CN103525309B - A kind of double-component aqueous multi-color lacquer coating - Google Patents
A kind of double-component aqueous multi-color lacquer coating Download PDFInfo
- Publication number
- CN103525309B CN103525309B CN201310421161.3A CN201310421161A CN103525309B CN 103525309 B CN103525309 B CN 103525309B CN 201310421161 A CN201310421161 A CN 201310421161A CN 103525309 B CN103525309 B CN 103525309B
- Authority
- CN
- China
- Prior art keywords
- component
- raw material
- water
- double
- adhesive aid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of double-component aqueous multi-color lacquer coating, it is made up of first and second liang of components, and coating of the present invention has good cohesive force to base material, and film is stablized, and protected effect is good, and by force ornamental, has good artistic effect.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of double-component aqueous multi-color lacquer coating.
Background technology
Water-based (water-water) multicolor finish be actually a kind of with the small-particle of water emulsion coating as disperse phase, the multinomial suspension system being external phase with the protecting glue aqueous solution.Obtain uniform and stable suspensoid, just must make latex coating in the process adding the protecting glue aqueous solution, protection glue does not occur to the dilution of latex coating, the problem that the condensation of coating and pigment permeate in the protecting glue aqueous solution.Realize the suspensoid of this water-water; just must in moment water emulsion coating being scattered in the protecting glue aqueous solution; the water-fast flexible membrane of one deck is formed on coating particles surface; this layer of flexible membrane is except can outside the phase mutual diffusion of the coating composition in block film and the protecting glue component except film; can also prevent from assembling between coating particles, condensing, after spraying, along with the evaporation of moisture; mutually pile up between coating particles and merge, final formation multicolour pattern film.
Summary of the invention
The object of the invention is exactly to provide a kind of double-component aqueous multi-color lacquer coating.
The present invention is achieved by the following technical solutions:
A kind of double-component aqueous multi-color lacquer coating, it is characterized in that it is made up of first and second liang of components, described first component is made up of the raw material of following weight parts:
Softening water 300-350, Natvosol 6-10,2-amino-2-methyl-1-propanol 0.8-1, tripoly phosphate sodium STPP 4-6, octylisothiazolinone 1-3, dimethyl silicone oil 1-2, rutile titanium white powder 30-35, water-ground limestone 200-250, calcined kaolin 30-40, elastic emulsion 250-300, ethylene glycol monobutyl ether 8-10, wetting dispersing agent BD-30714-6, mixed solution 170-180, adhesive aid 6-10;
By above-mentioned each raw material mixing except mixed solution, adhesive aid, fully add mixed solution, adhesive aid successively after mixing, fully grind, obtain described first component;
Described mixed solution is made up of the raw material mixing of following weight parts:
Softening water 150-200, trisodium phosphate 1-3, Stearyl alcohol 10-15;
Described adhesive aid is made up of the raw material of following weight parts:
Benzene emulsion 60-70, tragacanth gum 6-8, Zinc Pyrithione 1-2, sodium silicoaluminate 4-6, butyl polyacrylate 1-2, Natvosol 2-4,2,6 ditertiary butyl p cresol 0.1-0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6 ditertiary butyl p cresol, dispersed with stirring 10-15 minute under the speed of 400-600 rev/min, raised temperature is 60-80 DEG C, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, fully after mixing, add each raw material of residue, the steam heating of 80-100 DEG C is crossed after stirring, the system solid content of making is 60-65%, is cooled to normal temperature, obtains described adhesive aid.
Described component B is made up of the raw material of following weight parts:
Softening water 400-450, trisodium phosphate 1-3, assorted base paint 200-260, elastic emulsion 240-260, dimethyl silicone oil 0.6-1, ethylene glycol monobutyl ether 15-20, the swelling non-associative thickener ASE-602-4 of alkali, deionized water 40-50,2-amino-2-methyl-1-propanol 0.5-1;
By each raw material mixing of above-mentioned second component, abundant ball milling, obtains described second component.
A preparation method for double-component aqueous multi-color lacquer coating, comprises the following steps:
Above-mentioned first and second liang of components are mixed according to the weight ratio of 1-2:1-2, is fully uniformly mixed, obtain described double-component aqueous multi-color lacquer coating.
Advantage of the present invention is:
Coating of the present invention has good cohesive force to base material, and film is stablized, and protected effect is good, and by force ornamental, has good artistic effect.
Embodiment
Embodiment 1
A kind of double-component aqueous multi-color lacquer coating, it is characterized in that it is made up of first and second liang of components, described first component is made up of the raw material of following weight parts:
Softening water 350, Natvosol 10,2-amino-2-methyl-1-propanol 0.8, tripoly phosphate sodium STPP 4, octylisothiazolinone 1, dimethyl silicone oil 2, rutile titanium white powder 35, water-ground limestone 250, calcined kaolin 40, elastic emulsion 300, ethylene glycol monobutyl ether 10, wetting dispersing agent BD-30716, mixed solution 180, adhesive aid 10;
By above-mentioned each raw material mixing except mixed solution, adhesive aid, fully add mixed solution, adhesive aid successively after mixing, fully grind, obtain described first component;
Described mixed solution is made up of the raw material mixing of following weight parts:
Softening water 200, trisodium phosphate 3, Stearyl alcohol 15;
Described adhesive aid is made up of the raw material of following weight parts:
Benzene emulsion 70, tragacanth gum 8, Zinc Pyrithione 2, sodium silicoaluminate 6, butyl polyacrylate 1, Natvosol 2,2,6 ditertiary butyl p cresol 0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6 ditertiary butyl p cresol, dispersed with stirring 15 minutes under the speed of 600 revs/min, raised temperature is 80 DEG C, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, fully after mixing, add each raw material of residue, the steam heating of 100 DEG C is crossed after stirring, the system solid content of making is 65%, is cooled to normal temperature, obtains described adhesive aid.
Described component B is made up of the raw material of following weight parts:
The swelling non-associative thickener ASE-604 of softening water 450, trisodium phosphate 1, assorted base paint 260, elastic emulsion 260, dimethyl silicone oil 0.6, ethylene glycol monobutyl ether 20, alkali, deionized water 50,2-amino-2-methyl-1-propanol 0.5;
By each raw material mixing of above-mentioned second component, abundant ball milling, obtains described second component.
A preparation method for double-component aqueous multi-color lacquer coating, comprises the following steps:
Above-mentioned first and second liang of components are mixed according to the weight ratio of 1:1, is fully uniformly mixed, obtain described double-component aqueous multi-color lacquer coating.
Performance test:
Coating adhesion 1 grade;
Stability in storage: 1 year.
Claims (2)
1. a double-component aqueous multi-color lacquer coating, it is characterized in that it is made up of first and second liang of components, described first component is made up of the raw material of following weight parts:
Softening water 300-350, Natvosol 6-10,2-amino-2-methyl-1-propanol 0.8-1, tripoly phosphate sodium STPP 4-6, octylisothiazolinone 1-3, dimethyl silicone oil 1-2, rutile titanium white powder 30-35, water-ground limestone 200-250, calcined kaolin 30-40, elastic emulsion 250-300, ethylene glycol monobutyl ether 8-10, wetting dispersing agent BD-30714-6, mixed solution 170-180, adhesive aid 6-10;
By above-mentioned each raw material mixing except mixed solution, adhesive aid, fully add mixed solution, adhesive aid successively after mixing, fully grind, obtain described first component;
Described mixed solution is made up of the raw material mixing of following weight parts:
Softening water 150-200, trisodium phosphate 1-3, Stearyl alcohol 10-15;
Described adhesive aid is made up of the raw material of following weight parts:
Benzene emulsion 60-70, tragacanth gum 6-8, Zinc Pyrithione 1-2, sodium silicoaluminate 4-6, butyl polyacrylate 1-2, Natvosol 2-4,2,6 ditertiary butyl p cresol 0.1-0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6 ditertiary butyl p cresol, dispersed with stirring 10-15 minute under the speed of 400-600 rev/min, raised temperature is 60-80 DEG C, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, fully after mixing, add each raw material of residue, the steam heating of 80-100 DEG C is crossed after stirring, the system solid content of making is 60-65%, is cooled to normal temperature, obtains described adhesive aid;
Described component B is made up of the raw material of following weight parts:
Softening water 400-450, trisodium phosphate 1-3, assorted base paint 200-260, elastic emulsion 240-260, dimethyl silicone oil 0.6-1, ethylene glycol monobutyl ether 15-20, the swelling non-associative thickener ASE-602-4 of alkali, deionized water 40-50,2-amino-2-methyl-1-propanol 0.5-1;
By each raw material mixing of above-mentioned second component, abundant ball milling, obtains described second component.
2. a preparation method for double-component aqueous multi-color lacquer coating as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned first and second liang of components are mixed according to the weight ratio of 1-2:1-2, is fully uniformly mixed, obtain described double-component aqueous multi-color lacquer coating.