CN103497653B - A kind of top ceiling powder coating - Google Patents
A kind of top ceiling powder coating Download PDFInfo
- Publication number
- CN103497653B CN103497653B CN201310396031.9A CN201310396031A CN103497653B CN 103497653 B CN103497653 B CN 103497653B CN 201310396031 A CN201310396031 A CN 201310396031A CN 103497653 B CN103497653 B CN 103497653B
- Authority
- CN
- China
- Prior art keywords
- powder coating
- top ceiling
- raw material
- powder
- compounded mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Does is the invention discloses a kind of top ceiling powder coating, it made up of the raw material of following weight parts: unsaturated polyester resin CC441? 30-35, epoxy resin E12? 15-20, decabromodiphenyl oxide 10-13, primary ammonium phosphate 1-2, vinylformic acid 2-3, trimeric cyanamide 2-3, termil 1-2, glycerine 2-3, dimethylcyclohexylamine 1-2, titanium dioxide 2-3, talcum powder 2-3, compounded mix 4-6; Coating planeness of the present invention is good, good decorating effect, and strong adhesion has certain flame retardant resistance, can form good flameproof protection to base material.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of top ceiling powder coating.
Background technology
Powder coating, as environmental protection, energy-conservation, economic, efficient product, replaces liquid paint gradually, becomes tempo and the fastest coating new technology of scale.In current art of powder coatings, be all common indoor decorative powder coating or outdoor weatherability powder coating substantially.Functional powder coating also relates to the fields such as epoxy heavy antisepsis type, conductivity type, insulated type, the type of resistance to combustion, scumbling type, therefore studies novel high-performance powder coating and can play better booster action for nation-building, social life.
Summary of the invention
The object of the invention is exactly to provide a kind of top ceiling powder coating.
The present invention is achieved by the following technical solutions:
A kind of top ceiling powder coating, is characterized in that what it was made up of the raw material of following weight parts:
Unsaturated polyester resin CC44130-35, epoxy resin E1215-20, decabromodiphenyl oxide 10-13, primary ammonium phosphate 1-2, vinylformic acid 2-3, trimeric cyanamide 2-3, termil 1-2, glycerine 2-3, dimethylcyclohexylamine 1-2, titanium dioxide 2-3, talcum powder 2-3, compounded mix 4-6;
Described compounded mix is made up of the raw material of following weight parts:
Gibbsite 10-20, laterite 30-40, aluminium nitride 4-6, sodium silicate 3-4, ricinolic acid 1-2, oxidized polyethlene wax 3-4, lead sulfate tribasic 0.1-0.2;
By above-mentioned laterite, gibbsite mixing, 3-5 hour is calcined at 500-600 DEG C, after discharging cooling, mix with aluminium nitride, sodium silicate, lead sulfate tribasic, add suitable quantity of water grinding, the hydrochloric acid adding 10-20% regulates PH to be 4-5, being heated to system temperature is 70-90 DEG C, and being ground to fineness is 300-400 order, and repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, obtains powder; Mixed with other remaining component by gained powder, namely grinding evenly obtains described compounded mix.
A preparation method for top ceiling powder coating, comprises the following steps:
After above-mentioned each raw material mixing, melt extrude under input forcing machine, air-cooled, pulverize in pulverizer, then abrasive dust is 30-40 micron to median size, obtains described top ceiling powder coating.
Advantage of the present invention is:
Coating planeness of the present invention is good, good decorating effect, and strong adhesion has certain flame retardant resistance, can form good flameproof protection to base material.
Embodiment
Embodiment 1,
A kind of top ceiling powder coating, it is made up of the raw material of following weight parts (kilogram):
Unsaturated polyester resin CC44135, epoxy resin E1220, decabromodiphenyl oxide 13, primary ammonium phosphate 1, vinylformic acid 3, trimeric cyanamide 3, termil 1, glycerine 3, dimethylcyclohexylamine 2, titanium dioxide 2, talcum powder 3, compounded mix 4;
Described compounded mix is made up of the raw material of following weight parts:
Gibbsite 20, laterite 40, aluminium nitride 6, sodium silicate 3, ricinolic acid 2, oxidized polyethlene wax 3, lead sulfate tribasic 0.2;
By above-mentioned laterite, gibbsite mixing, calcine 3 hours at 600 DEG C, after discharging cooling, mix with aluminium nitride, sodium silicate, lead sulfate tribasic, add suitable quantity of water grinding, the hydrochloric acid adding 20% regulates PH to be 4, being heated to system temperature is 90 DEG C, and being ground to fineness is 400 orders, and repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, obtains powder; Mixed with other remaining component by gained powder, namely grinding evenly obtains described compounded mix.
A preparation method for top ceiling powder coating, comprises the following steps:
After above-mentioned each raw material mixing, melt extrude under input forcing machine, air-cooled, pulverize in pulverizer, then abrasive dust is 30-40 micron to median size, obtains described top ceiling powder coating.
Performance test:
Solvent resistant: 240 hours, unchanged;
Salt-fog test (1000h): unchanged.
Claims (2)
1. a top ceiling powder coating, is characterized in that what it was made up of the raw material of following weight parts:
Unsaturated polyester resin CC44130-35, epoxy resin E1215-20, decabromodiphenyl oxide 10-13, primary ammonium phosphate 1-2, vinylformic acid 2-3, trimeric cyanamide 2-3, termil 1-2, glycerine 2-3, dimethylcyclohexylamine 1-2, titanium dioxide 2-3, talcum powder 2-3, compounded mix 4-6;
Described compounded mix is made up of the raw material of following weight parts:
Gibbsite 10-20, laterite 30-40, aluminium nitride 4-6, sodium silicate 3-4, ricinolic acid 1-2, oxidized polyethlene wax 3-4, lead sulfate tribasic 0.1-0.2;
By above-mentioned laterite, gibbsite mixing, 3-5 hour is calcined at 500-600 DEG C, after discharging cooling, mix with aluminium nitride, sodium silicate, lead sulfate tribasic, add suitable quantity of water grinding, the salt acid for adjusting pH adding 10-20% is 4-5, being heated to system temperature is 70-90 DEG C, and being ground to fineness is 300-400 order, and repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, obtains powder; Mixed with other remaining component by gained powder, namely grinding evenly obtains described compounded mix.
2. a preparation method for top ceiling powder coating as claimed in claim 1, is characterized in that comprising the following steps:
After above-mentioned each raw material mixing, melt extrude under input forcing machine, air-cooled, pulverize in pulverizer, then abrasive dust is 30-40 micron to median size, obtains described top ceiling powder coating.