CN103497653A - Powdery paint for ceiling - Google Patents
Powdery paint for ceiling Download PDFInfo
- Publication number
- CN103497653A CN103497653A CN201310396031.9A CN201310396031A CN103497653A CN 103497653 A CN103497653 A CN 103497653A CN 201310396031 A CN201310396031 A CN 201310396031A CN 103497653 A CN103497653 A CN 103497653A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- powder coating
- raw material
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a powdery paint for a ceiling. The paint comprises the following raw materials by weight: 30 to 35 parts of an unsaturated polyester resin CC441, 15 to 20 parts of an epoxy resin E12, 10 to 13 parts of decabromodiphenyl ether, 1 to 2 parts of ammonium biphosphate, 2 to 3 parts of acrylic acid, 2 to 3 parts of melamine, 1 to 2 parts of tetrachloroisophthalonitrile, 2 to 3 parts of glycerin, 1 to 2 parts of dimethylcyclohexylamine, 2 to 3 parts of titanium dioxide, 2 to 3 parts of talcum powder and 4 to 6 parts of a composite filling material. The paint provided by the invention has good smoothness, a good decorative effect, strong adhesion and flame resistance and can realize good fire protection on a substrate.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of top ceiling powder coating.
Background technology
Powder coating, as environmental protection, energy-conservation, economic, efficient product, replaces liquid paint gradually, becomes the fastest coating new technology of tempo and scale.In current art of powder coatings, be all common indoor decorative powder coating or outdoor weatherability powder coating basically.Functional powder coating also relates to the fields such as the heavy anti-corrosive type of epoxy, conductivity type, insulated type, the type of anti-combustion the, scumbling type, and therefore studying the novel high-performance powder coating can play better booster action for nation-building, social life.
Summary of the invention
The object of the invention is exactly for a kind of top ceiling powder coating is provided.
The present invention is achieved by the following technical solutions:
A kind of top ceiling powder coating is characterized in that what it was comprised of the raw material of following weight parts:
Unsaturated polyester resin CC441 30-35, epoxy resin E12 15-20, decabromodiphenyl oxide 10-13, primary ammonium phosphate 1-2, vinylformic acid 2-3, trimeric cyanamide 2-3, termil 1-2, glycerine 2-3, dimethylcyclohexylamine 1-2, titanium dioxide 2-3, talcum powder 2-3, compounded mix 4-6;
Described compounded mix is comprised of the raw material of following weight parts:
Gibbsite 10-20, laterite 30-40, aluminium nitride 4-6, flower bulb alkali 3-4, ricinolic acid 1-2, oxidized polyethlene wax 3-4, lead sulfate tribasic 0.1-0.2;
Above-mentioned laterite, gibbsite are mixed, calcining 3-5 hour under 500-600 ℃, after discharging is cooling, with aluminium nitride, flower bulb alkali, lead sulfate tribasic, mix, add suitable quantity of water and grind, the hydrochloric acid adjusting PH that adds 10-20% is 4-5, being heated to system temperature is 70-90 ℃, and being ground to fineness is the 300-400 order, and the repeated hydrogenation sodium oxide is adjusted to neutrality, spraying drying, obtain powder; The gained powder is mixed with other remaining component, grind and evenly obtain described compounded mix.
The preparation method of powder coating for a kind of top ceiling comprises the following steps:
After above-mentioned each raw material is mixed, under the input forcing machine, melt extrude, air-cooled, through in pulverizer, pulverized, then abrasive dust to median size is the 30-40 micron, obtains described top ceiling powder coating.
Advantage of the present invention is:
Coating planeness of the present invention is good, good decorating effect, and strong adhesion, have certain flame retardant resistance, can form good flameproof protection to base material.
Embodiment
Embodiment 1,
A kind of top ceiling powder coating, it is comprised of the raw material of following weight parts (kilogram):
Unsaturated polyester resin CC441 35, epoxy resin E12 20, decabromodiphenyl oxide 13, primary ammonium phosphate 1, vinylformic acid 3, trimeric cyanamide 3, termil 1, glycerine 3, dimethylcyclohexylamine 2, titanium dioxide 2, talcum powder 3, compounded mix 4;
Described compounded mix is comprised of the raw material of following weight parts:
Gibbsite 20, laterite 40, aluminium nitride 6, flower bulb alkali 3, ricinolic acid 2, oxidized polyethlene wax 3, lead sulfate tribasic 0.2;
Above-mentioned laterite, gibbsite are mixed, under 600 ℃, calcining is 3 hours, after discharging is cooling, with aluminium nitride, flower bulb alkali, lead sulfate tribasic, mix, add suitable quantity of water and grind, adding 20% hydrochloric acid, to regulate PH be 4, being heated to system temperature is 90 ℃, and being ground to fineness is 400 orders, and the repeated hydrogenation sodium oxide is adjusted to neutrality, spraying drying, obtain powder; The gained powder is mixed with other remaining component, grind and evenly obtain described compounded mix.
The preparation method of powder coating for a kind of top ceiling comprises the following steps:
After above-mentioned each raw material is mixed, under the input forcing machine, melt extrude, air-cooled, through in pulverizer, pulverized, then abrasive dust to median size is the 30-40 micron, obtains described top ceiling powder coating.
Performance test:
Anti-solvent: 240 hours, unchanged;
Salt-fog test (1000h): unchanged.
Claims (2)
1. a top ceiling powder coating is characterized in that what it was comprised of the raw material of following weight parts:
Unsaturated polyester resin CC441 30-35, epoxy resin E12 15-20, decabromodiphenyl oxide 10-13, primary ammonium phosphate 1-2, vinylformic acid 2-3, trimeric cyanamide 2-3, termil 1-2, glycerine 2-3, dimethylcyclohexylamine 1-2, titanium dioxide 2-3, talcum powder 2-3, compounded mix 4-6;
Described compounded mix is comprised of the raw material of following weight parts:
Gibbsite 10-20, laterite 30-40, aluminium nitride 4-6, flower bulb alkali 3-4, ricinolic acid 1-2, oxidized polyethlene wax 3-4, lead sulfate tribasic 0.1-0.2;
Above-mentioned laterite, gibbsite are mixed, calcining 3-5 hour under 500-600 ℃, after discharging is cooling, with aluminium nitride, flower bulb alkali, lead sulfate tribasic, mix, add suitable quantity of water and grind, the hydrochloric acid adjusting PH that adds 10-20% is 4-5, being heated to system temperature is 70-90 ℃, and being ground to fineness is the 300-400 order, and the repeated hydrogenation sodium oxide is adjusted to neutrality, spraying drying, obtain powder; The gained powder is mixed with other remaining component, grind and evenly obtain described compounded mix.
2. the preparation method of powder coating for a top ceiling as claimed in claim 1 is characterized in that comprising the following steps:
After above-mentioned each raw material is mixed, under the input forcing machine, melt extrude, air-cooled, through in pulverizer, pulverized, then abrasive dust to median size is the 30-40 micron, obtains described top ceiling powder coating.