CN105733474A - Glue capable of realizing firm bonding - Google Patents
Glue capable of realizing firm bonding Download PDFInfo
- Publication number
- CN105733474A CN105733474A CN201410738388.5A CN201410738388A CN105733474A CN 105733474 A CN105733474 A CN 105733474A CN 201410738388 A CN201410738388 A CN 201410738388A CN 105733474 A CN105733474 A CN 105733474A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- water
- formaldehyde
- sodium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of glues, specifically to a glue capable of realizing firm bonding. The glue has good bonding effect, enables bonded objects hard to separate and is low in production cost, environment-friendly and non-irritant. The glue comprises the following raw materials: 7 to 15 parts of polyvinyl alcohol, 6 to 13 parts of acetic acid, 4 to 6 parts of perfume, 5 to 10 parts of hide glue, 3 to 7 parts of an emulsifier, 3 to 9 parts of formaldehyde, 8 to 11 parts of propionic acid alcohol, 1 to 7 parts of sodium hydroxide, 5 to 9 parts of a viscous reinforcing agent and 20 to 60 parts of water.
Description
One, technical field:
The present invention relates to bonding technique field, be specifically related to a kind of bonding firmly glue.
Two, background technology:
Glue is the intermediate connecting bi-material, how to occur with water preparation, belongs to fine chemistry industry class, of a great variety, mainly with the sorting technique of sizing, physical aspect, method for curing and adherend material.Common are instant glue (502 common ethyl α-cyanoacrylate brute force instant adhesives are a kind of), epoxy bond class, anaerobism glue, UV glue (ultraviolet photo-curing class), PUR, pressure sensitive adhesive, latex class etc..
Glue is just able to the material of bonding two objects.Glue is not self-existent, and it must be coated in competence exertion bonding effect between two objects.Chemical composition in glue, in aqueous environments.Polymer body in the glue one of petroleum derivative (vinyl acetate in white glue be) is all rounded particle, and the radius of general particle is between 0.5～5 μm.Object bonding, it is simply that realize by the pulling force between the polymer body in glue.In glue, water is exactly the carrier of middle polymer body, and water ballast polymer body and is immersed at leisure in the tissue of object.After the moisture in glue disappears, the polymer body in glue just relies on mutual pulling force, by two objects combining tightly.In the use of glue, glue-spread too much will make the polymer body in glue mutually crowded together；Good pulling force is not produced between polymer body.Polymer body is mutually crowded, thus not becoming captivation the strongest each other.Meanwhile, the moisture between polymer body is also not easy to vapor away.Here it is why in bonding process " glued membrane is more thick, reason that the bonding effect of glue is more poor ".Glue-spread is too much, and what glue played greatly is " filling effect " rather than bonding effect, and what bonding between object was leaned on is not the cohesive force of glue, but " cohesiveness " of glue.
Three, summary of the invention:
The present invention is to solve the weak point in above-mentioned background technology, it is provided that a kind of bonding firmly glue, its plybonding effect is good, and environmental protection is non-stimulated.
For achieving the above object, the technical solution used in the present invention is: a kind of bonding firmly glue, it is characterised in that: described glue is made up of following raw material: polyvinyl alcohol, acetic acid, spice, hide glue, emulsifying agent, formaldehyde, propanoic acid alcohol, sodium hydroxide, viscosity-increasing agent and water.
Described glue is made up of following raw material: polyvinyl alcohol 7-15 part, acetic acid 6-13 part, spice 4-6 part, hide glue 5-10 part, emulsifying agent 3-7 part, formaldehyde 3-9 part, propanoic acid alcohol 8-11 part, sodium hydroxide 1-7 part, viscosity-increasing agent 5-9 part and water 20-60 part.
Described glue is made up of following raw material: polyvinyl alcohol 13 parts, acetic acid 8 parts, spice 5 parts, hide glue 9 parts, emulsifying agent 5 parts, 7 parts of formaldehyde, propanoic acid alcohol 10 parts, sodium hydroxide 5 parts, viscosity-increasing agent 6 parts and water 20-60 part.
Compared with prior art, the present invention has the advantage that as follows with effect: glue formula adhesive effect of the present invention is good, is not easy separately, and production cost is low, environmental protection is non-stimulated after being stained with.
Four, detailed description of the invention:
Embodiment one:
A kind of bonding firmly glue is made up of following raw material: polyvinyl alcohol 7 parts, acetic acid 6 parts, spice 4 parts, hide glue 5 parts, emulsifying agent 3 parts, 3 parts of formaldehyde, propanoic acid alcohol 8 parts, sodium hydroxide 1 part, viscosity-increasing agent 5 parts and 20 parts of water.
Embodiment two:
A kind of bonding firmly glue is made up of following raw material: polyvinyl alcohol 15 parts, acetic acid 13 parts, spice 6 parts, hide glue 10 parts, emulsifying agent 7 parts, 9 parts of formaldehyde, propanoic acid alcohol 11 parts, sodium hydroxide 7 parts, viscosity-increasing agent 9 parts and 60 parts of water.
Embodiment three:
A kind of bonding firmly glue is made up of following raw material: polyvinyl alcohol 13 parts, acetic acid 6 parts, spice 5 parts, hide glue 8 parts, emulsifying agent 7 parts, 3 parts of formaldehyde, propanoic acid alcohol 9 parts, sodium hydroxide 1-7 part, viscosity-increasing agent 7 parts and 40 parts of water.
Embodiment four:
A kind of bonding firmly glue is made up of following raw material: polyvinyl alcohol 13 parts, acetic acid 8 parts, spice 5 parts, hide glue 9 parts, emulsifying agent 5 parts, 7 parts of formaldehyde, propanoic acid alcohol 10 parts, sodium hydroxide 5 parts, viscosity-increasing agent 6 parts and water 20-60 part.
Embodiment five:
A kind of bonding firmly glue is made up of following raw material: polyvinyl alcohol 14 parts, acetic acid 12 parts, spice 5 parts, hide glue 8 parts, emulsifying agent 6 parts, 7 parts of formaldehyde, propanoic acid alcohol 10 parts, sodium hydroxide 1-7 part, viscosity-increasing agent 7 parts and 50 parts of water.
Claims (3)
1. a bonding firmly glue, it is characterised in that: described glue is made up of following raw material: polyvinyl alcohol, acetic acid, spice, hide glue, emulsifying agent, formaldehyde, propanoic acid alcohol, sodium hydroxide, viscosity-increasing agent and water.
2. the bonding firmly glue of one according to claim 1, it is characterised in that: described glue is made up of following raw material: polyvinyl alcohol 7-15 part, acetic acid 6-13 part, spice 4-6 part, hide glue 5-10 part, emulsifying agent 3-7 part, formaldehyde 3-9 part, propanoic acid alcohol 8-11 part, sodium hydroxide 1-7 part, viscosity-increasing agent 5-9 part and water 20-60 part.
3. the bonding firmly glue of one according to claim 1, it is characterised in that: described glue is made up of following raw material: polyvinyl alcohol 13 parts, acetic acid 8 parts, spice 5 parts, hide glue 9 parts, emulsifying agent 5 parts, 7 parts of formaldehyde, propanoic acid alcohol 10 parts, sodium hydroxide 5 parts, viscosity-increasing agent 6 parts and water 20-60 part.