CN101638538A - Waterborne suede paint and preparation method thereof - Google Patents
Waterborne suede paint and preparation method thereof Download PDFInfo
- Publication number
- CN101638538A CN101638538A CN200810041230A CN200810041230A CN101638538A CN 101638538 A CN101638538 A CN 101638538A CN 200810041230 A CN200810041230 A CN 200810041230A CN 200810041230 A CN200810041230 A CN 200810041230A CN 101638538 A CN101638538 A CN 101638538A
- Authority
- CN
- China
- Prior art keywords
- water
- paint
- defoamer
- weight parts
- coalescence aid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides waterborne suede paint, which mainly comprises water, talc, light calcium, defoamer, ammonia water, styrene-acrylic emulsion, film-forming additives, glass beads and color paste. The invention also provides a method for preparing the waterborne suede paint. The paint has the advantages that the paint is outstanding in suede and stereoscopic sense, free from pollution, harmless to human body and free from incendivity, ensures strong water resistance and acid-alkali resistance of film, enables decorative surfaces to have high-grade nap-like effects, can be mixed to have dozens of soft colors, and is beneficial to waste utilization by utilizing waste glass beads of fly-ash glass factories.
Description
Technical field
The present invention relates to a kind of waterborne suede coating and preparation method thereof.
Background technology
General building coating commonly used, mainly by the latex bonding material, color stuffing, auxiliary agent are formed, its fair need are regularly repaired, and colourful three-dimensional coating cost is high, contains the plastic components height, and certain incendivity arranged, film water-fast, resistance to acids and bases is relatively poor, existing simultaneously coating is all existing defective aspect velvet and the stereoscopic sensation, the most important thing is human body harm comparatively serious.
Summary of the invention
The objective of the invention is to: a kind of waterborne suede coating and preparation method thereof is provided.
Another object of the present invention is to provide a kind of preparation method of the present invention.
The object of the present invention is achieved like this:
The invention discloses a kind of waterborne suede coating, in weight percentage, this system component is:
Benzene emulsion 20～30%
Water 20～40%
Talcum powder 10～15%
Fine particle calcium carbonate 10～20%
Film coalescence aid 1.5～2%
Glass microballon 20～30%
Mill base 0.1～0.5%
Defoamer 1～2%
Ammoniacal liquor 1～2%
Described film coalescence aid is selected from ethylene glycol ethyl ether or butyl glycol ether;
Described defoamer is selected from tributyl phosphate or water-based silicone oil.
Described glass microballon can adopt the scrap glass microballon of flyash glasswork.
The component raw material that the present invention adopts is general raw material and gets by market purchasing.
The invention also discloses a kind of preparation method of waterborne suede coating of the present invention, may further comprise the steps:
Successively water, talcum powder, fine particle calcium carbonate, defoamer and ammoniacal liquor are added in the stirrer by a certain percentage, after the high-speed stirring, add benzene emulsion, film coalescence aid, glass microballon and mill base more successively, promptly make finished product after stirring.
Outstanding velvet of coating of the present invention and stereoscopic sensation, pollution-free, harmless, no incendivity, film water-fast, resistance to acids and bases is strong, makes facing produce effect like senior imitative fine hair, adjustablely allot tens kinds of soft tones, the scrap glass microballon of product utilization flyash glasswork, favourable utilization of waste material.
Embodiment
The following examples can make those skilled in the art more fully understand the present invention, but do not limit the present invention in any way.
Embodiment 1
Adding the talcum powder of 10 weight parts, the fine particle calcium carbonate of 15 weight parts, the defoamer of 1.5 weight parts and the ammoniacal liquor of 1 weight part in the water of 20 weight parts successively adds in the stirrer, after the high-speed stirring, add the benzene emulsion of 25 weight parts, the film coalescence aid of 2 weight parts, the powder coal ash glass-microballons of 25 weight parts and the blue mill base of 0.5 flyash more successively, promptly make finished product after stirring.
Its performance: viscosity 118KU; Package stability (50 ℃/7 days) viscosity; Thixotropy index 3.75; Fineness 45um (GB/T1724-79); Water-resistance property of coating 96hr (GB/T1733-93); Abrasion resistance 2000 times (GB9266-88).
Embodiment 2
Adding the talcum powder of 10 weight parts, the fine particle calcium carbonate of 10 weight parts, the defoamer of 1.3 weight parts and the ammoniacal liquor of 2 weight parts in the water of 20 weight parts successively adds in the stirrer, after the high-speed stirring, add the benzene emulsion of 30 weight parts, the film coalescence aid of 1.5 weight parts, the powder coal ash glass-microballons of 25 weight parts and the red mill base of 0.2 flyash more successively, promptly make finished product after stirring.
Its performance: viscosity 118KU; Package stability (50 ℃/7 days) viscosity; Thixotropy index 3.75; Fineness 45um (GB/T1724-79); Water-resistance property of coating 96hr (GB/T1733-93); Abrasion resistance 2000 times (GB9266-88).
Embodiment 3
Adding the talcum powder of 10 weight parts, the fine particle calcium carbonate of 10 weight parts, the defoamer of 1 weight part and the ammoniacal liquor of 1.5 weight parts in the water of 35 weight parts successively adds in the stirrer, after the high-speed stirring, add the benzene emulsion of 20 weight parts, the film coalescence aid of 2 weight parts, the powder coal ash glass-microballons of 20 weight parts and the yellow mill base of 0.5 flyash more successively, promptly make finished product after stirring.
Its performance: viscosity 118KU; Package stability (50 ℃/7 days) viscosity; Thixotropy index 3.75; Fineness 45um (GB/T1724-79); Water-resistance property of coating 96hr (GB/T1733-93); Abrasion resistance 2000 times (GB9266-88).
Claims (2)
1. waterborne suede coating, in weight percentage, this system component is:
Benzene emulsion 20～30%
Water 20～40%
Talcum powder 10～15%
Fine particle calcium carbonate 10～20%
Film coalescence aid 1.5～2%
Glass microballon 20～30%
Mill base 0.1～0.5%
Defoamer 1～2%
Ammoniacal liquor 1～2%
Described film coalescence aid is selected from ethylene glycol ethyl ether or butyl glycol ether;
Described defoamer is selected from tributyl phosphate or water-based silicone oil.
2. method for preparing waterborne suede coating as claimed in claim 1 may further comprise the steps:
Successively water, talcum powder, fine particle calcium carbonate, defoamer and ammoniacal liquor are added in the stirrer by a certain percentage, after the high-speed stirring, add benzene emulsion, film coalescence aid, glass microballon and mill base more successively, promptly make finished product after stirring.