agent this be to use made material, comprise the inorganic adhesives such as water glass, and the organic binder bond such as synthetic resins, synthetic rubber.The features such as splicing (bonding, bonding, cementing, gluing) refers to that homogeneity or heterogeneous body surface stick with glue the technology that agent links together, and has stress distribution continuous, lightweight, or sealing, and most technological temperatures are low.Glued joint the connection that is specially adapted to unlike material, different thickness, ultra-thin specification and complex component.Glued joint RECENT DEVELOPMENTS the fastest, application industry is extremely wide, and high-and-new science and technology progress and people's daily life improvement are had to great effect.Therefore, research, all kinds of tackiness agent of development and production are very important.
Through Chinese publication retrieval, do not find the scheme identical with present patent application.
Summary of the invention:
The object of the invention is to; A kind of Flock Adhesive stick is proposed.
Flock Adhesive stick of the present invention, it is characterized in that: by weight, by methyl acrylate 25-50 part, Propylene glycol monoacrylate 6-10 part, ethyl propenoate 260-300 part, vinylformic acid 9-15 part, N-methacrylic acid acid amides 6-10 part, E-S1 epoxy is counted fat 90-120 part, benzoyl peroxide 1-5 part, N, N-dimethyl benzylamine 1-3 part, vinyl acetate 50-80 part forms, after solid materials is dissolved at 70-75 ℃ with ethanol, be diluted to 15% ethanolic soln, whole materials are added, and at room temperature stirring reaction 12-22 hour, obtains product.
Flock Adhesive stick of the present invention, the flocking that can adapt to various occasions is used, more than bond strength reaches the twice of prior art.
The present invention compared with prior art its beneficial effect is: have raw material and be easy to get, cost is low, and environmental protection is easy to use, effective advantage.
Embodiment:
Below in conjunction with embodiment, the invention will be further described, but embodiments of the present invention are not limited to this.
Flock Adhesive stick of the present invention, raw materials usedly buys acquisition.
Embodiment 1
Flock Adhesive stick of the present invention, it is characterized in that: by weight, by methyl acrylate 25-50 part, Propylene glycol monoacrylate 6-10 part, ethyl propenoate 260-300 part, vinylformic acid 9-15 part, N-methacrylic acid acid amides 6-10 part, E-S1 epoxy is counted fat 90-120 part, benzoyl peroxide 1-5 part, N, N-dimethyl benzylamine 1-3 part, vinyl acetate 50-80 part forms, after solid materials is dissolved at 70-75 ℃ with ethanol, be diluted to 15% ethanolic soln, whole materials are added, and at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 2
Flock Adhesive stick of the present invention, is characterized in that: by weight, and by 25 parts of methyl acrylates, 6 parts of Propylene glycol monoacrylates, 260 parts of ethyl propenoates, 9 parts, vinylformic acid, 6 parts of N-methacrylic acid acid amides, E-S1 epoxy is counted 90 parts, fat, 1 part of benzoyl peroxide, N, 1 part of N-dimethyl benzylamine, 50 parts of compositions of vinyl acetate, after solid materials is dissolved at 70-75 ℃ with ethanol, be diluted to 15% ethanolic soln, whole materials are added, and at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 3
Flock Adhesive stick of the present invention, it is characterized in that: by weight, by 50 parts of methyl acrylates, 10 parts of Propylene glycol monoacrylates, 300 parts of ethyl propenoates, 15 parts, vinylformic acid, 10 parts of N-methacrylic acid acid amides, E-S1 epoxy is counted 120 parts, fat, 5 parts of benzoyl peroxides, N, 3 parts of N-dimethyl benzylamines, 80 parts of compositions of vinyl acetate, after solid materials is dissolved at 70-75 ℃ with ethanol, be diluted to 15% ethanolic soln, whole materials are added, and at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 4
Flock Adhesive stick of the present invention, is characterized in that: by weight, and by 25 parts of methyl acrylates, 10 parts of Propylene glycol monoacrylates, 260 parts of ethyl propenoates, 15 parts, vinylformic acid, 6 parts of N-methacrylic acid acid amides, E-S1 epoxy is counted 120 parts, fat, 1 part of benzoyl peroxide, N, 3 parts of N-dimethyl benzylamines, 50 parts of compositions of vinyl acetate, after solid materials is dissolved at 70-75 ℃ with ethanol, be diluted to 15% ethanolic soln, whole materials are added, and at room temperature stirring reaction 12-22 hour, obtains product.
Embodiment 5
Flock Adhesive stick of the present invention, is characterized in that: by weight, and by 50 parts of methyl acrylates, 6 parts of Propylene glycol monoacrylates, 300 parts of ethyl propenoates, 9 parts, vinylformic acid, 10 parts of N-methacrylic acid acid amides, E-S1 epoxy is counted 90 parts, fat, 5 parts of benzoyl peroxides, N, 1 part of N-dimethyl benzylamine, 80 parts of compositions of vinyl acetate, after solid materials is dissolved at 70-75 ℃ with ethanol, be diluted to 15% ethanolic soln, whole materials are added, and at room temperature stirring reaction 12-22 hour, obtains product.
Flock Adhesive stick of the present invention, product specification, quality: solid content is more than 80%, and its 1% solution pH value is 7.0-7.5; Viscosity 100-120 centipoise.
Claims (1)
1. a Flock Adhesive stick, it is characterized in that: by weight, by methyl acrylate 25-50 part, Propylene glycol monoacrylate 6-10 part, ethyl propenoate 260-300 part, vinylformic acid 9-15 part, N-methacrylic acid acid amides 6-10 part, E-S1 epoxy is counted fat 90-120 part, benzoyl peroxide 1-5 part, N, N-dimethyl benzylamine 1-3 part, vinyl acetate 50-80 part forms, after solid materials is dissolved at 70-75 ℃ with ethanol, be diluted to 15% ethanolic soln, whole materials are added, and at room temperature stirring reaction 12-22 hour, obtains product.