CN103525309A - Double-component waterborne colorful paint coating - Google Patents
Double-component waterborne colorful paint coating Download PDFInfo
- Publication number
- CN103525309A CN103525309A CN201310421161.3A CN201310421161A CN103525309A CN 103525309 A CN103525309 A CN 103525309A CN 201310421161 A CN201310421161 A CN 201310421161A CN 103525309 A CN103525309 A CN 103525309A
- Authority
- CN
- China
- Prior art keywords
- component
- raw material
- mixed
- water
- double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a double-component waterborne colorful paint coating. The double-component waterborne colorful paint coating comprises a component A and a component B. The coating disclosed by the invention has the advantages of good adhesion against a substrate, stability in coating, good protection effect, strong decoration and great artistic effect.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of double-component aqueous multi-color lacquer coating.
Background technology
Water-based (water Bao Shui) multicolor finish is actually a kind of small-particle with water emulsion coating as disperse phase, take and protects the multinomial suspension system that glue solution is external phase.Obtain uniform and stable suspensoid, just must make latex coating in adding the process of protecting glue solution, do not protect the dilution of glue to latex coating, the condensing and problem that pigment permeates in from glue solution to protection of coating.Realize the suspensoid of this water Bao Shui; just must be in the moment that water emulsion coating is scattered in to protection glue solution; on coating particles surface, form the water-fast flexible membrane of one deck; outside the phase mutual diffusion of coating composition in can block film of this layer of flexible membrane and the protection glue component film; can also prevent between coating particles, assembling, condensing, after spraying, along with the evaporation of moisture; between coating particles, mutually pile up and merge, finally forming multicolour pattern and film.
Summary of the invention
The object of the invention is exactly for a kind of double-component aqueous multi-color lacquer coating is provided.
The present invention is achieved by the following technical solutions:
A multi-color lacquer coating, is characterized in that it is comprised of first and second liang of components, and described first component is comprised of the raw material of following weight parts:
Softening water 300-350, Natvosol 6-10,2-amino-2-methyl-1-propanol 0.8-1, tripoly phosphate sodium STPP 4-6, octyl group isothiazolinone 1-3, dimethyl silicone oil 1-2, rutile titanium white powder 30-35, water-ground limestone 200-250, calcined kaolin 30-40, elastic emulsion 250-300, ethylene glycol monobutyl ether 8-10, wetting dispersing agent BD-3071 4-6, mixed solution 170-180, adhesive aid 6-10;
Above-mentioned each raw material except mixed solution, adhesive aid is mixed, after fully mixing, add successively mixed solution, adhesive aid, fully grind, obtain described first component;
Described mixed solution is mixed and to be formed by the raw material of following weight parts:
Softening water 150-200, trisodium phosphate 1-3, Stearyl alcohol 10-15;
Described adhesive aid is comprised of the raw material of following weight parts:
Benzene emulsion 60-70, tragacanth gum 6-8, Zinc Pyrithione 1-2, sodium silicoaluminate 4-6, butyl polyacrylate 1-2, Natvosol 2-4,2,6-ditertbutylparacresol 0.1-0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6-ditertbutylparacresol, dispersed with stirring 10-15 minute under the speed of 400-600 rev/min, rising temperature is 60-80 ℃, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, after fully mixing, add each raw material of residue, after stirring, cross the steam heating of 80-100 ℃, the system solid content of making is 60-65%, is cooled to normal temperature, obtains described adhesive aid.
Described component B is comprised of the raw material of following weight parts:
Softening water 400-450, trisodium phosphate 1-3, base paint 200-260 of all kinds, elastic emulsion 240-260, dimethyl silicone oil 0.6-1, ethylene glycol monobutyl ether 15-20, the non-associative thickener ASE-60 of alkali swelling 2-4, deionized water 40-50,2-amino-2-methyl-1-propanol 0.5-1;
Each raw material of above-mentioned second component is mixed, and fully ball milling, obtains described second component.
A preparation method for double-component aqueous multi-color lacquer coating, comprises the following steps:
Above-mentioned first and second liang of components are mixed according to the weight ratio of 1-2:1-2, be fully uniformly mixed, obtain described double-component aqueous multi-color lacquer coating.
Advantage of the present invention is:
Coating of the present invention has good cohesive force to base material, films stable, protects effectively, and ornamental strong, has good artistic effect.
Embodiment
Embodiment 1
A multi-color lacquer coating, is characterized in that it is comprised of first and second liang of components, and described first component is comprised of the raw material of following weight parts:
Softening water 350, Natvosol 10,2-amino-2-methyl-1-propanol 0.8, tripoly phosphate sodium STPP 4, octyl group isothiazolinone 1, dimethyl silicone oil 2, rutile titanium white powder 35, water-ground limestone 250, calcined kaolin 40, elastic emulsion 300, ethylene glycol monobutyl ether 10, wetting dispersing agent BD-3071 6, mixed solution 180, adhesive aid 10;
Above-mentioned each raw material except mixed solution, adhesive aid is mixed, after fully mixing, add successively mixed solution, adhesive aid, fully grind, obtain described first component;
Described mixed solution is mixed and to be formed by the raw material of following weight parts:
Softening water 200, trisodium phosphate 3, Stearyl alcohol 15;
Described adhesive aid is comprised of the raw material of following weight parts:
Benzene emulsion 70, tragacanth gum 8, Zinc Pyrithione 2, sodium silicoaluminate 6, butyl polyacrylate 1, Natvosol 2,2,6-ditertbutylparacresol 0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6-ditertbutylparacresol, under the speed of 600 revs/min, dispersed with stirring is 15 minutes, rising temperature is 80 ℃, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, after fully mixing, add each raw material of residue, after stirring, cross the steam heating of 100 ℃, the system solid content of making is 65%, is cooled to normal temperature, obtains described adhesive aid.
Described component B is comprised of the raw material of following weight parts:
Softening water 450, trisodium phosphate 1, base paint of all kinds 260, elastic emulsion 260, dimethyl silicone oil 0.6, ethylene glycol monobutyl ether 20, the non-associative thickener ASE-60 4 of alkali swelling, deionized water 50,2-amino-2-methyl-1-propanol 0.5;
Each raw material of above-mentioned second component is mixed, and fully ball milling, obtains described second component.
A preparation method for double-component aqueous multi-color lacquer coating, comprises the following steps:
Above-mentioned first and second liang of components are mixed according to the weight ratio of 1:1, be fully uniformly mixed, obtain described double-component aqueous multi-color lacquer coating.
Performance test:
1 grade of coating adhesion;
Stability in storage: 1 year.
Claims (2)
1. a double-component aqueous multi-color lacquer coating, is characterized in that it is comprised of first and second liang of components, and described first component is comprised of the raw material of following weight parts:
Softening water 300-350, Natvosol 6-10,2-amino-2-methyl-1-propanol 0.8-1, tripoly phosphate sodium STPP 4-6, octyl group isothiazolinone 1-3, dimethyl silicone oil 1-2, rutile titanium white powder 30-35, water-ground limestone 200-250, calcined kaolin 30-40, elastic emulsion 250-300, ethylene glycol monobutyl ether 8-10, wetting dispersing agent BD-3071 4-6, mixed solution 170-180, adhesive aid 6-10;
Above-mentioned each raw material except mixed solution, adhesive aid is mixed, after fully mixing, add successively mixed solution, adhesive aid, fully grind, obtain described first component;
Described mixed solution is mixed and to be formed by the raw material of following weight parts:
Softening water 150-200, trisodium phosphate 1-3, Stearyl alcohol 10-15;
Described adhesive aid is comprised of the raw material of following weight parts:
Benzene emulsion 60-70, tragacanth gum 6-8, Zinc Pyrithione 1-2, sodium silicoaluminate 4-6, butyl polyacrylate 1-2, Natvosol 2-4,2,6-ditertbutylparacresol 0.1-0.3, water are appropriate;
The 10-20% of above-mentioned weight tragacanth gum is joined in 10-15 times of water, add Natvosol and 2,6-ditertbutylparacresol, dispersed with stirring 10-15 minute under the speed of 400-600 rev/min, rising temperature is 60-80 ℃, add Zinc Pyrithione, sodium silicoaluminate, butyl polyacrylate, after fully mixing, add each raw material of residue, after stirring, cross the steam heating of 80-100 ℃, the system solid content of making is 60-65%, is cooled to normal temperature, obtains described adhesive aid;
Described component B is comprised of the raw material of following weight parts:
Softening water 400-450, trisodium phosphate 1-3, base paint 200-260 of all kinds, elastic emulsion 240-260, dimethyl silicone oil 0.6-1, ethylene glycol monobutyl ether 15-20, the non-associative thickener ASE-60 of alkali swelling 2-4, deionized water 40-50,2-amino-2-methyl-1-propanol 0.5-1;
Each raw material of above-mentioned second component is mixed, and fully ball milling, obtains described second component.
2. a preparation method for double-component aqueous multi-color lacquer coating as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned first and second liang of components are mixed according to the weight ratio of 1-2:1-2, be fully uniformly mixed, obtain described double-component aqueous multi-color lacquer coating.